CN1181402A - 'Ruyu' water durable paint - Google Patents
'Ruyu' water durable paint Download PDFInfo
- Publication number
- CN1181402A CN1181402A CN 96118785 CN96118785A CN1181402A CN 1181402 A CN1181402 A CN 1181402A CN 96118785 CN96118785 CN 96118785 CN 96118785 A CN96118785 A CN 96118785A CN 1181402 A CN1181402 A CN 1181402A
- Authority
- CN
- China
- Prior art keywords
- water
- polyvinyl alcohol
- features
- ultramarine
- ruyu
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A water-proof paint is prepared fro mwollastonite (120-150 Wt. portions), calcium hydroxide (50-150), light calcium carbonate (80-100), bentone (2-3), polyvinyl alcohol (18-20), 10% aqueous solution of boric acid (1.5-2), dibutyl phthalate (0.5-0.7), titanium oxide (2-5), ultramarine (2-25) and water, and features no poison and no damage to human body. The painted surface with it features jade-like appearance, high smoothness and finish degree, not cracking, high strength and hardness, no generation of bubbles, and water washing resistance (over 1000 times).
Description
The present invention relates to a kind of building coating, refer in particular to the water resistant abrasive proof coating that is used for metope.
In known prior art, the polyvinyl formal interior wall coating, it mainly consists of the polyvinyl alcohol hemiformal.Polyvinyl alcohol water solution, has certain adhesive property, can form clear films after the drying, but the water tolerance of this film is relatively poor, polyvinyl alcohol can improve its water resistance by acetalation, but the intensification of acetalation can influence its solubility property in water again, its end product is water-fast vinyl-formal resin, thereby in coatings industry, commercially available 803 interior wall coatings, actual what adopt is the aqueous solution of polyvinyl alcohol hemiformal, thereby the use properties of the coating products of producing with its has certain limitation, and its water-fast scrubbing property is about 100 times.
The purpose of this invention is to provide the novel wallcovering that a kind of water-fast scrubbing property surpasses 1000 times, use this coating after, the rete that metope forms is hard as smooth as jade.
Embodiment of the present invention are: adopt polyvinyl alcohol and boric acid to form water-fast the scrubbing property that complex compound improves coating, and then adding toughner dibutyl phthalate, the suspension agent wilkinite, good to have, the wollastonite powder of zero diopter, enhancing and suspension property is as main pigment extender, add again and join light calcium carbonate and calcium hydroxide, the titanium dioxide consumption that the minimizing valency is high, other adds an amount of yellow whitening agent ultramarine that removes.
Advantage of the present invention is: the metope layer that uses this coating to form is smooth smooth, highly polished, color and luster is even, non-foaming, not shedding, do not crack, have higher intensity and hardness, just like smooth, rigid surface as the jade, the water-fast performance of scrubbing is good, surpass more than 1000 times, this coating is nontoxic, and is tasteless, harmless.
Embodiment,
Getting 20 kilograms of polyvinyl alcohol is dissolved in 330 kg of water, under stirring state, add 0.5 kilogram of dibutyl phthalate, 2.5 kilograms in ultramarine, treat that above-mentioned composition all dissolves the back and adds 50 kilograms in the calcium hydroxide be soaked in water, 100 kilograms of light calcium carbonates, the wollastonite powder 120 kg, 2 kilograms of wilkinites, 2 kilograms of titanium dioxides, be stirred into suspension, add 2 kilograms of fully stirrings of boric acid aqueous solution of 10% again, make itself and polyvinyl alcohol finish complex reaction, filtration is anhydrated and part is stayed filter pulp, is as beautiful water resistant coating finished product.
Because the gap of material quality, in Industrial processes, the consumption weight ratio of various compositions can fluctuate in following ranges.
Wollastonite powder 120～150
Calcium hydroxide 50～150
Light calcium carbonate 80～100
Wilkinite 2～3
Polyvinyl alcohol 18～20
Boric acid 10% aqueous solution 1.5～2
Dibutyl phthalate 0.5～0.7
Titanium dioxide 2～5
Ultramarine 2～2.5
Claims (1)
1. a water resistant coating is characterized in that, it contains the composition of following weight ratio:
Wollastonite powder 120～150
Calcium hydroxide 50～150
Light calcium carbonate 80～100
Wilkinite 2～3
Polyvinyl alcohol 18～20
Boric acid 10% aqueous solution 1.5～2
Dibutyl phthalate 0.5～0.7
Titanium dioxide 2～5
Ultramarine 2～2.5
Water is an amount of.