CN1557761A - Glazed heat-insulating polyphenylene tile and its construction process - Google Patents
Glazed heat-insulating polyphenylene tile and its construction process Download PDFInfo
- Publication number
- CN1557761A CN1557761A CNA2004100017795A CN200410001779A CN1557761A CN 1557761 A CN1557761 A CN 1557761A CN A2004100017795 A CNA2004100017795 A CN A2004100017795A CN 200410001779 A CN200410001779 A CN 200410001779A CN 1557761 A CN1557761 A CN 1557761A
- Authority
- CN
- China
- Prior art keywords
- cement
- brick
- sand
- layer
- heat insulating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The color heat insulating polystyrene brick consists of surface layer, middle layer and bottom layer. The surface layer consists of cement, sand, brightening agent and micro swelling agent; the middle layer consists of cement, broken stone, coarse whiting powder and polymer adhesive; and the bottom layer consists of cement, coarse whiting powder, sand, polymer adhesive, polystyrene grain, waterproof agent and setting accelerator. The construction process with the color heat insulating polystyrene brick includes leveling with cement mortar; forming waterproof mortar layer with materials including cement, coarse whiting powder, sand, polymer adhesive and waterproof agent; and laying the color heat insulating polystyrene brick. The color heat insulating polystyrene brick has good decoration effect, high strength, and high heat insulating and sound absorbing effect.
Description
Technical field
The present invention relates to a kind of block member that is mainly used in the isolated of buildings roof floor slab and protection, especially a kind of have glory polyphenyl heat insulating brick and a construction techniques thereof well heat insulation, water resistance.
Background technology
Heat insulation, waterproof, insulation, the sound insulation on building roofing, roof and to beautify etc. be a great problem of building trade, its specification of quality height, influence factor complexity such as environment.Existing insulating brick has the chicken girt of employing reinforced cement pearl insulating brick, non-fired high-strength float bead heat insulation brick, sintered insulating hollow brick, nido vacuum heat-insulation brick, haydite terrace ventilating heat-proof brick, marbled finish insulating brick, covered insulating brick, nichrome wire insulating brick etc.The CN2071214U patent provides a kind of insulating brick, and its one side is a plane surface, and another side is provided with recessed portion parallel to each other or that intersect in length and breadth, and the cross section of recessed portion is arch.The CN1113532A patent application discloses a kind of roof heat insulation insulating brick and composition of raw materials thereof, and is formulated by pearlstone, cinder, cement, water, rock wool (aluminum silicate fiber), glass fibre, carbide slag etc., gets final product according to conventional brick-making method.The CN1073232A patent application discloses a kind of roof insulation brick, and it comprises on brick body, the brick body and be processed with cavity that the below of brick body is provided with feet.The CN2507942Y patent disclosure Roofing brick used of a kind of buildings roof, in the groove of spill facing tile, embed a porous plastics.A kind of covered insulating brick of CN2344466Y patent disclosure (plate) is made of heat insulating layer, covered surface layer, and the heat insulating layer is coated with the covered precoat.The CN2479092Y patent provides a kind of light heat-insulation brick, plate; be composited by brick layer and waterproof light concrete layer; wherein the brick layer is cement rank brick, concrete slab or ceramic tile etc., and the waterproof light concrete layer is granular polystyrene concrete, lightweight aggregate concrete or gas concrete etc.Adopt composite molding technique, interlayer does not use any other adhesives.The CN2519825Y patent provides a kind of improved insulating brick, its upper strata, each side layer constitute by the mixolimnion of cement, sand, resin, lower floor's middle body is made of polystyrene layer, and on the polystyrene layer of bottom surface, contain the cement mixolimnion in conjunction with on it by thin, make each interface of cement mixing layer and polystyrene be intimate-association state.
Summary of the invention
The object of the present invention is to provide a kind of is raw material with cement, dicalcium powder, sand, rubble, additive etc., heat insulation, insulation, good water-proof effect, ultimate compression strength is big, the glory polyphenyl heat insulating brick and the construction techniques thereof that are used for construction work that density water-intake rate and thermal conductivity are less.
The said glory polyphenyl of the present invention heat insulating brick by upper layer, middle layer and bottom totally 3 layers form, the material component of upper layer and be by the content of mass ratio: cement: sand: brightening agent: micro-expanding agent=1: (1.5～2.5): (0.03～0.06): (0.02～0.04), the thickness of upper layer are 5～8mm; The material component in middle layer and be by the content of mass ratio: cement: microlith: dicalcium powder: polymer adhesive=1: (1.5～2.5): (0.5～0.8): (0.04～0.07), microlith granularity are 2～4mm, and the thickness in middle layer is 8～10mm; The material component of bottom and be: cement: dicalcium powder: sand: polymer adhesive: granular polystyrene: water-resisting agent: accelerating chemicals=1: (0.5～0.8): (0.3～0.6): (0.05～0.08): (0.03～0.05): (0.04～0.07): (0.01～0.02) by the content of mass ratio, the granularity of granular polystyrene is 2.5～4mm, and the thickness of bottom is 23～25mm.Should add suitable quantity of water when making glory polyphenyl heat insulating brick, generally can be by 40%～60% of cement quality.
The cement of upper layer can adopt colored cement, or white cement, or white cement and colored cement, and its proportioning is selected according to need.
The processing step of the said glory polyphenyl of the present invention heat insulating brick constructional method is:
1, the screed-coat of on the roof slope making layer, constructing:
The screed-coat material is a sand-cement slurry, and its content by mass ratio is cement: sand=1: (3～5), thickness are 20～40mm.
2, construction waterproof screed on screed-coat:
Waterproof mortar layer material and be by the content of mass ratio: cement: dicalcium powder: sand: polymer adhesive: water-resisting agent=1: (0.8～1): (1～1.5): (0.1～0.2): (0.05～0.1), its thickness are 5～10mm.After stirring in proportion, waterproof mortar spreads upon on the screed-coat surface layer.
3, on the waterproof mortar layer, lay glory polyphenyl heat insulating brick:
The setting-out routing is decided benchmark before the tile work, and the distance between brick and the brick is promptly stitched the wide 10mm that is, reserves the lattice seam at roofing, and stitching wide is 20mm.Lattice seam scope is 6m * 6m, and lattice seam pointing is modifying asphalt sealing material or synthetic macromolecule sealing material.Planeness or inclined-plane degree must be controlled at the 2m error and be no more than 3mm during tile work.The brickwork joint packing material in the brickwork joint degree of depth is 20～30mm with the compacting of 1: 3 dried wet cement mortar.Water is moistening in stitching before the compacting.Stay 5～20mm degree of depth to add 10%～20% water-resisting agent with 3: 1 sand-cement slurry and stir with dried wet cement mortar compacting press polish, guarantee that whole roofing does not seep water, will keep clean during whole roofing joint filling, the hollowing phenomenon must not appear in brick and basic unit.
4, the timely water seasoning in whole roofing completion back.
In building operation, should add suitable quantity of water, press 40%～60% of cement quality usually.
Compare with existing insulating brick, because heat insulating brick of the present invention is rational in infrastructure, starting material are selected and the prescription advanced person, and its upper layer adopts colored cement, brightening agent etc., therefore any surface finish, bright forms the glory surface with reduction intensity of illumination and decorative effect.Because being microlith, the middle layer mixes earth resistance to compression tack coat, so the ultimate compression strength height, durable in use, not fragile.Because bottom adopts raw materials such as granular polystyrene, and upper layer and bottom formation twice insulating, good heat-insulation and heat-preservation and sound-absorbing effect therefore had.After testing, its thermal conductivity, density, ultimate compression strength and water-intake rate etc. all are higher than the technical requirements of product standard.Simultaneously, the weight of heat insulating brick of the present invention is lighter, cheap, is fit to environmental requirement, is a kind of novel material of construction.Because the material weight of using in the heat insulating brick architectural construction technology of the present invention is light, cohesive force is strong, technology advanced person, reduced processing step, so the bulk strength height, do not had cracking, brickwork joint adopts the water-proof material jointing, whole roofing does not seep water, form twice waterproof system with the waterproof mortar layer, heat-insulation and heat-preservation sound-absorbing etc. are effective, and construction costs can save 30%～50%, duration obviously shortens, and its economic benefit and social benefit are obvious.
Description of drawings
Fig. 1 is the structural representation of glory polyphenyl heat insulating brick.
Fig. 2 is a glory polyphenyl heat insulating brick roofworks integrated construction synoptic diagram.
Embodiment
Following examples will the present invention is further illustrated.
Embodiment 1:
Referring to Fig. 1, the said glory polyphenyl of the present invention heat insulating brick by upper layer A, middle layer B and bottom C totally 3 layers form, the raw material of upper layer and be: cement: sand: brightening agent: micro-expanding agent=1: 1.5: 0.06 by the content of mass ratio: 0.03, the thickness of upper layer is 8mm; The raw material in middle layer and be: cement: microlith: dicalcium powder: polymer adhesive=1: 2: 0.5 by the content of mass ratio: 0.05, the microlith granularity is 3mm, the thickness in middle layer is 9mm; The raw material of bottom and be: cement: dicalcium powder: sand: polymer adhesive: granular polystyrene: water-resisting agent: accelerating chemicals=1: 0.5: 0.3: 0.08: 0.03: 0.05: 0.015 by the content of mass ratio, the granularity of granular polystyrene is 3mm, and the thickness of bottom is 23mm.
The cement of upper layer can adopt white cement and colored cement, and its proportioning is 1: 1.
The heat insulating brick specification of gained is elected 250mm (length) * 250mm (wide) * 40mm (thick) as.Planeness≤2mm, diagonal lines is poor≤4mm, length and width, thickness deviation are ± 3mm.
Brightening agent is selected from that the Guangzhou is super moulds that material company limited is super moulds the board product, and model is ESP-8; Micro-expanding agent is selected from Wuhan huge England Premier League king company limited three male board products, and model is JYQ796; Polymer adhesive is selected from Shenzhen willing ox waterproof company limited Nike and reaches the board product, and model is NKD-7, or Huangshi people from city and extraordinary building materials company limited product; Water-resisting agent is selected from Shenzhen willing ox waterproof company limited Nike and reaches the board product, and model is NKD-6, or Xianyang water-proof material factory product; Accelerating chemicals is selected from Wuhan huge England Premier League king company limited three male board products, and model is JYQ798; Dicalcium powder is selected from Longyan, Fujian Province ruddiness Building Materials Factory ruddiness board product, and model is HG-01; The plastics granular polystyrene is selected from Xiamen City's letter can reach industry and trade company limited product.
Referring to Fig. 2, the said glory polyphenyl of the present invention heat insulating brick constructional method adopts following processing step:
Construction screed-coat 3 on the sloping layer on the roof construction layer 54: the screed-coat material is a sand-cement slurry, and its content by mass ratio is cement: sand=1: 4, thickness are 30mm.Construction waterproof screed 2 on screed-coat 3: waterproof mortar layer material and be by the content of mass ratio: cement: dicalcium powder: sand: polymer adhesive: water-resisting agent=1: 0.8: 1.3: 0.15: 0.07, its thickness was 7mm.After stirring in proportion, waterproof mortar spreads upon on the screed-coat surface layer.Lay glory polyphenyl heat insulating brick 1 on the waterproof mortar layer: the setting-out routing is decided benchmark before the tile work, and the seam between brick and the brick is wide to be 10mm, reserves the lattice seam at roofing, and stitching wide is 20mm.Lattice seam scope is 6m * 6m, and lattice seam pointing is the modifying asphalt sealing material.Planeness or inclined-plane degree must be controlled at the 2m error and be no more than 3mm during tile work.The brickwork joint packing material in brickwork joint degree of depth 30mm with the compacting of 1: 3 dried wet cement mortar.Water is moistening in stitching before the compacting.Stay the 10mm degree of depth to add 15% water-resisting agent with 3: 1 sand-cement slurry and stir with dried wet cement mortar compacting press polish, guarantee that the whole roofing of seam does not seep water, will keep clean during whole roofing joint filling, the hollowing phenomenon must not appear in brick and basic unit.
Embodiment 2:
Similar to Example 1, its difference is the raw material of upper layer and by the content of mass ratio is: colored cement: sand: brightening agent: micro-expanding agent=1: 2: 0.05: 0.04, and the thickness of upper layer is 6mm; The raw material in middle layer and be: cement: microlith: dicalcium powder: polymer adhesive=1: 2.5: 0.6: 0.07 by the content of mass ratio, the microlith granularity is 2mm, the thickness in middle layer is the raw material of 8mm bottom and by the content of mass ratio is: cement: dicalcium powder: sand: polymer adhesive: granular polystyrene: water-resisting agent: accelerating chemicals=1: 0.6: 0.5: 0.05: 0.05: 0.07: 0.02, the granularity of granular polystyrene is 2.5mm, and the thickness of bottom is 25mm.
Referring to Fig. 2, the said glory polyphenyl of the present invention heat insulating brick constructional method is identical with embodiment 1.
Construction screed-coat 3 on roof slope making layer 4: the screed-coat material is a sand-cement slurry, and its content by mass ratio is cement: sand=1: 4, thickness are 20mm.Construction waterproof screed 2 on screed-coat 3: waterproof mortar layer material and be by the content of mass ratio: cement: dicalcium powder: sand: polymer adhesive: water-resisting agent=1: 0.9: 1.5: 0.2: 0.05, its thickness was 10mm.After stirring in proportion, waterproof mortar spreads upon on the screed-coat surface layer.Lay glory polyphenyl heat insulating brick 1 on the waterproof mortar layer: the setting-out routing is decided benchmark before the tile work, and the seam between brick and the brick is wide to be 10mm, reserves the lattice seam at roofing, and stitching wide is 20mm.Lattice seam scope is 6m * 6m, and lattice seam pointing is the modifying asphalt sealing material.Planeness or inclined-plane degree must be controlled at the 2m error and be no more than 3mm during tile work.The brickwork joint packing material in brickwork joint degree of depth 25mm with the compacting of 1: 3 dried wet cement mortar.Water is moistening in stitching before the compacting.Stay the 20mm degree of depth to add 10% water-resisting agent with 3: 1 sand-cement slurry and stir with dried wet cement mortar compacting press polish, guarantee that whole roofing does not seep water, will keep clean during whole roofing joint filling, the hollowing phenomenon must not appear in brick and basic unit.
Embodiment 3:
Similar to Example 1, its difference is the raw material of upper layer and by the content of mass ratio is: cement: sand: brightening agent: micro-expanding agent=1: 2.5: 0.03: 0.02, and the thickness of upper layer is 5mm; The raw material in middle layer and be: cement: microlith: dicalcium powder: polymer adhesive=1: 1.5: 0.8 by the content of mass ratio: 0.04, the microlith granularity is 4mm, the thickness in middle layer is 10mm; The raw material of bottom and be: cement: dicalcium powder: sand: polymer adhesive: granular polystyrene: water-resisting agent: accelerating chemicals=1: 0.8: 0.6: 0.06: 0.04: 0.04: 0.01 by the content of mass ratio, the granularity of granular polystyrene is 4mm, and the thickness of bottom is 24mm.
Referring to Fig. 2, the said glory polyphenyl of the present invention heat insulating brick constructional method is identical with embodiment 1.
Construction screed-coat 3 on roof slope making layer 4: the screed-coat material is a sand-cement slurry, and its content by mass ratio is cement: sand=1: 5, thickness are 40mm.Construction waterproof screed 2 on screed-coat 3: waterproof mortar layer material and be by the content of mass ratio: cement: dicalcium powder: sand: polymer adhesive: water-resisting agent=1: 1: 1: 0.1: 0.1, its thickness was 5mm.After stirring in proportion, waterproof mortar spreads upon on the screed-coat surface layer.Lay glory polyphenyl heat insulating brick 1 on the waterproof mortar layer: the setting-out routing is decided benchmark before the tile work, and the seam between brick and the brick is wide to be 10mm, reserves the lattice seam at roofing, and stitching wide is 20mm.Lattice seam scope is 6m * 6m, and lattice seam pointing is the synthetic macromolecule sealing material.Planeness or inclined-plane degree must be controlled at the 2m error and be no more than 3mm during tile work.The brickwork joint packing material in brickwork joint degree of depth 20mm with the compacting of 1: 3 dried wet cement mortar.Water is moistening in stitching before the compacting.Stay the 5mm degree of depth to add 20% water-resisting agent with 3: 1 sand-cement slurry and stir with dried wet cement mortar compacting press polish, guarantee that whole roofing does not seep water, will keep clean during whole roofing joint filling, the hollowing phenomenon must not appear in brick and basic unit.
Claims (3)
1, glory polyphenyl heat insulating brick, it is characterized in that by upper layer, middle layer and bottom totally 3 layers form, the raw material of upper layer and be by the content of mass ratio: cement: sand: brightening agent: micro-expanding agent=1: 1.5～2.5: 0.03～0.06: 0.02～0.04, the thickness of upper layer are 5～8mm; The raw material in middle layer and be by the content of mass ratio: cement: microlith: dicalcium powder: polymer adhesive=1: 1.5～2.5: 0.5～0.8: 0.04～0.07, microlith granularity are 2～4mm, and the thickness in middle layer is 8～10mm; The raw material of bottom and be: cement: dicalcium powder: sand: polymer adhesive: granular polystyrene: water-resisting agent: accelerating chemicals=1: 0.5～0.8: 0.3～0.6: 0.05～0.08: 0.03～0.05: 0.04～0.07: 0.01～0.02 by the content of mass ratio, the granularity of granular polystyrene is 2.5～4mm, and the thickness of bottom is 23～25mm.
2, glory polyphenyl heat insulating brick as claimed in claim 1 is characterized in that the cement of upper layer adopts colored cement, or white cement, or white cement and colored cement.
3, glory polyphenyl heat insulating brick construction techniques is characterized in that the steps include:
1), the screed-coat of constructing on the roof slope making layer: the screed-coat material is a sand-cement slurry, and its content by mass ratio is cement: sand=1: 3～5, thickness are 20～40mm;
2), construction waterproof screed on screed-coat: waterproof mortar layer material and be: cement: dicalcium powder: sand: polymer adhesive: water-resisting agent=1: 0.8～1: 1～1.5: 0.1～0.2: 0.05～0.1 by the content of mass ratio, its thickness is 5～10mm, spreads upon on the screed-coat surface layer after waterproof mortar stirs in proportion;
3), lay glory polyphenyl heat insulating brick on the waterproof mortar layer: the setting-out routing is decided benchmark before the tile work, seam between brick and the brick is wide to be 10mm, reserve the lattice seam at roofing, stitching wide is 20mm, lattice seam scope is 6m * 6m, lattice seam pointing is modifying asphalt sealing material or synthetic macromolecule sealing material, and planeness or inclined-plane degree must be controlled at the 2m error and be no more than 3mm during tile work; The brickwork joint packing material in the brickwork joint degree of depth is 20～30mm with the compacting of 1: 3 dried wet cement mortar; Water is moistening in stitching before the compacting; Stay 5～20mm degree of depth to add 10%～20% water-resisting agent with 3: 1 sand-cement slurry and stir with dried wet cement mortar compacting press polish, guarantee that whole roofing does not seep water, will keep clean during whole roofing joint filling, the hollowing phenomenon must not appear in brick and basic unit;
4) the timely water seasoning in whole roofing completion back.