[go: up one dir, main page]

CN112668156B - 一种非金属件贮存寿命计算方法 - Google Patents

一种非金属件贮存寿命计算方法 Download PDF

Info

Publication number
CN112668156B
CN112668156B CN202011471204.5A CN202011471204A CN112668156B CN 112668156 B CN112668156 B CN 112668156B CN 202011471204 A CN202011471204 A CN 202011471204A CN 112668156 B CN112668156 B CN 112668156B
Authority
CN
China
Prior art keywords
metallic parts
hardened layer
thickness
time
test
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN202011471204.5A
Other languages
English (en)
Other versions
CN112668156A (zh
Inventor
吕瑛
张伟
岳晓加
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Beijing Institute of Remote Sensing Equipment
Original Assignee
Beijing Institute of Remote Sensing Equipment
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Beijing Institute of Remote Sensing Equipment filed Critical Beijing Institute of Remote Sensing Equipment
Priority to CN202011471204.5A priority Critical patent/CN112668156B/zh
Publication of CN112668156A publication Critical patent/CN112668156A/zh
Application granted granted Critical
Publication of CN112668156B publication Critical patent/CN112668156B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供一种非金属件贮存寿命计算方法。其包括：第一步、选定表征非金属件退化的指标，将非金属件硬化层厚度作为非金属件新的退化指标；第二步、试验过程中定期检测非金属件硬化层厚度，包括：使用扫描电子显微对非金属件进行微观组织分子观测，测量硬度测试压痕处的硬化层厚度，按照一定时间间隔测试硬化层厚度，将测试数值按照时间点进行详细记录。第三步、拟合非金属件硬化层厚度‑时间退化模型，评估贮存寿命，包括：根据上述测得的非金属件硬化层厚度‑时间退化数据，得到非金属件硬化层厚度随时间的退化模型。本发明解决以往某些非金属件在进行贮存试验时，主要参数和硬度等指标未出现趋势性变化，不能评估贮存寿命的问题。

Description

一种非金属件贮存寿命计算方法
技术领域
本发明涉及非金属件技术领域，特别是一种贮存试验过程中性能没有明显变化情况下的非金属件贮存寿命计算方法。
背景技术
某些非金属件在进行贮存试验时，主要参数和硬度等指标未出现趋势性变化，不能给出常规的性能退化模型，无法有效评估贮存寿命，导致试验失败。需要寻找另外一种能够表征非金属件退化的新指标，通过试验过程中定时测量，拟合出新的退化模型，从而对非金属件贮存寿命进行预测。
发明内容
本发明目的在于提供一种非金属件贮存寿命计算方法，解决以往某些非金属件在进行贮存试验时，主要参数和硬度等指标未出现趋势性变化，不能评估贮存寿命的问题。
对此，本发明提出一种非金属件贮存寿命计算方法，其包括：第一步、选定表征非金属件退化的指标，将非金属件硬化层厚度作为非金属件新的退化指标；第二步、试验过程中定期检测非金属件硬化层厚度，包括：使用扫描电子显微对非金属件进行微观组织分子观测，测量硬度测试压痕处的硬化层厚度，按照一定时间间隔测试硬化层厚度，一般按照每1000h进行一次测试，将测试数值按照时间点进行详细记录。第三步、拟合非金属件硬化层厚度-时间退化模型，评估贮存寿命，包括：根据上述测得的非金属件硬化层厚度-时间退化数据，得到非金属件硬化层厚度随时间的退化模型。
本发明解决以往某些非金属件在进行贮存试验时，主要参数和硬度等指标未出现趋势性变化，不能评估贮存寿命的问题。在不显著增加试验时间和成本的条件下，解决了传统方法不能评估非金属件贮存寿命的问题，具有较高的推广价值。
具体实施方式
本发明提出一种非金属件贮存寿命计算方法，其包括：
第一步、选定表征非金属件退化的指标
用扫描电子显微镜对非金属件进行微观组织分析，观测到非金属件表面出现了硬化现象，硬化层越厚表明非金属件退化越严重，因此将非金属件硬化层厚度作为非金属件新的退化指标。
第二步、试验过程中定期检测非金属件硬化层厚度
使用扫描电子显微对非金属件进行微观组织分子观测，主要观察和测量硬度测试压痕处的硬化层厚度，按照一定时间间隔测试硬化层厚度，一般按照每1000h间隔进行一次测试，将测试数值按照时间点进行详细记录。通过对非金属件表面进行微观组织观察与测量，量化非金属试件表面硬化层厚度随时间变化。
第三步、拟合非金属件硬化层厚度-时间退化模型，评估贮存寿命
根据上述测得的非金属件硬化层厚度-时间退化数据，通过数学方法按照公式(1)进行拟合，求出待定系数A、B，得到非金属件硬化层厚度随时间的退化模型。
H(t)＝A·exp(B·t) (1)
其中：
H(t)——非金属件硬化层厚度；
t——贮存试验时间；
A、B——待定系数，一般情况下A＞0，0＜B＜1。
根据上述退化模型，给定非金属件硬化层厚度的失效阈值(失效阈值一般为非金属件硬化层初始性能值恶化50％)，可以计算得出非金属件的贮存寿命见式(2)。
Figure BDA0002833821960000021
本方法所针对的非金属件可以是导热垫，导热垫的材料可以是诸如硅橡胶的橡胶材料。
本发明在不显著增加试验时间和成本的条件下，解决了传统方法不能评估非金属件贮存寿命的问题，具有较高的推广价值。

Claims (3)

1.一种非金属件贮存寿命计算方法，其特征在于，其包括：
第一步、选定表征非金属件退化的指标，将非金属件硬化层厚度作为非金属件新的退化指标；
第二步、试验过程中定期检测非金属件硬化层厚度，包括：
使用扫描电子显微对非金属件进行微观组织分子观测，测量硬度测试压痕处的硬化层厚度，按照一定时间间隔测试硬化层厚度，将测试数值按照时间点进行详细记录；
第三步、拟合非金属件硬化层厚度-时间退化模型，评估贮存寿命，包括：
根据上述测得的非金属件硬化层厚度-时间退化数据，得到非金属件硬化层厚度随时间的退化模型；
第三步、拟合非金属件硬化层厚度-时间退化模型，评估贮存寿命，包括：
根据上述测得的非金属件硬化层厚度-时间退化数据，通过数学方法按照公式(1)进行拟合，求出待定系数A、B，得到非金属件硬化层厚度随时间的退化模型，
H(t)＝A·exp(B·t)(1)
其中：
H(t)——非金属件硬化层厚度；
t——贮存试验时间；
A、B——待定系数，其中A＞0，0＜B＜1；
根据上述退化模型，给定非金属件硬化层厚度的失效阈值，可以计算得出非金属件的贮存寿命见式(2)，
Figure FDA0004182438550000011
2.根据权利要求1所述的方法，其特征在于，按照每1000h的时间间隔进行一次硬化层厚度测试。
3.根据权利要求1所述的方法，其特征在于，失效阈值为非金属件硬化层初始性能值恶化50％。
CN202011471204.5A 2020-12-14 2020-12-14 一种非金属件贮存寿命计算方法 Active CN112668156B (zh)