CN112745598A - High-flame-retardant photo-oxidation-aging-resistant polyvinyl chloride profile and preparation method thereof - Google Patents
High-flame-retardant photo-oxidation-aging-resistant polyvinyl chloride profile and preparation method thereof Download PDFInfo
- Publication number
- CN112745598A CN112745598A CN202011582721.XA CN202011582721A CN112745598A CN 112745598 A CN112745598 A CN 112745598A CN 202011582721 A CN202011582721 A CN 202011582721A CN 112745598 A CN112745598 A CN 112745598A
- Authority
- CN
- China
- Prior art keywords
- parts
- mass
- antioxidant
- polyvinyl chloride
- flame retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides high-flame-retardance photo-oxidative aging-resistant polyvinyl chloride and a preparation method thereof, belonging to the technical field of section bar preparation. The invention is composed of raw materials with the mass portions of 85-95 portions of polyvinyl chloride, 10-15 portions of inorganic flame retardant, 5-10 portions of organic flame retardant, 2-4 portions of heat stabilizer, 0.1-0.5 portion of lubricant, 15-20 portions of impact modifier, 1-3 portions of titanium dioxide, 1-3 portions of ultraviolet absorbent, 6-9 portions of antioxidant and 0.2-0.4 portion of fluorescent brightener; the raw materials are mixed according to the mass part ratio, and then are processed at constant temperature and are formed by co-extrusion, thus obtaining the invention. The PVC profile has the effects of high flame retardance and photo-oxidative aging resistance, prolongs the service life of the PVC profile when exposed to the external environment, greatly improves the fireproof flame retardance, has good economic value, and meets the actual requirements of industrial production.
Description
Technical Field
The invention relates to the technical field of section bar preparation, in particular to a polyvinyl chloride section bar with high flame retardance and photooxidation aging resistance and a preparation method thereof.
Background
The PVC profile is an industrial and domestic PVC product which is formed by adding various functional additives into PVC resin and then extruding at high temperature, and can be divided into hard PVC profile and soft PVC profile according to the performance, wherein the hard PVC profile is mainly used for building aspects, such as manufacturing PVC doors and windows, PVC bottom plates, PVC pipes and the like; the soft PVC section bar is used for manufacturing PVC hoses, transmission cables and the like. The PVC section added with the functional auxiliary agent has the advantages of ageing resistance, ultraviolet resistance, corrosion resistance, high strength, low price and good heat preservation and heat insulation performance, can partially replace materials such as aluminum sections, steel and the like, and has lower pollution degree than aluminum sections.
The PVC profile product undergoes the lead-in period and the high-speed development period, and as one of products of scientific and technological development, the PVC profile is rapidly developed in the field of doors and windows, and a wide space is provided for the development of the national building material industry.
However, polyvinyl chloride sectional materials and doors and windows produced by various domestic manufacturers are generally conventional sectional materials, have poor flame-retardant and fireproof performance, are easy to cause hidden trouble accidents, have poor effect on solving the problem of photo-oxidative aging of the PVC sectional materials, influence the service life of the door and window sectional materials, and particularly have more obvious influence in certain strong-light areas.
Disclosure of Invention
The technical problem to be solved by the invention is as follows:
the existing polyvinyl chloride sectional material is poor in flame-retardant and fireproof performance, is easy to cause hidden trouble accidents, and solves the problem that the PVC sectional material is poor in photo-oxidative aging effect, so that the service life of the door and window sectional material is influenced.
The invention adopts the technical scheme for solving the technical problems that:
the high-flame-retardant photo-oxidation-aging-resistant polyvinyl chloride profile is prepared from the following raw materials in parts by mass: 85-95 parts of polyvinyl chloride, 10-15 parts of inorganic flame retardant, 5-10 parts of organic flame retardant, 2-4 parts of heat stabilizer, 0.1-0.5 part of lubricant, 15-20 parts of impact modifier, 1-3 parts of titanium dioxide, 1-3 parts of ultraviolet absorbent, 6-9 parts of antioxidant and 0.2-0.4 part of fluorescent brightener;
the inorganic flame retardant comprises the following raw material components, by mass, 1-3 parts of antimony trioxide, 1-3 parts of magnesium hydroxide, 1-3 parts of aluminum hydroxide, 1-3 parts of ammonium polyphosphate and 1-3 parts of red phosphorus; antimony trioxide is the earliest applied flame retardant and is suitable for the preparation processes of epoxy resin, polyurethane, polyvinyl chloride and the like; the magnesium hydroxide is mainly applied to the fields of chemical industry, environmental protection and the like, is used as an excellent flame retardant and filler for high polymer materials such as plastics, rubber and the like, can also play a role in preventing fuming and generating no dripping and toxic gas, and is widely applied; ammonium polyphosphate and red phosphorus are also adopted, so that a good flame retardant effect can be achieved by compounding, and the processing performance and the mechanical performance of the profile can be improved;
the organic flame retardant comprises the following raw materials, by mass, 2-5 parts of tributyl phosphate and 2-7 parts of tricresyl phosphate; the organic flame retardant has the excellent performance of environmental protection and no pollution, and the fireproof flame-retardant effect of the profile can be improved by matching with the inorganic flame retardant;
the heat stabilizer comprises the following raw materials, by mass, 0.5-2 parts of tribasic lead sulfate, 0.5-2 parts of dibasic lead phosphite and 0.5-2 parts of dibasic o-dimethyl lead phosphate; the lead salt stabilizer has stronger thermal stability function, belongs to a class of main stabilizers and is widely applied to PVC;
the lubricant is one or two of calcium stearate and stearic acid; stearic acid and calcium stearate have a heat stabilizing effect in addition to a lubricating effect;
the impact modifier is ACR impact modifier; ACR is a plastic adjuvant with double functions of impact resistance modification and processing modification, and because the ACR has a core-shell structure, a PVC product has excellent impact resistance, weather resistance and stability and has good economic benefit;
the ultraviolet absorbent comprises the raw material components of, by mass, 0.1-0.5 part of TBS, 0.3-0.3 part of UV-3270.1, 50.1-0.3 part of triazine, 90.2-1 part of UV-90.2 and 0.2-1 part of BAD;
the antioxidant comprises the raw material components of, by mass, 10102-5 parts of an antioxidant and DSTP2-5 parts of an antioxidant; the antioxidant 1010 and the antioxidant DSTP are compounded for use, so that the oxidation process of the PVC profile can be delayed or inhibited, the aging of the material is prevented, and the service life of the material is prolonged.
Optionally, the feed additive is prepared from the following raw materials in parts by mass: 85-90 parts of polyvinyl chloride, 12-14 parts of inorganic flame retardant, 7-9 parts of organic flame retardant, 2-4 parts of heat stabilizer, 0.2-0.4 part of lubricant, 16-18 parts of impact modifier, 1.5-2.5 parts of titanium dioxide, 1.5-2.5 parts of ultraviolet absorbent, 7-8 parts of antioxidant and 0.25-0.35 part of fluorescent brightener;
the inorganic flame retardant comprises the following raw material components, by mass, 2-3 parts of antimony trioxide, 2-3 parts of magnesium hydroxide, 2-3 parts of aluminum hydroxide, 2-3 parts of ammonium polyphosphate and 2-3 parts of red phosphorus;
the organic flame retardant comprises the following raw materials, by mass, 3-5 parts of tributyl phosphate and 3-6 parts of tricresyl phosphate;
the heat stabilizer comprises the following raw materials, by mass, 0.5-1.5 parts of tribasic lead sulfate, 0.5-1.5 parts of dibasic lead phosphite and 0.5-1.5 parts of dibasic o-dimethyl lead phosphate;
the lubricant is one or two of calcium stearate and stearic acid;
the impact modifier is ACR impact modifier;
the ultraviolet absorbent comprises the raw material components of, by mass, 0.2-0.3 part of TBS, 0.3-0.3 part of UV-3270.1, 50.1-0.3 part of triazine, 90.3-1 part of UV-and 0.2-1 part of BAD;
the antioxidant comprises the raw material components of, by mass, 10102-5 parts of an antioxidant and DSTP2-5 parts of an antioxidant.
Optionally, the feed additive is prepared from the following raw materials in parts by mass: 88 parts of polyvinyl chloride, 13 parts of inorganic flame retardant, 8 parts of organic flame retardant, 3 parts of heat stabilizer, 0.3 part of lubricant, 17 parts of impact modifier, 2 parts of titanium dioxide, 2 parts of ultraviolet absorbent, 7 parts of antioxidant and 0.3 part of fluorescent brightener;
the inorganic flame retardant comprises the following raw materials, by mass, 2 parts of antimony trioxide, 3 parts of magnesium hydroxide, 2 parts of aluminum hydroxide, 3 parts of ammonium polyphosphate and 3 parts of red phosphorus;
the organic flame retardant comprises the following raw materials, by mass, 3-5 parts of tributyl phosphate and 3-6 parts of tricresyl phosphate;
the heat stabilizer comprises the following raw materials, by mass, 1 part of tribasic lead sulfate, 1 part of dibasic lead phosphite and 1 part of dibasic o-dimethyl lead phosphate;
the lubricant is calcium stearate or stearic acid;
the impact modifier is ACR impact modifier;
the ultraviolet absorbent comprises the following raw material components, by mass, 0.2 part of TBS, 0.2 part of UV-3270.2 part of triazine-50.2 part of UV-90.7 part of BAD;
the antioxidant comprises the raw material components of, by mass, 10103 parts of an antioxidant and 4 parts of an antioxidant DSTP.
Optionally, the polyvinyl chloride is PVC SG-5 or PVC SG-6.
A preparation method of a polyvinyl chloride profile with high flame retardance and photooxidation aging resistance comprises the following steps:
(1) adding 85-95 parts of polyvinyl chloride, 10-15 parts of inorganic flame retardant, 5-10 parts of organic flame retardant, 2-4 parts of heat stabilizer, 0.1-0.5 part of lubricant, 15-20 parts of impact modifier, 1-3 parts of titanium dioxide, 1-3 parts of ultraviolet absorbent, 6-9 parts of antioxidant and 0.2-0.4 part of fluorescent brightener into a high-speed mixer, and heating to 140 ℃ for mixing;
(2) cooling the mixed material obtained in the step (1) to 32-42 ℃, and standing for 40 minutes at constant temperature to obtain a co-extruded material;
(3) and (3) sending the co-extruded material subjected to constant temperature treatment in the step (2) into a co-extruder, wherein the temperature of a charging barrel of the co-extruder is set at 165-170 ℃, the temperature of a machine head is set at 170 ℃, and the thickness of the co-extruded layer is 0.45-0.55 mm.
Optionally, the mixing time in the step (1) is 6-10 minutes.
Compared with the prior art, the invention has the beneficial effects that:
according to the high-flame-retardant light-oxygen aging-resistant polyvinyl chloride and the preparation method thereof, the high-flame-retardant property is improved by adding the organic flame retardants of tributyl phosphate and tricresyl phosphate and the inorganic flame retardants of antimony trioxide, magnesium hydroxide, aluminum hydroxide, ammonium polyphosphate and red phosphorus, the fireproof flame retardance can reach the UL-94V-0 standard, and the organic flame retardants and the inorganic flame retardants do not contain halogen, so that the polyvinyl chloride has the characteristics of environmental protection and can improve the processing performance and the mechanical performance of materials;
the invention adopts five ultraviolet absorbers of TBS, UV-327, triazine-5, UV-9 and BAD, can strongly absorb ultraviolet rays and has excellent synergistic effect; the antioxidant 1010 and the antioxidant DSTP are compounded for use, so that the oxidation process of the PVC profile can be delayed or inhibited, the aging of the material is prevented, and the service life of the material is prolonged; the ACR impact modifier is adopted, so that the plasticizing process of the PVC profile can be accelerated, the weather resistance of the PVC profile can be improved, namely the ultraviolet resistance and the ageing resistance of the material are improved, the melt viscosity of the material can be reduced, the processing performance of plastics is improved, the impact strength, the low temperature resistance and the weather resistance of the PVC profile are improved, and the service life of the PVC profile is prolonged; the use of calcium stearate or stearic acid can improve the flowability and mold release of the material during processing.
The high-flame-retardant photooxidation-aging-resistant polyvinyl chloride profile prepared by the invention has various properties exceeding the national standards, has good ultraviolet resistance, oxidation resistance and aging resistance, greatly prolongs the service life of the PVC profile in exposed air, and has the advantages of environmental protection, high strength and good flame retardant property.
Detailed Description
In order to make the aforementioned objects, features and advantages of the present invention comprehensible, specific embodiments thereof are described in detail below.
Example 1
(1) Adding 85 parts of polyvinyl chloride, 2 parts of antimony trioxide, 2 parts of magnesium hydroxide, 2 parts of aluminum hydroxide, 2 parts of ammonium polyphosphate, 2 parts of red phosphorus, 2 parts of tributyl phosphate, 3 parts of tricresyl phosphate, 0.5 part of tribasic lead sulfate, 0.5 part of dibasic lead phosphite, 1 part of dibasic o-dimethyl lead, 0.1 part of calcium stearate, 15 parts of ACR impact modifier, 1 part of titanium dioxide, 0.1 part of TBS, UV-3270.1 parts, 50.1 parts of triazine-90.2 parts, 0.5 part of BAD, 10103 parts of antioxidant, 3 parts of antioxidant DSTP and 0.25 part of fluorescent brightener into a high-speed mixer, and heating to 130 ℃ for mixing;
(2) cooling the mixed material obtained in the step (1) to 32 ℃, and standing at a constant temperature for 40 minutes to obtain a co-extruded material;
(3) and (3) sending the co-extruded material subjected to constant temperature treatment in the step (2) into a co-extruder, wherein the temperature of a charging barrel of the co-extruder is set to be 165 ℃, the temperature of a machine head is set to be 170 ℃, and the thickness of the co-extruded layer is 0.45 mm.
Example 2
(1) Adding 88 parts of polyvinyl chloride, 2.3 parts of antimony trioxide, 2.3 parts of magnesium hydroxide, 2.3 parts of aluminum hydroxide, 2.3 parts of ammonium polyphosphate, 2.3 parts of red phosphorus, 3 parts of tributyl phosphate, 4 parts of tricresyl phosphate, 1 part of tribasic lead sulfate, 1 part of dibasic lead phosphite, 1 part of dibasic o-dimethyl lead, 0.2 part of calcium stearate, 17 parts of ACR impact modifier, 1.8 parts of titanium dioxide, 0.2 part of TBS, UV-3270.2, 50.2 parts of triazine-3, UV-90.3 parts, 0.6 part of BAD, 10104 parts of antioxidant, DSTP4 parts of antioxidant and 0.28 part of fluorescent whitening agent into a high-speed mixer, and heating to 133 ℃ to mix;
(2) cooling the mixed material obtained in the step (1) to 35 ℃, and standing at a constant temperature for 40 minutes to obtain a co-extruded material;
(3) and (3) sending the co-extruded material subjected to constant temperature treatment in the step (2) into a co-extruder, wherein the temperature of a charging barrel of the co-extruder is set to be 166 ℃, the temperature of a machine head is set to be 170 ℃, and the thickness of the co-extruded layer is 0.47 mm.
Example 3
(1) Adding 92 parts of polyvinyl chloride, 2 parts of antimony trioxide, 2 parts of magnesium hydroxide, 3 parts of aluminum hydroxide, 3 parts of ammonium polyphosphate, 3 parts of red phosphorus, 4 parts of tributyl phosphate, 4 parts of tricresyl phosphate, 1 part of tribasic lead sulfate, 1 part of dibasic lead phosphite, 1.5 parts of dibasic o-dimethyl lead, 0.4 part of calcium stearate, 18 parts of ACR impact modifier, 2.5 parts of titanium dioxide, 0.4 part of TBS (TBS), UV-3270.2 parts, 50.2 parts of triazine-90.7 parts, 0.7 part of BAD (barium phosphate), 10104 parts of antioxidant, DSTP4 parts of antioxidant and 0.32 part of fluorescent brightener into a high-speed mixer, and heating to 138 ℃ for mixing;
(2) cooling the mixed material obtained in the step (1) to 38 ℃, and standing at a constant temperature for 40 minutes to obtain a co-extruded material;
(3) and (3) sending the co-extruded material subjected to constant temperature treatment in the step (2) into a co-extruder, wherein the temperature of a charging barrel of the co-extruder is set at 168 ℃, the temperature of a machine head is set at 170 ℃, and the thickness of the co-extruded layer is 0.52 mm.
Example 4
(1) Adding 95 parts of polyvinyl chloride, 3 parts of antimony trioxide, 3 parts of magnesium hydroxide, 3 parts of aluminum hydroxide, 3 parts of ammonium polyphosphate, 3 parts of red phosphorus, 5 parts of tributyl phosphate, 5 parts of tricresyl phosphate, 2 parts of tribasic lead sulfate, 1 part of dibasic lead phosphite, 1 part of dibasic o-dimethyl lead, 0.5 part of calcium stearate, 20 parts of ACR impact modifier, 3 parts of titanium dioxide, 0.5 part of TBS, UV-3270.3 parts, 50.3 parts of triazine-3, UV-90.5 parts of BAD, 0.4 part of antioxidant 10104, antioxidant DSTP5 parts and 0.35 part of fluorescent brightener into a high-speed mixer, and heating to 140 ℃ to mix;
(2) cooling the mixed material obtained in the step (1) to 42 ℃, and standing at a constant temperature for 40 minutes to obtain a co-extruded material;
(3) and (3) sending the co-extruded material subjected to constant temperature treatment in the step (2) into a co-extruder, wherein the temperature of a charging barrel of the co-extruder is set to be 170 ℃, the temperature of a machine head is set to be 170 ℃, and the thickness of the co-extruded layer is 0.55 mm.
The mechanical and physical properties of the polyvinyl chloride with high flame retardance and photo-oxidative aging resistance prepared in the above examples 1 to 4 were tested, and the results are shown in the following table 1:
the test results in table 1 show that the polyvinyl chloride plastic with high flame retardance and photo-oxidative aging resistance prepared by the method has good flame retardance and ultraviolet irradiation and oxidation resistance, so that the method can be adopted during production and manufacturing of the polyvinyl chloride section, and the experimental results show that the raw material proportion and the process parameters adopted in the example 3 have better effects.
Although the present disclosure has been described above, the scope of the present disclosure is not limited thereto. Various changes and modifications may be effected therein by one of ordinary skill in the pertinent art without departing from the spirit and scope of the present disclosure, and these changes and modifications are intended to be within the scope of the present disclosure.
Claims (6)
1. The high-flame-retardance photo-oxidation-aging-resistant polyvinyl chloride profile is characterized by being prepared from the following raw materials in parts by mass: 85-95 parts of polyvinyl chloride, 10-15 parts of inorganic flame retardant, 5-10 parts of organic flame retardant, 2-4 parts of heat stabilizer, 0.1-0.5 part of lubricant, 15-20 parts of impact modifier, 1-3 parts of titanium dioxide, 1-3 parts of ultraviolet absorbent, 6-9 parts of antioxidant and 0.2-0.4 part of fluorescent brightener;
the inorganic flame retardant comprises the following raw material components, by mass, 1-3 parts of antimony trioxide, 1-3 parts of magnesium hydroxide, 1-3 parts of aluminum hydroxide, 1-3 parts of ammonium polyphosphate and 1-3 parts of red phosphorus;
the organic flame retardant comprises the following raw materials, by mass, 2-5 parts of tributyl phosphate and 2-7 parts of tricresyl phosphate;
the heat stabilizer comprises the following raw materials, by mass, 0.5-2 parts of tribasic lead sulfate, 0.5-2 parts of dibasic lead phosphite and 0.5-2 parts of dibasic o-dimethyl lead phosphate;
the lubricant is calcium stearate or stearic acid;
the impact modifier is ACR impact modifier;
the ultraviolet absorbent comprises the raw material components of, by mass, 0.1-0.5 part of TBS, 0.3-0.3 part of UV-3270.1, 50.1-0.3 part of triazine, 90.2-1 part of UV-90.2 and 0.2-1 part of BAD;
the antioxidant comprises the raw material components of, by mass, 10102-5 parts of an antioxidant and DSTP2-5 parts of an antioxidant.
2. The polyvinyl chloride profile with high flame retardance and photooxidative aging resistance as claimed in claim 1, is prepared from the following raw materials in parts by mass: 85-90 parts of polyvinyl chloride, 12-14 parts of inorganic flame retardant, 7-9 parts of organic flame retardant, 2-4 parts of heat stabilizer, 0.2-0.4 part of lubricant, 16-18 parts of impact modifier, 1.5-2.5 parts of titanium dioxide, 1.5-2.5 parts of ultraviolet absorbent, 7-8 parts of antioxidant and 0.25-0.35 part of fluorescent brightener;
the inorganic flame retardant comprises the following raw material components, by mass, 2-3 parts of antimony trioxide, 2-3 parts of magnesium hydroxide, 2-3 parts of aluminum hydroxide, 2-3 parts of ammonium polyphosphate and 2-3 parts of red phosphorus;
the organic flame retardant comprises the following raw materials, by mass, 3-5 parts of tributyl phosphate and 3-6 parts of tricresyl phosphate;
the heat stabilizer comprises the following raw materials, by mass, 0.5-1.5 parts of tribasic lead sulfate, 0.5-1.5 parts of dibasic lead phosphite and 0.5-1.5 parts of dibasic o-dimethyl lead phosphate;
the lubricant is calcium stearate or stearic acid;
the impact modifier is ACR impact modifier;
the ultraviolet absorbent comprises the raw material components of, by mass, 0.2-0.3 part of TBS, 0.3-0.3 part of UV-3270.1, 50.1-0.3 part of triazine, 90.3-1 part of UV-and 0.2-1 part of BAD;
the antioxidant comprises the raw material components of, by mass, 10102-5 parts of an antioxidant and DSTP2-5 parts of an antioxidant.
3. The polyvinyl chloride profile with high flame retardance and photooxidative aging resistance as claimed in claim 2 is prepared from the following raw materials in parts by mass: 88 parts of polyvinyl chloride, 13 parts of inorganic flame retardant, 8 parts of organic flame retardant, 3 parts of heat stabilizer, 0.3 part of lubricant, 17 parts of impact modifier, 2 parts of titanium dioxide, 2 parts of ultraviolet absorbent, 7 parts of antioxidant and 0.3 part of fluorescent brightener;
the inorganic flame retardant comprises the following raw materials, by mass, 2 parts of antimony trioxide, 3 parts of magnesium hydroxide, 2 parts of aluminum hydroxide, 3 parts of ammonium polyphosphate and 3 parts of red phosphorus;
the organic flame retardant comprises the following raw materials, by mass, 3-5 parts of tributyl phosphate and 3-6 parts of tricresyl phosphate;
the heat stabilizer comprises the following raw materials, by mass, 1 part of tribasic lead sulfate, 1 part of dibasic lead phosphite and 1 part of dibasic o-dimethyl lead phosphate;
the lubricant is calcium stearate or stearic acid;
the impact modifier is ACR impact modifier;
the ultraviolet absorbent comprises the following raw material components, by mass, 0.2 part of TBS, 0.2 part of UV-3270.2 part of triazine-50.2 part of UV-90.7 part of BAD;
the antioxidant comprises the raw material components of, by mass, 10103 parts of an antioxidant and 4 parts of an antioxidant DSTP.
4. The polyvinyl chloride profile with high flame retardance and photooxidative aging resistance as claimed in claim 3, wherein: the polyvinyl chloride is PVC SG-5 or PVC SG-6.
5. The preparation method of the polyvinyl chloride profile with high flame retardance and photooxidative aging resistance as claimed in claim 1, which comprises the following steps:
(1) adding 85-95 parts of polyvinyl chloride, 10-15 parts of inorganic flame retardant, 5-10 parts of organic flame retardant, 2-4 parts of heat stabilizer, 0.1-0.5 part of lubricant, 15-20 parts of impact modifier, 1-3 parts of titanium dioxide, 1-3 parts of ultraviolet absorbent, 6-9 parts of antioxidant and 0.2-0.4 part of fluorescent brightener into a high-speed mixer, and heating to 140 ℃ for mixing;
(2) cooling the mixed material obtained in the step (1) to 32-42 ℃, and standing for 40 minutes at constant temperature to obtain a co-extruded material;
(3) and (3) sending the co-extruded material subjected to constant temperature treatment in the step (2) into a co-extruder, wherein the temperature of a charging barrel of the co-extruder is set at 165-170 ℃, the temperature of a machine head is set at 170 ℃, and the thickness of the co-extruded layer is 0.45-0.55 mm.
6. The preparation method of the polyvinyl chloride profile with high flame retardance and photooxidative aging resistance according to claim 5, is characterized in that: the mixing time in the step (1) is 6-10 minutes.