CN202744455U - 增透减反射镀膜玻璃 - Google Patents
增透减反射镀膜玻璃 Download PDFInfo
- Publication number
- CN202744455U CN202744455U CN 201220350208 CN201220350208U CN202744455U CN 202744455 U CN202744455 U CN 202744455U CN 201220350208 CN201220350208 CN 201220350208 CN 201220350208 U CN201220350208 U CN 201220350208U CN 202744455 U CN202744455 U CN 202744455U
- Authority
- CN
- China
- Prior art keywords
- film
- reflection
- plated film
- refractive index
- films
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
本实用新型提供一种透光率高、生产成本低的增透减反射镀膜玻璃，包括玻璃基板，所述玻璃基板表面镀有由至少3层膜组成的增透减反射镀膜，增透减反射镀膜由高折射率镀膜和低折射率镀膜依次交替层叠形成，增透减反射镀膜总厚度为50nm～8000nm，与玻璃基板表面接触的第一膜层为高折射率镀膜。所述高折射率镀膜为TiO2膜或Nr2O5膜，所述低折射率镀膜为SiO2膜。所述增透减反射镀膜包括3～8层镀膜。本实用新型的有益效果在于：玻璃基板表面镀有由高折射率镀膜低折射率镀膜依次交替层叠的增透减反射镀膜，透光率高；膜层材质选取合理，加工方便、成本低；膜层组合方式丰富，适应性广。
Description
技术领域
本实用新型涉及玻璃制造技术领域，具体是指一种增透减反射镀膜玻璃。
背景技术
镀膜玻璃已广泛应用于触摸屏、液晶屏及眼镜片等技术领域，常见镀膜玻璃镀膜层采用不锈钢、氮化钛、镍铬合金等材质，起到装饰或抗辐射等作用。在显示屏领域需要高透光率的玻璃基材，现有技术中也出现了镀有减反射镀膜的玻璃，例如专利号为201120006605.3的实用新型公开了一种减反射玻璃，其玻璃基片上下表面各对称镀有四层减反射镀膜，四层镀膜依次为Nr2O5、 
、Nr2O5、
，由于Nr2O5材料价格较高，难于推广，单层膜过薄，加工工艺较复杂，生产成本高；并且，该种减反射玻璃型号单一，不能适应各种应用场合，适用范围窄。
发明内容
本实用新型针对现有技术存在的缺陷，提供一种透光率高、生产成本低的增透减反射镀膜玻璃（AR玻璃）。
本实用新型采用的方案是：增透减反射镀膜玻璃，包括玻璃基板，所述玻璃基板表面镀有由至少3层膜组成的增透减反射镀膜，增透减反射镀膜由高折射率镀膜和低折射率镀膜依次交替层叠形成，增透减反射镀膜总厚度为50nm～8000nm，与玻璃基板表面接触的第一膜层为高折射率镀膜。
进一步，所述高折射率镀膜为
膜或
膜，所述低折射率镀膜为
膜。
进一步，所述增透减反射镀膜包括3～8层镀膜。
进一步，所述每一膜层厚度为5 nm～8000nm。
进一步，所述每一膜层由磁控溅射镀膜方式镀膜成形。
本实用新型的有益效果在于：玻璃基板表面镀有由高折射率镀膜低折射率镀膜依次交替层叠的增透减反射镀膜，透光率高；膜层材质选取合理，加工方便、成本低；膜层组合方式丰富，适应性广。
附图说明
图1为本实用新型的结构示意图。
具体实施方式
以下结合附图对本实用新型作进一步详细描述：
参照图1，增透减反射镀膜玻璃，包括玻璃基板1，玻璃基板1表面镀有由至少3层高折射率镀膜和低折射率镀膜依次交替层叠形成的增透减反射镀膜，增透减反射镀膜总厚度为50nm～8000nm，与玻璃基板表面接触的第一膜层为高折射率镀膜。
为兼顾增透效果和材料成本，高折射率镀膜为
膜或膜，低折射率镀膜为膜。为适应各种应用场合，增透减反射镀膜包括3～8层镀膜，镀有3层镀膜的AR玻璃透光率约为95%，镀有5层以上镀膜的AR玻璃透光率约为99%，此透光率范围基本满足各种高透光玻璃需要。图1中以玻璃基板上镀5层镀膜为例，膜层2为
膜、膜层3为
膜、膜层4为
膜、膜层5为
、膜层6为
膜。
本实施例中，每一膜层厚度为5nm～8000nm。为提高加工效果及增透效果，每一膜层由磁控溅射镀膜方式镀膜成形。
虽然本实用新型已通过参考优选的实施例进行了图示和描述，但是，本领域普通技术人员应当了解，可以不限于上述实施例的描述，在权利要求书的范围内，可作形式和细节上的各种变化。
Claims (5)
1.增透减反射镀膜玻璃，包括玻璃基板，其特征在于：所述玻璃基板表面镀有由至少3层膜组成的增透减反射镀膜，增透减反射镀膜由高折射率镀膜和低折射率镀膜依次交替层叠形成，增透减反射镀膜总厚度为50nm～8000nm，与玻璃基板表面接触的第一膜层为高折射率镀膜。
2.根据权利要求1所述的增透减反射镀膜玻璃，其特征在于：所述高折射率镀膜为 TiO2膜或Nr2O5膜，所述低折射率镀膜为SiO2膜。
3.根据权利要求1所述的增透减反射镀膜玻璃，其特征在于：所述增透减反射镀膜包括3～8层镀膜。
4.根据权利要求1或2或3所述的增透减反射镀膜玻璃，其特征在于：所述每一膜层厚度为5nm～8000nm。
5.根据权利要求1或2或3所述的增透减反射镀膜玻璃，其特征在于：所述每一膜层由磁控溅射镀膜方式镀膜成形。