CN87101818A - Rolling cold-bending molding technology and process units thereof - Google Patents

Abstract

The present invention is for a kind of transverse shear deformation that utilizes makes local longitudinal extension zone on the sheet material roll the thin cold bending shaping method that does not have linear deformation, adopts this method can make thin and the calendering member that heavily stressed place is thick in low stress place to improve stock utilization.The device of realizing this method is made up of with a pair of vertical adjustable pressure roller of exerting pressure to axle tire gyroaxis the gyroaxis tire of the two corresponding circle conical surfaces by one.Certain zone produces distortion on the material under the effect of shearing force, and the zone of this longitudinal extension is rolled thin on the sheet material.Pressure acts in the Normal plane of band length to avoid longitudinal stretching.

Description

The present invention relates generally to the cold roll forming sheet metal strip, specifically about continuous cold rolling process with produce the method and the device of sheet metal strip.This technology and device are to be used to make the vertical attenuation of sheet metal strip, and the zone, lateral separation forms different-thickness, relates to the product that makes with this kind band simultaneously.

Many calendering section bars all are to be that the sheet metal in required cross section is made by roll forming.For example: furred ceiling keel, anchoring piece and corrugated sheet metal, but be not limited to these.Under many occasions, the purposes of section bar is so just can more effectively utilize the material of forming profiles if metal specific location in section bar is built up in addition.

A keel sideband load-bearing skeleton and another side has the lower flange normally for example.Skeleton links to each other with the web of lower flange by the centre.In this T type element structure, the structural strength effect that skeleton and bottom wing genesis are main, and web plays the structural strength effect hardly, its major function makes skeleton and lower flange keep spacing exactly.Therefore, reduce, and the two ends that make the metal of shaping keel accumulate in member are skeleton and place, lower flange as web thickness.The metal material of keel is just further made full use of so.

Invest assignee of the present invention's United States Patent (USP) certificate patent No. № .4,206,578 have described a kind of benefit that material is accumulated in the keel at two ends and produces therefrom, select and edit in this for reference.

In addition, if the words that the thickness of relative its both sides of thickness of metal anchorage and channel-section steel epiplastron is reduced to some extent also can make material be effectively utilized.Equally as a rule, very thin connection web is effectively utilized its material on the corrugated sheet metal.

In general, strap cold rolling is become thickness attenuation in the zone of vertically appointment in the past and section bar of the original thickness of other zone maintenance can also be accomplished.For example I-beam is under the hot state always in the past, what promptly rolling became on recrystallization temperature, so before rolling, the material of shaping I-beam has higher plasticity.The section bar of other variable cross-section is usually also at hot extruding or roll forming down.

In the typical clod wash roll forming that section thickness changes, thin plate band or sheet material pass through in two relative rollings, and between two rollings exert pressure its thickness plasticity is diminished in the two sides of band.In this conventional rolling process, band at first produces distortion at length direction, its length is increased, if the reduction of thickness is to finish equably on the whole width of band, then any problem can not occur, evenly take place because extend on the whole width of band.

On the other hand, keep on all the other longitudinal lengths thickness curved simultaneously if adopt conventional cold roll forming to reduce thickness on a certain longitudinal length of band in the past, will run into very big difficulty so, this is because the part that thickness reduces more is tending towards making band to extend, and thickness does not reduce or the part of not attenuation will keep not curved.This can make band take place to curl with bending and lose original flat surface.Therefore, this process can not be used for producing above-mentioned general section bar.

United States Patent (USP) certificate № .4,233,833 propose a kind of mode that adopts roll forming process to produce sheet metal strip, make band reduce and other parts remain unchanged to longitudinal thickness at the position of appointment.The method that this patent is invented is, band is by paired corrugating roll, and the both sides of band laterally are limited in the fixed range respectively simultaneously.The purpose of this method is the material in processed bending is just applied a horizontal tension force, and its extending transversely and thickness are reduced.This patent has further been narrated smooth operation subsequently.It is not believed that the method described in this new patent.Whether the method described in this new patent of dare not concluding at present develops to some extent or has dropped into industrial production.

The present invention be directed to and produce the various metallic articles that roll, these metallic articles require to reduce its metal consumption widely and in fact at all do not influence its intensity and function.The present invention be directed to the process and the equipment of these cold rolled metal goods simultaneously.Concerning some purposes, people wish METAL HEATING PROCESS to is lower than the selected temperature of recrystallization temperature, but the technical process that the present invention introduces is preferably at room temperature implemented.Therefore, the term that is adopted " cold bending " or " cold rolling " here, its implication promptly is to be lower than recrystallization temperature at metal to produce, and preferably at room temperature produces.

A to the effect that relevant cold rolling new principle of the present invention, this principle makes might utilize the cold rolling sheet metal strip that has different-thickness in the district of lateral separation along band longitudinal extension direction of producing, and band does not take place to curl or bending simultaneously.

The characteristics of this new process just are to apply to strip surface the operation of a shearing force, this shearing force favours strip surface and is positioned at the Normal plane of band length substantially, therefore, vertical component of this shearing force is very little, the appointed area is under the effect of shearing force on the sheet material, generation detrusion and corresponding metal are drawn thin, do not produce linear deformation basically; Make shearing force do relative moving to form the elongated area of a vertical attenuation along the length direction of band steel, this extends the region is thin than position contiguous on the band.

In a specific best shown device, the length direction at separately station upper edge band applies the band territory broadening of shearing force gradually thickness has been reduced.

According to the specific device shown in another, longitudinally horizontal adjacent qualification station applies shearing force on the band steel, with shaping article one weakened section or thinning belt, then every crossing a not thinning belt adjacent with article one thinning belt, apply shearing force more in the same way, be shaped a quilt every the spaced second thinning belt of crossing in rectangular district, repeat the rolling process in this interval until the overall width that obtains required thinning belt.Two or more of this device formed thereby mutually between the weakened section that connects by a not thinning belt that is rather narrow the interval.

In two illustrated devices, deformation force is from the tire axle of widely different commentaries on classics and the pressure roller of widely different commentaries on classics, and pressure roller is to be used for along narrow rolling deformation district to the band steel deformation force of exerting pressure.The bearing of trend of this deformed area is consistent with the length direction of band.Because the length of deformed area substantially exceeds its width, thereby the frictional force of tire axle and pressure roller has limited vertically flowing of metal and has made the lateral flow of the basic upper edge of metal flow resistance minimum.

In addition, in two devices, metal is limited in the side of deformed area, flows to this side to limit it, and nearly all lateral flow is all taken place to the opposite side direction.

In this specific best shown device, the shearing force and the strip surface that are applied on the alternate station tilt at angle, this angle is a constant at each alternate station soil, control the size of shearing force simultaneously, thickness of strip is sheared is deformed into a minimum thickness, it is long-pending to make this thickness equal band original thickness and this inclination angle sine.Have been found that and to reduce linear deformation and crackle harmful on the attenuation band by limiting above-mentioned attenuation amount, but in some instances, when the curved thin amount of band surpasses this sine value significantly, also got ideal results.

Adopt the high speed cold rolling plant can realize the process of foregoing invention, produce the sheet metal strip of endless.On band calendering each cross section in the longitudinal direction, the wall thickness of some section remains unchanged.And the wall thickness of some section is thinner than the original thickness of band greatly.When finishing band and shearing the attenuation process, on the band longitudinally the attenuation metal material do not produce stretcher strain basically, so the glacing flatness of band is influenced hardly.Adopt the cross force that applies symmetry to band to finish detrusion and draw the thin guiding problem that has solved band simultaneously in addition.

New the improving one's methods that another content proposed according to the present invention can be produced stretching structure spare, promptly makes the low regional attenuation of structural member upper stress by detrusion and the high zone thickening of stress, thereby further effectively utilizes metal.

The invention provides a kind of new method of manufacturing the calendering structural member, this method makes on the member longitudinal region be sheared attenuation and sclerosis in manufacturing process, thereby has improved the using rate of metal of this kind member.

According to new method provided by the invention, can make certain longitudinal extension zone attenuation on the calendering band of coating, this method allows row calendering again after the coating on band, and coating is not damaged.

The invention provides a kind of method, under the effect of detrusion power, make the zone attenuation of band longitudinal extension with the sheet metal strip calendering.

The invention provides a kind of method of producing novel keel, thereby make the metal at its web place be thinner than the metal at load-bearing skeleton and place, lower flange.

The invention provides a kind of method of new improved production anchoring piece, promptly by detrusion make anchoring piece the web plate section attenuation so that the metal on the anchoring piece rationally distribute.

The invention provides a kind of method of making novel watt of ridge metal structure, make wall thickness on watt ridge face greater than the wall thickness at web place.

The invention provides a kind of new equipment that is used for finishing above-mentioned each process.

All the elements of the present invention are all shown bright in accompanying schematic figure, narration one by one in the detailed description below simultaneously.

Figure 1 shows that the perspective view that will draw band by the metal that the inventive method is produced.

Figure 2 shows that the side view of a milling train, this milling train is used for the section bar shown in Figure 1 that is shaped.

Fig. 3, Fig. 4, Fig. 5 are to cut open the partial cutaway schematic of getting along relevant section line among Fig. 2 with Fig. 6, in turn show the deformation process of bright section bar shown in Figure 1;

Fig. 3 a is that the local enlarged diagram in the structure shown in Figure 3 shows the bright shearing force that puts on the sheet metal strip;

Fig. 7 is the profile of keel of the present invention;

Fig. 7 a is the local amplification profile of keel among Fig. 7;

Fig. 8 is a U type channel-section steel of the present invention, can be used as anchoring piece;

Fig. 8 a is the partial cutaway schematic of modifying device, shows the detrusion of the bright channel-section steel shown in Figure 8 that is used for being shaped;

Fig. 9 is the profile of H type anchoring piece of the present invention;

Figure 10 is the section of one section metal curved corrugated sheet of the present invention;

Figure 11 is a part section, shows bright another kind of modifying device.This device watt ridge metallic plate among Figure 10 that is used for progressively being shaped.

Figure 12 is one section perspective view to band shown in Figure 1 similar rolling prolonging band, but it is that illustrated second kind of device makes among the present invention.

Figure 13 is the local amplification sectional view that intercepts along 13-13 line among Figure 12.

Figure 14 is the zoomed-in view of garden circle institute mark among Figure 12, shows the bright fishbone shape texture that forms on the weakened section not that is positioned between two adjacent thinning belt.

Figure 15 is the partial cutaway schematic of first station in other two kinds of devices, and initial attenuation process produces thus.

Figure 16 is the partial cutaway schematic of second station in second kind of device of the present invention.

Figure 17 is the partial cutaway schematic of the 3rd station in second kind of device of the present invention.

Figure 18 is the partial cutaway schematic of the 4th station, on crossing with steel one not after the weakened section this station of order work second weakened section that is shaped and adjoins.

Figure 19 is the zoomed-in view of rolling deformed area on the sheet metal strip.

Referring to accompanying drawing.Shown in Figure 1 roll that to prolong member be that the band steel is made by the method for the invention detrusion.When producing furred ceiling with keel and similar component according to the present invention, preferably adopt thickness to be about 0.02 inch or thinner again sheet material, but should invention also be suitable for thicker sheet metal, because the implication of " sheet material " (sheet metal) speech also comprises thicker material sometimes, i.e. cut deal (plate).As shown in the figure, the central authorities of member 10 have the sidewall 12,13 of a planomural 11, two left and right sides extensions to adjoin with flanging 14,16 respectively, and flanging 14,16 is laterally staggered and perpendicular with the adjacent wall 12,13 that links to each other substantially in the median wall both sides.

The thickness of mesospore 11 and two side edgefolds 14,16: T ₁Basically the original thickness with the band steel of formed parts 10 is identical, and it is T that distortion makes two side 12,13 attenuates ₂, the hardness at this position is higher than other position on the member, and this is because distortion and rolling due to the work hardening that takes place in the thin process.

Among the figure, sidewall 12,13 and the plane A that has angle perpendicular to mesospore 11.Prolong method, thickness T according to this specific rolling ₂Should be equal to or greater than T ₁SineA.State in detail as following, experiment showed, that rolling thin amount by control can reduce to minimum with undesirable linear deformation on the side or crackle trend, this rolls is thinly determined by the Sine formula.In many examples, two side 12,13 is all rolled because of detrusion is as thin as T ₂, T here ₂Equal T substantially ₁SineA.The width of member 10, i.e. distance between the outer 17,18 of flanging 14,16 equals to be used for the former width of band of rolling member 10 substantially.

Used method and device when Fig. 2-6 illustrates band 21 continuous cold rollings are become the shape of member 10.Device among the figure comprises that four stations are 23-26, yet, also can adopt littler or more station according to the size of special requirement and member.Distortion operation some exaggeration among Fig. 2-6, this is in order to show bright each the relevant step when prolonging metal of rolling better.

As seen from Figure 3, station 23 has a rotating shaft tire 41.Its structure is that a tire roller is contained on the driven shaft 42.The middle body of axle tire 41 is a garden cylindrical surface 46, and two ends are frusto- conical surface 47,48, and frusto- conical surface 47,48 is A with the central vertical plane 44 formed angles of axle tire 41, and this carried in Fig. 1.The width on post surface, garden 46 equals the mesospore width of member 10 among Fig. 1.

In station 23, there is a pair of pressure roller 51,52 to be positioned at a tire top.Two pressure roller 51,52 shapes are identical, but dress is on the contrary, all be contained on the same axle 53, be equally spaced with central plane 44, axle 53 two ends are axle journal, being contained in can be around axis 54 rotation on the support, and the axis 43 and the axis 54 of axle 42 are positioned at same vertical plane simultaneously.

There is pair of pistons formula hydraulic cylinder regulator 56,57 to force on the pressure roller 51,52 among the figure, makes it to turn round simultaneously with axle tire 41.The cylinder body of hydraulic cylinder regulator 56,57 is contained on the frame 60, piston rod 58,59 are connected with axle 53 two ends by bearing 61, when regulating the cylinder pressurization, then the direction along arrow 62 indications applies downward pressure near pressure roller 51,52 places on axle 53.

Two pressure rollers are 51,52 to be garden shape, are used for shape band 21 to produce detrusions, and the pressure roller 52 among the 3a clearly illustrates that two pressure roller applied pressures equate, although because two rollers dresses are identical to opposite shape.In Fig. 3 a, the diameter maximum of the round Xie66Chu of pressure roller 52, the working face 67,67 and 41 surperficial 48 run-in synchronisms of axle tire that radially inwardly extend and promptly form truncated cone in these order 66 places, figure angle.As shown in the figure, truncated cone working face 67 and axle on the tire 41 corresponding working face 48 parallel, in some special case, uneven cooperating face also has the possibility of use.

In operation, the gap of band 21 between the conical surface 47,48 of the working face 67 of two pressure rollers 51,52 and corresponding axis tire 41 sent to continuously.Regulate cylinder 56,57 and impose sufficient pressure extruded metal, make its distortion, produce the banded regions 68 of attenuate, the thickness T behind banded regions 68 attenuates along band ₂Be the thickness of the sidewall 12,13 of member 10 among Fig. 1.

The detrusion of band 21 has produced banded regions 68, but should what vertically not extend by district's metal, and consequently this district's band does not produce warpage.This rolling mode is shown in Fig. 3 a.The power of pressure roller 52 is depressed by the direction of arrow 71, and the shearing force 71 that is applied by pressure roller 52 is to tilt mutually with the outer surface 65 of its adjacent ribbon, and the plane at place is orthogonal to the longitudinal axis of band substantially, like this this power component that just has nothing vertical.As shown in the figure, power 71 can be decomposed into the component 72 of the outer surface 65 that is parallel to band 21, and another component 73 is orthogonal to this surface.

When two axles 42,53 are parallel, be applied to inclining to separating and being B of shearing force 71 and surface 48 and 65 on the band 21 by pressure roller 52.In the example shown in the figure, separate B and equal structure among Fig. 1 and make the A that separates in 10.

When detrusion and this are invented when consistent, the attenuate amount of banded regions 68 is to change with the size that pressure roller 52 is pressed in the power on the metal, experiment showed, maximum roll to prolong compare T ₂/ T ₁(T wherein ₁For band is former thick, T ₂For being out of shape the thickness of back banded regions 68) preferably should be no more than sineB, the crackle or the linear deformation that cause with the metal of avoiding being out of shape.For example, if required thickness reduces by 50%, the sine that the pressure roller shape that matches so preferably should satisfy angle B is not more than 0.5.Be that angle B should be equal to or less than 30 °.To make T when realizing this invention ₂Deng T ₁SineB makes T then gradually ₂Equal T ₁SineA, after the detrusion, it is former wide that the transverse width of band 21 equals band substantially so, and this characteristic perhaps is favourablely to have during corrugated sheet metal in system, and this point will have illustrated in the back.

Attenuate banded regions 68 on the band 21 progressively broadens on several station 24-26 subsequently and reaches desired width up to the two side of bypassing to both sides, the 68a-c place as shown in Fig. 4-6.The driven pillow block 41a-c preferably axle tire 41 with above-mentioned is identical, and they correspondingly are used for station 24-26, and the pressure roller that all has pair of matched to close on each station makes band be subjected to detrusion and attenuate, and its effect is similar with the effect of above-mentioned pressure roller 51,52.

About Fig. 4, pressure roller 51a, 52a are contained on the rotatable axle 53a, load by the hydraulic cylinder regulator (not shown), similar with adjusting cylinder 56,57 among Fig. 3, each pressure roller 51a, 52a have a truncated cone working face 67a, and be corresponding with the working face 67 of the working face of pressure roller 51,52.Radially extend internally from the interior rib of working face 67a, be second surperficial 70a, this surface pressure has been rolled thin part during at last station 23 at band, surface 70a has more retreated a bit to 67a, or loosened a bit, that is leave a very little amount, about 0.003-0.005 English inch from the surface of contiguous axle tire 41a.The effect of this second face is to prevent that metal is to the band central part backward extrusion that does not have attenuate.The semi-coast of roller surface 70a can be in the operation of rolling, wall exempt from last station the sidewall of attenuate 68 impressed on the surface, can limit metal simultaneously, avoid producing anti-squeezing.

Press shown in the figure, at station 25(Fig. 5) in pressure roller 51b, 52b similar to pressure roller 51a, 52a among Fig. 4, but it unloads surperficial 70b, wideer than 70a, this is the part that covers 23,24 attenuates of preceding two stations for comprehensive, similarly, 70c ground, the unloading of pressure roller 51c, 52c surface is widened equally in station 26, to cover the lightening holes of first three station.

In most of the cases, always wish to finish detrusion in case progressively the banded regions of attenuation thickness is all even basically, yet the irregular equal banded regions of some thickness is because the tolerance of making and repeatedly stroke is caused.In addition, in some instances, may require to change the width of two adjacent pressure rollers, the thickness of banded regions is changed to some extent.When relating to thickness T ₂The time, should be understood that the banded regions thickness of attenuate is only T ₂, in complete uniform banded regions is also included within on thickness.

From above, the technology of this invention equipment therefor is fairly obvious, and band does not have the restriction of length, continuously by several station 23-26.When station 23, therefore 68 positions of band because pressure roller 51,52 is outwardly-bent with the effect of axle tire 46, simultaneously owing to shearing force 71 makes it attenuation, and makes metal both lateral sides direction extend, and vertically do not produce distortion basically.

During by the operation of appointment rules, angle A remains unchanged, the attenuation of band steel, its thickness is not less than original thickness and angle A sine is long-pending, this is for fear of the linear deformation of metal and crackle, and when band arrived next station by a station, the pressure roller of next station just contacted the banded regions adjacent not ironed district ironed with a last station, therefore the width of ironed banded regions progressively increases, till desired width.

Because two pressure rollers on each station are symmetrical, and the power on the metal of being pressed onto equates substantially and direction is opposite, therefore, is with that two formed guide effects in angle are enough to band is led on the steel, need not to establish in addition guiding mechanism.

In the said apparatus, band 10 is through being the shape of symmetry after cold rolling, so the minimizing of thickness, and the width of ironed banded regions all equates.In this case, preferably adopt the symmetry axis tire shown in the figure, promptly have columniform central part, with the truncated cone that is positioned at the identical garden of having of both sides cone angle.This invention also has characteristic widely, can produce asymmetrical member, as has two independently vertical banded regions, the member that its thickness and width have nothing in common with each other.In this case, an axle tire may be provided with central part or central part is not a cylinder.In addition, the coning angle at axle tire two ends also may difference or two ends be not cone, even the rotation of pressure roller is not parallel to a tire line, thereby or hydraulic cylinder regulator be added in the different angle B of change of direction of two power on the pressure roller.

In general, the axle tire drives by the electric power (not shown).The power that the adjusting cylinder puts on the pressure roller can be regulated, to guarantee to produce needed attenuate amount.

Preferably adopt hydraulicdriven adjusting cylinder, the regulating system of being made up of them can produce some spring actions, and like this, the thickness productization that makes it the material that is rolled can not influence applied force tempestuously.For example, if axle 53 mechanically is fixed on a given position, small varied in thickness just can produce violent vibration in regulating system.If make the power that puts on pressure roller in the system, the variation of thickness and have some to float with pressure roller, then shearing force is uniformly substantially, thus the identical detrusion ratio that obtains.

In fact, determined by obtain on the adjacent station the attenuate amount be to successively decrease, it is believed that this is owing to be close to the cause of the metal generation work hardening that just is sheared deformed region.In fact, the metal tape of being close to radial regional 66 places is slightly to be tending towards increasing thickness.

Because each station is close to the metal at pressure roller place and always is tending towards increasing thickness, therefore obviously be that laterally extruding or mobile takes place metal, cause some will be rolled thin metal generation work hardening at next station at once, the reason that this work hardening is considered to cause respectively the weakened section thickness by adjacent station to increase can adopt and a kind ofly solve the problem that the weakened section wall thickness increases with the 2nd kind of corresponding method of device shown in Figure 12 of the present invention-18.According to second kind of device, with continuing band steel 21 is passed through Figure 15, three stations of first group shown in 16 and 17, at first station shown in Figure 15, still adopt a tire axle that has a cylinder outer surface 202 and a pair of reciprocal identical frusto-conical surface 203, be similar to the tire axle of first kind of device, however for rough schematic view so only illustrated a frusto-conical surface 203.In this device, pressure roller 204 is made of the barrel portion 206 of the Cylinder part 202 alternate certain distances on the tire axle, and this distance is the original thickness of band steel 21.Equally, two change relative of relative identical shaped pressure roller 204 with the tire axle, therefore one side of pressure roller 204 rolled band steels and another pressure roller 204 are simultaneously at the opposite side of the opposite side rolled band steel of tire axle.Each pressure roller 204 by one with constitute corresponding to 203 separately frusto-conical surfaces 207 of taper seat, the inner in this cross section is connected with Cylinder surface 206, equally, the garden conical surface 207 of pressure roller 204 and the chosen original thickness that is substantially equal to steel 21 of the distance of 203 of the corresponding conical surfaces, therefore, the conical surface 207 does not play the rolling thin strip steel.

What radially be close to the conical surface 207 is truncated cone working face 208, and this face is connected with the conical surface 207 according to a radiation-like plane 209.As shown in the figure, the distance of 203 of the garden conical surfaces is substantially equal to required thin the measuring of rolling less than the original thickness of band steel 21 on garden awl working face 208 and the adjacent tire axle 201.Should be appreciated that tire axle 201 rotates around parallel diaxon respectively with two pressure rollers, form is identical with first kind of device, and same, two pressure rolls are depressed by identical piston rod and actuator cylinder.

When being with steel 21 by the station between pressure roller and the tire axle, garden awl working face 208 contacts with corresponding band steel zone, and this zone is deformed, and produces the strip 224 of a longitudinal extension, and this strip is narrower.

Equally, the power that acts on the band steel makes metal produce lateral flow and almost vertically not mobile.Therefore be with steel to keep straight, draw the metal part on the conical surface 208 to be limited by the conical surface 207 and garden cylinder 206 basically in shown in Figure 15, thus avoided metal instead squeeze and reflux.Therefore, distortion causes that the metal on the band steel laterally outflows.In this case, pressure roller is made of post surface, a garden 211, and this angle 212, face mat garden is connected mutually with garden awl working face 208, thereby the flanging extension, and is parallel with the middle part of band steel, rather than vertical with skew wall resembling in first kind of device basically.

At second station, a tire axle 201a and two pressure roller 204a are arranged equally, see Figure 16.The pressure roller of first station among pressure roller 204a and Figure 16 is different, in Figure 15, the transverse width of garden awl working face 208a has increased, and extends behind the first station weakened region, and make with first station and roll the band steel 224a transversely deforming that thin zone 224 joins, thereby increased the overall width of thinning belt.Equally, this garden awl working face is consistent with the rolling thin strip direction of before being out of shape on first station in Figure 16, is subjected to equally limiting, so anti-squeezing can not taken place, new rolling band steel zone is upward moved outside the angle side direction of conical surface 203a along tire axle 201a.In addition, produce hardly during the metal transversely deforming vertically and flow, the band steel keeps straight.

The 3rd station shown in Figure 17 is still with the same manner broadening thinning belt 224 and 224a, pressure roller 204b has garden awl working face 208b, and its width is bored working face greater than the garden of the second station pressure roller among Figure 17, thereby produces further lateral flow, thinning belt 224 and 224a width increase, shown in 224b.Experiment shows, when being shaped cold rolling common high-quality steel, can adopt three continuous stations to come the banded regions of broadening attenuation and not be considered to the thickness that work hardening causes to reduce.Yet if increase same station in succession again, the decrease of belt steel thickness will reduce significantly.Therefore, the 4th station shown in Figure 180 be used for skipping band steel the preceding paragraph not the fillet district of attenuation so that the band steel is not connected by the rolling banded regions that influences in front with one section.

The pressure roller of the 4th station shown in Figure 180 is by a garden cylinder 206c, and a garden conical surface 207c and a conical surface 208c form, and their size is consistent with the corresponding surface of the 3rd station among Figure 17.Yet pressure roller 204c has a garden awl working face 216c, and this face and conical surface 208c are relaxed 217 intervals, district by one.At this station, laterally inwardly limited except that relaxing the metal in district, the strip 226c that second is narrow vertically is shaped along the band steel.Because the band steel metal that is contacted with garden awl working face 216c does not produce work hardening before this as yet, so can carry out attenuate to greatest extent to it, usually, band will pass through another station (not shown), and this station will be with the mode identical with broadening first band broadening second band gradually.Jump work step if roll the overall width of thin material between requiring, all stations so subsequently will provide identical mitigation part again, skip the work hardening district between promptly requiring for the second time.

In the device shown in Figure 15-18,3 continuous roll gauges are arranged before jumping work step between one, should be clear and definite, although can jump the continuous groove part that is provided with between work step more or less, decide on rolling stock thickness and required attenuation amount.Therefore, jump the restriction of work step between the present invention is not subjected to establish behind the jumping work step between three times again.

Figure 12 shows the band 220 that second kind of device of bright a kind of usefulness produced, and the band with shown in Figure 1 is identical to a great extent.Equally, this band has mesospore 221, and its thickness is T ₁, equate with the original thickness of band steel.This device in, the skew wall 222 that diverges to about member or band 220 still have, they still with flanging 223 terminating together.In this case, flanging extends and parallels with mesospore 222 basically, because pressure roller is to constitute their keeping parallelisms by post surface, garden 211 by garden post surface 211c.

But, in this device, the skew wall 222 that diverges to is made up of article one attenuate band 224-224b and second attenuate band 226c, both are positioned at 227 both sides, muscle shape district, article one, the attenuate band is to form on first group of three station in Figure 15-17, second attenuate band is two shapings in Figure 18, immediately by thereafter station (not shown) broadening gradually, since between jump work step and cause muscle shape district 227, thereby two the ribbon district be able to uniform attenuation, therefore, both or little, very narrow muscle shape thing had existed, and also can obtain enough thin distortion of rolling.

Figure 13 is a profile that doubles to amplify, and the 13-13 that cuts among order Figure 12 cuts open portion's face, should point out, two thinning belt 224-224b and 226c have uniform thickness T ₂And flanging 223 and mesospore 221 original thickness of retainer belt steel still also should illustrate in addition, and muscle shape district 227 it seems as if has a spot of folding or crape is bent at 231 places, we think that this is because in the deformation process of the 4th station of Figure 18, and little metal is instead squeezed and caused after jump work step.Because metal is not limited at garden awl working face 216c later immediately, mainly is the cause of buffer portion 217c, has therefore produced some and has instead squeezed.

Figure 14 shows that bright crape song is tending towards in muscle shape district 227 and takes place, and just with shown in this enlarged drawing, song is that the texture with herringbone produces, and crape bent portions 231 is to tilt and stack is arranged, therefore, the bent right and wrong rule of crape shown in Figure 13, form herringbone.It is believed that this herringbone decorative pattern that produces at the bent place of crape is to be caused by the material residual stress that produces in the attenuation process before the jumping work step.When the crape curly hair is given birth to, make these internal stress be released, thereby cause the herringbone decorative pattern in muscle shape district 227, although muscle portion is irregular a bit, this it played the required booster action in attenuation position on the band.

An instantiation of this invention is exactly at room temperature rolling 2.559 cun wide, and 0.015 cun thick band steel, band steel are the common irons through cold rolling and coating.Lubricated when rolling with oily soap (oilsoap), through the banded regions of two attenuates of the rolling formation of the shearing of 12 road groove parts.Each banded regions thickness is 0.009 cun, and width is 0.915 cun, and angle A is 28 °.The percentage of attenuate is 40%, rolling after, the face width while arriving is 3.300 inches.

Another example is the not coating aluminium belt material of rolling dead-soft under the room temperature, and wide is 2.359 inch, and thick is 0.023 inch, through shearing two banded regions that laterally separate each other of rolling formation, the thickness behind each district's attenuate is 0.015 inch, and wide is 0.915 inch, angle is 28 °, and attenuate percentage is 35%.

In above-mentioned each example, T ₂With T ₁Ratio greater than the sine value at angle, therefore, this attenuation is by due to the shearing force, yet another attenuation is than surpassing in the special case of angle A sine value, and original thickness is that the common quality strip steel of 0.013 inch adopts second kind of above-mentioned device at room temperature to carry out rolling, equally, the cone angle of roll is 28 °.First thinning belt 224, the thickness of 224c between 0.0028 inch-0.0046 inch, the second, the thickness of attenuation 226 then fluctuates between 0.0034 inch-0.006 inch, in this embodiment, T ₂/ T ₁=21%-46%, therefore, the attenuate amount has substantially exceeded the sine value at 28 ° of angles, and however, crackle does not take place and tears wound in metal, is with steel to keep straight simultaneously.

It is believed that in this situation, initial deformation only is detrusion, further flowing has then surpassed SineA, but does not produce too much vertically flowing and the glacing flatness of influence band steel.Therefore, although distortion has surpassed the pure shear distortion, substantially all occur in a lateral direction.

This lateral flow of metal results from the contact area of band steel in distortion 241 zones of roll, and as shown in figure 19, long represents with L, promptly along being with the steel length direction, is depicted as arrow 242 on the figure, and width W is along horizontal direction.As shown in the figure, length L is 3 times of width W at least, in this case, wherein be with between steel and the roll rolling land along very long on the band steel longitudinal direction, and relative length is very narrow in a lateral direction, act on that the frictional force of band on the steel has limited the distortion of length direction and very little to the resistance of transversely deforming, although thereby pressure surpassed and produced the required power of pure shear distortion and the attenuation rate surpasses SineA, the distortion overwhelming majority that steel band produced still is horizontal.Particularly when the member of the weakened section that has longitudinal extension with as thin as a wafer metallic plate production, its attenuation ratio should be more than or equal to sineA, thereby produces detrusion easily yet in many cases.

Member 80 shown in Fig. 7 and the 7a is the furred ceiling keel that make according to this invention.This member is to be formed by a whole band bending, comprises web 81, relative two lower flanges 83 and 84 of the load-bearing skeleton of web 81 tops and web 81 bottoms.In this member, as shown in Figure 7, away from web one side one independent cover 86 is housed in the lower flange.Yet in many examples, need not adorn cover, whole keel are curved by a band steel.

Cold rolling component forming keel 80 among the most handy Fig. 1 or Figure 12 shown in the member 220, in this case, whole load-bearing skeleton is to be formed by the former material that is positioned at mesospore 11 places on the member 10, wall thickness is T ₁, in addition, two-layer web is made of original sidewall 12,13, and every layer thickness is T ₂, the lower flange then preferably rolls into by rolling the flanging 16,17 that prolongs on the member 10, and its thickness equals T ₁

If with above-mentioned distortion and have the strap cold rolling shaping keel that roll thin district, so, just concentrate at metal on the keel that roll on the load-bearing skeleton and lower flange of member, web has been an attenuate then.As previously mentioned, web stress little therefore with two-layer web attenuate with economical with materials, and the intensity of keel is not affected.For example its load-bearing skeleton 82 of keel is about wide, the 1.5 inch height of 1/4 inch, the about 1 inch height of web, and two lower flange beam overalls are slightly less than 1 inch, wide about 4.5 inch of band that so rolling these keel are required.

If the metal wall thickness is equal on the keel of Cheng Qin everywhere, total metal content on the so used band steel unit length then approximately is 4.5 times of amount of metal on the equal length keel, otherwise, as if web thickness being rolled into skeleton and lower flange thickness partly, and the strip width that is used for forming the T position is when being 3.5 inch, and then the required amount of metal of unit length keel then is 3.5 times of amount of metal on the equal length band steel.Therefore the amount of metal that is used to make the thin web plate keel is 3.5/4.5 with the ratio of the used amount of metal of uniform wall thickness keel, or only need wait 78% of the used amount of metal of wall thickness keel, and the thin web plate keel can be saved about metal of about 22% so.

The saving amount of metal changes with the width of attenuate amount and thinning area.In last example, attenuate is than being can save about 22% metal at 50% o'clock.For given utilization scope, the saving amount of metal reduces with the reduction of attenuate ratio.

Another characteristic of this invention is to make the band of coating produce distortion, and does not make coating be subjected to brokenly showing.For example, normally adopt the sheet material the went up coating in advance keel that are shaped.This band that gives the spreading material was coated with lacquer or hot dipping often and crossed zinc, but their all detrusion, and the attenuate cross section do not show and its coating is decreased.Fig. 7 a more clearly shows bright, and detrusion and the coating 87,88 that rolls into before the keel still keep former coating layer thickness in the thin zone of leniently convicting somebody.But,, shown in the 88a, then be thinner than the coating layer thickness that load-bearing skeleton and bottom wing stretch tight and locate as Figure 87 a along the coating layer thickness of web 81 parts.

Because being used for the band steel of rolling section bar can implement coating under the flat state before shaping easily, therefore can former coating is rolled thin when making section bar be vital a large amount of.In addition, the coating of belt steel surface is actually and helps deformation process in many cases, because coating can reduce the wearing and tearing on pressure roller and axle tire surface and adhere to.Add so so, in many cases, when distortion, cooling fluid still need be arranged and moisten numb agent.

In addition, the attenuation in longitudinal extension district also can increase its hardness on the band.This also is useful concerning a lot of section bars.For example in the keel shown in Fig. 7 and Fig. 7 a,,, reduce thereby compensated the intensity that reduces to bring because of thickness because its hardness increases after shearing attenuation though two-layer web is thinner than other position of keel.As a rule, also will there be joint at the two ends of keel web so that keel are coupled together.United States Patent (USP) certificate, № S.3,501,185 and 4,108,563 can be for reference.This patent illustration illustrates the integral joint that is riveted on the web respectively and divides end connector.Although web is thinner, because sclerosis still has enough intensity.

Extention shown in Fig. 8 and 9 on the member, this also can shut out by this invention.Fig. 8 is depicted as a channel member, and the anchoring piece when it can be used as dry wall, this member are to be made of the edge of a wing 92,93 that extend middle pectoral plate 91 and side.Fig. 8 clearly illustrates that except that the middle part 94 of web 91 very much, the thickness T on the edge of a wing 92,93 ₁Be substantially equal to two ones of web thickness.This in addition structure is because of web 91 attenuate, and the metal that forms channel just concentrates on the edge of a wing, thereby has maximum structural strength.

It is similar that the rolling mode of channel shown in Figure 8 and rolling shown in Fig. 1 or 12 are prolonged part, but shown in Fig. 8 a, when detrusion, support the axle the form of the foetus shape of band, have the width of very narrow middle part 46m.So the web 91 behind the attenuate is substantially equal to the width of 46m.Channel among Fig. 8, right not shown coating in addition, but this channel can be with the metal rolled shaping of giving application layer.Coating also reduces its thickness along the thinning area, the keel in Fig. 7 and 7a, in case the distortion finish after, channel is that available general rolling is made.

Figure 9 shows that H shape web, or cap ned.It can be as the anchoring piece 101 of dry wall, and this anchoring piece comprises that thickness is T ₂Terminate in enlarged undercut portions 102, its thickness is obviously than the thickness T of the edge of a wing 103 and 104 ₁Little.Such structure also is to have saved metal because the metal of formation anchoring piece concentrates on along place, the edge of a wing, simultaneously, and the so rolling intensity maximum that makes place, the edge of a wing.The anchoring piece 101 of H shape also can be earlier through preliminary attenuate, like that, and then rolling shown in Fig. 8 a with commonsense method, with the shape of shaping anchoring piece.If necessary, also can give application layer, coating can also still overlay on the metal surface in attenuation when distortion.

Figure 10 and 11 is depicted as a kind of device of rolling this section bar of new follow-on corrugated sheet metal.Through rolling the corrugated sheet metal 111 that prolongs, its cross section as shown in figure 10, this section bar comprises plane 112 and lower plane 113, its thickness is all T ₁, promptly former lamella thickness or be used for the band steel original thickness of rolling corrugated sheet metal 111.Last lower plane 112,113 all connects with the web 116,117 that tilts, and as mentioned above, they are all because of the detrusion attenuate, and its web thickness is T ₂, significantly than thickness T ₁Approach.

As mentioned above, angle 2A is about 60 degree between two connecting walls that diverge to 116,117.Press sine formula, T ₂Approximate T ₁Half.Because this thickness relationship, the corrugated sheet metal among Figure 10 can progressively shut out very easily with device shown in Figure 11.In this device, each independently an axle tire 118 be used for a rolling watt of ridge, its relevant pressure roller 119,120 matches with each tire 117.Here should illustrate that shown in Figure 11 only is a station.Carry out the similar station of work successively and be in order to increase the width of thin-walled, equate with shown in Figure 11 up to the width of thin-walled.

Last plane 112 keeps its original widths, and the width of lower plane has reduced, and this is because thin-walled progressively increases the cause of width until shown in Figure 10 113 width.In this technology, the same with above-mentioned situation, because reduction process is to finish according to the requirement of angle A sine value, so the overall width of band is constant.For example, if former band wide is 4 feet, though the width of web increase to some extent, and to the top, two positions, the end 111 and 113 tilt, and roll into the corrugated sheet metal width and still are about 4 feet.In addition, meet the rule of A angle sine value as web thickness, then the interval of adjacent shaft tire also remains unchanged in thinning process.

Sometimes, may require to shut out earlier corrugated sheet metal, and then longitudinal shear becomes sectional band resemble Figure 10.This band that vertically prescinds is a kind of section bar blank that is used for rolling final required member sometimes.

Though the specific device of this invention is illustrated by illustration, and is illustrated, but still can take the variety of way correct or its parts are rearranged, this and explanation and the institute's requirement this invention done without prejudice to this paper it.

Claims (53)

1, a kind of is on the calendering band of T with original thickness, and the belt-like zone at a longitudinal extension rolls thin cold bending method at least, is characterized in:

(a) apply the shearing force of a localization to a certain selected section of above-mentioned band (10 or 23).The surface tilt of the relative band of this shearing force is B at angle, and acts on basically in the Normal plane of band length direction, therefore vertically almost do not having shearing component, thereby in detrusion metal attenuation process subsequently, band does not produce linear deformation.Simultaneously band laterally adjacent part do not produce draw thin.

(b) and along the band length direction produce the strip section (12,13 and 68) of corresponding mobile to produce a longitudinal extension.

2, by coffee one characteristics of method described in the claim 1, promptly control the measure that band (10 or 23) is applied the shearing force size, so that the thickness (T of the banded section of attenuation (12,12 and 68) ₂) at least with band original thickness T ₁Equate with the amassing of angle B sine.

3, the characteristics that have by measure described in the claim 2 promptly apply enough shearing forces to band (10 or 23), reduce to long-pending identical thickness sinusoidal with angle B and original thickness T with the thickness with above-mentioned banded section.

4, the characteristics that have by method described in the claim 2, be about to above-mentioned banded section (12,13 and 68) and to its laterally spaced one similar banded section (12,13 and 68) roll simultaneously thin so that be applied to power balance roughly on the band.

5, the characteristics that have by method described in the claim 1, be about to above-mentioned banded section (12,13 and 68) and to its laterally spaced one similar banded section (12,13 and 68) roll simultaneously thin so that the power that is applied on the band arrives balance greatly.

6, the characteristics that have by method described in the claim 5, promptly providing has the axle of axle journal tire (41), and this mold has corresponding inclined-plane (47,48) around the widely different commentaries on classics of axis (43) and at two ends.Band 923) is pressed towards this inclined-plane to produce above-mentioned distortion.

7, the characteristics that have by method described in the claim 6 promptly utilize above-mentioned corner angle on the tire to realize the guiding of bands (23).Corresponding corner angle match on these corner angle and the band.

8, the characteristics that have by method described in the claim 1, promptly band is covered with coating, and is rolled thin along the coating of above-mentioned banded section in above-mentioned deformation process.

9, by a kind of method described in the claim 1, its characteristics are continuously band to be shaped to keel (80), wherein between the lower flange (83,84) of not attenuation and the web (81) of the banded section formation of the attenuation between load-bearing skeleton (82) keel.

10, by a kind of method described in the claim 1, characteristics are continuously band to be shaped to a structural member (101), wherein weakened section (102) be positioned at zone that stress reduces and not the weakened section section be positioned at the bigger zone of stress.

11, a kind ofly will draw the cold bending method that band is configured as the longitudinal extension attenuation section that thickness reduces, the black horse characteristics are that band (10 or 23) is longitudinally passed through between the axle tire (41) of widely different commentaries on classics and pressure roller (51,52).Apply both sides opposing inclined power by axle tire and pressure roller to band, make the attenuation section of longitudinal extension under the effect of shearing force, produce transversely deforming, simultaneously vertically almost not distortion.

12, a kind ofly will roll band or shape is the cold bending method that extends longitudinally the direction reduced thickness, be characterized in providing symmetrical rotating shaft tire, these tire two ends have two circular cones (47 identical but that direction is opposite, 48), the centre links to each other with one section non-cone (46), band (10 or 23) is pressed to the conical surface at two ends by the shearing force of mutual balance.Shearing force makes two vertical section transversely deformings on the band, rolls thin longitudinal extension section (12,13 and 68) thereby produce two.

13, by a kind of method described in the claim 12, its characteristics are sequentially simultaneously band to be pressed in this mold on by identical axle tire (41) band (10 or 23), make with front attenuation part adjacent metal and under the effect of shearing force, do not have transversely deforming, thereby broadening weakened region (12,13 and 68).

14, by a kind of method described in the claim 13, its characteristics are weakened region (12,13 and 68) thickness continues to roll thin the amassing of sine that is substantially equal to band (10 or 23) original thickness and each taper seat (47,48) and shearing force included angle B until its thickness.

15,, be characterized in that banded section applies strip surface with coating before thin rolling, and make metal on the weakened region and coating roll thin simultaneously and do not damage coating basically by a kind of method described in the claim 11.

16, by a kind of method described in the claim 11, its characteristics have been to provide the taper seat with about 60 angles (47,48), and the thickness of attenuation section (12,13 and 68) rolled are as thin as about 50% of former band thickness.

17, by a kind of method described in the claim 12, its characteristics are continuously band to be shaped to keel (80), wherein roll the middle pectoral plate (81) that thin zone forms keel.Do not roll load-bearing skeleton (82) and lower flange (83,84) at thin part formation web two ends on the band.

18, by a kind of method described in the claim 12, its characteristics are continuously band to be shaped to a kind of member, and the web of member (91 and 102) is made up of the thin part of rolling on the band, and do not roll the edge of a wing (92 that thin part forms member compound plate two ends on the band, 93 and 103,104).

19, by a kind of method described in the claim 18, its characteristics are to adopt above-mentioned continuous forming process to produce a kind of flute profile anchoring piece.

20, by a kind of method described in the claim 18, promptly adopt above-mentioned continuous forming process to produce a kind of H type anchoring piece (101).

21, a kind of cold bending shaping method of corrugated sheet metal, be characterized in, the horizontal alternate of band but first position (112) of longitudinal extension in axle tire (118) upper support, apply detrusion power in both sides, first position step by step then, make second position (116,117) attenuation, and first position formed tangible angle.When two second positions at first position of ining succession by the 3rd position (113) when separating, detrusion stops.

22, by a kind of method described in the claim 21, be characterized in Jiang Er district (116,117) be bent into perpendicular to the plane of A at angle, the plane of a district (112), and Jiang Er district thickness rolls to be as thin as and equals district's thickness substantially and angle A sine is amasss.

23, by a kind of method described in the claim 21, be characterized in that the width of flat metal sheets equates with the width of finished product corrugated sheet metal basically.

24, the straight calendering band of the calendering strap cold rolling of the even original depth of a kind of usefulness shaping, be characterized in that original vertical district band (11) has separated and has band original thickness (12,13) two sides, second, the 3rd vertical interval is positioned at two clevers in original vertical interval, under the effect of detrusion, the thickness in 12 districts and 13 districts is evenly rolled thin and less than the thickness of former band.

25, by a kind of calendering band described in the claim 24, its characteristics are that two districts (12) He San district (13) favour original area (11), and with become inclination angle A with the vertical plane of original area, the thickness in He Er district, three districts equals original thickness and angle A sine is amasss at least simultaneously.

26, by a kind of calendering band described in the claim 25, the thickness that is characterized in this band Shang Er district (12) He San district (13) is substantially equal to a district (11) thickness and angle A amber string is amasss.

27, by a kind of calendering band described in the claim 25, four district He Wu district (16,17) that its characteristics are to have on this band original thickness lays respectively at the side of two districts He San district (12,13), and is symmetrical with a district (11).

28, by a kind of calendering band described in the claim 27, its characteristics are four districts (16) He Wu district (17) by lateral separation, a district (11), and the hardness in two districts (12) He San districts (13) is higher than He Si district, a district, five districts.

29, by a kind of calendering band described in the claim 24, its characteristics are to have on the band four districts (16) of original thickness, and five districts (17) lay respectively at two of (12) three districts (13), two districts and connect, and are symmetrical with a district (11).

30, a kind of cold rolling member that is shaped by the calendering strap cold rolling of even original depth (T), its characteristics equal original thickness (T for this member by a thickness ₁) the district (11) of longitudinal extension and two form along member (10) longitudinal extension and with the elongated skew wall (12,13) of district's adjacency, the angle between two skew walls is to give two times that decide angle A, the thickness T of two skew walls ₂=T ₁SinA.

31, by a kind of calendering member described in the claim 30, its characteristics are that this member (10) has the flanging (14,16) that extend on both sides, thereby flanging links to each other with the skew wall on both sides, a district and makes a flanging and a district separately.

32, by a kind of calendering member described in the claim 31, its characteristics are that a district (11) that links to each other with skew wall (12,13) is flat.Its flanging (14,16) is perpendicular with skew wall.

33, by a kind of calendering member described in the claim 30, its characteristics are that one district (11) is a plane, and the flanging that adjoins with its skew wall is laterally alternate.

34, by a kind of calendering member described in the claim 30, its characteristics are that the coating thickness in a district (11) scope on this band is constant and coating on the skew wall (12,13) is rolled thin.

35, a kind of furred ceiling keel, the web frame of middle pectoral plate that these keel are formed by individual band and web upper end and the lower flange of both sides, web base are formed, this web frame and lower flange are made of the band of even initial wall thickness, the characteristics of these keel are that its web is by forming than thin equal thick strip, said individual band then forms the web (81) that obtains through detrusion, the hardness of web is higher than load-bearing skeleton (82) and lower flange (83,84).

36, by a kind of calendering member described in the claim 35, its characteristics are deposited with coating along the outer surface of keel at least, agree coating maintenance (on the band) the original thickness on load-bearing skeleton (82) and lower flange (83,84) and coating on the web (81) is thinner.

37, a kind of middle pectoral plate that curves by individual band of usefulness, one at web load-bearing skeleton and lower flange formation keel that stretch out about the web another side on one side, the outer surface of these keel is covered with coating, the characteristics of these keel are that bone adds (82) and lower flange (83,84) the thickness and the thickness of face coat thereof remain unchanged, and the coating layer thickness of the thickness of web (81) and web surface is rolled thin.

38, a kind of characteristics of metal corrugated sheet metal are each web (16,17) bending, make it and become inclination angle A perpendicular to the plane of first position and second position (12,13), and the thickness of web equal the thickness at first position and second position and amass with angle A sine is.

39, a kind of beams of metal of calendering, this beam is made of a web and a wing plate that extends along web one side that forms with sheet metal strip.Its characteristics be wing plate (92,93 and (103,104) keep the thickness of thickness web (91) of former band then because of the detrusion attenuation of metal.

40, by a kind of beam described in the claim 39, be characterized in that this beam is a channel-section steel.

41, by a kind of beam described in the claim 39, be characterized in that this beam is a H type beam.

42, a kind of device that is used for the rolling sheet metal.This device comprises around first widely different commentaries on classics of axis and axle tire, this tire axle journal provides an inclined plane, pressure roll around second axis rotation, its peripheral part and its inclined plane have a common boundary, and can favour above-mentioned inclined plane to its pressure direction of instrument that pressure roll is exerted pressure.This apparatus features is to roll the sheet material that prolongs and rotating during vertically by the time between axle tire (41) and the pressure roller (51,52) when one.With zone (68) detrusion of a longitudinal extension, its thickness is reduced and do not produce distortion vertically.

43, by a kind of device described in the claim 42, be characterized in that last other an identical tire and the pressure roller of this device rotates simultaneously, thereby step by step the metal on the longitudinal extension inclined-plane produced detrusion, make this face broadening.

44, by a kind of device described in the claim 42, be characterized in that this force application apparatus (56,57) provides an elastic force, pressure roll (51,52) is floated with the varied in thickness of compensation band.

45, by a kind of device described in the claim 42, its characteristics are positioned at same plane for first and second axles (43,54) on this device and are parallel to each other.

46, a kind of device that is used for rolled sheet, comprising: an axle tire around first widely different commentaries on classics of axis, this tire is by two corresponding garden poppet surfaces and be connected mid portion with two garden poppet surfaces and form, and has identical but the opposite garden of direction pressure roller, and its outer garden is adjoined mutually with above-mentioned garden poppet surface; Reach the direction that tilts with the pressure roller garden conical surface applies adjustable cylinder from power to pressure roller.The characteristics of this device (41) are, when one the calendering sheet material at axle tire and pressure roller (51, when vertically passing through 52), its tire and pressure roller rotate simultaneously, apply the shearing force of balance to sheet material, make zone (68) detrusion of awl both sides, garden longitudinal extension, thickness reduces and is not vertically deforming.

47,, be characterized in that the pressure roll (51,52) that this device upward links to each other with axle journal rotates around second axis (54), and parallel with first axle (43) by a kind of device described in the claim 46.

48, by a kind of device described in the claim 47, its characteristics are that compression tools (56,57) has elastic force for above-mentioned garden week (47,48) part and can regulate.

49, a kind of production one straight cold bending method of prolonging band of rolling, this kind band has the attenuation banded regions of longitudinal extension, this method comprises passes through rolled band steel between widely different positioner tool and widely different commentaries on classics pressure roller, apply rock deformation pressure with mold and pressure roller to the band steel along a narrow deformed area, this deformed area trend is consistent with band steel length direction basically, make the metal generation lateral flow on the band steel roll thin metal band-shaped district with shaping article one, not producing simultaneously the longitudinal metal that causes the crape song flows, apply the deformation force of side direction subsequently to a side of article one weakened section with mold and pressure roller, the rolling deformation district that this side and second are narrow is adjacent, equally, the bearing of trend of this deformed area and the vertical consistency of being with steel, make the metal on the band steel produce lateral flow with shaping second metal sheet band, the while does not make the metal generation on the band steel vertically flow and is directed at the crape song.

50,, comprise that promptly limiting on the band steel metal of shaping place flows to inboardly in the inboard of each deformed area to limit it, makes the metal of not finishing shaping laterally to the flows outside in the district that is shaped in addition simultaneously by a kind of method described in the claim 49.

51, by a kind of cold bending method described in the claim 49, promptly first and second banded regions are laterally adjacent one another are, form a continuous thinning area, and the width in this district is substantially equal to the width of two thinning belt.

52, by a kind of cold bending method described in the claim 49, promptly first and second weakened section are kept the band steel of original thickness laterally to be spaced apart from each other by one section.

53, by a kind of cold bending method described in the claim 49, i.e. the correspondence table face tilt of deformation force and band steel, metal is with the detrusion lateral flow.