CN87100368A - The bamboo plywood manufacture method - Google Patents
The bamboo plywood manufacture method Download PDFInfo
- Publication number
- CN87100368A CN87100368A CN87100368.6A CN87100368A CN87100368A CN 87100368 A CN87100368 A CN 87100368A CN 87100368 A CN87100368 A CN 87100368A CN 87100368 A CN87100368 A CN 87100368A
- Authority
- CN
- China
- Prior art keywords
- bamboo
- mao bamboon
- glued board
- poach
- flattening
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention belongs to the glued board manufacturing technology in the Wood-based Panel Production.With the mao bamboon is raw material, and its flattening method adopts the method for going inside and outside ring, subdivision, pressurization flattening after poach, wax boil twice softening processing.Bamboo wood after pressurization flattens can be used as production glued board required panel, backboard or central layer and uses after planing operation, dry setting.The glued board of making, its purposes are similar to the thick glued board of timber.Intensity, hardness, wearability are higher than the wood gluing plate, are a kind of good engineering structure new materials.
Description
The invention belongs to the glued board manufacturing technology in the Wood-based Panel Production.
Normal plywood revolves system veneer gummed by three layers or multilayer and forms.Because the shortage day by day of timber resources.A large amount of research is all carried out in countries in the world at raw material and aspect developing new product.During the forest of country in Southeast Asia money is former, except that timber, also have a large amount of various bamboos, wherein the bamboo bar of mao bamboon (PhyLLOStaChyS PubeCenS) thick perfectly straight, growth is rapid, physics, good mechanical performance.But,, then have a series of technical problem if make glued board with mao bamboon.Mainly be because the hollow that the bamboo bar is a self-sow to be formed (band joint) thin cylinder, reduce gradually from root to taper along the diameter and the thickness of its axis direction, and neither the one desirable circle of cross section.When the bamboo pole length surpasses one meter.Can't use the veneer rotary-cut technology in the manufacturing of wood gluing plate; Use reluctantly, the utilization rate of bamboo wood is also extremely low.Make glued board after mao bamboon along the circumferential direction if can being flattened, just can improve the utilization rate of mao bamboon greatly, and can give full play to the high advantage of the strength ratio timber of bamboo wood own.
Because the structure of mao bamboon is the cylindric of hollow, and certain thickness is arranged, therefore, as the flattening of directly pressurizeing of the thick bamboo tube that will cut open, will make bamboo wood longitudinally (axis direction) fragment into the bamboo chip of some strips.This is because the rigidity of bamboo wood is better, the elastic modulus E value up to 1074 kgfs/centimetre
2, its outer surface pressurized, inner surface tension during expansion, and stress value substantially exceeds the breakdown strength of bamboo wood.Therefore, how to solve the expansion problems of bamboo wood, become with the key in the bamboo wood production glued board technology.
Relevant units at home and abroad has adopted following several processing methods in bamboo plywood production at present.In Philippine utility model patent NO.43, mentioned and adopted adhesive and packing material to flatten the method for bamboo wood in " lamination bamboo wood " patented product production technology.Domestic then have weave into bamboo mat after bamboo wood split the thin bamboo strip, soak the method for producing the bamboo mat plywood product behind (or being coated with) glue again; Directly soak (or being coated with) glue after in addition bamboo wood being split the thin bamboo strip, stacked again gummed is produced the method for bamboo wood laminate.Above the whole bag of tricks, the adhesive consumption is big, and manual operations is many, and quality is wayward, so influenced using and promoting of product greatly.
Purpose of the present invention is exactly a kind of bamboo wood expanding method of suitability for industrialized production and bamboo plywood manufacturing process that technology is easy, utilization rate of bamboo is higher, properties of product are superior be convenient to of research.
The main processes that employing the present invention makes bamboo plywood is as follows:
1, raw material preparation-employing small-end diameter is greater than 50 millimeters fresh ripe mao bamboon.Mao bamboon fell the back shelter from heat or light, when preserving under the moist condition, had better not surpass half a year storage period.
2 ,-with the breadth size of mao bamboon, block the length that becomes to need by the production glued board.
3, acromere excision in the thick bamboo tube after going inside and outside ring-to block with special-purpose cutting machines.Also bamboo spring, the surf green of surfaces externally and internally can be removed 0.5~1 millimeter, be beneficial to softening and expansion.
4, partly-and general double subdivision, also can cut open into more than two.This operation also can be by coming before the operation 3.
5, the poach-bamboo wood behind the subdivision was immersed in the hot water more than 80 ℃ heating more than 1 hour.Water temperature should prolong soak time when low.
6, wax boils-bamboo wood behind the poach is put into 115~140 ℃ paraffin solution.Processing time is the bamboo wood 0.5~0.8 minute of every millimeters thick.Capping when the big or temperature of wall thickness is low; Take off limit when the big or temperature of wall thickness is high.Paraffin can be 50~70 ℃ general industry paraffin with fusing point.
7, launch-bamboo wood after wax is boiled puts into the flattening of once pressurizeing of two flat plate heats.Plate temperature is 130~140 ℃, flatten pressure and be 6~8 kgfs/centimetre
2, the dwell time is more than 120 seconds.Also can adopt other batch (-type) or continous way pressurized equipment successively feeding or segmentation launch, as the method launched of segmentation feeding pressurization or the method that the continuous feed pressurization launches in rotating drum successively in flat plate heat.
8, the bamboo chip of planing operation-after will flattening makes it reach the thickness that needs with woodworking thicknesser or other planing equipment surfaces externally and internally of suitably planishing.
9, dry setting-, will make bamboo chip produce restorable distortion because the bamboo chip after flattening has certain residual stress; Bamboo chip contains a large amount of moisture content simultaneously, can not satisfy the requirement of gluing technique.Therefore, need with bamboo chip pressure be not more than 0.5 kgf/centimetre
2, temperature is the drying of pressurizeing under 120~150 ℃ the condition, the whole moisture content that makes bamboo chip is less than 8%, and makes bamboo chip keep flat.
Bamboo chip after the drying setting promptly can be used as the required panel of plywood production, backboard, core material use.Later production process and wood gluing board production technology are basic identical.
Adopt method of the present invention, the bamboo wood method of deploying is easy, and flattening back bamboo chip width is 80~150 millimeters (relevant with former bamboo diameter).Bamboo chip inner surface (one side that the bamboo spring is arranged) produces the thin crackle that looses, and outer surface (one side that surf green is arranged) is not or seldom crackle arranged.After planing operation bamboo wood still do not loose from and the strip of sheet that is kept perfectly.Can change the number of plies, thickness, breadth, glue kind and structure as required and produce the product of many kinds, many specifications.Have that technology is simple, sizing material consumption is few, the mechanization degree advantages of higher.The product of making has kept that bamboo wood mechanical strength height own, hardness are big, the characteristics of good springiness.Changed fundamentally that mao bamboon footpath level is little, wall thin, defectives such as hollow and anisotropy.Its purposes is similar to the thick glued board of timber, is a kind of good structural timber.
Accompanying drawing 1 is a kind of structural representation of three layers of full bamboo plywood.
Adopt exemplary embodiments of the present invention as follows:
With the mao bamboon of small-end diameter D 〉=50 millimeter, block into certain length after, remove inside and outside ring, be split into two or three.Through poach, wax boil, pressurize flattening, planing, dry setting, produce the bamboo plywood product more than three layers or three layers after milling limit, arrangement, gluing, assembly, precompressed, hot pressing, cutting edge.The main processes parameter that adopts and launch effect, the product technology performance is as follows:
Poach-water temperature 〉=80 ℃, poach is more than 1.0 hours.
Wax boils-and the processing time is that the bamboo of every millimeter thickness boiled 0.5-0.8 minute.Different wax liquid temperatures see the following form to the influence that launches effect:
130~140 ℃ of expansion-hot pressing planar surface temperature, expansion pressure 6~8 kgfs/centimetre
2, the dwell time is more than 120 seconds.
120~150 ℃ of dry setting-temperature, pressure less than 0.5 kgf/centimetre
2, the whole moisture content of bamboo wood is 7~8%.
Adopt above-mentioned technological parameter, the plywood character of making can reach following index (use phenol glue);
1, volume heavy-be not less than 0.8 gram per centimeter
3;
2, moisture content-be not more than 7%;
3, MOR-vertically be not less than 900 kgfs/centimetre
2,
Laterally be not less than 500 kgfs/centimetre
2;
4, impact strength-be not less than 0.6 kgfm/centimetre
2;
5, glue-line shear strength-be not less than 20 kgfs/centimetre
2;
6, soak after 24 hours in the water, water absorption rate is not more than 20%; The thickness swelling coefficient is not more than 6%;
7, wood screw hold put forth effort to be not less than 180 kgfs/centimetre.
Product can replace timber to make the truck compartment board through application test, also can be used in the industries such as other vehicle, boats and ships, building, packing, and be a kind of good engineering structure new material.
Claims (6)
1, a kind of usefulness diameter D 〉=mao bamboon of 50 millimeters is made the method for glued board, after mao bamboon processing flattening, through planing, dry, produce the bamboo plywood product after milling limit, arrangement, gluing, assembly, precompressed, hot pressing cutting edge, it is characterized in that: the processing flattening method of mao bamboon adopts and removes inside and outside ring, subdivision, boils the softening method of handling back pressurization flattening of secondary through poach, wax.
2, the mao bamboon of a kind of diameter D according to claim 1 〉=50 millimeters is made the method for glued board, it is characterized in that boil the softening bamboo chip of handling back pressurization flattening of secondary through poach, wax, after planing operation, pressure be not more than 0.5 kgf/centimetre
2, temperature is the drying of pressurizeing under 120~150 ℃ the condition, to the whole moisture content of bamboo chip less than 8%.
3, a kind of usefulness diameter D 〉=mao bamboon of 50 millimeters is made the method for glued board.It is characterized in that the processing flattening method of mao bamboon adopts subdivision, removes inside and outside ring, the method that pressurization flattens after poach, wax boil the softening processing of secondary.
4, as claim 3 described bamboo plywood manufacture methods, it is characterized in that boil the softening bamboo chip of handling back pressurization flattening of secondary through poach, wax, after planing operation, pressure be not more than 0.5 kgf/centimetre
2, temperature is the drying of pressurizeing under 120~150 ℃ the condition, to the whole moisture content of bamboo chip less than 8%.
5, a kind of method of making glued board with the mao bamboon of D 〉=50 millimeter according to claim 1.It is characterized in that the technological requirement that wax boils processing is: the bamboo wood after poach is handled is put into 115~140 ℃ paraffin solution, and the processing time is that the bamboo wood of every millimeters thick boiled 0.5~0.8 minute.
6, a kind of method of making glued board with the mao bamboon of D 〉=50 millimeter according to claim 1, the method that flattens bamboo wood that it is characterized in that pressurizeing is: will put into flat plate heat through the bamboo wood after poach, wax boil that secondary is softening and handles, pressure be 6~8 kgfs/centimetre
2, the planar surface temperature is under 130~140 ℃ the condition, after pressurize is more than 120 seconds, flatten and take out.