DE1266983B - Contact material - Google Patents
Contact materialInfo
- Publication number
- DE1266983B DE1266983B DE1957S0054576 DES0054576A DE1266983B DE 1266983 B DE1266983 B DE 1266983B DE 1957S0054576 DE1957S0054576 DE 1957S0054576 DE S0054576 A DES0054576 A DE S0054576A DE 1266983 B DE1266983 B DE 1266983B
- Authority
- DE
- Germany
- Prior art keywords
- contact
- contact material
- contacts
- lead
- copper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Description
DEUTSCHESGERMAN
PATENTAMTPATENT OFFICE
AUSLEGESCHRIFTEDITORIAL
Int. Cl.:Int. Cl .:
Nummer:
Aktenzeichen:
Anmeldetag:
Auslegetag:Number:
File number:
Registration date:
Display day:
C 22cC 22c
Deutsche Kl.: 40 b -9/00 German class: 40 b -9/00
1266 983
S 54576 VI a/40 b 1. August 1957 25. April 19681266 983
S 54576 VI a / 40 b August 1, 1957 April 25, 1968
Bei Selbstschaltern, insbesondere bei Leitungsschutzschaltern, die aus den bisher bekannten Kontakt-Werkstoffen hergestellt sind, tritt bei Kurzschlußabschaltungen oder, wenn die geöffneten Kontakte bei Kurzschluß geschlossen werden, oft ein Verschweißen der Kontakte auf. Dieses kann zu Funktionsstörungen der Schalter führen.In the case of automatic switches, especially in the case of miniature circuit breakers, those made from the previously known contact materials are established, occurs in the event of short-circuit shutdowns or when the contacts are open are closed in the event of a short circuit, often a welding of the contacts. This can lead to malfunctions the switch lead.
Es sind gesinterte Kontakte aus einem binären System, das in flüssigem Zustand mischbar ist, nämlich eine Chrom-Zinn-Legierung mit einem Zinn- ίο gehalt von 1 bis 10°/0, bekannt und ferner Dreistofflegierungen, bestehend aus 1 bis lO°/o Kobalt, 1 bis 10°/0 Kadmium, Rest Kupfer, mit Löslichkeit der drei Komponenten ineinander sowie Verbindungsbildung zwischen den Komponenten. There are sintered contacts from a binary system that is miscible in the liquid state, namely a chromium-tin alloy ίο content of 1 to 10 ° / 0, known and further ternary alloys, consisting of 1 to lO ° / o with a tin cobalt, 1 to 10 ° / 0 cadmium, the remainder being copper, interlocking with solubility of the three components, and compound formation between the components.
Gegenstand der Erfindung ist ein Kontaktwerkstoff aus mindestens zwei Metallkomponenten — ausgenommen gemäß Patent 1087 813 hergestellte Kupfer-Blei-Verbundwerkstoffe —, bei dem unter den obengenannten Bedingungen kein Verschweißen eintritt. Er eignet sich daher hervorragend für Selbstschalter, insbesondere für Leitungsschutzschalter. Beim Kontaktwerkstoff gemäß der Erfindung weisen mindestens zwei Metallkomponenten im flüssigen Zustand eine beschränkte Mischbarkeit auf, und eine von diesen, nämlich Blei (Pb), Thallium (Tl), Wismut (Bi), Indium (In), Zinn (Sn) oder Kadmium (Cd), weist im Temperaturbereich zwischen 200 und 4000C eine KontaktwerkstoffThe subject of the invention is a contact material made of at least two metal components - with the exception of copper-lead composites produced in accordance with patent 1087 813 - in which no welding occurs under the above-mentioned conditions. It is therefore ideal for automatic switches, especially for miniature circuit breakers. In the contact material according to the invention, at least two metal components have limited miscibility in the liquid state, and one of these, namely lead (Pb), thallium (Tl), bismuth (Bi), indium (In), tin (Sn) or cadmium ( Cd), has a contact material in the temperature range between 200 and 400 ° C
Anmelder:Applicant:
Siemens Aktiengesellschaft, Berlin und München, 8520 Erlangen, Werner-von-Siemens-Str. 50Siemens Aktiengesellschaft, Berlin and Munich, 8520 Erlangen, Werner-von-Siemens-Str. 50
Als Erfinder benannt:Named as inventor:
Dr. techn. habil. Horst Schreiner, 8500 Nürnberg; Helmut Iwan, 8400 RegensburgDr. techn. habil. Horst Schreiner, 8500 Nuremberg; Helmut Iwan, 8400 Regensburg
flüssige Phase auf, und der Anteil dieser Metallkomponente ist auf 5 bis 20%, vorzugsweise auf 10%, bemessen, und zwar in folgenden Kombinationen: liquid phase, and the proportion of this metal component is 5 to 20%, preferably 10%, measured in the following combinations:
Pb mit Al, Fe, Co, Ni und/oder Cu, Tl mit Al, Fe, Co, Ni und/oder Cu,
Bi mit Al, Fe und/oder Co,
In mit Al,
Sn mit Co,
Cd mit Al.Pb with Al, Fe, Co, Ni and / or Cu, Tl with Al, Fe, Co, Ni and / or Cu, Bi with Al, Fe and / or Co,
In with Al,
Sn with Co,
Cd with Al.
Im einzelnen sind für diese Kombinationsmöglichkeiten nachfolgend in Klammern die Schmelzpunkte der betreffenden Metalle angegeben.In detail, the melting points for these possible combinations are given below in brackets of the metals concerned.
flüssiger Phase
zwischen 200 und 4000CComponent with
liquid phase
between 200 and 400 0 C
Phase zwischen 200 und 4000C
KomponenteWith the component
Phase between 200 and 400 0 C
component
(1440) (1452)Co Ni
(1440) (1452)
(327) • Pb
(327)
(660)Al
(660)
(1530)Fe
(1530)
(1440) (1452)Co Ni
(1440) (1452)
(1083)Cu
(1083)
(302) Tl
(302)
(660)Al
(660)
(1530)Fe
(1530)
(1440)Co
(1440)
(1083)Cu
(1083)
(271)Bi
(271)
(660)Al
(660)
(1530)Fe
(1530)
(158) In
(158)
(660)Al
(660)
(231)Sn
(231)
(1440)Co
(1440)
(321) CD
(321)
(660)Al
(660)
Die hervorragende Eignung des Kontaktwerkstoffes flüssige Phase bis zu verhältnismäßig tiefen Tempe-The excellent suitability of the contact material liquid phase up to relatively low temperatures
gemäß der Erfindung für die oben angegebenen 50 raturen im Engegebiet der Kontakte erhalten bleibt,according to the invention for the above 50 temperatures in the vicinity of the contacts is maintained,
Anwendungszwecke beruht darauf, daß die bei der so daß während einer verhältnismäßig langen ZeitApplications is based on the fact that the so that during a relatively long time
Strombelastung des Kontaktwerkstoffes entstehende die Kontakte mit kleiner öffnungskraft wieder ge-Current load of the contact material, the contacts are restored with a small opening force
809 540/351809 540/351
trennt werden können. Diese Wirkung wird bereits erzielt, wenn nur einer der Kontakte aus dem Werkstoff gemäß der Erfindung und der Gegenkontakt aus einem anderen Kontaktmaterial, z. B. aus Kupfer, besteht. Entsprechend genügt es bei Kontakten mit Doppelunterbrechungen, wenn entweder die bewegliche Brücke oder die beiden Festkontakte aus dem Kontaktwerkstoff gemäß der Erfindung hergestellt sind.can be separated. This effect is already achieved if only one of the contacts is made of the material according to the invention and the mating contact made of a different contact material, e.g. B. made of copper, consists. Accordingly, in the case of contacts with double interruptions, it is sufficient if either the movable one Bridge or the two fixed contacts made of the contact material according to the invention are.
Die Metallkomponente, die zwischen 200 und 400°C eine flüssige Phase aufweist, kann in der höher schmelzenden Komponente eingelagert sein; es kann aber auch der umgekehrte Fall vorliegen. In beiden Fällen handelt es sich um einen Einlagerungsverbundwerkstoff. Weiterhin ist es möglich, daß der Kontaktwerkstoff ein Durchdringungsverbundmaterial bildet, bei dem beide Komponenten zusammenhängende Gerüste bilden, die räumlich ineinandergeschoben sind.The metal component, which has a liquid phase between 200 and 400 ° C, can be in the higher-melting one Component to be stored; but it can also be the other way round. In both cases it is an embedding composite. It is also possible that the contact material forms an interpenetrating composite material in which both components are interconnected scaffolds form that are spatially nested.
Bei dem erfindungsgemäßen Kontaktwerkstoff kann, wenn z. B. Eisen als eine Komponente gewählt wird, die Blei-, Thallium- oder Wismutoberfläche von Eisenteilchen durchbrochen sein. Die wirksame Kontaktoberfläche wird also beispielsweise durch eine Blei-Eisen-Fläche gebildet. Ein solcher Werkstoff ist für gewisse Beanspruchungen brauchbar und äußerst preisgünstig, was auch für die Metalle Aluminium, Kobalt und Nickel gilt, wobei die letzten beiden Metalle insbesondere dann von technischem Interesse sind, wenn es darauf ankommt, Kontaktwerkstoffe mit höherer Härte (bezogen auf Kupfer) herzustellen.In the contact material according to the invention, if, for. B. Iron is chosen as a component, the lead, thallium or bismuth surface may be broken up by iron particles. The effective The contact surface is thus formed, for example, by a lead-iron surface. Such a material can be used for certain demands and is extremely inexpensive, which is also true for the metals aluminum, Cobalt and nickel applies, the last two metals in particular then being technical When it comes down to it, we are interested in contact materials with higher hardness (based on copper) to manufacture.
Die Vorteile solcher Kontakte sind aus der folgenden Tabelle für Kontakte auf Aluminiumbasis mit einem Gehalt von 5 % Blei» Thallium, Wismut, Indium oder Kadmium ersichtlich. Hierzu wurden von den Legierungen Al-Bi 95:5, Al-Pb 95:5 und Al-Cd 95:5 die Kontaktwiderstände im Neuzustand, der geschalteten Kontakte und nach dem öffnen von Schweißbrücken gemessen. Außerdem sind die Schweißstromgrenzen bei 3,5 kp Kontaktlast und die Öffnungskräfte gebildeter Schweißbrücken gemessen worden. Als Vergleich sind die entsprechenden Eigenschaften von Elektrolytkupfer- und Reinsilberkontakten angegeben. The benefits of such contacts are from the table below for aluminum-based contacts with a Content of 5% lead »thallium, bismuth, indium or Cadmium can be seen. For this purpose, the alloys Al-Bi 95: 5, Al-Pb 95: 5 and Al-Cd 95: 5 the contact resistances when new, the switched contacts and after the opening of welding bridges measured. In addition, the welding current limits at 3.5 kp contact load and the opening forces of the weld bridges formed were measured. The corresponding properties of electrolytic copper and pure silver contacts are given as a comparison.
im Neuzustand
mit Reibkomponente
Rk ■ ΙΟ5 (Ω)Contact resistance
in new condition
with friction component
Rk ■ ΙΟ 5 (Ω)
grenze J
(A)Welding current
limit J
(A)
nach dem Strom
durchgang
4 Perioden bei 50 Hz
Rk ■ ΙΟ5 (Ω)Contact resistance
after the stream
passage
4 periods at 50 Hz
Rk ■ ΙΟ 5 (Ω)
kraft P
(kp)Opening
by virtue of P
(kp)
nach dem Öffnen
der Kontakte
Rk · ΙΟ5 (Ω)Contact resistance
After opening
of contacts
Rk ΙΟ 5 (Ω)
Al-Pb 95: 5
Al—Cd 95: 5
E-Cu
AgAl-Bi 95: 5
Al-Pb 95: 5
Al-Cd 95: 5
Ecu
Ag
Minimal 5,2
Mittel 6,9
Maximal 20,0
Minimal 9,3
Mittel 12,5
Maximal 31,0
Minimal 12,0
Mittel 21,5
Maximal 8,0
Minimal 5,6
Mittel 6,7
Maximal 7,0
Minimal 4,4
Mittel 5,79.0 maximum
Minimum 5.2
Mean 6.9
Maximum of 20.0
Minimal 9.3
Medium 12.5
31.0 maximum
Minimum 12.0
Mean 21.5
8.0 maximum
Minimum 5.6
Medium 6.7
Maximum of 7.0
Minimal 4.4
Mean 5.7
6800
(3840)
3410
(2980)
2530
(5960)
5530
(7450)
7030(7240)
6800
(3840)
3410
(2980)
2530
(5960)
5530
(7450)
7030
5
11,1
7,8
5,3
6,5
15
6,8
8,5
4,4
3,2
3,7
2,1
1,8
2,020th
5
11.1
7.8
5.3
6.5
15th
6.8
8.5
4.4
3.2
3.7
2.1
1.8
2.0
0
0,008
3,1
0
1,9
3,0
0
0,86
0,7
0
0,13
3,3
0
0,870.05
0
0.008
3.1
0
1.9
3.0
0
0.86
0.7
0
0.13
3.3
0
0.87
9
12,2
65
14
30
70
13
28,3
59
9,6
22,1
3,0
1,9
2,218th
9
12.2
65
14th
30th
70
13th
28.3
59
9.6
22.1
3.0
1.9
2.2
Bei den in Klammern stehenden Schweißströmen traten Öffnungskräfte >3,5 kp auf.Opening forces occurred for the welding currents in brackets > 3.5 kp.
Somit liegen die Kontaktwiderstände der Kontakte im Neuzustand und nach dem Schalten in nicht zu aggressiver Atmosphäre in durchaus günstigen Grenzen. Die Schweißstromgrenzen der angegebenen Legierungen liegen auch gegenüber Ε-Kupfer recht günstig. Die Aluminiumlegierungen sind auf Grund der Schweißstrommessungen in nicht korrodierender Atmosphäre als Kontaktstoffe geeignet. Auch in korrodierender Atmosphäre sind diese Legierungen bei geeigneter konstruktiver Gestaltung der Schaltgeräte und bei entsprechender Reibkomponente beim Schließen der Kontakte geeignet. Bei dem Reibeschließen werden die Oberflächenschichten zerstört und ein metallischer Kontakt gewährleistet. Der höhere Kontaktwiderstand erfordert eine höhere Kontaktlast, um der für ein Schaltgerät tragbaren Erwärmung Rechnung zu tragen. So sind Kontakte aus erfindungsgemäßen Aluminiumlegierungen insbesondere auch für häufig schaltende Schaltgeräte' die in korrodierender Atmosphäre arbeiten müssen, gut geeignet.Thus, the contact resistances of the contacts are not closed when they are new and after switching to aggressive atmosphere within reasonable limits. The welding current limits of the specified Alloys are also quite cheap compared to Ε-copper. The aluminum alloys are due of welding current measurements in a non-corrosive atmosphere are suitable as contact materials. Also in These alloys are in a corrosive atmosphere with a suitable structural design of the switchgear and suitable with a corresponding friction component when closing the contacts. At the friction closing the surface layers are destroyed and a metallic contact is guaranteed. Of the higher contact resistance requires a higher contact load in order to be portable for a switching device Warming to take into account. Thus, contacts made from aluminum alloys according to the invention are in particular also for frequently switching switching devices that have to work in a corrosive atmosphere, well suited.
Die Herstellung des Kontaktwerkstoffes gemäß der Erfindung kann auf dem Schmelzwege oder auf dem Sinterwege erfolgen. Das letztere Verfahren ist deshalb besonders vorteilhaft, weil der Kontaktwerkstoff gemäß der Erfindung im kalten Zustand schwer verformbar ist; das Sinterverfahren ermöglicht die Herstellung von Fertigformteilen. Ein weiterer Vorteil des Kontaktwerkstoffes gemäß der Erfindung ist seine Oxydationsbeständigkeit. Diese beruht auf dem verhältnismäßig hohen Dampfdruck der niedrigschmelzenden Metallkomponente, der zur Folge hat, daß der sich beim Auftreten der flüssigen Phase bildende Metalldampf die Kontaktfläche vor Oxydation schützt. Die Kontaktoberflächen behalten daher nach schweren Belastungen ein metallisch glänzendes Aussehen. Die Verhinderung der Bildung von Oberflächenoxydschichten ist deshalbThe production of the contact material according to the invention can be on the melting route or on the sinter way. The latter method is particularly advantageous because the contact material according to the invention is difficult to deform when cold; the sintering process enables Manufacture of finished molded parts. Another advantage of the contact material according to of the invention is its resistance to oxidation. This is based on the relatively high vapor pressure the low-melting metal component, which has the consequence that when the Metal vapor forming a liquid phase protects the contact surface from oxidation. The contact surfaces therefore retain a shiny metallic appearance after heavy loads. The prevention the formation of surface oxide layers is therefore
besonders wichtig, weil dadurch unerwünschte Vergrößerungen des Übergangswiderstandes im Kontaktengegebiet vermieden werden.especially important because this causes undesirable increases in the contact resistance in the contact area be avoided.
Claims (2)
In mit Al,
Sn mit Co,
Cd mit Al.Pb with Al, Fe, Co, Ni and / or Cu, Tl with Al, Fe, Co, Ni and / or Cu, Bi with Al, Fe and / or Co,
In with Al,
Sn with Co,
Cd with Al.