CN1563135A - Improved resin of epoxy-ester and preparation method - Google Patents
Improved resin of epoxy-ester and preparation method Download PDFInfo
- Publication number
- CN1563135A CN1563135A CN 200410014606 CN200410014606A CN1563135A CN 1563135 A CN1563135 A CN 1563135A CN 200410014606 CN200410014606 CN 200410014606 CN 200410014606 A CN200410014606 A CN 200410014606A CN 1563135 A CN1563135 A CN 1563135A
- Authority
- CN
- China
- Prior art keywords
- epoxy ester
- epoxy
- ester resin
- resin
- anhydride
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A modified epoxyester resin can be obtained by reacting on vegetable oil containig conjugated double bond, maleic anhydride and soya-bean oil fatty acid or recinoleic acid with epoxy as well as mixing certain amount of anhydromatic amide. The preparation process includes additive reaction and exterification.
Description
Technical field
The present invention relates to a kind of epoxy ester resin and preparation method of improvement, relate in particular to a kind of of light color, do not return thick, fast and simple epoxy ester resin of production technique and preparation method when doing.
Background technology
Usually the synthetic of epoxy ester resin is by vegetable oil acid (for example eleostearic acid, soy(a)-bean oil fatty acid, linolenic acid, ricinolic acid, Chinese catalpa oleic acid) and Resins, epoxy (molecular-weight average 900-1400; oxirane value 0.09-022) gets through esterification; and be raw material with the eleostearic acid in the vegetable oil acid; better when the epoxy ester resin that obtains is done, so the more employing eleostearic acid of actual production is made raw material.Vegetable oil acid is got through acidifying by vegetables oil, however the acidifying of acidization, particularly tung oil, not only technology is comparatively complicated, needs to carry out in special device, and it needs through acidifying, neutralization, washing three big processes, and the acidifying yield is not high, only be about 80-85% usually, thereby raw material consumption is bigger.This technology makes the epoxy ester resin preparation cost higher relatively, and gained epoxy ester resin color is darker, and discomfort is fit to do tinted paint, long easily returning slightly of time.In addition, vegetable oil acid and Resins, epoxy esterification gained epoxy ester resin, slower when lacquering is done, influence the fast of coating and do.
Summary of the invention
First purpose of the present invention is to overcome the deficiency of above-mentioned prior art, provides a kind of production technique simple, and cost is low, and color of resin is shallow, stores and does not return thick epoxy ester resin.
Another object of the present invention also is to provide a kind of and not only possesses These characteristics, and lacquering fast epoxy ester resin when doing.
A further object of the present invention is to provide a kind of preparation method of above-mentioned epoxy ester resin.
Epoxy ester resin of the present invention is characterized in that the vegetables oil addition with containing conjugated double bond obtains the cis-butenedioic anhydride vegetables oil by being added with MALEIC ANHYDRIDE, substitutes vegetable oil acid, with the esterification of Resins, epoxy, thereby Resins, epoxy is carried out modification.Specifically, epoxy ester resin of the present invention, by the vegetables oil that contains conjugated double bond of 15～30% (wt), 0.1～0.5% MALEIC ANHYDRIDE, 25～40% soy(a)-bean oil fatty acid and/or ricinolic acid, and 40～55% Resins, epoxy reaction and getting.
MALEIC ANHYDRIDE among the present invention (hereinafter to be referred as cis-butenedioic anhydride), mainly play crosslinked bridging agent effect, promptly carry out addition reaction by cis-butenedioic anhydride and the vegetables oil that contains conjugated double bond (as commonly used but be not limited to tung oil, oleum lini, Chinese catalpa oil), make so originally can not be directly and Resins, epoxy carry out the vegetables oil that contains conjugated double bond of esterification, can under the effect of cis-butenedioic anhydride bridging agent, carry out esterification, and esterification can be carried out in homogeneous phase with Resins, epoxy.The reaction weight ratio that contains the vegetables oil and the cis-butenedioic anhydride of conjugated double bond, with 15～30% (wt): 0.1～0.5% relatively for suitable, if the cis-butenedioic anhydride consumption is on the low side, can cause the vegetables oil cis-butenedioic anhydrideization that contains conjugated double bond incomplete, reaction mass meeting clouding or layering are unfavorable for follow-up and esterification Resins, epoxy; Consumption is too much, can cause follow-up esterification speed too fast and wayward again, becomes glue easily.Therefore the present invention on experimental basis, draw 15～30%: 0.1～0.5% comparatively suitable, but non-finger limit of accuracy value, more a spot of increase and decrease, performance impact is not fairly obvious, in view of the above, anyly departs from a small quantity in the reasonable scope, belongs to the scope of the invention yet.The present invention contains in the vegetables oil of conjugated double bond, is good with tung oil especially, and the gained epoxy ester resin is formed coating, hardness of paint film, all good when doing behind the lacquering.Epoxy resin ester of the present invention, similar with the required Resins, epoxy of vegetables oil acid system, have no special requirements.
Equally, the present invention contain conjugated double bond the reaction weight ratio of vegetables oil, soy(a)-bean oil fatty acid or ricinolic acid, Resins, epoxy with 15～30%: 25～40%: 40～55% is comparatively suitable, also is the preferable suitable value of test back gained, is not the limit of accuracy value.If it is excessive to contain vegetables oil, soy(a)-bean oil fatty acid or the ricinolic acid consumption of conjugated double bond, in the time of then can influencing paint film and do, hardness and chemical resistance descend; Otherwise, the paint film flexibility variation, the easy embrittlement of paint film, and cost increases.But more a spot of increase and decrease, performance impact are not fairly obvious, in view of the above, anyly depart from a small quantity in the reasonable scope, belong to the scope of the invention yet.
The present invention further reduces the epoxy ester resin cost, and the drying rate and the grinability that improve the lacquering paint film, a kind of better is esterification gained epoxy ester to be mixed again convert the apple anhydride dehydration resin, and epoxy ester of the present invention and apple anhydride dehydration resin mixed converted weight ratio with 100 (wt): 15～25 is more suitable.Apple anhydride dehydration resin dosage is too much, though the resin dry rate is accelerated, can cause the paint film embrittlement, and this is undesirable; Dosage is very few, does not have the effect of accelerating the rate of doing and accelerating grinability.
Feature of epoxy ester resin of the present invention is: the molecular characterization that contains cis-butenedioic anhydride vegetables oil and Resins, epoxy esterification in the epoxy ester resin, and apple anhydride dehydration resin (if adding), this is that epoxy ester resin of the present invention is different from an important difference by vegetable oil acid esterification gained epoxy ester resin.
The preparation of epoxy ester resin of the present invention comprises at first making vegetables oil and the MALEIC ANHYDRIDE addition reaction (Diels-Alder) that contains conjugated double bond, obtains the cis-butenedioic anhydride vegetables oil, and then mixes with Resins, epoxy and to carry out esterification.Soy(a)-bean oil fatty acid or ricinolic acid and cis-butenedioic anhydride do not react, therefore can be in preceding adding, also can add in the back, but a kind of better mode of the present invention, be that 15～30% vegetables oil that contain conjugated double bond, 0.1～0.5% cis-butenedioic anhydride, 25～40% soy(a)-bean oil fatty acid and/or ricinolic acid are once added, after addition reaction obtains cis-butenedioic anhydride vegetables oil, soy(a)-bean oil fatty acid and/or ricinolic acid mixture, add the mixing of required (40～55%) Resins, epoxy again and carry out esterification, help the material homogeneous response like this.
The present invention contains the addition reaction of the vegetables oil and the cis-butenedioic anhydride of conjugated double bond, better is to pine for carrying out adding, and helps the quickening of reacting like this.Described heating, wherein comparatively suitable to carry out in 110 ℃ of-180 ℃ of temperature especially, temperature of reaction is too high, and cis-butenedioic anhydride easily distils, and can cause the imbalance of reaction ratio, and the vegetables oil cis-butenedioic anhydrideization is incomplete; Reaction temperature is spent low, then can prolong reaction time again.Addition reaction finishes the esterification reaction temperature of back and Resins, epoxy, and is similar substantially with the esterification reaction temperature of common vegetable oil acid and Resins, epoxy, no particular requirement.
The Deils-Alder reaction principle that the present invention contains the vegetables oil of conjugated double bond and cis-butenedioic anhydride is as follows:
Gained cis-butenedioic anhydride vegetables oil carries out esterification with Resins, epoxy again, and its reaction principle and condition and common vegetable oil acid and Resins, epoxy esterification reacting phase are no longer carefully stated together.
The preparation of epoxy ester resin of the present invention can also be with esterification gained epoxy ester, through being cooled to 80-160 ℃ and 15～25% (WT is in epoxy ester) apple anhydride dehydration resin uniform mixing.Mixing temperature is too high, and then solvent easily produces volatilization in the apple anhydride dehydration resin; Mixing temperature is low excessively, and uniform mixing time lengthening then is so that the present invention proposes 80-160 ℃ of mixing is comparatively suitable.
Epoxy ester resin of the present invention, make bridging agent owing to adopt cis-butenedioic anhydride, can make the vegetables oil that contains conjugated double bond with cis-butenedioic anhydride addition reaction (Diels-Alder) after obtain the cis-butenedioic anhydride vegetables oil, carry out esterification with this alternative vegetable oil acid with soy(a)-bean oil fatty acid and/or ricinolic acid, Resins, epoxy.Not only can directly utilize the vegetables oil that contains conjugated double bond to participate in reaction, make it absolutely to obtain utilizing, the raw material availability height, thereby improved the more expensive vegetables oil utilization ratio of price, reduced product and production cost, preparation technology is simple, cost is low, and the gained epoxy ester resin is not only of light color, and fineness is good, stores and does not return slightly.Remix apple anhydride dehydration resin is abandoned and is converted modification, the gained modified epoxy ester resin not only can reduce the consumption of the more expensive vegetables oil of price, Resins, epoxy, further reduces cost, about 3-10% that can reduce cost, but also help improving the drying rate and the grinability of lacquering paint film.Secondary batching of the present invention, esterification after the first addition, technology is simple, and control is easy, and esterification is abundant.Epoxy ester resin of the present invention uses as the film-forming resin of antifouling paste, insullac and enamel paint equally, and it is fast that gained coating has drying rate, and grinability and good corrosion resistance make coating have more best performance.
Below in conjunction with three embodiments, further specify the present invention, but the embodiment of the invention should not be construed as to concrete qualification of the present invention.
Embodiment
Embodiment 1: get 20% tung oil, and 0.16% cis-butenedioic anhydride, 30% soy(a)-bean oil fatty acid drops in the stainless steel cauldron, seals dog-house, opens blow-off valve, logical CO
2Behind the gas 15min, begin to stir.Be warming up to 160 ℃-170 ℃, insulation 30min.Insulation drops into 49.84% Resins, epoxy after finishing again, seals dog-house, opens condenser cooling water, opens return valve, adds backflow dimethylbenzene, is warming up to 180 ℃, and insulation 2h rises to 210 ℃ of insulations with the time about 1.5h then.Behind 210 ℃ of insulation 2h, control in the sampling, qualified until middle control.Logical immediately nitrogen or CO after middle control is qualified
2, be cooled to about 100 ℃, slowly add letdown solvent dun and apple anhydride dehydration resin 20% (in epoxy ester resin), beat circulation 1h after, sampling is transferred sticking, surveys fineness, suitable after, the press filtration packing.Concrete technical parameter sees the following form.
Embodiment 2: oleum lini 18%, cis-butenedioic anhydride 0.1%, ricinolic acid 35%, Resins, epoxy 46.9%.The preparation method can add oleum lini and cis-butenedioic anhydride earlier after addition reaction, ricinolic acid and Resins, epoxy is added again, and all the other are substantially with embodiment 1.Gained epoxy ester resin surface drying 30 minutes was done solid work 15 hours, and all the other indexs are similar substantially to embodiment 1.
Embodiment 3: Chinese catalpa oil 26%, cis-butenedioic anhydride 0.35%, soy(a)-bean oil fatty acid 15%, ricinolic acid 13%, Resins, epoxy 45.65%.The preparation method is substantially with embodiment 1, and gained epoxy ester resin surface drying 30 minutes was done solid work 15 hours, and all the other indexs are similar substantially to embodiment 1.
Modified epoxy ester resin of the present invention and conventional epoxy ester resin and the lacquering technical indicator contrast table of producing
Epoxy ester resin performance comparison table
| Sequence number | Project | Epoxy ester resin of the present invention | Conventional epoxy ester resin |
| ??1 | Outward appearance (range estimation) | Brown yellow transparent liquid | Brown yellow transparent liquid |
| ??2 | Solids content % | ????50±2 | ????50±2 |
| ??3 | Color and luster (Fe-Co) number≤ | ????10 | ????12 |
| ??4 | S/25 ℃ of viscosity (being coated with-4 glasss) | ????80～160 | Below 80 |
| ??5 | Fineness (scraper plate fineness) um≤ | ????20 | Return thick |
Epoxy ester iron oxide red primer performance comparison table
| Sequence number | Project | Iron oxide red primer of the present invention | Conventional iron oxide red primer |
| ??1 | Fineness (scraper plate fineness) um≤ | ????45 | ????45 |
| ??2 | Time of drying (surface drying) | 20 minutes | 1 hour |
| (doing solid work) | 12 hours | 20 hours | |
| ??3 | Shock-resistant 50Kg.cm | By | By |
| ??4 | Hardness (pencil) | ????HB | ????HB |
| ??5 | Snappiness mm | ????1 | ????1 |
| ??6 | Sticking power (drawing the circle method) level | ????1～2 | ????1～2 |
| ??7 | Anti-30%NaCl hour | ????72 | ????48 |
| ??8 | Film thickness um | ????20 | ????20 |
Claims (9)
1, a kind of epoxy ester resin is characterized in that the vegetables oil that contains conjugated double bond by 15～30% (making WT), 0.1～0.5% MALEIC ANHYDRIDE, 25～40% soy(a)-bean oil fatty acid and/or ricinolic acid, and 40～55% Resins, epoxy reaction and getting.
2,, it is characterized in that the said vegetables oil that contains conjugated double bond is a tung oil according to the described epoxy ester resin of claim 1.
3,, it is characterized in that said esterification gained epoxy ester remix has the apple anhydride dehydration resin of (in epoxy ester) 15～25% (wt) according to claim 1 or 2 described epoxy ester resins.
4, according to the described epoxy ester resin of claim 3, it is characterized in that containing in the said epoxy ester resin molecular characterization of cis-butenedioic anhydride vegetables oil and Resins, epoxy esterification, and the apple anhydride dehydration resin.
5, the described epoxy ester resin preparation method of a kind of claim 1, it is characterized in that at first making the vegetables oil and the MALEIC ANHYDRIDE addition reaction (Diels-Alder) that contain conjugated double bond, obtain the cis-butenedioic anhydride vegetables oil, and then mix with Resins, epoxy and to carry out esterification.
6, according to the described epoxy ester resin preparation method of claim 5, the vegetables oil, the MALEIC ANHYDRIDE that it is characterized in that soy(a)-bean oil fatty acid and/or ricinolic acid and contain conjugated double bond add simultaneously.
7,, it is characterized in that containing the vegetables oil of conjugated double bond and the addition reaction of cis-butenedioic anhydride is carried out in 110 ℃ of-180 ℃ of temperature according to the described epoxy ester resin preparation method of claim 5.
8,, it is characterized in that the apple anhydride dehydration resin uniform mixing of gained epoxy ester and 15～25% (WT is in epoxy ester) according to claim 5,6 or 7 described epoxy ester resin preparation methods.
9, described according to Claim 8 epoxy ester resin preparation method is characterized in that reacting the gained epoxy ester and is cooled to 80-160 ℃, and adding apple anhydride dehydration mixed with resin is even.