CN1762724A - Facing tile and its preparation method - Google Patents
Facing tile and its preparation method Download PDFInfo
- Publication number
- CN1762724A CN1762724A CN 200510061460 CN200510061460A CN1762724A CN 1762724 A CN1762724 A CN 1762724A CN 200510061460 CN200510061460 CN 200510061460 CN 200510061460 A CN200510061460 A CN 200510061460A CN 1762724 A CN1762724 A CN 1762724A
- Authority
- CN
- China
- Prior art keywords
- cured
- cobblestone
- mould
- preparation
- perfusion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a tapestry brick and making method, which comprises the following parts: basal lamina, tapestry layer and pebble-type rock layer with part bearing on the tapestry layer, wherein the baring adjacent rock exists slit; the top of each rock lies in the same plane. The making method comprises the following steps: separating initially; refining; fixing; pouring the basal lamina; removing wax; pouring wax in the basal model again; pouring the tapestry layer; solidifying; maintaining; detecting package in the warehouse. The invention accomplishes bright color, living image through transforming the tapestry layer and model graph, which is convenient to convey due to strong firmness.
Description
Technical field
The invention belongs to a kind of construction, belong to especially that a kind of to make full use of natural cobblestone shape building stones be tapestry brick for building of raw material and preparation method thereof.
Background technology
Before the present invention makes, utilize cobblestone shape building stones both at home and abroad, for example cobblestone is that raw material making tapestry brick yet there are no report.Certainly, utilize cobblestone as finishing material, for example common occurrence as the ground surface material in leisure trail, park.The laying method in this leisure trail generally is as basalis with concrete, before treating that the basalis end is solidified fully, the roughly consistent cobblestone shape building stones of back specification, shape will be selected, cobblestone for example, adopt rice transplanting formula method according to the order of sequence, reserve the slit around every cobblestone and be inserted on the basalis, basalis solidify the back cobblestone leisure trail, welcome by the people.If when laying cobblestone, can take into full account the factor such as color, pattern of cobblestone again, really to be that loved by all, economical and practical, construction cost is low do not say that people can not only enjoy the temperament and interest of the Nature in the leisure trail, can also on the trail, carry out useful body-building, for example the light step is capable, massages sole acupoint whereby, reaches the purpose of taking exercises, therefore, the people resident that particularly lives in the business district wishes that periphery has such leisure trail all the time.But,, therefore, be difficult to satisfy broad masses of the people's life requirement because present stage does not also have batch production to produce the technology of cobblestone leisure trail tapestry brick.
Summary of the invention
For satisfying broad masses of the people's life requirement, solve the problems of the technologies described above, the present invention aims to provide a kind of tapestry brick and preparation method thereof, this tapestry brick is a raw material with natural cobblestone shape building stones, adopt the batch production mode to make the tapestry brick on similar existing cobblestone road surface, preparation method is simple, and it is convenient to lay.
For achieving the above object, the present invention has adopted following technical solution: the structural feature of this tapestry brick is: the cobblestone shape stone layer that it is exposed outside finish coat by basalis, finish coat and part constitutes, and has the slit between exposed adjacent building stones.
During concrete enforcement, every exposed building stones top is equal to the distance of finish coat, that is: the top of every block of building stones is in the same plane.
A kind of preparation method that is used for above-mentioned tapestry brick has following step: primary election, and selected, be installed with, basalis perfusion is taken off curedly, and it is cured that basic mode is irritated again, and the finish coat perfusion is solidified maintenance and test package and is put in storage;
(1) primary election: just select the consistent relatively cobblestone of size with classifying screen;
(2) selected:
A: machine choosing: with classifying screen cobblestone is sieved,
B: the person, preparing the exposed roughly similar person of cobblestone one end shape is certified products;
(3) polishing:
A: cobblestone is put into polishing machine polish,
B: polish once more after in polishing machine, adding iron sand;
(4) be installed with: inject liquid curedly in the mould frame, the setting height of overflow launder is ended to the mould circle limit,, the cobblestone clearance-type vertically is positioned on the template of mould frame near before the cured solidification temperature at cured temperature drop, waits to solidify;
(5) basalis perfusion: press 1 part of cement, fine sand 1-4 part preparation base-material is stand-by, and mould is placed on the shaking platform, pours base-material into, adds while vibrating, and flat frame ends;
(6) take off cured: after base-material solidifies, mould put into take off high temperature pond, cured pond water, liquid has curedly only overflow from overflow launder is taken out into basic mode;
(7) basic mode irritates cured again: through overflow launder with liquid state cured pouring in the basic mode mould frame, end to the isopipe root line, wait to solidify;
(8) finish coat perfusion: press 1 part of cement, 2-3 part microlith preparation lining, the basic mode mould frame that will have overflow launder earlier on one side up, and place on the shaking platform, to prepare lining through overflow launder pours in the gap of solidifying between cured layer and the basalis, the perfusion while vibrating is overflowed to lining from overflow launder and to be ended, solidify 24 hours cured to get on, remove mould finished product;
(9) solidify maintenance: room temperature left standstill more than 7 days;
(10) check, packing, warehouse-in can dispatch from the factory after 28 days.
Another kind is used for the preparation method of above-mentioned tapestry brick, has following step: primary election, and selected, be installed with, basalis perfusion is taken off curedly, and it is cured that basic mode is irritated again, and the finish coat perfusion is solidified maintenance and test package and is put in storage;
(1) primary election: just select the consistent relatively cobblestone of size with classifying screen;
(2) selected:
A: machine choosing: with classifying screen cobblestone is sieved,
B: the person, preparing the exposed roughly similar person of cobblestone one end shape is certified products;
(3) polishing:
A: cobblestone is put into polishing machine polish,
B: polish once more after in polishing machine, adding iron sand;
(4) be installed with: inject liquid curedly in the mould frame, the setting height of overflow launder is ended to the mould circle limit,, the cobblestone clearance-type vertically is positioned on the template of mould frame near before the cured solidification temperature at cured temperature drop, waits to solidify;
(5) finish coat perfusion: press 1 part of cement, 2-3 microlith part preparation lining places mould on the shaking platform, pours the preparation lining into, adds while vibrating, and setting height is ended, and waits to solidify;
(6) basalis perfusion: press 1 part of cement, fine sand part preparation base-material is stand-by, and mould is placed on the shaking platform, pours base-material into, adds while vibrating, and flat frame ends, and solidifies more than 24 hours;
(7) take off cured: mould put into takes off cured high temperature pond water, liquid has curedly only overflow from overflow launder, remove mould finished product;
(8) solidify maintenance: room temperature left standstill more than 7 days;
(9) check, packing, warehouse-in can dispatch from the factory after 28 days.
Beneficial effect: the present invention is from making full use of the theory of the Nature natural stone, adopt the modern industry means of production, solved that people want to solve suitability for industrialized production cobblestone tapestry brick all the time and the technical problem that do not have to solve, to satisfy broad masses of the people's life requirement.It is different that this brick is laid on the trail of laying in the cobblestone trail that forms behind the ground and the prior art, the level height of its every cobblestone in existing trail is uneven because of construction reason, this product then is on the same horizontal plane, in addition, by finish coat, template picture and text The Application of Technology, bright in luster, the lifelike effect of picture and text that product can reach, firmness is good, convenient transportation.
The drawing explanation
Fig. 1 is the perspective view of present embodiment tapestry brick, and cobblestone in the substrate finish coat only draws local to be inserted among the figure;
Fig. 2 is the perspective view of an embodiment mould;
Fig. 3 is a polishing machine master TV structure schematic diagram;
Fig. 4 is a bobbing machine master TV structure schematic diagram.
The specific embodiment
Referring to Fig. 1 to Fig. 4.Sequence number in the accompanying drawing is represented respectively: discharging opening 1, cylinder 2, helical blade 3, water-supply-pipe 4, feed hopper 5, gear 6, gearbox 7, motor 8, under-chassis 9, frame 10, outer edge 11, overflow launder 12, interior edge 13, inner formword 14, template 15, support 16, vibrating motor 17, shaking platform 18, basalis 19, cobblestone 20, finish coat 21, slit 22.
Present embodiment adopts cobblestone 20 as exposed raw material externally, and its part is exposed on finish coat 21, and height can be provided with as required, and another part inserts in finish coat 21, the basalis 19.Basalis 19 is solidified and is formed by cement, husky mixing.Have slit 22 between the exposed adjacent cobblestone 20, and the top of every exposed cobblestone 20 is equal to the distance of finish coat 21, that is: the top of every cobblestone 20 is in the same plane.
The production method of this tapestry brick is as follows:
[making example one]:
According to user's request, make corresponding mould in advance, mould structure is as shown in Figure 2.It is made of template 15, inside and outside edge, wherein edge 13 is provided with the overflow launder 12 parallel with template 15 in one, and the top line of overflow launder 12 flushes with the overhead height of outer edge 11, is used for the cured height of setting filling, this highly in fact also is the exposed height of cobblestone, also is the thickness of cured layer.On the template 15 that interior edge surrounds, be provided with the picture and text that are provided with as required, be used for indicating the position of inserting cobblestone,
This preparation method that is used for above-mentioned tapestry brick has following step: primary election, and selected, be installed with, basalis perfusion is taken off curedly, and it is cured that basic mode is irritated again, and the finish coat perfusion is solidified maintenance and test package and is put in storage;
(1) primary election: with 3 centimetres of artificial consistent relatively cobblestones of size of just selecting of classifying screen that order is big;
(2) selected:
A: machine choosing: with 3 centimetres of big machine classifying screens of order cobblestone is sieved, do postsearch screening;
B: the person, choice criteria is: preparing the exposed roughly similar person of cobblestone one end shape is certified products;
(3) polishing:
A: the cobblestone after will screening is put into rotary polishing machine and is polished, and the time is more than 2 hours;
B: then, the iron sand of diameter 3-5 millimeter is put into polishing machine, polish once more more than 2 hours;
(4) be installed with: in the mould frame, inject liquid cured about 80 degree, edge 12 isopipe root lines only (the overflow launder door is closed, and available wax seal closes) to the mould frame; Earlier need be stained with a positioning bonding agent on the exposed end end top at cobblestone, as plasticine, behind cured temperature drop to 40 degree, with cobblestone need exposed end vertically downward clearance-type be positioned on the template of mould, wait to solidify;
(5) basalis perfusion: press 1 part of cement, fine sand 1-4 part preparation base-material is stand-by, and mould is placed on the shaking platform, pours base-material into, adds while vibrating, and flat frame ends;
(6) take off cured: after base-material solidifies, mould put into takes off cured pond 80 degree Chi Shuizhong, treat that liquid cured having overflow from overflow launder take out into basic mode;
(7) basic mode irritates cured again: the horizontal positioned mould, through overflow 12 grooves with liquid state cured pouring in the basic mode mould frame, end to overflow launder 12 bottom line, wait to solidify;
(8) finish coat perfusion: press 1 part of cement, the sub-2-3 part preparation of microlith lining, the interior edge 13 that will have overflow launder 12 earlier up, and place on the shaking platform, to prepare lining through overflow launder 12 pours in the gap of solidifying between cured layer and the basalis, the perfusion while vibrating, 12 only overflow to lining from overflow launder;
(9) solidify maintenance: room temperature leave standstill 24 hours cured to get on, remove mould, finished product;
(10) check, packing, warehouse-in can dispatch from the factory after 28 days.
[making example two]:
This preparation method that is used for above-mentioned tapestry brick has following step: primary election, and selected, be installed with, basalis perfusion is taken off curedly, and it is cured that basic mode is irritated again, and the finish coat perfusion is solidified maintenance and test package and is put in storage;
(1) primary election: with 3 centimetres of artificial consistent relatively cobblestones of size of just selecting of classifying screen that order is big;
(2) selected:
A: machine choosing: with 3 centimetres of big machine classifying screens of order cobblestone is sieved, do postsearch screening;
B: the person, choice criteria is: preparing the exposed roughly similar person of cobblestone one end shape is certified products;
(3) polishing:
A: the cobblestone after will screening is put into rotary polishing machine and is polished, and the time is more than 2 hours;
B: then, the iron sand of diameter 3-5 millimeter is put into polishing machine, polish once more more than 2 hours;
(4) be installed with: inject liquid cured about 80 degree in the mould frame, the overflow launder bottom line only to the mould circle limit; Earlier need be stained with a positioning bonding agent on the exposed end end top at cobblestone, as plasticine, behind cured temperature drop to 40 degree, with cobblestone need exposed end vertically downward clearance-type be positioned on the template of mould, solidified 1 hour;
(5) finish coat perfusion: press 1 part of cement, 2.5 parts of preparations of microlith lining places mould on the shaking platform, pours the preparation lining into, adds while vibrating, and ends to the overflow launder top line, solidifies 3 hours;
(6) basalis perfusion: press 1 part of cement, fine sand part preparation base-material is stand-by, and mould is placed on the shaking platform, pours base-material into, adds while vibrating, and flat frame ends, and solidifies more than 24 hours;
(7) take off cured: mould put into takes off cured 95 degree Chi Shuizhong, liquid has curedly only overflow from overflow launder 12, remove mould finished product;
(8) solidify maintenance: room temperature left standstill more than 7 days;
(9) check, packing, warehouse-in can dispatch from the factory after 28 days.
Referring to Fig. 3, this polishing machine is by discharging opening 1, cylinder 2, and helical blade 3, water-supply-pipe 4, feed hopper 5, gear 6, gearbox 7, motor 8, under-chassis 9, frame 10 constitutes.A horizontal axis is arranged in the polishing barrel, and axle is provided with screw blade, and blade drives cobblestone and rotates, and reaches the polishing purpose.After adding iron sand, under rotary state, rely on the further fine grinding of friction of iron sand and cobblestone.
Fig. 4 is the schematic diagram of bobbing machine.By support 16, vibrating motor 17, shaking platform 18 constitutes.Shaking platform 18 edges are provided with a housing, and motor 17 adopts 1.1 plate vibrator.
[making example three]:
According to user's request, make corresponding mould in advance, mould structure is as shown in Figure 2.It is made of template 15, inside and outside edge, wherein edge 13 is provided with the overflow launder 12 parallel with template 15 in one, and the top line of overflow launder 12 flushes with the overhead height of outer edge 11, is used for the cured height of setting filling, this highly in fact also is the exposed height of cobblestone, also is the thickness of cured layer.On the template 15 that interior edge surrounds, be provided with the picture and text that are provided with as required, be used for indicating the position of cobblestone intercalation,
This preparation method that is used for above-mentioned tapestry brick has following step: primary election, and selected, be installed with, basalis perfusion is taken off curedly, and it is cured that basic mode is irritated again, and the finish coat perfusion is solidified maintenance and test package and is put in storage;
(1) primary election: with 3 centimetres of artificial consistent relatively cobblestones of size of just selecting of classifying screen that order is big;
(2) selected:
A: machine choosing: with 3 centimetres of big machine classifying screens of order cobblestone is sieved, do postsearch screening;
B: the person, choice criteria is: preparing the exposed roughly similar person of cobblestone one end shape is certified products;
(3) polishing:
A: the cobblestone after will screening is put into rotary polishing machine and is polished, and the time is more than 2 hours;
B: then, the iron sand of diameter 3-5 millimeter is put into polishing machine, polish once more more than 2 hours;
(4) be installed with: in the mould frame, inject liquid cured about 80 degree, edge 12 isopipe root lines only (the overflow launder door is closed, and available wax seal closes) to the mould frame; Earlier need be stained with a positioning bonding agent on the exposed end end top at cobblestone, as plasticine, behind cured temperature drop to 40 degree, with cobblestone need exposed end vertically downward clearance-type be positioned on the template of mould, wait to solidify;
(5) basalis perfusion: press 1 part of cement, fine sand 1-4 part preparation base-material is stand-by, and mould is placed on the shaking platform, pours base-material into, adds while vibrating, and flat frame ends;
(6) take off cured: after base-material solidifies, mould put into takes off cured pond 80 degree Chi Shuizhong, treat that liquid cured having overflow from overflow launder take out into basic mode;
(7) basic mode irritates cured again: the horizontal positioned mould, through overflow 12 grooves with liquid state cured pouring in the basic mode mould frame, end to overflow launder 12 bottom line, wait to solidify;
(8) finish coat perfusion: press 1 part of cement, 0.01 part colorant, 3 parts of microlith preparation linings, with the interior edge 13 that has an overflow launder 12 up, and place on the shaking platform, to prepare lining through overflow launder 12 and pour in the gap of solidifying between cured layer and the basalis, the perfusion while vibrating, 12 only overflow to lining from overflow launder;
(9) solidify maintenance: room temperature leave standstill 24 hours cured to get on, remove mould, finished product;
(10) check, packing, warehouse-in can dispatch from the factory after 28 days.
[making example four]:
This preparation method that is used for above-mentioned tapestry brick has following step: primary election, and selected, be installed with, basalis perfusion is taken off curedly, and it is cured that basic mode is irritated again, and the finish coat perfusion is solidified maintenance and test package and is put in storage;
(1) primary election: with 3 centimetres of artificial consistent relatively cobblestones of size of just selecting of classifying screen that order is big;
(2) selected:
A: machine choosing: with 3 centimetres of big machine classifying screens of order cobblestone is sieved, do postsearch screening;
B: the person, choice criteria is: preparing the exposed roughly similar person of cobblestone one end shape is certified products;
(3) polishing:
A: the cobblestone after will screening is put into rotary polishing machine and is polished, and the time is more than 2 hours;
B: then, the iron sand of diameter 3-5 millimeter is put into polishing machine, polish once more more than 2 hours;
(4) be installed with: inject liquid cured about 80 degree in the mould frame, the overflow launder bottom line only to the mould circle limit; Earlier need be stained with a positioning bonding agent on the exposed end end top at cobblestone, as plasticine, behind cured temperature drop to 40 degree, with cobblestone need exposed end vertically downward clearance-type be positioned on the template of mould, solidified 1 hour;
(5) finish coat perfusion: press 1 part of cement, 0.05 part of colorant, 2 parts of microlith part preparation linings place mould on the shaking platform, pour the preparation lining into, add while vibrating, and end to the overflow launder top line, solidify 3 hours;
(6) basalis perfusion: press 1 part of cement, fine sand part preparation base-material is stand-by, and mould is placed on the shaking platform, pours base-material into, adds while vibrating, and flat frame ends, and solidifies more than 24 hours;
(7) take off cured: mould put into takes off cured 95 degree Chi Shuizhong, liquid has curedly only overflow from overflow launder 12, remove mould finished product;
(8) solidify maintenance: room temperature left standstill more than 7 days;
(9) check, packing, warehouse-in can dispatch from the factory after 28 days.
The cement of mentioning among the embodiment can be selected white cement or other cement as required, and the general diameter of fine sand should be less than 2 millimeters, and the general diameter of microlith should be less than 3 millimeters.
Claims (6)
1, a kind of tapestry brick is characterized in that: the cobblestone shape stone layer (20) that is exposed outside finish coat (21) by basalis (19), finish coat (21) and part constitutes, and has slit (22) between exposed adjacent building stones.
2, a kind of tapestry brick as claimed in claim 1 is characterized in that: every exposed building stones top is equal to the distance of finish coat (21), that is: the top of every block of building stones is in the same plane.
3, a kind of preparation method that is used for tapestry brick as claimed in claim 1 or 2 has following step: primary election, and selected, be installed with, basalis perfusion is taken off curedly, and it is cured that basic mode is irritated again, and the finish coat perfusion is solidified maintenance and test package and is put in storage;
(1) primary election: just select the consistent relatively cobblestone of size with classifying screen;
(2) selected:
A: machine choosing: with classifying screen cobblestone is sieved,
B: the person, preparing the exposed roughly similar person of cobblestone one end shape is certified products;
(3) polishing:
A: cobblestone is put into polishing machine polish,
B: polish once more after in polishing machine, adding iron sand;
(4) be installed with: inject liquid curedly in the mould frame, the setting height of overflow launder is ended to the mould circle limit,, the cobblestone clearance-type vertically is positioned on the template of mould frame near before the cured solidification temperature at cured temperature drop, waits to solidify;
(5) basalis perfusion: press 1 part of cement, fine sand 1-4 part preparation base-material is stand-by, and mould is placed on the shaking platform, pours base-material into, adds while vibrating, and flat frame ends;
(6) take off cured: after base-material solidifies, mould put into take off high temperature pond, cured pond water, liquid has curedly only overflow from overflow launder is taken out into basic mode;
(7) basic mode irritates cured again: through overflow launder with liquid state cured pouring in the basic mode mould frame, end to the isopipe root line, wait to solidify;
(8) finish coat perfusion: press 1 part of cement, 2-3 part microlith preparation lining, the basic mode mould frame that will have overflow launder earlier on one side up, and place on the shaking platform, to prepare lining through overflow launder pours in the gap of solidifying between cured layer and the basalis, the perfusion while vibrating is overflowed to lining from overflow launder and to be ended, solidify 24 hours cured to get on, remove mould finished product;
(9) solidify maintenance: room temperature left standstill more than 7 days;
(10) check, packing, warehouse-in can dispatch from the factory after 28 days.
4, a kind of preparation method as claimed in claim 3 is characterized in that: also added micro-colorant during the preparation lining.
5, another kind is used for the preparation method of tapestry brick as claimed in claim 1 or 2, has following step: primary election, and selected, be installed with, basalis perfusion is taken off curedly, and it is cured that basic mode is irritated again, and the finish coat perfusion is solidified maintenance and test package and is put in storage;
(1) primary election: just select the consistent relatively cobblestone of size with classifying screen;
(2) selected:
A: machine choosing: with classifying screen cobblestone is sieved,
B: the person, preparing the exposed roughly similar person of cobblestone one end shape is certified products;
(3) polishing:
A: cobblestone is put into polishing machine polish,
B: polish once more after in polishing machine, adding iron sand;
(4) be installed with: inject liquid curedly in the mould frame, the setting height of overflow launder is ended to the mould circle limit,, the cobblestone clearance-type vertically is positioned on the template of mould frame near before the cured solidification temperature at cured temperature drop, waits to solidify;
(5) finish coat perfusion: press 1 part of cement, 2-3 microlith part preparation lining places mould on the shaking platform, pours the preparation lining into, adds while vibrating, and setting height is ended, and waits to solidify;
(6) basalis perfusion: press 1 part of cement, fine sand part preparation base-material is stand-by, and mould is placed on the shaking platform, pours base-material into, adds while vibrating, and flat frame ends, and solidifies more than 24 hours;
(7) take off cured: mould put into takes off cured high temperature pond water, liquid has curedly only overflow from overflow launder, remove mould finished product;
(8) solidify maintenance: room temperature left standstill more than 7 days;
(9) check, packing, warehouse-in can dispatch from the factory after 28 days.
6, a kind of preparation method as claimed in claim 5 is characterized in that: also added micro-colorant during the preparation lining.