CN115306087A - 预铺防水卷材 - Google Patents
预铺防水卷材 Download PDFInfo
- Publication number
- CN115306087A CN115306087A CN202210913992.1A CN202210913992A CN115306087A CN 115306087 A CN115306087 A CN 115306087A CN 202210913992 A CN202210913992 A CN 202210913992A CN 115306087 A CN115306087 A CN 115306087A
- Authority
- CN
- China
- Prior art keywords
- coating
- asphalt
- oil
- layer
- sand
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本申请实施例公开了一种预铺防水卷材。所述卷材包括：胎基层；第一沥青涂盖料层和第二沥青涂盖料层，其分别设于所述胎基层的两侧表面上，其中，所述第二沥青涂盖料层的表面上粘附有防粘颗粒以形成防粘表面；封油涂层，其涂布在所述防粘表面上；耐紫外涂层，其涂布在所述封油涂层的表面上。根据本申请实施例的涂盖料，封油涂层由于本身性质，具有阻隔极性低的或分子量小的有机物扩散的性能，可以阻挡沥青涂盖料层中所含的软化油等轻组分迁移到预铺防水卷材表面，覆盖到防粘颗粒表面或从防粘颗粒底部迁移，从而可以避免防粘颗粒易脱落失效；另外，封油涂层可以有效避免轻组分迁移而造成的耐紫外涂层变色的问题。
Description
技术领域
本申请属于建筑材料技术领域，尤其涉及一种预铺防水卷材。
背景技术
卷材，可以预铺于施工场地，且具有一定防水功能，是由高强度的胎基层、沥青涂盖料层、防粘颗粒层等组成的叠层结构，拥有预铺反粘的特性，其防粘颗粒层可以起隔离作用，防粘颗粒还能与后浇混凝土结合起到粘接及锚固的作用。
当卷材预铺在施工场地进行使用时，工人需要在卷材上面进行捆扎钢筋等施工操作，对卷材进行踩踏和挤压，常规产品容易因踩踏导致颗粒下陷沥青料露出而出现粘脚问题；而且因改性沥青涂盖料层与防粘颗粒直接连接，连接面积较小，产品在雨淋或水浸泡的情况下，水分子容易进入沥青涂盖料层与防粘颗粒间的界面，导致防粘颗粒与改性沥青料的粘接力下降从而出现泡水掉砂问题。
发明内容
本申请实施例提供一种预铺防水卷材，旨在解决卷材中防粘颗粒层易脱落失效的问题。
本申请第一方面的实施例提供一种预铺防水卷材，所述卷材包括：
胎基层；
第一沥青涂盖料层和第二沥青涂盖料层，其分别设于所述胎基层的两侧表面上，其中，所述第二沥青涂盖料层的表面上粘附有防粘颗粒以形成防粘表面；
封油涂层，其涂布在所述防粘表面上；
耐紫外涂层，其涂布在所述封油涂层的表面上。
在本申请的一些实施例中，所述第一沥青涂盖料层和第二沥青涂盖料层分别包括沥青、沥青改性剂、软化油、胶粉、填料和抗氧剂。
在本申请的一些实施例中，所述沥青选自石油沥青、天然沥青、煤焦沥青或其组合；和/或，
所述沥青改性剂选自苯乙烯-丁二烯-苯乙烯嵌段共聚物、苯乙烯-异戊二烯-苯乙烯、丁苯橡胶、氢化苯乙烯-丁二烯-苯乙烯嵌段共聚物、无规聚丙烯或其组合。
在本申请的一些实施例中，所述防粘颗粒的粒度为20～80目；和/或，
所述防粘颗粒选自白云石砂、云母砂、方解石砂、花岗岩砂、石英砂、碳酸钙砂、镁钙砂、瓷砂、铁砂、莫来砂、人造砂或其组合。
在本申请的一些实施例中，所述封油涂层包括聚乙烯醇；和/或，
所述封油涂层的厚度为0.5～10μm，可选为1～5μm。
在本申请的一些实施例中，所述封油涂层还包括偶联剂，所述偶联剂选自硅烷偶联剂、钛酸酯偶联剂、铝酸酯偶联剂或其组合。
在本申请的一些实施例中，所述偶联剂包括具有甲基丙烯酸基、氨基、脲基、环氧基、(甲基)丙烯酰氧基中的任意一种或几种官能团的硅烷偶联剂。
在本申请的一些实施例中，至少部分所述防粘颗粒之间存在空隙，并且所述封油涂层和所述耐紫外涂层分别在所述防粘颗粒之间的空隙处形成凹陷。
在本申请的一些实施例中，所述耐紫外涂层与所述封油涂层的总厚度≤所述防粘颗粒的平均粒径范围下限值的1/10；和/或，
所述耐紫外涂层与所述封油涂层的总厚度为5～80μm；可选为10～50μm。
在本申请的一些实施例中，所述卷材还包括：隔离膜层，所述隔离膜层设于所述第一沥青涂盖料层的表面。
本申请提供的预铺防水卷材，包括：卷材包括：胎基层；第一沥青涂盖料层和第二沥青涂盖料层，其分别设于所述胎基层的两侧表面上，其中，所述第二沥青涂盖料层的表面上粘附有防粘颗粒以形成防粘表面；封油涂层，其涂布在所述防粘表面上；耐紫外涂层，其涂布在所述封油涂层的表面上；封油涂层由于本身性质，具有阻隔极性低的或分子量小的有机物扩散的性能，可以阻挡沥青涂盖料层中所含的软化油等轻组分迁移到预铺防水卷材表面，覆盖到防粘颗粒表面或从防粘颗粒底部迁移，从而可以避免防粘颗粒易脱落失效；另外，封油涂层可以有效避免轻组分迁移而造成的耐紫外涂层变色的问题。
附图说明
为了更清楚地说明本申请实施例的技术方案，下面将对本申请实施例中所需要使用的附图作简单地介绍，显而易见地，下面所描述的附图仅仅是本申请的一些实施例，对于本领域普通技术人员来讲，在不付出创造性劳动的前提下，还可以根据附图获得其他的附图。
图1为本申请一实施例提供的预铺防水卷材的结构示意图。
其中，图中各附图标记为：
1、隔离膜层；2、第一沥青涂盖料层；3、胎基层；4、第二沥青涂盖料层；5、防粘颗粒；6、封油涂层；7、耐紫外涂层。
具体实施方式
为了使本申请的发明目的、技术方案和有益技术效果更加清晰，以下结合实施例对本申请进行进一步详细说明。应当理解的是，本说明书中描述的实施例仅仅是为了解释本申请，并非为了限定本申请。
为了简便，本文仅明确地公开了一些数值范围。然而，任意下限可以与任何上限组合形成未明确记载的范围；以及任意下限可以与其它下限组合形成未明确记载的范围，同样任意上限可以与任意其它上限组合形成未明确记载的范围。此外，尽管未明确记载，但是范围端点间的每个点或单个数值都包含在该范围内。因而，每个点或单个数值可以作为自身的下限或上限与任意其它点或单个数值组合或与其它下限或上限组合形成未明确记载的范围。
在本文的描述中，需要说明的是，除非另有说明，“以上”、“以下”为包含本数，“一种或多种”中的“多种”的含义是两种以上，“一个或多个”中的“多个”的含义是两个以上。
本申请的上述发明内容并不意欲描述本申请中的每个公开的实施方式或每种实现方式。如下描述更具体地举例说明示例性实施方式。在整篇申请中的多处，通过一系列实施例提供了指导，这些实施例可以以各种组合形式使用。在各个实施例中，列举仅作为代表性组，不应解释为穷举。
现有技术中，卷材中的防粘颗粒在被踩踏等环境中，易与沥青料发生位移，使沥青涂盖料露出，出现粘脚问题；另外，沥青涂盖料层与防粘颗粒连接面积较小，在雨淋或水浸泡的情况下，水分子容易进入沥青涂盖料层与防粘颗粒间的界面，导致防粘颗粒与沥青涂盖料的粘接力下降，降低使用寿命。
基于此，发明人进行了大量的研究，发现可以通过设置一层封油涂层，进而使卷材中各层相互协同作用下，使用于防水卷材的涂盖料可以在减少软化油使用量的基础上，使防粘颗粒在卷材中作用更持久，从而保持卷材的优良性能，延长卷材的使用寿命。
卷材
本申请第一方面的实施例提供了一种预铺防水卷材，所述卷材包括：
胎基层；
第一沥青涂盖料层和第二沥青涂盖料层，其分别设于所述胎基层的两侧表面上，其中，所述第二沥青涂盖料层的表面上粘附有防粘颗粒以形成防粘表面；
封油涂层，其涂布在所述防粘表面上；
耐紫外涂层，其涂布在所述封油涂层的表面上。
根据本申请实施例，通过设置封油涂层，封油涂层的本身材质可以防止低分子类有机物的迁移扩散，从而可以阻碍软化油、增塑剂等轻组分向外迁移；封油涂层为膜状物，耐紫外涂层可以有效阻隔水分子进入沥青涂盖料层与防粘颗粒间的界面，从而增强了卷材的稳定性与耐久性。轻组分还包括沥青中的一些小分子有机物。
根据本申请实施例，由于现有的防粘颗粒的排布存在空隙，无法完全遮挡阳光中的紫外线的照射和破坏，易引起沥青涂盖料层性能下降或失效，本申请设置了耐紫外涂层；当沥青涂盖料从卷材中迁移出，耐紫外涂层受其影响，发生变色并降低其耐紫外线照射的性能，封油涂层的设置可以有效避免轻组分迁移到耐紫外涂层，从而有效保护了耐紫外涂层的外观，使预铺防水卷材具有更长和更稳定的耐紫外线照射功能。
根据本申请实施例的预铺防水卷材，通过对卷材中不同层的设置，使得各层之间起到协同增效作用，从而赋予卷材以良好的稳定性、防水性、耐紫外线照射和耐久性，延长其使用寿命。
在一些实施例中，胎基层可以由高分子胎基、聚酯胎基、玻纤胎基或复合胎基等任意一种或几种胎基组成，也可以为胎基经过改性沥青浸涂料浸涂后形成，本申请实施例对胎基层的种类没有特别的限制，可根据实际需求进行选择，当胎基层选自上述种类，能够兼具良好的拉伸性能、机械强度。
在一些实施例中，耐紫外涂层可以通过用耐紫外涂料喷涂或淋涂、辊涂等方式涂布于卷材，经干燥后形成；所述耐紫外涂料主要成膜物质可以为柔性树脂，耐紫外涂料中还可以包括溶剂类、乳液类或反应类树脂，耐紫外涂料中还可以包含弹性体和合成树脂。
示例性地，柔性树脂包括并不限于丙烯酸树脂、VAE树脂、聚氨酯树脂、醇酸树脂、聚酯树脂、丁苯胶乳、氯丁胶乳、苯乙烯-丁二烯-苯乙烯嵌段共聚物(SBS)、苯乙烯-异戊二烯-苯乙烯(SIS)、氢化苯乙烯-丁二烯-苯乙烯嵌段共聚物(SEBS)、乙烯-丙烯共聚物为中间弹性嵌段的线型三嵌共聚物(SEPS)的一种或多种组合。
在一些实施例中，耐紫外涂料还可以包括颜填料，颜填料对紫外线具有反射作用，包括但不限于钛白粉、碳酸钙、纳米碳酸钙、碳酸镁、滑石粉、硫酸钡、锌钡白、云母粉、高岭土、玻璃微珠、金属粉中的一种或多种组合。耐紫外涂料中添加了颜填料可以增强抗粘连性。
在一些实施例中，耐紫外涂料还可以包括偶联剂，包括但并不限于硅烷偶联剂、酞酸酯偶联剂、铝酸酯偶联剂中的一种或多种组合。
在一些实施例中，耐紫外涂料中的偶联剂具有含甲基丙烯酸基、氨基、脲基、环氧基、甲基丙烯酰氧基硅烷等一种或几种官能团的偶联剂。
根据本申请实施例，耐紫外涂料中添加偶联剂可以提高耐紫外涂层与封油层之间附着力，以及提高喷印油墨的界面附着力。耐紫外涂层中可以含有偶联剂，也解决了卷材产品无法进行喷印操作或喷印后雨淋或泡水脱色渗色问题。
在一些实施例中，所述第一沥青涂盖料层和第二沥青涂盖料层分别包括沥青、沥青改性剂、软化油、胶粉、填料和抗氧剂。
根据本申请实施例，第一沥青涂盖料层和第二沥青涂盖料层中的各组分没有特别的限制，可根据实际需求进行选择。第一沥青涂盖料层和第二沥青涂盖料层中的轻组分包括来源于沥青的烃类和烯烃类物质、软化油等，软化油中可以包含废机油、减线油、橡胶油任意一种或几种。本申请实施例中，软化油这类轻组分可以使涂盖料中各种聚合物的分散，改善沥青的低温性能，达到调节沥青涂盖料的黏稠度的效果，如果软化油不在涂盖料组分中，会降低卷材的高低温性能和耐久性。
根据本申请的实施例，胶粉吸收基质沥青中的芳香分等而发生溶胀，可以对基质沥青起到改性作用，可以提高涂盖料的稳定性、粘接性以及防滑和耐磨性能。示例性地，胶粉包括硫化橡胶。填料作为涂盖料的补强材料，可以提高涂盖料的抗老化性能。示例性地，填料包括滑石粉、重质碳酸钙、蒙脱土和高岭土中的至少一种。
在一些实施例中，第一沥青涂盖料层和第二沥青涂盖料层还可以包括增塑剂，增塑剂也属于沥青涂盖料中的轻组分，如增塑剂迁移出沥青涂盖料会降低沥青涂盖料的性能，从而影响卷材的性能。
在一些实施例中，所述沥青选自石油沥青、天然沥青、煤焦沥青或其组合。
根据本申请的实施例，上述沥青的选择没有特别的限制，可根据实际需求进行选择。示例性地，当涂盖料中的沥青选用石油沥青时，石油沥青中包含烃类及非烃类衍生物这一类轻组分，当烃类及非烃类衍生物迁移出涂盖料，会使卷材的剥离强度下降，影响卷材的外观，降低卷材性能。
在一些实施例中，所述沥青改性剂选自苯乙烯-丁二烯-苯乙烯嵌段共聚物、苯乙烯-异戊二烯-苯乙烯、丁苯橡胶、氢化苯乙烯-丁二烯-苯乙烯嵌段共聚物、无规聚丙烯或其组合。
根据本申请的实施例，沥青改性剂是指在沥青或沥青混合料中加入的天然或人工合成的有机或无机材料，可熔融或分散在沥青中以改善或提高沥青的性能的物质。由于沥青改性剂能够有效阻止涂盖料中各组分间由于极性差异而导致的相分离，沥青改性剂可以使沥青涂盖料构成的沥青防水卷材的粘接性、低温柔性及耐久性等整体性能优异。
在一些实施例中，所述防粘颗粒的粒度为20～80目。
根据本申请的实施例，防粘颗粒的粒度选自上述粒径时，便于封油涂层和耐紫外线涂层在防粘颗粒空隙处形成凹陷。为避免防粘颗粒中灰尘或杂质过多导致质量问题，对超出标上述粒度范围的颗粒视为杂质进行限量控制，即超出规格粒度的杂质总质量占所以防粘颗粒的总质量≤5％。
在一些实施例中，所述防粘颗粒选自白云石砂、云母砂、方解石砂、花岗岩砂、石英砂、碳酸钙砂、镁钙砂、瓷砂、铁砂、莫来砂、人造砂或其组合。
在一些实施例中，所述防粘颗粒可以为石砂。
根据本申请的实施例，防粘颗粒可以为无机颗粒或有机颗粒，防粘颗粒可以没有白度、光反射率、光透射率及颜色要求，没有特别的限制，可根据实际需求进行选择，当防粘颗粒选自上述种类，能够具有良好的防粘性能。
在一些实施例中，为了提高产品的辨识度，采用墨水对防粘颗粒表面进行喷码或印刷，当卷材被雨淋或水浸泡后，墨水容易掉色。根据本申请实施例，在耐紫外涂层表面进行喷码或印刷，由于封油涂层的存在，封油涂层可以隔绝涂盖料层中的轻组分对墨水的作用，解决了墨水易掉色的问题，另外耐紫外涂层中可以含有偶联剂，避免了墨水易掉色。
在一些实施例中，所述封油涂层包括聚乙烯醇。
根据本申请的实施例，可以选用质量分数为1％～7％的聚乙烯醇水溶液通过喷涂或淋涂、辊涂等方式涂布于卷材表面后干燥形成的一种薄层结构。聚乙烯醇水溶液成膜后具有一定强度；聚乙烯醇具有耐溶剂性，且极性低的有机物很难通过聚乙烯醇，可以避免沥青涂盖料层中的轻组分渗透迁移。
在一些实施例中，聚乙烯醇的数均分子量可以为20000～250000。
在一些实施例中，聚乙烯醇的聚合度可以为400～2500，具有较佳的溶解性，可以有效涂布于防粘表面上。
在一些实施例中，封油涂层的厚度为0.5～10μm，可选为1～5μm。
根据本申请实施例，通过控制封油涂层的厚度为0.5～10μm，如封油涂层的厚度大于10μm，影响了防粘颗粒的表面形貌，使卷材与混凝土的剥离力下降，耐老化性降低；如封油涂层的厚度小于0.5μm，不能成膜起不到封油作用。
在一些实施例中，所述封油涂层还包括偶联剂，所述偶联剂选自硅烷偶联剂、钛酸酯偶联剂、铝酸酯偶联剂或其组合，含有偶联剂的封油涂层可以分别增强与防粘颗粒、耐紫外涂层之间附着力。
在一些实施例中，所述偶联剂包括具有甲基丙烯酸基、氨基、脲基、环氧基、(甲基)丙烯酰氧基中的任意一种或几种官能团的硅烷偶联剂。
在一些实施例中，至少部分所述防粘颗粒之间存在空隙，并且所述封油涂层和所述耐紫外涂层分别在所述防粘颗粒之间的空隙处形成凹陷。
根据本申请实施例，为了实现卷材与浇混凝土的粘接性能且保证封闭性能，所述封油涂层和耐紫外涂层干燥后没有完全充满防粘颗粒之间的空隙，保持了防粘颗粒原始的表面形貌，耐紫外涂层表面具有凹陷。
在一些实施例中，所述耐紫外涂层与所述封油涂层的总厚度≤所述防粘颗粒的平均粒径范围下限值的1/10。
根据本申请实施例，当耐紫外涂层与封油涂层的总厚度≤所述防粘颗粒的平均粒径范围下限值的1/10，厚，可以不改变防粘颗粒表面形貌，使用时，增强卷材与混凝土之间摩擦力，提高两者之间的剥离强度。
在一些实施例中，耐紫外涂层与封油涂层的总厚度为5～80μm；可选为10～50μm。
根据本申请实施例，所述耐紫外涂层与所述封油涂层经涂布干燥后的总厚度为5～80μm；优选为10～50μm；通过控制耐紫外涂层与封油涂层的总厚度，便于在不改变防粘颗粒表面的形貌基础上，形成凹陷，通过上述的凹陷增强了卷材与混凝土的摩擦能力，增强了卷材与混凝土的剥离强度。
在一些实施例中，所述卷材还包括：隔离膜层，所述隔离膜层设于所述第一沥青涂盖料层的表面。
根据本申请实施例，隔离膜可以为聚乙烯(Polyethylene，PE)膜、聚对苯二甲酸乙二醇酯(polyethylene glycol terephthalate，PET)和聚丙烯(polypropylene，PP)中的至少一种；隔离膜层的设置可以提供卷材耐紫外老化性能和涂盖料层的耐紫外老化性能，还可以使卷材具有优异的粘接性能和抗褶皱性能。
在一些实施例中，如图1所示，一种预铺防水卷材的结构如下：
胎基层3；
第一沥青涂盖料层2和第二沥青涂盖料层4，其分别设于所述胎基层3的两侧表面上，其中，所述第二沥青涂盖料4层的表面上粘附有防粘颗粒5以形成防粘表面；
封油涂层6，其涂布在所述防粘表面上；
耐紫外涂层7，其涂布在所述封油涂层的表面上；
隔离膜层1，所述隔离膜层1设于所述第一沥青涂盖料层2的表面。
卷材的制备方法
一种预铺防水卷材的制备方法，所述方法包括以下步骤：
S1.制备沥青涂盖料；
S2.将胎基进行预浸处理，以得到预浸胎基；
S3.将所述沥青涂盖料分别涂布于所述预浸胎基两侧表面，以得到胎基层、第一沥青涂盖料层和第二沥青涂盖料层；
S4.加热所述第二沥青涂盖料层至温度为50～90℃，将防粘颗粒设于所述第二沥青涂盖料层表面，进行压实，以得到附有防粘颗粒的第二沥青涂盖料；
S5.将封油涂料涂布于所述附有防粘颗粒的第二沥青涂盖料，进行干燥，以得到封油涂层；
S6.将耐紫外涂料涂布于所述封油涂层，进行干燥，以得到所述卷材。
可选的，将墨水喷射于耐紫外涂层表面，以提高卷材的辨识度；可选的，将卷材降温收卷，即得预铺防水卷材产品。
本申请实施例中，沥青涂盖料可以保温160～180℃备用；第二沥青涂盖料层可以被加热至表面温度为50～90℃后，通过撒砂装置均匀撒上防粘颗粒；封油涂料可以经温度为50～110℃的鼓风烘道后，干燥形成封油涂层，耐紫外涂料可以经温度为50～110℃的鼓风烘道后，干燥形成耐紫外涂层。
实施例
下述实施例更具体地描述了本申请公开的内容，这些实施例仅仅用于阐述性说明，因为在本申请公开内容的范围内进行各种修改和变化对本领域技术人员来说是明显的。除非另有声明，以下实施例中所报道的所有份、百分比、和比值都是基于重量计，而且实施例中使用的所有试剂都可商购获得或是按照常规方法进行合成获得，并且可直接使用而无需进一步处理，以及实施例中使用的仪器均可商购获得。
实施例1
一种沥青预铺防水卷材，其由PE隔离膜层、第一沥青涂盖料层、聚酯胎基层、第二沥青涂盖料层、莫来石砂防粘颗粒层、封油涂层和耐紫外涂层组成，聚酯胎基层的厚度为1.0mm，第一沥青涂盖料层厚度为1mm，第二沥青涂盖料层厚度为1mm，莫来石砂的粒径范围为0.2～0.45mm，封油涂层的干厚度为1μm，耐紫外涂层的厚度为10μm。
所述第一沥青涂盖料层和第二沥青涂盖料层分别由以下质量百分比的组分组成：
沥青(70#) 40.9％
橡胶油 11％
沥青改性剂 (SBS 411)3.5％
沥青改性剂 (SBR) 1.5％
再生胶粉 13％
填料(200目重钙) 30％
抗氧剂(BASF 1010) 0.1％
所述第一沥青涂盖料层由以下方法制备：
(1)往反应釜中分别投入称量好的沥青、橡胶油，以400～500rpm转速搅拌升温至150～160℃；
(2)依次分别缓慢投入称量好的沥青改性剂，以700～800RPM转速搅拌升温至180±5℃恒温搅拌30min；
(3)搅拌中缓慢投入称量好的再生胶粉，恒温180±5℃以700～800RPM转速搅拌2～3h至胶粉和沥青改性剂熔融完全及胶粉充分溶胀；
(4)搅拌中缓慢投入称量好的抗氧剂，恒温180±5℃以700～800RPM转速搅拌15min，将所得物料经胶体磨研磨后经管道输入到分散釜中；
(5)搅拌中缓慢投入称量好的填料，恒温160～180℃以900～1000RPM高速分散1～2h至填料分散均匀，即得所述改性沥青涂盖料；
所述封油涂层由封油涂料干燥后形成，所述封油涂料主要由含有1％质量分数浓度的聚乙烯醇水溶液组成；
所述耐紫外涂层由耐紫外涂料干燥后形成，所述耐紫外涂料主要由以下质量百分比的组分组成：
树脂(热塑性橡胶SIS，岳化SIS 1105) 4.30％
树脂(加氢碳五石油树脂) 3.90％
树脂(低聚丁烯，大林PB1300) 3.50％
抗氧剂(BASF 168) 0.20％
紫外助剂(BASF 328) 0.10％
紫外助剂(BASF 770) 0.10％
溶剂(二氯甲烷) 57.00％
溶剂(碳酸二甲酯) 22.30％
分散剂(BYK103) 0.30％
颜填料(钛白粉杜钛R-706) 5.00％
颜填料(竹原SP纳米碳酸钙) 3.00％
增稠剂(德山DM-20S) 0.10％
偶联剂(KH-560) 0.10％
消泡剂 0.05％
流平剂 0.05％
上述耐紫外涂料按如下方法制备：
(1)将计量的溶剂的一半分别投入分散釜中，开启搅拌，控制转速300～400rpm；
(2)搅拌中依次投入计量的树脂，300～400rpm搅拌至树脂溶解完全；
(3)投入计量的一种或多种分散剂，边搅拌边缓慢投入分散釜中，控制转速400～500rpm搅拌5min；
(4)按顺序边搅拌边缓慢加入增稠剂、颜填料、抗氧剂、紫外助剂、消泡剂、流平剂，控制转速900～1000rpm分散15～20min；
(5)边搅拌边缓慢加入计量的偶联剂，控制转速600～700rpm分散5～10min；
(6)将物料通过管道传输至砂磨机或三辊机，研磨至最大细度≤5μm；
(7)将物料通过管道传输回分散釜，边搅拌边将剩余的溶剂投入分散釜中，300～400rpm搅拌10～15min；
(8)用200目滤网过滤出料备用。
所述卷材按如下方法制备：
(1)按所述改性沥青涂盖料制备方法制备改性沥青涂盖料，保温160～180℃备用，将准备好的胎基放置于相应放卷机并对齐，开启放卷机放卷，胎基经牵引后往生产线后端展开；
(2)胎基经过改性沥青预浸料池进行预浸处理，并经对辊挤压掉多余的预浸料后，胎基继续往后端展开；
(3)在经过涂胶模头的时候分别在胎基上表面及下表面均匀涂上相应厚度的改性沥青涂盖料，并在第一沥青涂盖料层表面覆盖上一层隔离膜后在牵引作用下继续向后端展开；
(4)所得卷材在经过加热烘道后被加热至第二沥青涂盖料层表面温度为50～90℃后通过撒砂装置在第二沥青涂盖料层表面均匀撒上所述颗粒形成颗粒层，然后经过辊压压实颗粒层，清砂装置清理掉多余的颗粒后继续往后端展开；
(5)所得卷材经喷涂通道1，并于卷材表面(颗粒层面)均匀喷涂一层所述封油涂料，涂料充分润湿颗粒层表面及颗粒层间隙的热熔胶表面后经过设置温度为50～110℃的鼓风烘道后干燥形成封油涂层，所得卷材继续往后端展开；
(6)所得卷材经喷涂通道2，并于卷材表面(封油涂层面)均匀喷涂一层所述耐紫外涂料，涂料充分润湿封油涂层表面后经过设置温度为50～110℃的鼓风烘道后干燥形成耐紫外涂层，所得卷材继续往后端展开；
(7)所得卷材经过喷印机喷上品牌LOGO或装饰性印刷内容后，继续往后端展开；
(8)所得卷材经降温装置降温后收卷，即得所述卷材成品。
实施例2
一种预铺防水卷材，其由PET涂硅油隔离膜层、第一沥青涂盖料层、聚酯胎基层、第二沥青涂盖料层、白云石砂防粘颗粒层、封油涂层以及耐紫外涂层组成，聚酯胎基层的厚度为1.2mm，第一沥青涂盖料层厚度为1.4mm，第二沥青涂盖料层厚度为1.4mm，白云石砂的粒径范围为0.3～0.6mm，封油涂层干厚度5μm，耐紫外涂层干厚度为30μm。
所述第一沥青涂盖料层和第二沥青涂盖料层分别由以下质量百分比的组分组成：
沥青(90#) 40.5％
橡胶油 10％
沥青改性剂(SBS 501) 3％
沥青改性剂(APP) 1％
沥青改性剂(SBR) 1.5％
再生胶粉 14.8％
填料(200目重钙) 29％
抗氧剂(二丁基羟基甲苯BHT) 0.2％
按实施例1改性沥青涂盖料制备方法制备改性沥青涂盖料。
所述封油涂层由封油涂料干燥后形成，所述封油涂料主要由含有3％质量分数浓度的聚乙烯醇水溶液组成；
所述耐紫外涂层由耐紫外涂料干燥后形成，所述耐紫外涂料主要由以下质量百分比的组分组成：
树脂(SEBS，科腾G1701) 4.50％
树脂(加氢DCPD树脂) 3.60％
树脂(低聚丁烯，大林PB950) 2.50％
抗氧剂(BASF 1010) 0.20％
紫外助剂(BASF 326) 0.10％
紫外助剂(BASF770) 0.10％
溶剂(二氯甲烷) 52.00％
溶剂(乙酸乙酯) 27.45％
分散剂(EFKA4608) 0.30％
颜填料(钛白粉龙蟒R-996) 4.00％
颜填料(2500目滑石粉) 5.00％
增稠剂(BYK-410) 0.05％
偶联剂(OFS-6040) 0.10％
消泡剂 0.05％
流平剂 0.05％
按实施例1所述制备方法制备得到耐紫外涂料。
按实施例1所述制备方法制备得到沥青基高分子预铺防水卷材。
实施例3
一种预铺防水卷材，由PP隔离膜层、第一沥青涂盖料层、玻纤胎基层、第二沥青涂盖料层、瓷砂防粘颗粒层、封油涂层以及耐紫外涂层组成，玻纤胎基层的厚度为1.2mm，第一沥青涂盖料层厚度为1.4mm，第二沥青涂盖料层厚度为1.4mm，瓷砂的粒径范围为0.25～0.5mm，封油涂层干厚度3μm，耐紫外涂层干厚度为15μm。
所述第一沥青涂盖料层和第二沥青涂盖料层分别由实施例1所述改性沥青涂盖料组成，并按实施例1改性沥青涂盖料制备方法制备改性沥青涂盖料。
所述封油涂层由封油涂料干燥后形成，所述封油涂料主要由含有7％质量分数浓度的聚乙烯醇水溶液组成；
所述耐紫外涂层由耐紫外涂料干燥后形成，所述耐紫外涂料主要由以下质量百分比的组分组成：
乳液(巴德富327K) 34％；
分散剂(陶氏9830) 0.3％；
颜填料(1000目煅烧高岭土) 10％
颜填料(钛白粉龙蟒R-996) 7％；
增稠剂(羟乙基纤维素醚) 0.1％；
偶联剂(KH-550) 0.3％；
消泡剂 0.2％
流平剂 0.1％；
乙醇 10％
清水 38.3％
所述耐紫外涂料按如下方法制备：
(1)将计量的乳液投入分散釜中，开启搅拌，控制转速300～400rpm；
(2)将计量的一种或多种润湿分散剂与占配方质量分数5％比例的清水预先混合后，边搅拌边缓慢投入分散釜中，控制转速400～500rpm搅拌5min；
(3)将增稠剂与占配方质量分数5％的清水预先混合后，边搅拌边缓慢投入分散釜中，控制转速500～600rpm分散10min；
(4)按顺序边搅拌边缓慢加入颜填料、消泡剂、流平剂，控制转速900～1000rpm分散15～20min；
(5)将物料通过管道传输至砂磨机或三辊机，研磨至最大细度≤10μm；
(6)将物料传输回分散釜中，搅拌中将剩余的清水及计量的乙醇缓慢加入搅拌釜中并搅拌均匀。
(7)边搅拌边以滴入法缓慢加入偶联剂，控制转速600～700rpm分散5～10min；
(8)用200目滤网过滤出料备用。按实施例1所述制备方法制备得到沥青基高分子预铺防水卷材。
实施例4
一种预铺防水卷材，其由PE隔离膜层、第一沥青涂盖料层、聚酯胎基层、第二沥青涂盖料层、石英砂防粘颗粒层、封油涂层以及耐紫外涂层组成，玻纤胎基层的厚度为1.0mm，第一沥青涂盖料层厚度为1.5mm，第二沥青涂盖料层厚度为1.5mm，石英砂的粒径范围为0.3～0.7mm，封油涂层干厚度5μm，耐紫外涂层干厚度为50μm。
所述第一沥青涂盖料层和第二沥青涂盖料层分别由实施例3所述改性沥青涂盖料组成，并按实施例1改性沥青涂盖料制备方法制备改性沥青涂盖料。
所述封油涂层由实施例3所述封油涂料干燥而成。
所述耐紫外涂层由实施例3所述耐紫外涂料干燥而成.
按实施例1所述制备方法制备得到卷材。
对比例1
制备一种预铺防水卷材，其组成及制备方法与实施例1基本相同，区别在于，本对比例1的耐紫外涂层厚度为90μm。
对比例2
制备一种预铺防水卷材，其组成及制备方法与实施例2基本相同，区别在于，本对比例2取消了所述耐紫外涂料中的偶联剂并用同等添加量的溶剂代替，即所述耐紫外涂料组成如下。
树脂(科腾G1701) 4.50％
树脂(加氢DCPD树脂) 3.60％
树脂(大林PB950) 2.50％
抗氧剂(BASF 1010) 0.20％
紫外助剂(326) 0.10％
紫外助剂(770) 0.10％
溶剂(二氯甲烷) 52.00％
溶剂(乙酸乙酯) 27.55％
分散剂(EFKA4608) 0.30％
颜填料(龙蟒R-996) 4.00％
颜填料(2500目滑石粉) 5.00％
增稠剂(BYK-410) 0.05％
消泡剂 0.05％
流平剂 0.05％
对比例3
制备一种预铺防水卷材，其组成及制备方法与实施例3基本相同，区别在于，本对比例3取消了实施例3中所述耐紫外涂层，其结构如下：
一种预铺防水卷材，其由PP隔离膜层、第一沥青涂盖料层、玻纤胎基层、第二沥青涂盖料层、瓷砂防粘颗粒层、封油涂层组成，玻纤胎基层的厚度为1.2mm，第一沥青涂盖料层厚度为1.4mm，第二沥青涂盖料层厚度为1.4mm，瓷砂的粒径范围为0.25～0.5mm，封油涂层干厚度3μm。
所述卷材按如下方法制备：
(1)按所述改性沥青涂盖料制备方法制备改性沥青涂盖料，保温160～180℃备用，将准备好的胎基放置于相应放卷机并对齐，开启放卷机放卷，胎基经牵引后往生产线后端展开；
(2)胎基经过改性沥青预浸料池进行预浸处理，并经对辊挤压掉多余的预浸料后，胎基继续往后端展开；
(3)在经过涂胶模头的时候分别在胎基上表面及下表面均匀涂上相应厚度的改性沥青涂盖料，并在第一沥青涂盖料层表面覆盖上一层隔离膜后在牵引作用下继续向后端展开；
(4)所得卷材在经过加热烘道后被加热至第二沥青涂盖料层表面温度为50～90℃后通过撒砂装置在第二沥青涂盖料层表面均匀撒上所述颗粒形成颗粒层，然后经过辊压压实颗粒层，清砂装置清理掉多余的颗粒后继续往后端展开；
(5)所得卷材经喷涂通道1，并于卷材表面(颗粒层面)均匀喷涂一层所述封油涂料，涂料充分润湿颗粒层表面及颗粒层间隙的热熔胶表面后经过设置温度为50～110℃的鼓风烘道后干燥形成封油涂层，所得卷材继续往后端展开；
(6)所得卷材经过喷印机喷上品牌LOGO或装饰性印刷内容后，继续往后端展开；
(7)所得卷材经降温装置降温后收卷，即得所述卷材成品。
对比例4
制备一种预铺防水卷材，其组成及制备方法与实施例4基本相同，区别在于，本对比例4取消了实施例4中所述封油涂层，其结构如下：
一种预铺防水卷材，其由PE隔离膜层、第一沥青涂盖料层、聚酯胎基层、第二沥青涂盖料层、石英砂防粘颗粒层以及耐紫外涂层组成，玻纤胎基层的厚度为1.0mm，第一沥青涂盖料层厚度为1.5mm，第二沥青涂盖料层厚度为1.5mm，石英砂的粒径范围为0.3～0.7mm，耐紫外涂层干厚度为50μm。
所述沥青基高分子预铺防水卷材按如下方法制备：
(1)按所述改性沥青涂盖料制备方法制备改性沥青涂盖料，保温160～180℃备用，将准备好的胎基放置于相应放卷机并对齐，开启放卷机放卷，胎基经牵引后往生产线后端展开；
(2)胎基经过改性沥青预浸料池进行预浸处理，并经对辊挤压掉多余的预浸料后，胎基继续往后端展开；
(3)在经过涂胶模头的时候分别在胎基上表面及下表面均匀涂上相应厚度的改性沥青涂盖料，并在第一沥青涂盖料层表面覆盖上一层隔离膜后在牵引作用下继续向后端展开；
(4)所得卷材在经过加热烘道后被加热至第二沥青涂盖料层表面温度为50～90℃后通过撒砂装置在第二沥青涂盖料层表面均匀撒上所述颗粒形成颗粒层，然后经过辊压压实颗粒层，清砂装置清理掉多余的颗粒后继续往后端展开；
(5)所得卷材经喷涂通道2，并于卷材表面(颗粒层面)均匀喷涂一层所述耐紫外涂料，涂料充分润湿颗粒层以及改性沥青料表面后经过设置温度为50～110℃的鼓风烘道后干燥形成耐紫外涂层，所得卷材继续往后端展开；
(6)所得卷材经过喷印机喷上品牌LOGO或装饰性印刷内容后，继续往后端展开；
(7)所得卷材经降温装置降温后收卷，即得所述卷材成品。
将实施例1～4制备得到的卷材和对比例1～4制备的卷材，根据产品实际应用情形对其进行部分应用性能测试结果如下表1所示，根据GB/T23457-2017标准测试部分重要性能结果如下表2所示。
表1实施例和对比例卷材的性能。
其中，N代表没有变色、没有掉砂或没有渗色等，Y代表了变色、掉砂或渗色。
表2实施例和对比例卷材的测试性能。
从表1可知，实施例1-4和对比例1-2中，设置有封油涂层，没有出现泡水后掉砂和暴晒后表面变色现象，而对比例3-4中，没有设置封油涂层，出现了掉砂和变色现象，对比例2中，耐紫外涂层中没有添加偶联剂，泡水是否脱色渗色的现象。综合表1可知，封油涂层的设置，可以避免卷材在泡水后掉砂和暴晒后表面变色，为卷材在苛刻条件下施工提供了强有力的保障。
从表2可知，实施例1～4均达到国标要求且性能优异，对比例1、3、4达不到国标要求，而表2中对比例2虽然性能达到国标要求，但其表1应用性能表现不佳，即，泡水后出现脱色现象；所以实施例相比于对比例，实施例1-4的各项性能较为优异。
以上所述，仅为本申请的具体实施方式，但本申请的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本申请揭露的技术范围内，可轻易想到各种等效的修改或替换，这些修改或替换都应涵盖在本申请的保护范围之内。因此，本申请的保护范围应以权利要求的保护范围为准。
Claims (10)
1.一种预铺防水卷材，其特征在于，所述卷材包括：
胎基层；
第一沥青涂盖料层和第二沥青涂盖料层，其分别设于所述胎基层的两侧表面上，其中，所述第二沥青涂盖料层的表面上粘附有防粘颗粒以形成防粘表面；
封油涂层，其涂布在所述防粘表面上；
耐紫外涂层，其涂布在所述封油涂层的表面上。
2.根据权利要求1所述的卷材，其特征在于，所述第一沥青涂盖料层和第二沥青涂盖料层分别包括沥青、沥青改性剂、软化油、胶粉、填料和抗氧剂。
3.根据权利要求2所述的卷材，其特征在于，所述沥青选自石油沥青、天然沥青、煤焦沥青或其组合；和/或，
所述沥青改性剂选自苯乙烯-丁二烯-苯乙烯嵌段共聚物、苯乙烯-异戊二烯-苯乙烯、丁苯橡胶、氢化苯乙烯-丁二烯-苯乙烯嵌段共聚物、无规聚丙烯或其组合。
4.根据权利要求1所述的卷材，其特征在于，所述防粘颗粒的粒度为20～80目；和/或，
所述防粘颗粒选自白云石砂、云母砂、方解石砂、花岗岩砂、石英砂、碳酸钙砂、镁钙砂、瓷砂、铁砂、莫来砂、人造砂或其组合。
5.根据权利要求1所述的卷材，其特征在于，所述封油涂层包括聚乙烯醇；和/或，
所述封油涂层的厚度为0.5～10μm，可选为1～5μm。
6.根据权利要求5所述的卷材，其特征在于，所述封油涂层还包括偶联剂，所述偶联剂选自硅烷偶联剂、钛酸酯偶联剂、铝酸酯偶联剂或其组合。
7.根据权利要求6所述的卷材，其特征在于，
所述偶联剂包括具有甲基丙烯酸基、氨基、脲基、环氧基、(甲基)丙烯酰氧基中的任意一种或几种官能团的硅烷偶联剂。
8.根据权利要求1所述的卷材，其特征在于，至少部分所述防粘颗粒之间存在空隙，并且所述封油涂层和所述耐紫外涂层分别在所述防粘颗粒之间的空隙处形成凹陷。
9.根据权利要求1或5所述的卷材，其特征在于，
所述耐紫外涂层与所述封油涂层的总厚度≤所述防粘颗粒的平均粒径范围下限值的1/10；和/或，
所述耐紫外涂层与所述封油涂层的总厚度为5～80μm；可选为10～50μm。
10.根据权利要求1中所述的卷材，其特征在于，所述卷材还包括：隔离膜层，所述隔离膜层设于所述第一沥青涂盖料层的表面。