CN1648329A - Burn-out printing size for textile - Google Patents
Burn-out printing size for textile Download PDFInfo
- Publication number
- CN1648329A CN1648329A CN 200410067686 CN200410067686A CN1648329A CN 1648329 A CN1648329 A CN 1648329A CN 200410067686 CN200410067686 CN 200410067686 CN 200410067686 A CN200410067686 A CN 200410067686A CN 1648329 A CN1648329 A CN 1648329A
- Authority
- CN
- China
- Prior art keywords
- sodium
- special printing
- burn
- textiles
- printing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention belongs to the field of the special printing technique in texture industrial production. In order to meet the requirement of people in pursuing novelty and fashion of fabric color and style, the present invention provides burn-out printing technique as one special fabric printing technique, especially the recipe of burn-out printing size. By means of the burn-out printing size and corresponding technological process, the present invention can produce special burn-out printing fabric with obtain translucent fiber gaps. The technique of the present invention makes it possible to produce peculiar clothing of novel and fashionable style.
Description
Technical field
The invention belongs to the textiles special printing technical field in the caused by spinning industrial production, specifically be meant printing in textiles after, the formula technique of printing paste with translucent etching special printing technology of obvious fiber gap.
Background technology
Along with flat the improving constantly of people pupil's running water, be not only the novel fashion of pursuing color and style to the requirement of clothes and other textiless, and require to have peculiar effect.Special printing is to cater to people to the peculiar requirement of textiles and a kind of stamp new technology that produces.At present, special printing, can be divided into traditional special printing, imitative precious special printing, emulation special printing, three-dimensional special printing, latent shadow special printing etc., the etching special printing belongs to three-dimensional special printing.
Summary of the invention
The problem to be solved in the present invention is to establish the constituent and the content thereof of burn-out printing size.The constituent of burn-out printing size and content are:
Fiber remover 15%～20%,
Alkaline agent 15%～20%,
Bleeding agent 1%
Extraordinary thickener 59%～69%.
Described fiber remover is NaOH, potassium hydroxide
Described alkaline agent is sodium carbonate, sodium bicarbonate.
Described bleeding agent is Seconary Alkane Sulphonate Sodium, sodium 2-ethylhexyl sulfate
Described thickener is the thickener of anti-highly basic A and the weak thickener of anti-weak base B
Printing technology is:
At stamp on the normal temperature equipment-at oven dry-decatize-washing-neutralization-oven dry-finished product under 135 ℃ ± 5 ℃ temperature under 100 ℃ ± 2 ℃ temperature.
The specific embodiment
The burnt-out fabric that adopts a kind of burn-out printing size for textile and printing technology to produce.At first extraordinary thickener is made the former paste of burn-out printing of 10% concentration, and made printing paste according to following constituent and content.
Carry out printing technology on normal temperature equipment, its technical process is:
At stamp on the normal temperature equipment-at oven dry-decatize-washing-neutralization-oven dry-finished product under 135 ℃ ± 5 ℃ temperature under 100 ℃ ± 2 ℃ temperature.
Embodiment 1:
NaOH 20%,
Sodium carbonate 15%,
Seconary Alkane Sulphonate Sodium 1%,
The former paste of 10% anti-highly basic A 64%,
Embodiment 2
Potassium hydroxide 20%,
Sodium bicarbonate 15%,
Seconary Alkane Sulphonate Sodium 1%,
The former paste of 10% anti-highly basic A 64%.
Embodiment 3:
NaOH 15%,
Sodium bicarbonate 15%,
Sodium 2-ethylhexyl sulfate 1%
The former paste of 10% anti-weak base B 69%.
Embodiment 4:
Potassium hydroxide 15%,
Sodium bicarbonate 15%,
Sodium 2-ethylhexyl sulfate 1%,
The former paste of 10% anti-weak base B 69%.
Embodiment 5:
NaOH 20%,
Sodium carbonate 15%,
The former paste of 10% anti-highly basic A 65%.
Embodiment 6:
Potassium hydroxide 15%,
Sodium bicarbonate 15%,
The former paste of 10% anti-weak base B 70%.
Claims (6)
1. the etching special printing of a textiles is starched, and it is characterized in that the composition and the content of described etching special printing slurry is:
Fiber remover 15%～20%,
Alkaline agent 15%～20%,
Bleeding agent 1%,
Extraordinary thickener 59%～69%.
2. the etching special printing of a kind of textiles as claimed in claim 1 slurry is characterized in that described fiber remover is NaOH, potassium hydroxide.
3. the etching special printing of a kind of textiles as claimed in claim 1 slurry is characterized in that described alkaline agent is sodium carbonate, sodium bicarbonate.
4. the etching special printing of a kind of textiles as claimed in claim 1 slurry is characterized in that described bleeding agent is Seconary Alkane Sulphonate Sodium, sodium 2-ethylhexyl sulfate.
5. the etching special printing of a kind of textiles as claimed in claim 1 slurry is characterized in that described extraordinary thickener is the thickener of anti-highly basic A and the thickener of anti-weak base B.
6. the etching special printing of a kind of textiles as claimed in claim 1 is starched, and it is characterized in that the prescription dosage embodiment of described etching special printing slurry has following six kinds:
Embodiment 1
NaOH 20%,
Sodium carbonate 15%,
Seconary Alkane Sulphonate Sodium 1%,
The former paste of 10% anti-highly basic A 64%,
Embodiment 2
Potassium hydroxide 20%,
Sodium bicarbonate 15%,
Seconary Alkane Sulphonate Sodium 1%,
The former paste of 10% anti-highly basic A 64%.
Embodiment 3:
NaOH 15%,
Sodium bicarbonate 15%,
Sodium 2-ethylhexyl sulfate 1%
The former paste of 10% anti-weak base B 69%.
Embodiment 4:
Potassium hydroxide 15%,
Sodium bicarbonate 15%,
Sodium 2-ethylhexyl sulfate 1%,
The former paste of 10% anti-weak base B 69%.
Embodiment 5:
NaOH 20%,
Sodium carbonate 15%,
The former paste of 10% anti-highly basic A 65%.
Embodiment 6:
Potassium hydroxide 15%,
Sodium bicarbonate 15%,
The former paste of 10% anti-weak base B 70%.