CN1635065A - Mineral wool acoustical absorption decorative panel releasing agent and process for preparing same - Google Patents
Mineral wool acoustical absorption decorative panel releasing agent and process for preparing same Download PDFInfo
- Publication number
- CN1635065A CN1635065A CN 200410012585 CN200410012585A CN1635065A CN 1635065 A CN1635065 A CN 1635065A CN 200410012585 CN200410012585 CN 200410012585 CN 200410012585 A CN200410012585 A CN 200410012585A CN 1635065 A CN1635065 A CN 1635065A
- Authority
- CN
- China
- Prior art keywords
- releasing agent
- mineral wool
- water
- polyacrylamide
- minutes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a synthetic material to be used as the releasing agent of mineral wool sound-absorbing decorative panel for substituting animal oil and fat, and its preparing process, wherein the material comprises (by weight ratio) stearic acid 1-2, sulfuric acid castor oil 0.5-1.2, polyoxythylene fatty alcohol ether sodium sulfate 0.9-1.8, water-soluble silicon oil 0.3-0.8, polyacrylamide 0.1-0.4, urea 2-6, pentaerythritol 0.8-1.6, metal surface protectant 0.2-0.3, EDTA 0.4-0.6, and balancing water.
Description
Technical field
The present invention relates to a kind of synthetic releasing agent and preparation method who in the production of mineral wool acoustic decoration board, substitutes the conventional animal grease release agent, belong to the additive preparation technical field that mineral wool is made.
Background technology
The production method of mineral wool acoustic decoration board of the prior art is to be major ingredient with the mineral wool, be aided with tens kinds of inorganic, Organic Chemicals such as W-Gum, staple glass fibre, sepiolite, zinc acetate, boric acid, borax, gelatine, paraffin, stearic acid, polyacrylamide again, through making beating, chute, raceway, roll forming, block-by-block holds up with iron plate again, is filled into oven dry back cutting in the baking oven one by one.The used releasing agent of the drying course of decorative sheet is based on animal oil always, and shortcoming one is to use inconvenience, could use after needing to melt earlier; The 2nd, unhygienic, all discharge various unpleasant pungent stinks at storage in the use, make that stink fills the air in the workshop, not only polluted air and environment, because of the animal oil flavor infiltrates in the mineral wool board bed of material, influenced quality product and foreign exchange earning again; The 3rd, cost is too high, and well-known, per ton the wanting at least of animal oil improved cost to mineral wool board more than 4000 yuan virtually.
Summary of the invention
The object of the present invention is to provide a kind of synthetic materials as releasing agent and the preparation method of animal grease surrogate,, improve the quality of mineral wool acoustic decoration board to reduce production costs as the mineral wool acoustic decoration board.
Technical scheme of the present invention is achieved in that this mineral wool acoustic decoration board releasing agent; the composition that it is characterized in that releasing agent comprises following weight percent: stearic acid 1-2; sulfated castor oil 0.5-1.2, polyoxyethylenated alcohol sodium sulfate 0.9-1.8, water-soluble silicon oil 0.3-0.8; polyacrylamide 0.1-0.4; urea 2-6, tetramethylolmethane 0.8-1.6, metal surface protectant 0.2-0.3; EDTA 0.4-0.6, water surplus.
The composition of described mineral wool acoustic decoration board releasing agent is following weight percent: stearic acid 2; sulfated castor oil 1.0; polyoxyethylenated alcohol sodium sulfate 1.0; water-soluble silicon oil 0.5, polyacrylamide 0.2, urea 5; tetramethylolmethane 0.8; metal surface protectant 0.2, EDTA 0.5, water surplus.
Comprise that also essence is an amount of in the composition of described mineral wool acoustic decoration board releasing agent.
The production method of described above-mentioned mineral wool acoustic decoration board releasing agent is characterized in that being finished by following step:
Water is injected in the reactor, heat to 60-95 ℃, add stearic acid and start stirrer simultaneously; stir after 20 minutes and to add sulfated castor oil and metal surface protectant, stir and add polyoxyethylenated alcohol sodium sulfate, water-soluble silicon oil after 20 minutes more successively; polyacrylamide; urea, tetramethylolmethane, EDTA; stir and stop heating after 40 minutes; add an amount of essence when being cooled to room temperature, restir metering in 10 minutes, packing both got.
Mineral wool acoustic decoration board releasing agent technical progress effect of the present invention shows 1, releasing agent is the aqua form, and low temperature is noncondensing, and is easy to use; 2, on component, use and the proximate additive combination raw material of decorative sheet material, pollution-free, noresidue, stripping result is good.3, reduce production cost, saved the animal grease resource.
Embodiment
Embodiment 1:
Releasing agent component: stearic acid 2, sulfated castor oil 1.2, polyoxyethylenated alcohol sodium sulfate (AES) 1.8, water-soluble silicon oil 0.8; polyacrylamide 0.4, urea 6, tetramethylolmethane 1.6, metal surface protectant (the last marine products of YZ140) 0.3; EDTA 0.6, and essence is an amount of, water surplus.
Preparation method: water is injected in the reactor, heat to 60-95 ℃, add stearic acid and start stirrer simultaneously; stir after 20 minutes and to add sulfated castor oil and metal surface protectant, stir and add polyoxyethylenated alcohol sodium sulfate, water-soluble silicon oil after 20 minutes more successively; polyacrylamide; urea, tetramethylolmethane, EDTA; stir and stop heating after 40 minutes; add an amount of essence when being cooled to room temperature, restir metering in 10 minutes, packing both got.
Embodiment 2:
The releasing agent component: stearic acid 1, sulfated castor oil 0.5, polyoxyethylenated alcohol sodium sulfate 0.9, water-soluble silicon oil 0.3, polyacrylamide 0.1, urea 2, tetramethylolmethane 0.8, metal surface protectant 0.2, EDTA 0.4, and essence is an amount of, water surplus.
Preparation method: with embodiment 1.
Embodiment 3:
The releasing agent component: stearic acid 1.5, sulfated castor oil 0.8, polyoxyethylenated alcohol sodium sulfate 1.5, water-soluble silicon oil 0.5, polyacrylamide 0.2, urea 4, tetramethylolmethane 1.0, metal surface protectant 1.5, EDTA 0.5, and essence is an amount of, water surplus.
Preparation method: with embodiment 1.
Embodiment 4:
The releasing agent component: stearic acid 2, sulfated castor oil 1.0, polyoxyethylenated alcohol sodium sulfate 1.0, water-soluble silicon oil 0.5, polyacrylamide 0.2, urea 5, tetramethylolmethane 0.8, metal surface protectant 0.2, EDTA 0.5, and essence is an amount of, water surplus.
Preparation method: with embodiment 1.
Listed examples of the present invention is intended to further illustrate method of the present invention, and scope of the present invention is not constituted any restriction.The product that obtains with the embodiment of the invention and all can obtain the alleged product of the present invention via claims 1,2,3,4 described methods of the present invention.
Claims (4)
1, mineral wool acoustic decoration board releasing agent; the composition that it is characterized in that releasing agent comprises following weight percent: stearic acid 1-2; sulfated castor oil 0.5-1.2, polyoxyethylenated alcohol sodium sulfate 0.9-1.8, water-soluble silicon oil 0.3-0.8; polyacrylamide 0.1-0.4; urea 2-6, tetramethylolmethane 0.8-1.6, metal surface protectant 0.2-0.3; EDTA 0.4-0.6, water surplus.
2, mineral wool acoustic decoration board releasing agent according to claim 1; the composition that it is characterized in that releasing agent is following weight percent: stearic acid 2; sulfated castor oil 1.0, polyoxyethylenated alcohol sodium sulfate 1.0, water-soluble silicon oil 0.5; polyacrylamide 0.2; urea 5, tetramethylolmethane 0.8, metal surface protectant 0.2; EDTA 0.5, water surplus.
3, mineral wool acoustic decoration board releasing agent according to claim 1 is characterized in that comprising that also essence is an amount of in the composition of releasing agent.
4, the production method of above-mentioned mineral wool acoustic decoration board releasing agent according to claim 1 is characterized in that being finished by following step:
Water is injected in the reactor, heat to 60-95 ℃, add stearic acid and start stirrer simultaneously; stir after 20 minutes and to add sulfated castor oil and metal surface protectant, stir and add polyoxyethylenated alcohol sodium sulfate, water-soluble silicon oil after 20 minutes more successively; polyacrylamide; urea, tetramethylolmethane, EDTA; stir and stop heating after 40 minutes; add an amount of essence when being cooled to room temperature, restir metering in 10 minutes, packing both got.