CN2683487Y - Bamboo-wooden gummed compartment baseboard for passenger-carrying vehicles - Google Patents
Bamboo-wooden gummed compartment baseboard for passenger-carrying vehicles Download PDFInfo
- Publication number
- CN2683487Y CN2683487Y CN 200420024584 CN200420024584U CN2683487Y CN 2683487 Y CN2683487 Y CN 2683487Y CN 200420024584 CN200420024584 CN 200420024584 CN 200420024584 U CN200420024584 U CN 200420024584U CN 2683487 Y CN2683487 Y CN 2683487Y
- Authority
- CN
- China
- Prior art keywords
- bamboo
- floor
- wood
- passenger cars
- veneer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种主要用竹材和木材为原料制成的载客汽车用竹木胶合车厢底板，其特征在于面层采用木质单板、芯层采用竹帘、底层采用竹席或木质单板，经涂/浸胶、组坯、热压等工艺制成。成品的物理、力学性能，完全符合《汽车车厢底板用竹篾胶合板(LY/T 1575－2000)》行业标准所规定的技术要求，不仅可直接满足普通客车对车厢底板的物理、力学性能和外观方面的要求，还可以根据高档客车的装饰需要，在车厢底板的上表面铺设塑料地板革或地毯以提高装饰效果，避免了地板革与底板易产生相对滑移、装配费工和铺设材料易损坏等缺陷。
A bamboo-wood glued compartment floor for passenger cars mainly made of bamboo and wood, characterized in that the surface layer is made of wood veneer, the core layer is made of bamboo curtains, the bottom layer is made of bamboo mat or wood veneer, after coating/ Made by dipping, billeting, hot pressing and other processes. The physical and mechanical properties of the finished product fully comply with the technical requirements stipulated in the industry standard "Bamboo Strip Plywood for Automobile Carriage Floors (LY/T 1575-2000)", which can not only directly meet the physical, mechanical properties and appearance of ordinary passenger cars on the car floor In terms of requirements, according to the decoration needs of high-end passenger cars, plastic floor leather or carpet can be laid on the upper surface of the carriage floor to improve the decorative effect, avoiding the relative slippage between the floor leather and the floor, labor-intensive assembly and easy damage to the laying materials and other defects.
Description
One, technical field
The utility model belongs to the wood-based plate manufacturing technology in the timber industry.
Two, background technology
The material that the passenger car cabin floor is commonly used is bamboo plywood, wood gluing plate, plastic molding board etc.Plastic molding board price height, and have shortcomings such as poor flexibility, human body tactile property be bad, now seldom adopt.Bamboo plywood has replaced the main flow material that the wood gluing plate becomes the passenger car cabin floor owing to mechanical property brilliance, good springiness.But the bamboo plywood surface material is generally hand-knitted bamboo mat or the softening bamboo chip that flattens, and appearance is attractive in appearance inadequately, and thermal insulation is also relatively poor.Common solution is to lay plastic floor leather or carpet to improve decorative effect at the upper surface of cabin floor.The main deficiency of this method is that flooring laminate separates with baseboard material, easily produces relative slippage, and not only assembling is taken a lot of work, and paver is fragile.
Three, summary of the invention
The purpose of this utility model is a kind of bamboo wood composite veneer structure of design, makes it sticking for whole with surperficial paver, and improve the plate surface evenness, the novel passenger car that reduces the sheet metal thickness deviation closes cabin floor with the bamboo wood glue.
Technical solution of the present utility model is: with Wooden veneer, bamboo curtain splint or Wooden veneer, bamboo curtain splint, bamboo mat is primary raw material, it is characterized in that surface layer (1) adopts Wooden veneer; Core material adopts bamboo curtain splint; Primer adopts bamboo mat or Wooden veneer.Through assembly, soak/gluing, drying, obtain passenger car cabin floor blank after hot-forming, on wide-belt sander, carry out thick surely sanding after being sawn into specification by the size of customer requirements, can obtain finished product passenger car cabin floor.The user can lay the assembling use behind the direct as required or bonding flooring laminate when making passenger vehicle.
Four, description of drawings
Fig. 1 is that surface layer, bamboo curtain splint are that sandwich layer, bamboo mat are the passenger car cabin floor structural representation of bottom for Wooden veneer, and surface layer among the figure (1) is a Wooden veneer, and (2) are vertical bamboo curtain splint, and (3) are horizontal bamboo curtain splint, and (4) are the bottom bamboo mat;
Fig. 2 is that surface layer, bamboo curtain splint are the passenger car cabin floor structural representation of sandwich layer and bottom surface for Wooden veneer, and surface layer among the figure (1) is a Wooden veneer, and (2) are vertical bamboo curtain splint, and (3) are horizontal bamboo curtain splint, and (4) are Wooden veneer.
Five, the specific embodiment
Embodiment one:
With bamboo curtain splint, bamboo mat, Wooden veneer is that raw material is made the passenger car cabin floor, its structure and manufacture method following (with reference to accompanying drawing 1):
Earlier bamboo is cutd open into thin bamboo strips used for weaving, be woven into bamboo mat and bamboo curtain splint respectively with thin bamboo strips used for weaving then.After bamboo mat and bamboo curtain splint are dried to water ratio≤8%,, be 20%～30% liquid phenolic resin adhesion agent dipping with solid content with multilayer bamboo curtain splint and one deck bamboo mat; Bamboo mat behind the impregnation and bamboo curtain splint are carried out ageing or low temperature drying.
To water ratio≤8%, single face is coated with the phenolic resin glue of solid content about 48% with wooden (poplar or pine) veneer drying, and glue-spread is controlled at 150～200g/m
2About; Ageing.
With the veneer is top layer (1), and bamboo curtain splint is sandwich layer (2), (3), and bamboo mat is that bottom (4) (with reference to accompanying drawing 1) carries out assembly.135～145 ℃ of temperature, carry out hot pressing under the condition of pressure 2.6～3.0MPa.
The half-finished product plate that is hot pressed into is sawn into the size that needs after stacking, cooling off, with wide-belt sander sanding is carried out on the veneer surface of top layer (1), and acquisition thickness of slab passenger car even, surfacing closes the cabin floor finished product with the bamboo wood glue.The physics of finished product, mechanical property meet the technical requirements of " automobile bodies base plate thin bamboo strips used for weaving veneer sheet (LY/T 1575-2000) " industry standard defined fully.
Embodiment two:
With bamboo curtain splint and Wooden veneer is that raw material is made the passenger car cabin floor, its structure and manufacture method following (with reference to accompanying drawing 2):
Earlier bamboo is cutd open into thin bamboo strips used for weaving, weave bamboo curtain splint with thin bamboo strips used for weaving then.After bamboo curtain splint is dried to water ratio≤8%, be 20%～30% liquid phenolic resin adhesion agent dipping with multilayer bamboo curtain splint solid content; Bamboo curtain splint behind the impregnation is carried out ageing or low temperature drying.
To water ratio≤8%, single face is coated with the phenolic resin glue of solid content about 48% with wooden (poplar or pine) veneer drying, and glue-spread is controlled at 150～200g/m
2About; Ageing.
With the veneer is top layer (1) and bottom (4), and bamboo curtain splint is that assembly is carried out in sandwich layer (2) and (3).135～145 ℃ of temperature, carry out hot pressing under the condition of pressure 2.6～3.0MPa.
The half-finished product plate that is hot pressed into is sawn into the size that needs after stacking, cooling off, with wide-belt sander sanding is carried out on the veneer surface of top layer (1), and acquisition thickness of slab passenger car even, surfacing closes the cabin floor finished product with the bamboo wood glue.The physics of finished product, mechanical property meet the technical requirements of " automobile bodies base plate thin bamboo strips used for weaving veneer sheet (LY/T 1575-2000) " industry standard defined fully.
Use passenger car provided by the utility model to close cabin floor with the bamboo wood glue, not only can directly satisfy the requirement of day bus to physics, mechanical property and the outward appearance aspect of cabin floor, can also be according to the decoration needs of high-grade bus, lay plastic floor leather or carpet to improve decorative effect at the upper surface of cabin floor, avoided flooring laminate easily to produce relative slippage with base plate, assemble and take a lot of work and defective such as paver is fragile.
Claims (1)
1. one kind is that the passenger car that raw material is made closes cabin floor with the bamboo wood glue with bamboo wood and timber mainly, it is characterized in that surface layer (1) adopts Wooden veneer, sandwich layer (2) and (3) employing bamboo curtain splint, bottom (4) to adopt bamboo mat or Wooden veneer.