CN112251078A - 一种用于水缸造景的可防水涂层及其制备方法 - Google Patents
一种用于水缸造景的可防水涂层及其制备方法 Download PDFInfo
- Publication number
- CN112251078A CN112251078A CN202011142262.3A CN202011142262A CN112251078A CN 112251078 A CN112251078 A CN 112251078A CN 202011142262 A CN202011142262 A CN 202011142262A CN 112251078 A CN112251078 A CN 112251078A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- pigment
- landscaping
- container
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种用于水缸造景的可防水涂层，包括以下重量份的原料：颜料90份；催化剂载体20份；醋酸异戊酯溶液50～60份；去离子水20～40份。本发明还提供一种用于水缸造景的可防水涂层的制备方法，包括以下步骤：取出90份颜料放于容器中；向容器中加入20份催化剂载体；向容器中加入50份醋酸异戊酯；使用玻璃棒搅拌，边搅拌边加入去离子水20～40份，直至搅拌均匀；将搅拌均匀后制得的可防水涂层移至30℃～65℃的保温容器里，烘干至胶状物。本发明可经济地应用于水族箱、鱼缸、草缸、水陆缸、雨淋水缸、浴缸等水缸的水下造景美化，解决了水缸造景长期泡水后易退色的问题，具有很高的市场推广价值。
Description
技术领域
本发明涉及涂料组合物，特别涉及一种用于水缸造景的可防水涂层及其制备方法。
背景技术
目前市面上的造景颜料有丙烯颜料、水彩颜料、无机硅质颜料、水性工艺品颜料，但均不具备防水尤其是长期泡水的性能，泡水后会出现涂层脱落、松散粉化、溶解、起泡问题。
为此，在应用于水缸造景的场景中，设计一种具备长期泡水又可防水的涂层，来解决上述问题，确保颜色涂层在造景上色后，可长期泡水不退色，具有实际意义。
中国专利申请文件CN106398503A公开了一种水性双组分水性聚氨酯涂料组合物，其A和B组成，A组分是一种或多种多元醇水性分散体或水性乳液；B组分是一种或多种亲水改性的异尔酮二异氰酸酯多聚体或预聚体，该专利不易常温固化，且应用于水缸造景场景中的耐水性差，防水性能差，不能长久浸泡于水缸中。
中国专利文件CN106609100A公开了一种防水涂料及其应用，包括A组分和B组分，A组分和B组分质量比为1:3-3:1；其中所述A组分组成为：脂肪族多聚异氰酸酯的重量份为10-20，弹性异氰酸酯固化剂的重量份为90-100；其中所述B组分组成为：聚天门冬氨酸酯树脂的重量份为30-60，聚合型改性聚天门冬氨酸酯树脂的重量份为20-40，活性超细功能填料浆料的重量份为5-25，分散剂的重量份为0.3-0.5，流平剂的重量份为0.2-0.5，消泡剂的重量份为0.2-0.5，颜填料的重量份为2-10。该专利应用于水缸造景场景中的非金属物体表面，防水耐水性能差，不能长久浸泡于水缸中。
发明内容
本发明为解决上述问题，提供一种用于水缸造景的可防水涂层，以可防水涂层解决现有技术中不能长期泡水，泡水后造景易退色的问题。
为实现上述目的，本发明采用的技术方案是：一种用于水缸造景的可防水涂层，包括以下重量份的原料：
颜料90份；
催化剂载体20份；
醋酸异戊酯50份；
去离子水20～40份。
进一步地，所述颜料为丙烯颜料，水彩颜料，无机硅质颜料，或水性工艺品颜料的任何一种。
进一步地，所述无机硅质颜料为朱砂、红土、雄黄任何一种。
进一步地，所述催化剂载体为透明纳米二氧化硅溶液，硅含量为30％，平均粒径为10nm，PH值为8～9。
进一步地，所述醋酸异戊酯溶液，按重量比包括：
乙酸正丁酯15％
乙酸乙酯15％；
正丁醇12～15％；
乙醇10％；
丙酮10％；
二甲苯或甲苯35％～38％。
为实现上述目的，本发明还提供一种制备方法，一种制备用于水缸造景的可防水涂层的方法，包括以下步骤：
取出90份颜料放于容器中；
向容器中加入20份催化剂载体；
向容器中加入50～60份醋酸异戊酯溶液；
使用玻璃棒搅拌，边搅拌边加入去离子水20～40份，直至搅拌均匀；
将搅拌均匀后制得的可防水涂层移至30℃～65℃的保温容器里，烘干至胶状物。
将丙烯颜料、水彩颜料、无机硅质颜料、水性工艺品颜料等颜料通过本发明技术方案的改进后，从而使其具备防水泡水的属性，从而使需要上色并要求颜色涂层能长期泡水的物件能够长期泡水；对颜料原料的兼容性强，具有很强的经济性。
有益效果：通过上述技术方案，制备出的本可防水涂层，可有效地应用于水族箱、鱼缸、草缸、水陆缸、雨淋水缸、浴缸等水缸的水下造景美化，解决了现有技术中不能长期泡水，泡水后造景易退色的问题，具有很高的市场推广价值。
具体实施方式
下面结合具体实施例对本发明作进一步的说明，以便更清楚、直观地理解本发明。
制备透明纳米二氧化硅溶液，使该溶液达到硅含量为30％，平均粒径为10nm， PH值为8～9。
实施例一：
制备醋酸异戊酯溶液，按重量比制作：
乙酸正丁酯15％；
乙酸乙酯15％；
正丁醇12％；
乙醇10％；
丙酮10％；
二甲苯38％。
实施例二：
制备醋酸异戊酯溶液，按重量比制作：
乙酸正丁酯15％；
乙酸乙酯15％；
正丁醇15％；
乙醇10％；
丙酮10％；
甲苯35％。
实施例三：
按如下重量份称取：
颜料90克；
透明纳米二氧化硅溶液20克；
取实施例一的醋酸异戊酯溶液50克；
去离子水20克。
将上述90克颜料放于容器中；向容器中加入上述20克透明纳米二氧化硅溶液；向容器中加入50克实施例一的醋酸异戊酯溶液；使用玻璃棒搅拌，边搅拌边加入去离子水20克，直至搅拌均匀；将搅拌均匀后制得的可防水涂层移至30℃～65℃的保温容器里，烘干至胶状物。
实施例四：
按如下重量份称取：
颜料90克；
透明纳米二氧化硅溶液20克；
醋酸异戊酯溶液60克；
去离子水40克。
将上述90克颜料放于容器中；向容器中加入上述20克透明纳米二氧化硅溶液；向容器中加入60克实施例二的醋酸异戊酯溶液；使用玻璃棒搅拌，边搅拌边加入去离子水40克，直至搅拌均匀；将搅拌均匀后制得的可防水涂层移至30℃～65℃的保温容器里，烘干至胶状物。
实施例五：
按如下重量份称取：
颜料90克；
透明纳米二氧化硅溶液20克；
醋酸异戊酯溶液55克；
去离子水30克。
将上述90克颜料放于容器中；向容器中加入上述20克透明纳米二氧化硅溶液；向容器中加入55克实施例二的醋酸异戊酯溶液；使用玻璃棒搅拌，边搅拌边加入去离子水30克，直至搅拌均匀；将搅拌均匀后制得的可防水涂层移至60℃的保温容器里，烘干至胶状物。
对比例一：
取无机硅质颜料朱砂100克。
对比例二：
取无机硅质颜料雄黄100克。
将实施例三、实施例四、实施例五分别与对比例一、对比例二进行测试，发现应用实施例三、实施例四、实施例五的水缸造景中的涂层的防水效果好，长期浸泡不退色，而对比例一、对比例二的防水效果不好，浸泡后掉色。
综上所述，本发明具有突出的实质性特点和显著的进步，实现了一种用于水缸造景的可防水涂层，可经济地应用于水族箱、鱼缸、草缸、水陆缸、雨淋水缸、浴缸等水缸的水下造景美化，解决了水缸造景长期泡水后易退色的问题，具有很高的市场推广价值。
以上所述仅为本发明的优选实施例，利用本发明说明书内容所作的等效形状或等效结构的变换，均应理解为本发明的专利保护范围内。
Claims (6)
1.一种用于水缸造景的可防水涂层，其特征在于，包括以下重量份的原料：
颜料90份；
催化剂载体20份；
醋酸异戊酯溶液50～60份；
去离子水20～40份。
2.根据权利要求1所述的用于水缸造景的可防水涂层，其特征在于：所述颜料为丙烯颜料，水彩颜料，无机硅质颜料，或水性工艺品颜料的任何一种。
3.根据权利要求2所述的用于水缸造景的可防水涂层，其特征在于：所述无机硅质颜料为朱砂、红土、雄黄任何一种。
4.根据权利要求1所述的用于水缸造景的可防水涂层，其特征在于：所述催化剂载体为透明纳米二氧化硅溶液，硅含量为30％，平均粒径为10nm，PH值为8～9。
5.根据权利要求1所述的用于水缸造景的可防水涂层，其特征在于，所述醋酸异戊酯溶液，按重量比包括：
乙酸正丁酯15％；
乙酸乙酯15％；
正丁醇12～15％；
乙醇10％；
丙酮10％；
二甲苯或甲苯35％～38％。
6.一种权利要求1至5中任一权利要求所述的用于水缸造景的可防水涂层的制备方法，其特征在于，包括以下步骤：
取出90份颜料放于容器中；
向容器中加入20份催化剂载体；
向容器中加入50～60份醋酸异戊酯溶液；
使用玻璃棒搅拌，边搅拌边加入去离子水20～40份，直至搅拌均匀；
将搅拌均匀后制得的可防水涂层移至30℃～65℃的保温容器里，烘干至胶状物。