CN113346082A - 一种带有海藻酸钠的碱锰电池及制备方法 - Google Patents

一种带有海藻酸钠的碱锰电池及制备方法 Download PDF

Info

Publication number
CN113346082A
CN113346082A CN202110592544.1A CN202110592544A CN113346082A CN 113346082 A CN113346082 A CN 113346082A CN 202110592544 A CN202110592544 A CN 202110592544A CN 113346082 A CN113346082 A CN 113346082A
Authority
CN
China
Prior art keywords
sodium alginate
alkaline manganese
zinc
electrolyte
manganese battery
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202110592544.1A
Other languages
English (en)
Inventor
余谷峰
卢冬
卢旭杰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhengjiang Mustang Battery Co ltd
Original Assignee
Zhengjiang Mustang Battery Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhengjiang Mustang Battery Co ltd filed Critical Zhengjiang Mustang Battery Co ltd
Priority to CN202110592544.1A priority Critical patent/CN113346082A/zh
Publication of CN113346082A publication Critical patent/CN113346082A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种带有海藻酸钠的碱锰电池及制备方法。该碱锰电池采用粘度为200‑500mPa.s的低粘度海藻酸钠作为锌膏粘结剂。制备方法如下：第一步，将占混合物总重量为0.2％‑0.6％、粘度为200‑500mPa.s的海藻酸钠加入至锌粉内搅拌均匀，得到锌粉与海藻酸钠的混合物；第二步，向电解液内加入浓度为1％‑10％的ZnO，并进行快速搅拌；第三步，将第一步中得到的混合物加入至电解液内，海藻酸钠与的氧化锌络合，在电解液的作用下形成稳定三维网状的锌膏；第四步，将第三步得到的锌膏注入半成品碱锰电池内，并将电池封口，即得到完整的碱锰电池。本发明通过适量的海藻酸钠与适量的氧化锌络合，在电解液的作用下形成稳定三维网状的凝胶，使得锌粉之间的接触更加紧密，减少内阻，增大放电性能。

Description

一种带有海藻酸钠的碱锰电池及制备方法
技术领域
本发明涉及电池制备技术领域，具体为一种带有海藻酸钠的碱锰电池及制备方法。
背景技术
目前的碱锰电池中采用由聚丙烯酸系列和聚丙希酸钠构成的粘结剂来作为锌膏粘结剂，其主要起到分散并稳定锌粉和吸收电解液作用，锌膏粘结剂的选用影响着锌膏状态，从而影响电池的放电性能。国内电池厂家为了得到更高性能的电池，逐渐增加氧化锌含量，而传统的卡波姆系列粘结剂在氧化锌作用下，锌膏状态变得更加粘稠，流动性变差，锌膏组成成分搅拌不均匀，锌膏机无法将流动性差的锌膏均匀的注入电池内，从而导致同一批次电池的放电性能不均一。
发明内容
本发明的目的在于提供一种带有海藻酸钠的碱锰电池及制备方法，本发明通过适量的海藻酸钠与适量的氧化锌络合，在电解液的作用下形成稳定三维网状的凝胶，使得锌粉之间的接触更加紧密，减少内阻，增大放电性能，并且锌膏的流动性得到改善，有利于锌膏机的注入，提高了电池放电性能的均匀性。
为实现上述目的，本发明提供如下技术方案：一种带有海藻酸钠的碱锰电池，所述碱锰电池采用低粘度海藻酸钠作为锌膏粘结剂。
优选的，所述海藻酸钠的粘度为200-500mPa.s。
一种带有海藻酸钠的碱锰电池的制备方法，包括以下步骤：
第一步，将占混合物总重量为0.2％-0.6％、粘度为200-500mPa.s的海藻酸钠加入至锌粉内搅拌均匀，得到锌粉与海藻酸钠的混合物；
第二步，向电解液内加入浓度为1％-10％的ZnO，并进行快速搅拌；
第三步，将第一步中得到的混合物加入至电解液内，海藻酸钠与的氧化锌络合，在电解液的作用下形成稳定三维网状的锌膏；
第四步，将第三步得到的锌膏注入半成品碱锰电池内，并将电池封口，即得到完整的碱锰电池。
优选的，所述电解液为KOH电解质溶液。
与现有技术相比，本发明的有益效果如下：
本发明采用低粘度海藻酸钠作为锌膏粘结剂，与传统的聚丙烯酸交联树脂/聚丙烯酸钠比较，海藻酸钠成本更为低廉，采用其制成的锌膏的流动性变好，有利于锌膏机的注入，且随时间延长，锌膏逐渐增稠，提高电池的抗震性，电池放电后的析气量明显低于传统的聚丙烯酸交联树脂/聚丙烯酸钠体系。
具体实施方式
下面将结合本发明的实施例，对本发明的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
本发明提供一种技术方案：一种带有海藻酸钠的碱锰电池，所述碱锰电池采用低粘度海藻酸钠作为锌膏粘结剂。
优选的，所述海藻酸钠的粘度为200-500mPa.s。
一种带有海藻酸钠的碱锰电池的制备方法，包括以下步骤：
第一步，将占混合物总重量为0.2％-0.6％、粘度为200-500mPa.s的海藻酸钠加入至锌粉内搅拌均匀，得到锌粉与海藻酸钠的混合物；
第二步，向电解液内加入浓度为1％-10％的ZnO，并进行快速搅拌；
第三步，将第一步中得到的混合物加入至电解液内，海藻酸钠与的氧化锌络合，在电解液的作用下形成稳定三维网状的锌膏；
第四步，将第三步得到的锌膏注入半成品碱锰电池内，并将电池封口，即得到完整的碱锰电池。
具体来说，所述电解液为KOH电解质溶液。
由海藻酸钠为粘结剂制得的电池和由聚丙烯酸/聚丙烯酸钠盐为粘结剂的制得的电池在3.9Ω的连放、1.5w恒功率放电以及750mA 0.2s 150mA 2.8s的三种放电方式下进行放电对比，1.5w恒功率未受到抑制，3.9Ω连放有5％的提升，750mA 0.2s 150mA 2.8s最高有近20％提升。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。

Claims (4)

1.一种带有海藻酸钠的碱锰电池，其特征在于，所述碱锰电池采用低粘度海藻酸钠作为锌膏粘结剂。
2.根据权利要求1所述的一种带有海藻酸钠的碱锰电池，其特征在于：所述海藻酸钠的粘度为200-500mPa.s。
3.一种带有海藻酸钠的碱锰电池的制备方法，其特征在于，包括以下步骤：
第一步，将占混合物总重量0.2％-0.6％、粘度为200-500mPa.s的海藻酸钠加入至锌粉内搅拌均匀，得到锌粉与海藻酸钠的混合物；
第二步，向电解液内加入浓度为1％-10％的ZnO，并进行快速搅拌；
第三步，将第一步中得到的混合物加入至电解液内，海藻酸钠与的氧化锌络合，在电解液的作用下形成稳定三维网状的锌膏；
第四步，将第三步得到的锌膏注入半成品碱锰电池内，并将电池封口，即得到完整的碱锰电池。
4.根据权利要求1所述的一种带有海藻酸钠的碱锰电池，其特征在于：所述电解液为KOH电解质溶液。
CN202110592544.1A 2021-05-28 2021-05-28 一种带有海藻酸钠的碱锰电池及制备方法 Pending CN113346082A (zh)