DE10200131A1 - Bending-elastic glass / polymer composites - Google Patents

Bending-elastic glass / polymer composites

Info

Publication number
DE10200131A1
DE10200131A1 DE10200131A DE10200131A DE10200131A1 DE 10200131 A1 DE10200131 A1 DE 10200131A1 DE 10200131 A DE10200131 A DE 10200131A DE 10200131 A DE10200131 A DE 10200131A DE 10200131 A1 DE10200131 A1 DE 10200131A1
Authority
DE
Germany
Prior art keywords
glass
polymer
composites
composites according
layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE10200131A
Other languages
German (de)
Inventor
Rainer Blum
Reinhold Schwalm
Ralph Mueller
Jean-Claude Heilig
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BASF SE
Original Assignee
BASF SE
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BASF SE filed Critical BASF SE
Priority to DE10200131A priority Critical patent/DE10200131A1/en
Priority to PCT/EP2003/000001 priority patent/WO2003055676A1/en
Priority to AU2003235725A priority patent/AU2003235725A1/en
Publication of DE10200131A1 publication Critical patent/DE10200131A1/en
Withdrawn legal-status Critical Current

Abstract

The invention relates to flat, flexible composites. Said composites are characterised in that they contain at least one glass layer, which is coated at least on one side with a polymer, said glass layer having a thickness of between 5 and 150 mu m.

Description

Die Erfindung betrifft flächige biegeelastische Verbunde, dadurch gekennzeichnet, dass sie zumindest eine Glasschicht enthalten, welche auf zumindest einer Seite mit einem Polymer beschichtet ist, und die Glasschicht eine Dicke von 5 bis 250 µm aufweist. The invention relates to flat, flexurally elastic composites, thereby characterized that they contain at least one layer of glass, which is coated on at least one side with a polymer is, and the glass layer has a thickness of 5 to 250 microns.

Weiterhin betrifft die Erfindung Anzeigensysteme, welche die vorstehenden Verbunde enthalten. Furthermore, the invention relates to display systems which above compounds included.

Glas-/Polymerverbunde sind bei splittersicheren Verglasungen bekannt. Derartige Verglasungen weisen Polymerschichten zwischen Glasplatten auf; diese sind mit den Glasplatten haftklebrig verbunden. Glass / polymer composites are used in shatterproof glazing known. Such glazings have polymer layers between them Glass plates on; these are tacky with the glass plates connected.

Weiter ist bekannt, Polymerbeschichtungen zum Schutz auf Glas aufzubringen. It is also known to use polymer coatings for protection on glass applied.

DE-A-30 18 085 beschreibt in diesem Zusammenhang die Verwendung von polymeren Haftkleberschichten zur Verbesserung der Haftung zwischen Glas und einer schützenden harten Polymerschicht. WO 93/11080, WO 90/06289 und WO 90/13523 offenbaren Überzugsmassen für Glasplatten oder Glasfasern auf Basis UV-reaktiver Verbindungen und Silanen als Haftvermittler. DE-A-30 18 085 describes the use in this context of polymer pressure sensitive adhesive layers to improve adhesion between glass and a protective hard polymer layer. WO 93/11080, WO 90/06289 and WO 90/13523 disclose Coating compounds for glass plates or glass fibers based on UV-reactive Compounds and silanes as adhesion promoters.

Gewünscht sind flächige Glas-/Polymerverbunde, welche eine hohe Dichtigkeit gegen Durchdringen von Gasen und Flüssigkeiten mit einer dauerhaften Biegeelastizität verbinden. Flat glass / polymer composites are desired, which have a high Tightness against penetration of gases and liquids with a permanent bending elasticity.

Demgemäss wurden die eingangs definierten Verbunde und Anzeigensysteme gefunden. Accordingly, the composites and Ad systems found.

Die flächigen biegeelastischen Verbunde enthalten zumindest eine Glasschicht mit einer Dicke von 5 bis 250 µm. Vorzugsweise ist die Dicke der Glasschicht maximal 150, insbesondere maximal 100 µm, insbesondere maximal 80 µm; die Dicke beträgt vorzugsweise mindestens 10 µm, insbesondere mindestens 20 µm. The flat, flexible, elastic composites contain at least one Glass layer with a thickness of 5 to 250 µm. Preferably the thickness of the glass layer a maximum of 150, in particular a maximum of 100 µm, in particular a maximum of 80 µm; the thickness is preferably at least 10 µm, especially at least 20 µm.

Die Verbunde können eine oder mehrerer, insbesondere ein oder zwei Glasschichten enthalten. Die Glasschichten des Verbundes können nur auf einer Seite mit einem Polymer beschichtet sein, vorzugsweise sind sie auf beiden Seiten mit dem Polymer beschichtet. The groups can one or more, in particular one or contain two layers of glass. The glass layers of the composite can only be coated with a polymer on one side, preferably they are on both sides with the polymer coated.

In einer besonderen Ausführungsform befindet sich zwischen Glas und Polymer ein Haftvermittler, um die Haftung der Polymerschicht zu verbessern. Unter Polymerschicht wird in dieser Anmeldung die Summe aus Polymerschicht und gegebenenfalls vorhandenem Haftkleber, bzw. Haftklebeschicht, verstanden, soweit sich aus dem jeweiligen Zusammenhang nichts anderes ergibt. In a special embodiment is between glass and polymer an adhesion promoter to ensure the adhesion of the polymer layer to improve. In this application, the Sum of the polymer layer and any present Pressure sensitive adhesive, or pressure sensitive adhesive layer, understood, as far as the nothing else results in the respective context.

Die einzelne Polymerschichten haben zusammen mit dem gegebenenfalls vorhandenen Haftvermittler vorzugsweise eine Dicke von 2 bis 500 µm, besonders bevorzugt von 5 bis 150, insbesondere 5 bis 100 µm und ganz besonders bevorzugt von 5 bis 50, insbesondere 5 bis 20 µm. The individual polymer layers together with the any bonding agent present, preferably a thickness of 2 up to 500 µm, particularly preferably from 5 to 150, in particular 5 to 100 µm and very particularly preferably from 5 to 50, in particular 5 to 20 µm.

Die Gesamtdicke des Verbundes beträgt vorzugsweise 10 bis 1000 µm; vorzugsweise ist der Verbund nicht dicker als 800, insbesondere nicht dicker als 600, besonders bevorzugt nicht dicker als 400 µm; vorzugsweise ist der Verbund nicht dünner als 20 und insbesondere nicht dünner als 50 µm. The total thickness of the composite is preferably 10 to 1000 microns; the composite is preferably not thicker than 800, in particular not thicker than 600, particularly preferably not thicker than 400 µm; preferably the composite is not thinner than 20 and in particular not thinner than 50 µm.

Bevorzugte Verbunde haben z. B. die nachstehende Struktur und Schichtabfolge a) oder b):

  • a) Pol.-Glas-Pol.
  • b) Pol.-Glas-Pol.-Glas-Pol.
  • c) Pol.-Glas-Haftkl.-Glas-Pol.
wobei Pol. für ein Polymerschicht, Haftkl. für eine Haftklebeschicht und Glas für eine Glasschicht stehen. Preferred networks have e.g. B. the following structure and layer sequence a) or b):
  • a) Pol. glass pole.
  • b) Pol.-Glas-Pol.-Glas-Pol.
  • c) Pol.-Glas-Haftkl.-Glas-Pol.
where Pol. for a polymer layer, Haftkl. stand for a layer of pressure-sensitive adhesive and glass for a layer of glass.

Die erfindungsgemäßen Verbunde sind biegeelastisch. Vorzugsweise ist die Biegeelastizität so groß ist, dass ein erfindungsgemäßer Verbund bei 21°C, 1 bar auf einen Radius von kleiner 30 cm, insbesondere kleiner 15 cm, besonders bevorzugt kleiner 10 cm, ganz besonders bevorzugt kleiner 5 cm und insbesondere kleiner 2 cm gebogen werden kann. The composites according to the invention are flexible. Preferably the bending elasticity is so great that an inventive Compound at 21 ° C, 1 bar to a radius of less than 30 cm, in particular less than 15 cm, particularly preferably less than 10 cm, entirely particularly preferably less than 5 cm and in particular less than 2 cm can be bent.

Zu den Materialien der einzelnen SchichtenThe materials of the individual layers

Als Glas kommen insbesondere alle üblichen anorganischen Gläser wie Silicatgläser, Boratgläser, Phosphatgläser und Quarz in Betracht. All common inorganic glasses come in particular as glass such as silicate glasses, borate glasses, phosphate glasses and quartz in Consideration.

Insbesondere kommen auch Gläser in Betracht, die in bekannter Weise vergütet sind, d. h. z. B. mit Metalloxiden beschichtet sind und so gegebenenfalls härter und/oder flexibler sind. In Betracht kommen auch Gläser, die unter einer sogenannten Vorspannung stehen, worunter eine Spannungsdifferenz zwischen dem Inneren und der Oberfläche der Glasschicht verstanden wird. Verfahren der Vergütung von Gläsern und der Erzeugung einer Vorspannung sind allgemein bekannt. In particular, glasses come into consideration which are known Are remunerated, d. H. z. B. are coated with metal oxides and so may be harder and / or more flexible. In consideration glasses also come under a so-called bias stand, including a voltage difference between the inside and the surface of the glass layer is understood. Procedure of Tempering of glasses and the generation of a tempering are well known.

In einer bevorzugten Ausführungsform wird die Haftung des Polymeren auf der Glasoberfläche durch Haftungsvermittler erhöht. In a preferred embodiment, the liability of the Polymers on the glass surface increased by adhesion promoters.

Die Haftungsvermittler befinden sich naturgemäß zwischen der Glas- und der Polymerschicht. The liability intermediaries are naturally between the Glass and the polymer layer.

Die Glasoberfläche kann dazu zunächst mit üblichen Haftungsvermittlern behandelt und anschließend mit dem Polymer beschichtet werden. Der Haftvermittler kann aber auch vorab dem Polymer zugesetzt werden; nach Beschichtung des Glases mit dem Polymeren reichert sich dann der Haftvermittler an der Grenzfläche Polymer/Glas an. To do this, the glass surface can first be coated with conventional ones Adhesion promoters treated and then coated with the polymer become. However, the adhesion promoter can also pre-polymer be added; after coating the glass with the polymer The adhesion promoter then accumulates at the interface Polymer / glass.

Als Haftungsvermittler kommen z. B. niedermolekulare Verbindungen in Betracht, welche chemisch oder physikalisch sowohl mit dem Glas als auch mit dem Polymer in Wechselwirkung treten. As liability brokers come e.g. B. low molecular weight compounds which chemically or physically both with the Glass as well as interact with the polymer.

Insbesondere kommen Verbindungen in Betracht, welche sich chemisch mit der Glasoberfläche über eine Si- oder Si-O-Gruppe verbinden. In particular, compounds are considered which are chemically with the glass surface via a Si or Si-O group connect.

Genannt seien insbesondere Haftvermittler mit Silan- oder Silikongruppen. Adhesion promoters with silane or Silicone groups.

Als Haftvermittler aufgeführt seien z. B. Alkoxyaminosilane, Alkoxyazidosilane, Polyamine, Poylsufosäuren, Polysufonium-, Polyphosphoniumverbindungen oder Azidosilane wie sie z. B. auch in der EP-A- 119011 oder US 4002651 beschrieben sind. As adhesion promoters are listed, for. B. alkoxyaminosilanes, Alkoxy azidosilanes, polyamines, polylsufo acids, polysufonium, Polyphosphonium compounds or azidosilanes such as z. B. also in EP-A-119011 or US 4002651.

Als Haftvermittler kommen auch Haftklebstoffe in Betracht. Pressure sensitive adhesives are also suitable as adhesion promoters.

Die Haftklebstoffe enthalten oder bestehen aus polymeren Bindemitteln, insbesondere Polymerlösungen oder besonders bevorzugt wässrigen Polymerdispersionen, vorzugsweise wässrigen Dispersionen von Polyacrylaten oder Styrol/Butadiencopolymerisaten. The pressure sensitive adhesives contain or consist of polymers Binders, especially polymer solutions or particularly preferred aqueous polymer dispersions, preferably aqueous Dispersions of polyacrylates or Styrene / Butadiencopolymerisaten.

Die polymeren Bindemittel haben vorzugsweise eine Glasübergangstemperatur von unter 20°C, insbesondere unter 0°C und besonders bevorzugt unter -20°C. The polymeric binders preferably have one Glass transition temperature below 20 ° C, especially below 0 ° C and especially preferably below -20 ° C.

In Betracht kommen auch Haftklebstoffe, die durch energiereiche Strahlung, insbesondere UV Strahlung, vernetzt sind. Derartige Haftklebstoffe besitzen zunächst eine geringe Viskosität und können leicht auf die Glasschicht aufgetragen werden, danach erfolgt die Vernetzung mit energiereichem Licht, insbesondere UV Licht, auf der Glasschicht, so dass sich der gewünschte Haftklebstoff ausbildet. Pressure sensitive adhesives that are caused by high-energy Radiation, especially UV radiation, are cross-linked. such Pressure sensitive adhesives initially have a low viscosity and can be easily applied to the glass layer afterwards networking takes place with high-energy light, in particular UV Light, on the layer of glass, so that the desired Forms pressure sensitive adhesive.

Die Glasübergangstemperatur wird durch Differentialthermoanalyse bestimmt. The glass transition temperature is determined by differential thermal analysis certainly.

Die Haftklebstoffe bilden vorzugsweise eine durchgehende Schicht auf der Glasoberfläche. Sie können dazu in einem separaten Beschichtungsvorgang durch übliche Methoden aufgebracht werden, soweit sie als Dispersion oder Lösung vorliegen, erfolgt nach dem Auftragen im allgemeinen eine Trocknung. The pressure sensitive adhesives preferably form a continuous layer on the glass surface. You can do this in a separate Coating process can be applied by conventional methods, insofar as they are present as a dispersion or solution, is carried out after Apply generally drying.

Vorzugsweise beträgt die Dicke dieser Haftklebeschicht nur wenige µm, im allgemeinen mindestens jedoch 0,2 insbesondere mindestens 0,5 und besonders bevorzugt mindestens 1 µm; die Dicke beträgt im allgemeinen maximal 10, bevorzugt maximal 7 und besonders bevorzugt maximal 5 µm. Die obigen Angaben über die Schichtdicke der Polymerschicht umfassen auch die Haftklebschicht als Teil der Polymerschicht. Die Haftklebeschicht kann auch direkt zwei Glasschichten verbinden, sie z. B. die obige Alternative c). The thickness of this pressure-sensitive adhesive layer is preferably only a few µm, but generally at least 0.2 in particular at least 0.5 and particularly preferably at least 1 µm; the thickness is in generally a maximum of 10, preferably a maximum of 7 and especially preferably at most 5 µm. The above information about the layer thickness of the Polymer layer also include the pressure sensitive adhesive layer as part of the Polymer layer. The pressure-sensitive adhesive layer can also have two Connect layers of glass, z. B. the above alternative c).

Zur PolymerschichtTo the polymer layer

Als Polymere in Betracht kommen durch radikalische Polymerisation erhältliche Polymere, Polykondensate, z. B. Polyester oder Polyaddukte, z. B. Polyurethane oder Polyimide oder Polyamide. Suitable polymers are radical polymerization available polymers, polycondensates, e.g. B. polyester or Polyadducts, e.g. B. polyurethanes or polyimides or polyamides.

Das Polymer kann als Polymerschmelze, Lösung oder Dispersion, als Polymerpulver oder bereits als Schicht vorgebildet, z. B. in Form einer Folie auf die Glasoberfläche aufgebracht werden. The polymer can be used as a polymer melt, solution or dispersion Polymer powder or already pre-formed as a layer, e.g. B. in the form a film can be applied to the glass surface.

Übliche Beschichtungsmethoden sind z. B. Rakeln, Koextrudieren oder Aufkaschieren von Polymerfolien oder sonstige bekannte Lackiertechniken, wie Sprühen etc. Common coating methods are e.g. B. doctor blades, coextruding or lamination of polymer films or other known Painting techniques such as spraying etc.

Im Fall einer Polymerfolie kann ein mitverwendeter Haftvermittler, z. B. auch ein Haftklebstoff, auf die Folie aufgebracht werden und die Folie dann auf das Glas geklebt werden. In the case of a polymer film, one that is used Adhesion promoter, e.g. B. also a pressure sensitive adhesive applied to the film and the film is then glued to the glass.

In einer besonderen Ausführungsform können auch zunächst die Aufbaukomponenten des Polymeren aufgebracht werden, z. B. radikalisch polymerisierbare Verbindungen (Monomere) oder daraus gebildete Prepolymere. Im Falle der Monomeren erfolgt dann die Polymerisation und Vernetzung, im Falle der Prepolymeren die Vernetzung auf der Glasoberfläche. Die Polymerisation bzw. Vernetzung kann durch Wärme, oder energiereiche Strahlung, z. B. NIR- Licht und/oder UV-Licht aktiviert werden. In a special embodiment, the Building components of the polymer are applied, for. B. Radically polymerizable compounds (monomers) or from them formed prepolymers. In the case of the monomers, the Polymerization and crosslinking, in the case of the prepolymers Networking on the glass surface. The polymerization or Networking can be achieved through heat or high-energy radiation, e.g. B. NIR Light and / or UV light can be activated.

Bei den radikalisch polymerisierten Polymeren, insbesondere auch bei solchen, die durch die vorstehende Polymerisation und/oder Vernetzung gebildet werden, kommen insbesondere auch solche in Betracht, die zu mehr als 60 Gew.-%, besonders bevorzugt zu mehr als 80 Gew.-% aus Monomeren mit mindestens einer Acryl- oder Methacrylgruppe bestehen (kurz Polyacrylate genannt). In the case of the radically polymerized polymers, in particular also in those caused by the above polymerization and / or Networking are formed, especially those come in Consider that more than 60 wt .-%, particularly preferably more than 80 wt .-% of monomers with at least one acrylic or Methacrylic group exist (shortly called polyacrylates).

Weiter sind auch Techniken bekannt, monomere Stoffe aus Gasphase oder Lösung auf ein Substrat aufzupolymerisieren. Techniques are also known, monomeric substances from the gas phase or polymerize solution onto a substrate.

Genannt seien z. B. Polymerfolien aus Polyolefinen, Polyestern, z. B. Polyethylentherephthalat. May be mentioned for. B. polymer films made of polyolefins, polyesters, z. B. polyethylene terephthalate.

Generell kommen als Polymere in Betracht, welche die üblichen Lacksysteme ausbilden, z. B. zweikomponentige Polyurethanlacke, aminoplastharzvernetzbare Einbrennlacke, säurehärtende Melaminharze, Epoxydharze, und UV-härtbare Lacke z. B. auf Basis monomerer und/oder oligomerer acrylisch ungesättigter Stoffe. Weiter sind für Anwendungen bei denen hohe Temperaturen und starke chemische Belastungen auftreten, Polyimide und Lösungen polyimidbildender Vorstufen von Bedeutung. In general, suitable polymers are those which have the usual Train paint systems, e.g. B. two-component polyurethane paints, Aminoplast resin-crosslinkable stoving lacquers, acid-curing Melamine resins, epoxy resins, and UV-curable paints e.g. B. based monomeric and / or oligomeric acrylic unsaturated substances. Further are for applications where high temperatures and strong chemical loads occur, polyimides and solutions polyimide-forming precursors of importance.

Bevorzugt sind Polymerschichten aus mit energiereicher, insbesondere UV-, Strahlung gehärteten Polymeren, insbesondere den oben beschriebenen Polyacrylaten; wobei die Härtung der Ausgangsverbindungen der Polyacrylate (Monomere, Oligomere und Prepolymere mit strahlungshärtbaren Gruppen, insbesondere Acryl, Methacrylgrupen) bevorzugt nach dem Beschichten mit Elektronenstrahlen oder durch UV Strahlung erfolgt. Preferred are polymer layers with high-energy, especially UV, radiation cured polymers, especially the polyacrylates described above; wherein the hardening of the Starting compounds of the polyacrylates (monomers, oligomers and Prepolymers with radiation-curable groups, especially acrylic, Methacrylic groups) preferably after coating with Electron beams or UV radiation.

In Betracht kommen z. B. auch Polymerschichten aus ausgelierten PVC-Plastisolen oder aus aromatischen Polyimiden. Consider z. B. also polymer layers from gelled PVC plastisols or from aromatic polyimides.

In Betracht kommen insbesondere auch Polymerschichten aus halogenhaltigen Polymeren, insbesondere Polyvinylidenchlorid. Polymer layers are particularly suitable halogen-containing polymers, especially polyvinylidene chloride.

Polymere, welche die Diffusion von Gasen, insbesondere Wasserdampf und Sauerstoff stark behindern oder verhindern sind besonders bevorzugt. Polymers that facilitate the diffusion of gases, in particular Water vapor and oxygen are severely obstructed or prevented particularly preferred.

Die Herstellung des erfindungsgemäßen Verbundes kann in einfacher Weise durch Beschichtung entsprechend dünner Glasplatten, aufgrund ihrer geringen Schichtdicke im folgenden Glasfolie genannt, mit dem Polymeren erfolgen. Enthält der Verbund mehrere Glasfolien, kann z. B. zunächst eine Glasfolie beidseitig beschichtet werden, danach kann auf einer der Polymer-beschichteten Seiten eine weitere Glasfolie aufgebracht werden, etc. The production of the composite according to the invention can be done in a simpler manner Way by coating correspondingly thin glass plates, called glass foil in the following due to its small layer thickness, done with the polymer. If the network contains several Glass foils, e.g. B. first coated a glass film on both sides can then be on one of the polymer-coated sides another glass film can be applied, etc.

Die Glasschichten können auch aus einzelnen flächigen Glaspartikeln aufgebaut sein, die sich zu einer Schicht zusammenfügen, wobei sich die einzelnen Glaspartikel vorzugsweise überlappen. The glass layers can also consist of individual flat Glass particles are built up that form a layer, the individual glass particles preferably overlap.

Bei den Glaspartikeln kann es sich um Bruchstücke handeln, welche durch gezieltes Zerbrechen ganzer Glasfolien erhältlich sind. Insbesondere kann ein Verbund, der eine oder mehrere Glasschichten enthält, so stark gebogen werden, dass die Glasschichten zerbrechen. Enthält der Verbund mehrere Glasschichten, so liegen aufgrund des unterschiedlichen Biegeradius der übereinanderliegenden Schichten die Bruchstellen der Glasschichten im allgemeinen nicht übereinander, so dass die Diffusion von Gasen weiterhin durch das Polymer behindert oder verhindert ist. The glass particles can be fragments, which can be obtained by deliberately breaking entire glass films. In particular, a composite comprising one or more Contains layers of glass that are bent so strongly that the Break layers of glass. If the composite contains several layers of glass, because of the different bending radius overlying layers the breaking points of the glass layers in the general not on top of each other, so the diffusion of gases is still hindered or prevented by the polymer.

Derartige gebrochene Glasschichten bewirken eine weitere Erhöhung der Biegeelastizität des Verbundes. Such broken glass layers cause a further increase the bending elasticity of the composite.

Zur Herstellung von Glasschichten aus sich überlappenden Glaspartikeln können die Glaspartikel z. B. zunächst aufgeschlemmt werden, beim Absetzen der Glaspartikel aus dieser Aufschlemmung bildet sich eine entsprechende kontinuierliche Schicht. For the production of layers of glass from overlapping Glass particles can the glass particles z. B. first slipped open when the glass particles settle out of this slurry a corresponding continuous layer is formed.

Zur weiteren Verringerung der Diffusion von Gasen durch die Glasschicht und zur Verbesserung der mechanischen Eigenschaften der Verbunde können die Bruchstücke ebenfalls mit Haftvermittlern versehen und verbunden werden. To further reduce the diffusion of gases through the Layer of glass and to improve the mechanical properties of the The fragments can also be bonded with bonding agents provided and connected.

Auch Glas-/Polymerverbunde, bei denen die Glasschichten aus überlappenden dünnen Glaspartikeln bestehen, zeigen eine sehr gute Transparenz. Also glass / polymer composites where the glass layers are made of overlapping thin glass particles show a very good Transparency.

Die erfindungsgemäßen Verbunde haben eine sehr hohe Elastizität, insbesondere eine hohe Biegeelastizität; auch bei kleinen Biegeradien brechen sie nicht. Weiterhin sind sie transparent und haben eine hohe Barrierewirkung gegen das Durchdiffundieren von Gasen. The composites according to the invention have a very high elasticity, in particular high bending elasticity; even with small ones They do not break bend radii. Furthermore, they are transparent and have a high barrier effect against the diffusion of Gases.

Die erfindungsgemäßen Verbunde eigenen sich für Anwendungen, bei denen eine hohe Biegsamkeit in Verbindung mit einer Diffusionsdichte gegen Gase benötigt wird. The composites according to the invention are suitable for applications in which are highly flexible in connection with a Diffusion density against gases is needed.

Die erfindungsgemäßen Verbunde sind vorzugsweise transparent, d. h. werden vorzugsweise werden transparente Polymere verwendet. The composites according to the invention are preferably transparent, d. H. transparent polymers are preferably used.

Die Verbunde eignen sich insbesondere als Bestandteil für Anzeigesysteme, bzw. Displays, insbesondere als Abdeckung und Träger. In Betracht kommen z. B. Flüssigkristallanzeigen. The composites are particularly suitable as a component for Display systems, or displays, in particular as a cover and carrier. Consider z. B. Liquid crystal displays.

Insbesondere eignen sie sich auch für Leuchtdiodenanzeigen (LED- Displays). They are also particularly suitable for light-emitting diode displays (LED Displays).

Besonders eignen sie sich für OLED-Anzeigen (organic light emitting diode), bei denen sich zwischen Abdeckung und Träger ein Licht emittierendes organisches Material befindet. They are particularly suitable for OLED displays (organic light emitting diode), where there is between the cover and the carrier Light emitting organic material is located.

Aufgrund ihres geringen Biegeradius eignen sie sich für aufrollbare Displays, insbesondere OLEDs. Z. B. können Computer oder Telekommunikationsgeräte, insbesondere Handys zur Platzersparnis aufgerollte Displays enthalten, die bei Bedarf entrollt werden. Auf diese Weise ist auch bei kleinen Geräten eine Darstellung der Information auf großen Displays möglich. Due to their small bending radius, they are suitable for roll-up displays, especially OLEDs. For example, computers or Telecommunications devices, in particular cell phones to save space Contain rolled up displays that can be unrolled if necessary. In this way, even with small devices, a representation of the Information on large displays possible.

BeispieleExamples

Es wurden Glasfolien (50 µm) mit Polyesterfolien, die einseitig (PEF 100/3), bzw. im Falle der doppellagigen Verbunde in Mittellage zweiseitig (PEF/6) mit einer 3 µm-Haftkleberschicht aus Polyacrylat versehen waren, kaschiert. Zum Kaschieren wurde ein Walzengerät mit zwei Gummiwalzen benutzt; damit war es möglich, die Verbunde herzustellen, ohne dass die Glasfolien zerbrachen (Verbunde A und C). Weiter wurden die Glaslagen in den Verbunde durch zweimaliges Ziehen in Längs- und Querrichtung über einen Dorn von 10 mm Dicke, in weitgehend überlappende Stücke von ca. 2 cm2 gebrochen (Verbunde B und D).
PEF 100/3 = Polyesterfolie 100 µm/Haftkleber 3 µm
PEF 100/6 = Haftkleber 3 µm/Polyesterfolie 100 µm/Haftkleber 3 µm
GLF 50 = Glasfolie 50 µm Glass foils (50 μm) were laminated with polyester foils which were provided on one side (PEF 100/3) or, in the case of the double-layer composites in the middle layer on both sides (PEF / 6), with a 3 μm pressure-sensitive adhesive layer made of polyacrylate. A roller device with two rubber rollers was used for laminating; this made it possible to produce the composites without breaking the glass foils (composites A and C). The glass layers in the composites were further broken by pulling twice in the longitudinal and transverse directions over a mandrel 10 mm thick, into largely overlapping pieces of approximately 2 cm 2 (composites B and D).
PEF 100/3 = 100 µm polyester film / 3 µm pressure sensitive adhesive
PEF 100/6 = adhesive 3 µm / polyester film 100 µm / adhesive 3 µm
GLF 50 = glass film 50 µm

Folgend Verbunde wurden hergestellt:
Verbund A: PEF 100/3 - GLF 50 - PEF 100/3, Glasschicht kohärent
Verbund B: PEF 100/3 - GLF 50 - PEF 100/3, Glasschicht gebrochen
Verbund C: PEF 100/3 - GLF 50 - PEF 100/6 - GLF 50 - PEF 100/3, Glasschicht kohärent
Verbund D: PEF 100/3 - GLF 50 - PEF 100/6 - GLF 50 - PEF 100/3, Glasschichten gebrochen
Verbund E: PEF 100/3 - PEF 100/3, mit der Haftklebeschicht gegeneinander kaschiert The following composites were made:
Composite A: PEF 100/3 - GLF 50 - PEF 100/3, glass layer coherent
Compound B: PEF 100/3 - GLF 50 - PEF 100/3, broken glass layer
Composite C: PEF 100/3 - GLF 50 - PEF 100/6 - GLF 50 - PEF 100/3, glass layer coherent
Composite D: PEF 100/3 - GLF 50 - PEF 100/6 - GLF 50 - PEF 100/3, broken glass layers
Composite E: PEF 100/3 - PEF 100/3, laminated with the adhesive layer against each other

Bei den gebrochenen Glasschichten überschneiden sich die Bruchlinien der einzelnen Glasschichten kaum. In the broken layers of glass, they overlap Hardly any fracture lines of the individual glass layers.

An diesen Verbunden wurde die Durchlässigkeit von Wasserdampf und Sauerstoff gemessen.
Wasserdampfdurchlässigkeit:


bei 23°C/85% gegen 0% relativer Feuchte
Sauerstoffdurchlässigkeit:
Maß


bei 23°C Ergebnistabelle

The permeability of water vapor and oxygen was measured on these compounds.
Water vapor permeability:


at 23 ° C / 85% against 0% relative humidity
Oxygen permeability:
measure


at 23 ° C result table

Claims (20)

1. Flächige biegeelastische Verbunde, dadurch gekennzeichnet, dass sie zumindest eine Glasschicht enthalten, welche auf zumindest einer Seite mit einem Polymer beschichtet ist, und die Glasschicht eine Dicke von 5 bis 250 µm aufweist. 1. Flat, flexible elastic composites, characterized in that they contain at least one glass layer which is coated on at least one side with a polymer, and the glass layer has a thickness of 5 to 250 microns. 2. Verbunde nach Anspruch 1, dadurch gekennzeichnet, dass die Glasschicht auf beiden Seiten mit einem Polymer beschichtet ist. 2. Compounds according to claim 1, characterized in that the Glass layer coated on both sides with a polymer is. 3. Verbunde nach einem der Ansprüche 1 oder 2, dadurch gekennzeichnet, dass sich zwischen Glas und Polymer Haftvermittler befinden. 3. Composites according to one of claims 1 or 2, characterized characterized in that there is a bonding agent between glass and polymer are located. 4. Verbunde nach einem der Ansprüche 1 bis 3, dadurch gekennzeichnet, dass die Polymerschicht zusammen mit dem gegebenenfalls vorhandenen Haftvermittler eine Dicke von 2 bis 500 µm aufweist. 4. Composites according to one of claims 1 to 3, characterized characterized in that the polymer layer together with the any existing adhesion promoter has a thickness of 2 to 500 microns having. 5. Verbunde nach einem der Ansprüche 1 bis 4, dadurch gekennzeichnet, dass der Verbund ein oder zwei Glasschichten enthält und die Gesamtdicke des Verbundes 10 bis 800 µm beträgt. 5. Composites according to one of claims 1 to 4, characterized characterized that the composite one or two layers of glass contains and the total thickness of the composite is 10 to 800 microns. 6. Verbunde nach einem der Ansprüche 1 bis 5, dadurch gekennzeichnet, dass die Biegeelastizität so groß ist, dass der Verbund bei 21°C, 1 bar auf einen Radius von kleiner 30 cm gebogen werden kann. 6. Composites according to one of claims 1 to 5, characterized characterized that the bending elasticity is so great that the Compound at 21 ° C, 1 bar to a radius of less than 30 cm can be bent. 7. Verbunde nach einem der Ansprüche 1 bis 6, dadurch gekennzeichnet, dass es sich bei dem Haftvermittler um niedermolekulare Verbindungen, z. B. Verbindungen mit Silangruppen, handelt. 7. Composites according to one of claims 1 to 6, characterized characterized that the adhesion promoter is low molecular weight compounds, e.g. B. compounds with silane groups, is. 8. Verbunde nach einem der Ansprüche 1 bis 7, dadurch gekennzeichnet, dass es sich bei dem Haftvermittler um einen Haftklebstoff auf Basis eines polymeren Bindemittels mit einer Glasübergangstemperatur unterhalb 20°C handelt. 8. Composites according to one of claims 1 to 7, characterized characterized that the adhesion promoter is a Pressure sensitive adhesive based on a polymeric binder with a Glass transition temperature is below 20 ° C. 9. Verbunde nach einem der Ansprüche 1 bis 8, dadurch gekennzeichnet, dass der polymere Haftvermittler durch energiereiche Strahlung, bevorzugt UV Strahlung vernetzt ist. 9. Composites according to one of claims 1 to 8, characterized characterized in that the polymeric adhesion promoter through high-energy radiation, preferably UV radiation, is crosslinked. 10. Verbunde nach einem der Ansprüche 1 bis 9, dadurch gekennzeichnet, dass der Haftklebstoff zwischen Polymerschicht und Glasschicht eine Haftklebstoffschicht ausbildet. 10. Composites according to one of claims 1 to 9, characterized characterized in that the pressure sensitive adhesive between the polymer layer and Glass layer forms a pressure sensitive adhesive layer. 11. Verbunde nach einem der Ansprüche 1 bis 9, dadurch gekennzeichnet, dass die Dicke der Haftklebstoffschicht 0,2 bis 25 µm beträgt. 11. Composites according to one of claims 1 to 9, characterized characterized in that the thickness of the pressure sensitive adhesive layer is 0.2 to Is 25 µm. 12. Verbunde nach einem der Ansprüche 1 bis 10, dadurch gekennzeichnet, dass die Polymerschicht aus UV-gehärteten Lackschichten besteht. 12. Composites according to one of claims 1 to 10, characterized characterized that the polymer layer made of UV-cured Lacquer layers exist. 13. Verbunde nach einem der Ansprüche 1 bis 10, dadurch gekennzeichnet, dass die Polymerschicht aus ausgelierten PVC-Plastisolen bestehen. 13. Compounds according to one of claims 1 to 10, characterized characterized in that the polymer layer is worn out PVC plastisols exist. 14. Verbunde nach einem der Ansprüche 1 bis 10, dadurch gekennzeichnet, dass die Polymerschicht aus aromatischen Polyimiden bestehen. 14. Composites according to one of claims 1 to 10, characterized characterized in that the polymer layer made of aromatic polyimides consist. 15. Verbunde nach einem der Ansprüche 1 bis 10, dadurch gekennzeichnet, dass die Polymerschicht aus halogenhaltigen Polymeren, insbesondere Polyvinylidenchlorid gebildet wird. 15. Composites according to one of claims 1 to 10, characterized characterized in that the polymer layer made of halogen-containing Polymers, especially polyvinylidene chloride is formed. 16. Verbunde nach einem der Ansprüche 1 bis 15, dadurch gekennzeichnet, dass die Glasschicht aus flächigen Glaspartikeln aufgebaut ist. 16. Composites according to one of claims 1 to 15, characterized characterized that the glass layer made of flat glass particles is constructed. 17. Verbunde nach Anspruch 16, dadurch gekennzeichnet, dass die die Glasschicht bildenden flächigen Glaspartikel durch Haftvermittler verbunden sind. 17. Compounds according to claim 16, characterized in that the the flat glass particles forming the glass layer Adhesion promoters are connected. 18. Verbunde nach einem der Ansprüche 1 bis 17, dadurch gekennzeichnet, dass sie transparent sind. 18. Compounds according to one of claims 1 to 17, characterized marked that they are transparent. 19. Anzeigesysteme, bzw. Displays, enthaltend Verbunde nach einem der Ansprüche 1 bis 18 als Bestandteil, insbesondere als Abdeckung oder Träger. 19. Display systems, or displays, containing assemblies according to one of claims 1 to 18 as a component, in particular as Cover or carrier. 20. Anzeigensysteme nach Anspruch 19 auf Basis von lichtemittierenden Dioden (LED), insbesondere von organischen lichtemittierenden Dioden (OLED). 20. Display systems according to claim 19 based on light emitting diodes (LED), especially organic ones light emitting diodes (OLED).
DE10200131A 2002-01-04 2002-01-04 Bending-elastic glass / polymer composites Withdrawn DE10200131A1 (en)