DE1469111C - Process for the production of hochfe most thread from crystalline polyolefins - Google Patents

Process for the production of hochfe most thread from crystalline polyolefins

Info

Publication number
DE1469111C
DE1469111C DE1469111C DE 1469111 C DE1469111 C DE 1469111C DE 1469111 C DE1469111 C DE 1469111C
Authority
DE
Germany
Prior art keywords
stretching
threads
heated
spinneret
polyolefins
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
Other languages
German (de)
Inventor
Gigh Del Mauro Emanuele Mailand Italo (Italien) DOIf
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Montedison SpA
Original Assignee
Montecatini Edison SpA
Publication date

Description

Die Erfindung bezieht sich auf ein Verfahren zur Herstellung von Mono- und Plurifilen aus kristallinen Olefinpolymeren und insbesondere aus mit stereospezifischen Katalysatoren hergestelltem Polypropylen nach dem Schmelzspinnverfahren.The invention relates to a process for the production of mono- and plurifiles from crystalline ones Olefin polymers and in particular from polypropylene made with stereospecific catalysts according to the melt spinning process.

In früheren Vorschlägen ist die Herstellung von Mono- und Plurifilen durch Auspressen von Olefinpolymeren, insbesondere Polypropylen, im geschmolzenen Zustand bereits beschrieben. Die nach den bekannten Verfahren erhaltenen Mono- und Plurifile besitzen bereits eine beträchtliche Zugfestigkeit, die jedoch im allgemeinen nicht über 6 bis 7 g/den liegt.In previous proposals, the production of mono- and plurifiles by extrusion of olefin polymers, in particular polypropylene, already described in the molten state. The ones after the known Process obtained mono- and plurifile already have a considerable tensile strength, but that generally does not exceed 6 to 7 g / den.

Aufgabe der vorliegenden Erfindung war es nun, Polyolefinfäden mit einer noch höheren Zugfestigkeit zu erzeugen.The object of the present invention was now to provide polyolefin threads with an even higher tensile strength to create.

Gegenstand der Erfindung ist ein Verfahren zur Herstellung von hochfesten Fäden auf der Basis von kristallinen Polyolefinen, die gegebenenfalls Färbemodifikatoren, Stabilisatoren, Mattierungsmittel, Pigmente oder Farbstoffe enthalten, durch Schmelzspinnen und anschTTeßendes Verstrecken, das dadurch gekennzeichnet ist, daß man die aus der Düse austretenden Fäden durch eine unmittelbar hinter der Spinndüse angeordnete, auf Temperaturen im Bereich zwischen 130 bis 300° C erhitzte rohrförmige Vorrichtung, deren Durchmesser 2 bis 5 cm größer als der der Spinndüse und die 2 cm bis 1 m lang ist, leitet, danach . mit Streckverhältnissen zwischen 1:2 und 1:10 bei Temperaturen zwischen 80 und 150°C in mit Heißluft,· Dampf oder einem ähnlichen Medium beheizten Streckvorrichtungen oder über eine erhitzte Platte verstreckt und im Falle der Verwendung von Färbemodifikatoren enthaltenden Polyolefinen die Fäden gegebenenfalls vor oder nach dem Verstrecken mit'The invention relates to a process for the production of high-strength threads based on crystalline polyolefins, optionally color modifiers, stabilizers, matting agents, pigments or contain dyes, through melt spinning and subsequent stretching, which thereby is characterized in that the emerging from the nozzle threads through an immediately behind the Spinneret arranged tubular device heated to temperatures in the range between 130 and 300 ° C, whose diameter is 2 to 5 cm larger than that of the spinneret and which is 2 cm to 1 m long, then leads . with stretching ratios between 1: 2 and 1:10 at temperatures between 80 and 150 ° C in hot air, Steam or similar medium heated stretchers or heated platen stretched and, in the case of the use of polyolefins containing color modifiers, the threads if necessary before or after stretching with '

ίο Formaldehyd, Isocyanaten oder Diepoxyverbindungen behandelt. ._ ■ > .ίο formaldehyde, isocyanates or diepoxy compounds treated. ._ ■>.

Das erfindungsgemäße Verfahren kann sowohl auf Polyolefine allein, als auch auf Mischungen von Polyolefinen mit Zusatzstoffen, wie Färbemodifikatoren, Stabilisatoren, Mattierungsmittel, Pigmente oder Farbstoffe, angewendet werden.The process according to the invention can be used both on polyolefins alone and on mixtures of polyolefins with additives such as color modifiers, stabilizers, matting agents, pigments or dyes, be applied.

Vorzugsweise verwendet man als kristallines Polyolefin im wesentlichen isotaktisches Polypropylen mit einer Grenzviskosität zwischen 2 und-5.It is preferred to use essentially isotactic polypropylene as the crystalline polyolefin an intrinsic viscosity between 2 and -5.

Als Färbemodifikatoren werden vorzugsweise durch Kondensation von Epichlorhydrin mit Aminen erhaltene basische Stickstoffverbindungen verwendet, während als Stabilisator eine aus 0,02 bis 2 Gewichtsprozent, bezogen auf das Polymere, eines aliphatischen Thioesters, einem DialkylphenolsulfidColor modifiers are preferably obtained by condensation of epichlorohydrin with amines basic nitrogen compounds are used, while a stabilizer from 0.02 to 2 percent by weight, based on the polymer, an aliphatic thioester, a dialkylphenol sulfide

Tabelletable

Zusammensetzung der MischungComposition of the mixture

Beispiel 1example 1 Beispiel 2Example 2

a) Polypropylen %a) polypropylene%

Grenzviskosität (bestimmt in Tetrahydronaphthalin bei 130°C) Limiting viscosity (determined in tetrahydronaphthalene at 130 ° C)

Aschegehalt Ash content

Rückstand nach Heptanextraktion Residue after heptane extraction

b) Calciumstearat % b) calcium stearate%

c) Stabilisator %c) stabilizer%

Laurylthiodipropionat Lauryl thiodipropionate

4,4'-Thio-bis-3-tert. butyl-metacresol 4,4'-thio-bis-3-tert. butyl metacresol

Spinnbedingungen:Spinning Conditions:

Schneckentemperatur Screw temperature

Spinnkopftemperatur Spinning head temperature

Spinndüsentemperatur Spinneret temperature

Spinndüsentyp ..... Spinneret type .....

Temperatur der erhitzten rohrförmigen Vorrichtung unterhalb der Spinndüse Temperature of the heated tubular device below the spinneret

Maximaldruck (kg/cm2) Maximum pressure (kg / cm 2 )

Aufwickelgeschwindigkeit (m/Min.) Winding speed (m / min.)

Streckbedingungen:Stretching conditions:

Temperatur temperature

Medium medium

Streckverhältnis Stretch ratio

Eigenschaften der verstreckten Faser:Properties of the drawn fiber:

Zugfestigkeit (g/den) Tensile strength (g / den)

' Dehnung (%) ' Strain (%)

3,003.00 2,502.50 0,01%0.01% 0,02%0.02% 94,00%94.00% 94,50A94.5 0 A 0,30.3 0,30.3 0,60.6 0,60.6 0,20.2 0,20.2 230° C230 ° C 230° C230 ° C 235 °C235 ° C 230° C230 ° C 285° C285 ° C 270° C270 ° C 40/0,8-16mm40 / 0.8-16mm 40/0,8· 16 mm40 / 0.8 x 16 mm 160° C160 ° C 140°C140 ° C 3030th 2525th 600600 600600 130°C130 ° C 130°C130 ° C Dampfsteam Dampfsteam 1:8,31: 8.3 1:8,51: 8.5 99 8,88.8 1818th 2020th

3 43 4

und Calciumstearat bestehendes Gemisch bevorzugt einem Schmelzpunkt von 17O0C, einem spezifischenand calcium stearate consisting mixture preferably a melting point of 17O 0 C, a specific

wird. Gewicht von 0,915 und einer Kristallinität, bestimmtwill. Weight of 0.915 and a crystallinity

Nach dem Verstrecken können die Fäden thermi- durch Röntgenuntersuchung, von 50% werden inAfter stretching, the threads can be thermally through X-ray examination, from 50% in

sehen Formstabilisierungsbehandlungen unter Bedin- einem Henschel-Mischer mit 30 g Calciumstearat,see shape stabilization treatments under conditions - a Henschel mixer with 30 g calcium stearate,

gungen einer freien oder gehinderten Schrumpfung 5 60 g Laurylthiodipropionat und 20 g 4,4'-Thio-bis-free or hindered shrinkage 5 60 g lauryl thiodipropionate and 20 g 4,4'-thio-bis-

sowie üblichen Endbehandlungen unterworfen werden. 3-tert. butyl-metacresol gemischt. Anschließend wirdas well as the usual final treatments. 3-tert. butyl metacresol mixed. Then will

Auf die aus Mischungen von Polyolefinen mit Färbe- das Gemisch in einem Werner-Extruder bei 210° C modifikatoren erhaltenen Fäden kann man außerdem granuliert und das Granulat in einer Schmelzspinnvor oder nach dem Verstrecken beispielsweise Form- vorrichtung bei einer Schneckentemperatur von 230°C, aldehyd, Diisocyanate oder Diepoxy verbindungen ein- io einer Spinnkopftemperatur von 235° C und einer Spinnwirken lassen, düsentemperatur von 285° C schmelzgesponnen. DieOn the mixture of polyolefins with dye the mixture in a Werner extruder at 210 ° C The threads obtained can also be granulated and the granules in a melt spinning process or after stretching, for example a molding device at a screw temperature of 230 ° C, Aldehyde, diisocyanate or diepoxy compounds have a spinning head temperature of 235 ° C and a spinning action let, nozzle temperature of 285 ° C melt-spun. the

Die Erfindung wird in dem folgenden Beispiel 1 verwendete Spinndüse hatte 40 Bohrungen, die jeweilsThe invention is used in the following Example 1 spinneret had 40 bores, each

sowie den weiteren tabellarisch zusammengestellten einen Durchmesser von 0,8 mm und eine Länge vonas well as the other tabular compiled a diameter of 0.8 mm and a length of

Beispielen erläutert. Beispiel 6 zeigt die kritische 16 mm aufwiesen. Die Temperatur des erhitztenExamples explained. Example 6 shows the critical 16 mm. The temperature of the heated

Grenze der erfindungsgemäßen Behandlung. Über- 15 Rohres unterhalb der Spinndüse betrug 160° C. Aus-Limit of the treatment according to the invention. Above the tube below the spinneret was 160 ° C.

raschenderweise wurde festgestellt, daß eine Behänd- gepreßt wurde mit einem Maximaldruck von 30 kg/cm2;Surprisingly, it was found that a manual press was carried out with a maximum pressure of 30 kg / cm 2 ;

lung unterhalb 130° C in merklicher Weise die Zug- die Aufwickelgeschwindigkeit betrug 600 m/Min. DasDevelopment below 130 ° C in a noticeable way the pulling speed was 600 m / min. The

festigkeit der Polypropylenfasern herabsetzt. versponnene Garn wurde dann bei 130°C in Gegenwart von Dampf mit einem Streckverhältnis von 1:8,3reduces the strength of the polypropylene fibers. Spun yarn was then spun at 130 ° C in the presence of steam with a draw ratio of 1: 8.3

B e i s ρ i e 1 1 ao verstreckt. Das verstreckte Garn hatte folgende mechanische Eigenschaften:B is ρ ie 1 1 ao stretched. The drawn yarn had the following mechanical properties:

890 g kristallines Polypropylen einer Grenzviskosi-890 g of crystalline polypropylene of a limiting viscosity

tat, bestimmt in Tetrahydronaphthalin bei 135°C, llter 5,04 dendid, determined in tetrahydronaphthalene at 135 ° C, age 5.04 den

von 3,00, einem Aschegehalt von 0,01 %, einem Rück- Zugfestigkeit 9 g/denof 3.00, an ash content of 0.01%, a back tensile strength of 9 g / den

stand nach der Extraktion mit n-Heptan von 94 %, 25 Dehnung 18 %·after extraction with n-heptane of 94%, 25 elongation 18%

Beispiel 3Example 3 Beispiel 4Example 4 Beispiel 5Example 5 Beispiel 6
(Vergleich)
Example 6
(Comparison)
3,003.00 3,003.00 2,002.00 3,003.00 0,01 »/00.01 »/ 0 0,04%0.04% 0,02%0.02% 0,01%0.01% 94,00%94.00% 95,6%95.6% 96,1%96.1% 94,00%94.00% 0,30.3 0,30.3 0,30.3 0,30.3 0,50.5 0,60.6 0,50.5 0,60.6 0,20.2 0,20.2 0,20.2 0,20.2 230°C230 ° C 24O0C24O 0 C 230° C230 ° C 230° C230 ° C 23O0C23O 0 C 240° C240 ° C 240° C240 ° C 235°C235 ° C 25O0C250 0 C 2950C295 0 C 285° C285 ° C 285°C285 ° C 50/1,3 · 26 mm50 / 1.3 x 26 mm 20/0,4 · 8 mm20 / 0.4 x 8 mm 20/0,4-0,8 mm20 / 0.4-0.8 mm 40/0,8· 16 mm40 / 0.8 x 16 mm 130°C130 ° C 280° C280 ° C 270° C270 ° C HO0CHO 0 C 3030th 4545 3535 3030th 8080 240240 320320 600600 150°C150 ° C 130°C130 ° C 135°C135 ° C 130°C130 ° C Dampfsteam WarmluftWarm air WarmluftWarm air Dampfsteam 1:101:10 1:6,281: 6.28 1:101:10 1:8,31: 8.3 9,59.5 14,514.5 11,511.5 5,85.8 1212th 2323 2020th 1414th

Claims (3)

Patentansprüche :Patent claims: 1. Verfahren zur Herstellung von hochfesten Fäden auf der Basis von kristallinen Polyolefinen, die gegebenenfalls Färbemodifikatoren, Stabilisatoren, Mattierungsmittel, Pigmente oder Färbstoffe enthalten, durch Schmelzspinnen und anschließendes Verstrecken, dadurch gekennzeichnet, daß man die aus der Düse austretenden Fäden durch eine unmittelbar hinter der Spinndüse angeordnete, auf Temperaturen im Bereich zwischen 130 bis 3000C erhitzte rohrförmige Vorrichtung, deren Durchmesser 2 bis 5 cm größer als der der Spinndüse und die 2 cm bis 1 m lang ist, leitet, danach mit Streckverhältnissen zwischen 1:2 und 1:10 bei Temperaturen zwischen 80 und 1500C in mit Heißluft, Dampf oder einem ähnlichen Medium beheizten Streckvorrichtungen oder über eine erhitzte Platte verstreckt und im Falle der Verwendung von Färbemodifikatoren enthaltenden Polyolefinen die Fäden gegebenenfalls vor oder nach dem Verstrecken mit Formaldehyd, Isocyanaten oder Diepoxyverbindungen behandelt.1. A process for the production of high-strength threads based on crystalline polyolefins, which optionally contain color modifiers, stabilizers, matting agents, pigments or dyes, by melt spinning and subsequent drawing, characterized in that the threads emerging from the nozzle through a directly behind the Tubular device arranged in a spinneret and heated to temperatures in the range between 130 to 300 0 C, the diameter of which is 2 to 5 cm larger than that of the spinneret and 2 cm to 1 m long, conducts, then with stretching ratios between 1: 2 and 1: 10 stretched at temperatures between 80 and 150 0 C in stretching devices heated with hot air, steam or a similar medium or over a heated plate and, in the case of the use of polyolefins containing color modifiers, the threads optionally treated with formaldehyde, isocyanates or diepoxy compounds before or after stretching . 2. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß man als kristallines Polyolefin im wesentlichen isotaktisches Polypropylen mit einer Grenzviskosität zwischen 2 und 5, bestimmt in Tetrahydronaphthalin bei 135° C, verwendet.2. The method according to claim 1, characterized in that the crystalline polyolefin is im essential isotactic polypropylene with an intrinsic viscosity between 2 and 5, determined in Tetrahydronaphthalene at 135 ° C. 3. Verfahren nach Anspruch 1 und 2, dadurch gekennzeichnet, daß man Polymerisate verwendet, die als Stabilisator Gemische aus 0,02 % eines aliphatischen Thioesters, einem Dialkylphenolsulfid und Calciumstearat enthalten.3. The method according to claim 1 and 2, characterized in that one uses polymers, as a stabilizer, mixtures of 0.02% of an aliphatic thioester, a dialkylphenol sulfide and calcium stearate.

Family

ID=