CN111838183A - 复合金属胶体无机抗菌剂及其制备方法、及其无机人造石 - Google Patents
复合金属胶体无机抗菌剂及其制备方法、及其无机人造石 Download PDFInfo
- Publication number
- CN111838183A CN111838183A CN202010809268.5A CN202010809268A CN111838183A CN 111838183 A CN111838183 A CN 111838183A CN 202010809268 A CN202010809268 A CN 202010809268A CN 111838183 A CN111838183 A CN 111838183A
- Authority
- CN
- China
- Prior art keywords
- silver
- copper
- antibacterial
- inorganic
- composite metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种复合金属胶体无机抗菌剂及其制备方法、及其无机人造石。所述复合金属胶体无机抗菌剂包括羟基磷酸锆微粉、银原子、铜原子和纳米二氧化钛；其中，纳米二氧化钛的表面微孔吸附有所述银原子和铜原子胶体，所述羟基磷酸锆微粉的表面吸附有银原子、铜原子和纳米二氧化钛胶体；所述银原子作为活化剂，所述铜原子作为待激活抗菌剂，所述纳米二氧化钛作为紫外杀菌体。含氧的湿润环境下，所述铜原子被氧化为具有抗菌活性的铜离子。所述复合金属胶体无机抗菌剂含有的抗菌活性物质不易流失。本发明采用所述的复合金属胶体无机抗菌剂制得的无机人造石，具有耐热性好、广谱抗菌、缓释性优良和采购成本低等特点，具有更加良好的成本优势。
Description
技术领域
本发明涉及抗菌剂和人造石技术领域，尤其涉及一种复合金属胶体无机抗菌剂及其制备方法、及其无机人造石。
背景技术
羟基磷酸锆钠的表面具有多孔型结构，比表面积大，吸附能力强，化学稳定性好，耐高温，并且与吸附在空隙内的抗菌金属离子之间具有很好的结合力，可以提高抗菌金属离子的缓释作用。羟基磷酸锆钠结构对多种金属离子具有兼容性，可以同时吸附多种金属离子。
现有技术的抗菌剂载有的银离子，遇到酸碱性较强的液体很快就流失，抗菌剂的缓释性差。
作为食品加工行业，尤其是医疗行业，为了减少细菌的感染和传递，选择使用含有抗菌物质的工作台，但是工作台需要频繁的清洁，有时需要使用酸性或者碱性较强的物料或者药剂，工作台中含有的普通抗菌剂很容易就失效。
银离子是杀菌特性优秀的抗菌剂，其原料来源多数为硝酸银，采购成本高。且硝酸银属于强氧化剂、腐蚀品、环境污染物，减少硝酸银的使用量更为环保。
故此，需要开发可以耐酸碱且可以使用替代银离子的其他原料以降低成本，并可制成具有良好的抗菌效果且不易流失的抗菌剂，满足以上行业的需求。
发明内容
本发明提出一种复合金属胶体无机抗菌剂及其制备方法、及其无机人造石，所使用的复合金属胶体无机抗菌剂不易流失，成本低且缓释性能良好。
为达此目的，本发明采用以下技术方案：
一种复合金属胶体无机抗菌剂，包括羟基磷酸锆微粉、银原子、铜原子和纳米二氧化钛；其中，所述纳米二氧化钛的表面微孔吸附有所述银原子和铜原子胶体，所述羟基磷酸锆微粉的表面吸附有银原子、铜原子和纳米二氧化钛胶体；所述银原子作为活化剂，所述铜原子作为待激活抗菌剂，所述纳米二氧化钛作为紫外杀菌体。
优选的，还包括氧化锌，所述氧化锌为稳定剂，所述氧化锌为吸附于羟基磷酸锆微粉的胶体，所述氧化锌用于延缓碱性环境下的氧化银被碱化，避免氧化银先转化为氢氧化银析出，而导致铜原子未能转化为铜离子。
优选的，吸附于所述羟基磷酸锆微粉和纳米二氧化钛吸附的铜原子、氧化锌和银原子的摩尔含量均依次降低。
优选的，所述羟基磷酸锆微粉吸附的所述铜原子、纳米二氧化钛、氧化锌和银原子的摩尔含量比为4:2:2:1。
进一步的，本发明还提出了以上所述的复合金属胶体无机抗菌剂的制备方法，包括以下具体的步骤：
S1)往水中添加硝酸银、纳米二氧化钛、硝酸铜和氧化锌并搅拌混合均匀，制得银铜锌硝酸溶液；
S2)在银铜锌硝酸溶液中加入羟基磷酸锆钠微粉，用稀硝酸和稀氢氧化钠溶液调整pH值，水浴恒温并快速搅拌均匀，制得羟基磷酸锆微粉吸附溶液；
S3)将所述羟基磷酸锆微粉吸附溶液放入烘箱烘干，制得羟基磷酸锆微粉吸附干粉；
S4)将所述羟基磷酸锆微粉吸附干粉送入还原烧结炉加热，焙烧；
S5)往恒温的还原烧结炉加入一氧化碳，进行还原反应，制得羟基磷酸锆微粉吸附焙烧粉；
S6)将所述羟基磷酸锆微粉吸附焙烧粉过筛，即制得所述的复合金属胶体无机抗菌剂。
进一步的，在所述步骤S1中，所述银铜锌硝酸溶液含有的硝酸铜、纳米二氧化钛、氧化锌、硝酸银和水的混合摩尔比为＝2.5:1:1:0.5:20；在所述步骤S2中，所述银铜锌硝酸溶液与羟基磷酸锆微粉的摩尔比为1:4，水浴温度为50℃，pH值为3-4。
进一步的，在所述步骤3中，所述烘干的温度100-120℃；在所述步骤S4中，所述焙烧的温度500-600℃，焙烧时间为3-4小时。
进一步的，在所述步骤S5中，加入所述一氧化碳的压力为0.1-0.15MPa，所述还原反应的时间为0.8-1小时；在所述步骤S6中，所述过筛的筛网的孔径为400目。
进一步的，本发明还提出了一种无机人造石，原料包括抗菌粘结液，所述抗菌粘结液的原料成分包括以上的所述的复合金属胶体无机抗菌剂，所述抗菌粘结液用于无机人造石的固态原料的粘结，所述抗菌粘结液均匀的分布于所述无机人造石中。
进一步的，所述复合金属胶体无机抗菌剂占无机人造石的总体质量的百分比为1-3％；所述抗菌粘结液的原料成分还包括水，所述抗菌粘结液为加入于无机人造石之前的预配制混合液。
本发明的有益效果为：
本发明所述的复合金属胶体无机抗菌剂，为载有银、铜金属胶体、纳米二氧化钛和氧化锌的羟基磷酸锆微粉，具有耐热性好、高效广谱抗菌、缓释性优良和紫外线强化杀菌等特点。本发明所述的复合金属胶体无机抗菌剂，相比载银的羟基磷酸锆抗菌剂，具有更加良好的成本优势。
本发明所述的复合金属胶体无机抗菌剂，含有双重的吸附载体和多种的杀菌抗菌物质，具有良好的广谱杀菌效果，且不易流失，适合对抗菌杀菌要求标准高的场所使用，尤其是医疗和食品加工行业。
纳米二氧化钛、氧化锌、硝酸铜的原料来源广泛，采购成本低，故此，本发明所述的复合金属胶体无机抗菌剂，相比现有技术的载有银离子的羟基磷酸锆抗菌剂，具有更好的成本优势且缓释性能更为优化。
本发明提出了所述的复合金属胶体无机抗菌剂的制备方法，制得的含有双重载体结构和多种抗菌物质的无机抗菌剂，便于存储方便使用。
本发明还提出了使用所述的复合金属胶体无机抗菌剂的无机人造石，制得的无机人造石的抗菌性能和抗菌耐久性能均非常优良。
具体实施方式
下面以具体实施方式进一步说明本发明的技术方案。
一种复合金属胶体无机抗菌剂，包括羟基磷酸锆微粉、银原子、铜原子和纳米二氧化钛；其中，所述纳米二氧化钛的表面微孔吸附有所述银原子和铜原子胶体，所述羟基磷酸锆微粉的表面吸附有银原子、铜原子和纳米二氧化钛胶体；所述银原子作为活化剂，所述铜原子作为待激活抗菌剂，所述纳米二氧化钛作为紫外杀菌体。
所述复合金属胶体无机抗菌剂中，银原子作为活化剂，铜原子作为待激活抗菌剂，纳米二氧化钛作为紫外杀菌体；所述纳米二氧化钛为锐钛型纳米二氧化钛。
所述羟基磷酸锆微粉由羟基磷酸锆钠制得，具有亲水基，与水溶液具有良好的相容性。羟基磷酸锆钠比表面积大表面能高，可作为理想的杀菌抗菌金属离子的载体，可以存储大量的杀菌抗菌金属胶体，可以减少杀菌抗菌金属胶体的流失，并提高杀菌抗菌金属离子的释放浓度和缓释能力。
载负于羟基磷酸锆微粉和纳米二氧化钛的银铜金属胶体可释放出活性的银原子、铜原子，金属原子胶体比金属离子胶体更不易受潮流失，可使抗菌物质的缓释有效期得到延长。
当银原子在含氧的湿润环境中时，如与水、酸或碱性溶液接触，银原子被氧化为银离子；银原子、银离子和铜原子同时存在时，银离子/银的电极电位是0.80伏特，铜离子/铜的电极电位是0.34伏特，由于存在电极电位的电位差，金属胶体中的银离子可以氧化胶体中的铜原子为胶体铜离子，而银离子被还原为银原子，其化学反应式为2Ag++Cu＝2Ag+Cu++，其电势差得到释放E0＝ψAg+/Ag-ψCu++/Cu)＝0.80-0.34＝+0.46伏特，胶体中的铜原子转化成具有杀菌抗菌活性的Cu++离子。
在含氧的湿润环境中时，银原子氧化成银离子，银离子氧化胶体中的铜原子为胶体铜离子，为具有抗菌活性的铜离子，所述复合金属胶体无机抗菌剂的抗菌活性被激活。干燥的所述复合金属胶体无机抗菌剂具有良好的稳定性，抗菌活性物质不易流失。
本发明选用的纳米二氧化钛为锐钛型纳米二氧化钛，锐钛型纳米二氧化钛为白色粉末状物品，化学性能稳定，具有强大的光催化氧化还原能力、化学稳定性高、无毒，380nm以下可见光即可激发，所以在太阳光或紫外光作用下，具有极强氧化作用，能将甲醛、甲胺、苯、二甲苯、氨、TVOC等有害有机物、污染物臭气、细菌等氧化分解成无害的二氧化碳和水。具有抑菌、杀菌、消毒、去除污染物、亲水性、自洁性等特性，还具有廉价无毒，且具有耐酸碱化学稳定性好的特点。
纳米二氧化钛在紫外线的照射下具有良好的杀菌作用，且对有机污染物的氧化分解具有催化作用，锐钛型纳米二氧化钛还具有较好的吸附性能。非常适合日常需要用紫外线杀菌的工作环境，可以提高杀菌去污的效果，可以协助被吸附的抗菌物质提高广谱杀菌的有效率。
本发明所述的复合金属胶体无机抗菌剂，含有双重的吸附载体和多种的杀菌抗菌物质，具有良好的广谱杀菌效果，且不易流失，适合对抗菌杀菌要求标准高的场所使用，尤其是医疗和食品加工行业。
优选的，还包括氧化锌，所述氧化锌为稳定剂，所述氧化锌为吸附于羟基磷酸锆微粉的胶体，所述氧化锌用于延缓碱性环境下的氧化银被碱化，避免氧化银先转化为氢氧化银析出，而导致铜原子未能转化为铜离子。
氧化锌是具有良好抗菌效果的抗菌剂，且具有光敏杀菌性能，其原料来源广泛，采购成本低，硝酸银为本发明的银原子的原料，与硝酸银粉剂相比氧化锌粉剂具有非常优越的成本优势。
氧化银胶体吸附于复合金属胶体无机抗菌剂具有更好的稳定性不易流失，所述复合金属胶体无机抗菌剂含有多种活性抗菌物质，具有更宽的产品应用范围和更全面的抗菌效果，在提高了缓释性能的同时也具有更好的成品优势。
吸附于复合金属胶体无机抗菌剂的氧化锌，用于保护碱性环境下的氧化银被碱化，避免氧化银转化为氢氧化银而析出，从而降低铜原子转化为铜离子的转化率，导致所述复合金属胶体无机抗菌剂的抗菌性能降低。只有当氧化锌被反应消耗完了之后，氧化银才被碱化转化为氢氧化银而析出。
氧化锌具有良好的活性，可以改善银离子碱性环境下的析出的不良影响，化学反应机理如下。
银离子在碱性环境下，与碱基反应生成氢氧化银沉淀
Ag++OH-＝AgOH↓(白色)
氢氧化银沉淀不稳定分解为氧化银沉淀
2AgOH＝Ag2O↓(黑褐色)+H2O
当氧化锌和氧化银共存时，碱性环境下氧化锌的化学反应活性高于氧化银，氧化锌先与碱基发生化学反应，可延缓和阻止氧化银的沉淀析出。
ZnO++2OH-＝Zn(OH)2↓(白色)
适用氧化锌作为银离子的稳定剂，可提高所述复合金属胶体无机抗菌剂的抗菌性能的稳定性，通过增加氧化锌的用量和比例并可拓宽所述复合金属胶体无机抗菌剂的碱性适用区间。
优选的，吸附于所述羟基磷酸锆微粉和纳米二氧化钛吸附的铜原子、氧化锌和银原子的摩尔含量均依次降低。
优选的，所述羟基磷酸锆微粉吸附的所述铜原子、纳米二氧化钛、氧化锌和银原子的摩尔含量比为4:2:2:1。
本发明所述的复合金属胶体无机抗菌剂，含氧的湿润环境含有的银原子可以有效地将铜原子转化为铜离子。在保留银原子的转化铜离子的功效的情况下，降低原料中硝酸银的使用量，提高硝酸铜、氧化锌的使用量可以有效提高所述的复合金属胶体无机抗菌剂的成本优势，且更为环保。
所述羟基磷酸锆微粉吸附的铜原子、纳米二氧化钛、氧化锌和银原子的摩尔含量比为4:2:2:1时具有更好的性价比，既可保障所述的复合金属胶体无机抗菌剂具有良好的抗菌效果，又同时可以获得更好的成本优势。
纳米二氧化钛需要在近紫外线和低频可见光照下才能具有杀菌作用，纳米二氧化钛同时作为部分的抗菌金属离子的吸附载体，故此，铜原子、纳米二氧化钛、氧化锌和银原子的总质量中纳米二氧化钛不宜超过25％的摩尔含量比，否则吸附于纳米二氧化钛的铜原子、纳米二氧化钛、氧化锌和银原子过多，羟基磷酸锆微粉中的铜原子、氧化锌和银原子的吸附率就偏低了。而铜原子、纳米二氧化钛、氧化锌和银原子中纳米二氧化钛的摩尔含量比低于20％，则在紫外线照射下的杀菌率偏低，不适合高标准的使用场所的要求。
所述氧化锌和银原子的摩尔含量比为2:1，可以降低氧化银先被碱化的几率，可以提高所述羟基磷酸锆微粉吸附的铜原子转化为铜离子的转化率，可以保障所述复合金属胶体无机抗菌剂的抗菌性能的稳定性。
进一步的，本发明还提出了以上所述的复合金属胶体无机抗菌剂的制备方法，包括以下具体的步骤：
S1)往水中添加硝酸银、纳米二氧化钛、硝酸铜和氧化锌并搅拌混合均匀，制得银铜锌硝酸溶液；
S2)在银铜锌硝酸溶液中加入羟基磷酸锆钠微粉，用稀硝酸和稀氢氧化钠溶液调整pH值，水浴恒温并快速搅拌均匀，制得羟基磷酸锆微粉吸附溶液；
S3)将所述羟基磷酸锆微粉吸附溶液放入烘箱烘干，制得羟基磷酸锆微粉吸附干粉；
S4)将所述羟基磷酸锆微粉吸附干粉送入还原烧结炉加热，焙烧；
S5)往恒温的还原烧结炉加入一氧化碳，进行还原反应，制得羟基磷酸锆微粉吸附焙烧粉；
S6)将所述羟基磷酸锆微粉吸附焙烧粉过筛，即制得所述的复合金属胶体无机抗菌剂。
本发明所述的复合金属胶体无机抗菌剂的制备方法，先将羟基磷酸锆微粉浸汲在硝酸银、纳米二氧化钛、硝酸铜和氧化锌的水溶液中，纳米二氧化钛不溶于硝酸溶液，硝酸银、硝酸铜和氧化锌的浓度较高且大于纳米二氧化钛的浓度时，纳米二氧化钛的表面吸附有其中部分的Ag+、Cu++和Zn++离子，其余的部分的Ag+、Cu++和Zn++离子吸附于羟基磷酸锆微粉，具有较大的比表面积的羟基磷酸锆微粉将纳米二氧化钛吸附在其表面，形成双重的复合载体。故此，本发明所述的复合金属胶体无机抗菌剂具有更为高效和广谱的抗菌性能。
由于羟基磷酸锆钠耐高温稳定性，在常温下进行抗菌金属离子盐溶液吸附后，再进过高温烘烧将抗菌金属离子氧化为氧化物，使抗菌金属离子在羟基磷酸锆钠的结合力增强，再进一步将金属离子还原为金属原子，使游离出的抗菌金属原子受到控制，保证了载体中的抗菌金属元素产生良好的缓释效果，具有长期的抗菌功效。
吸附于羟基磷酸锆微粉和纳米二氧化钛的金属离子有Ag+、Cu++和Zn++离子，纳米二氧化钛吸附于羟基磷酸锆微粉，烘干羟基磷酸锆微粉后接着在高温焙烧，Ag+、Cu++和Zn++离子转化为氧化银、氧化铜和氧化锌，进而在高温真空下用一氧化碳还原氧化银和氧化铜为银原子胶体和铜原子胶体，纳米二氧化钛和氧化锌不能一氧化碳被还原仍以胶体形式吸附于羟基磷酸锆微粉表面，含有银铜原子的金属胶体和氧化锌胶体吸附于羟基磷酸锆微粉表面形成具有抗菌活性的羟基磷酸锆微粉。
普通的氧化锌粉剂，经过溶解为Zn++离子，再被氧化再氧化锌，并形成胶体吸附于羟基磷酸锆微粉表面氧化锌，具有广谱抗菌性能，对于白色念珠菌有良好的抗菌效果。
纳米二氧化钛为白色粉末状物品，化学性能稳定，具有强大的光催化氧化还原能力、化学稳定性高、无毒，380nm以下可见光即可激发，所以在太阳光或紫外光作用下，具有极强氧化作用，能将甲醛、甲胺、苯、二甲苯、氨、TVOC等有害有机物、污染物臭气、细菌等氧化分解成无害的二氧化碳和水。具有抑菌、杀菌、消毒、去除污染物、亲水性、自洁性等特性，还具有廉价无毒，化学稳定性好的特点。
纳米二氧化钛在紫外线的照射下具有良好的杀菌作用，且对有机污染物的氧化分解具有催化作用，纳米二氧化钛还具有较好的吸附性能。非常适合日常需要用紫外线杀菌的工作环境，可以提供杀菌去污的效果，可以协助被吸附的抗菌物质提高广谱杀菌的有效率。
本发明的纳米二氧化钛可采用纳米钛白粉，氧化锌采用氧化锌粉剂，氧化铜采用硝酸铜粉剂，原料来源广泛，采购成本低。
因此，本发明所述的复合金属胶体抗菌剂，为载有银原子、铜原子、纳米二氧化钛和氧化锌的羟基磷酸锆微粉，具有耐热性好、高效广谱抗菌、缓释性优良和紫外线强化杀菌等特点。本发明所述的复合金属胶体抗菌剂，相比载银的羟基磷酸锆抗菌剂，具有更加良好的成本优势。
进一步的，在所述步骤S1中，所述银铜锌硝酸溶液含有的硝酸铜、纳米二氧化钛、氧化锌、硝酸银和水的混合摩尔比为＝2.5:1:1:0.5:20；在所述步骤S2中，所述银铜锌硝酸溶液与羟基磷酸锆微粉的摩尔比为1:4，水浴温度为50℃，pH值为3-4。
混合摩尔比硝酸铜:纳米二氧化钛:氧化锌:硝酸银:水＝2.5:1:1:0.5:20，含有的银铜锌离子和纳米二氧化钛抗菌活性物质的合计百分比含量较高，可以提高羟基磷酸锆的吸附效率。
所述银铜锌硝酸溶液与羟基磷酸锆微粉的配比为1:4的摩尔比，含有的抗菌活性物质的浓度高，所述的复合金属胶体无机抗菌剂可以具有良好的抗菌效果，便于储存和使用。
水浴温度为50℃，pH值为3-4，可以提高银离子的溶解和吸附效率。
进一步的，在所述步骤3中，所述烘干的温度100-120℃；在所述步骤S4中，所述焙烧的温度500-600℃，焙烧时间为3-4小时。
烘干温度不低于100℃，可以充分的烘干所述羟基磷酸锆微粉吸附溶液中含有的水分。
硝酸银和硝酸铜在高温焙烧为氧化银和氧化铜，进而在高温真空下用一氧化碳还原氧化银和氧化铜为金属胶体，银铜金属胶体聚集在羟基磷酸锆微粉表面凝聚成具有抗菌活性的羟基磷酸锆微粉。
440℃为硝酸银的分解温度，在500℃以上焙烧，可确保硝酸银完全分解氧化为氧化银，硝酸铜的分解温度低于硝酸银的分解温度，硝酸铜的分解氧化更为完全。通过高温处理还可以增加银离子被吸附的强度，延长抗菌剂的缓释有效期，在500-600℃的效果比较好，超过600℃则会破坏银离子的活性，影响银离子析出和被还原的比例。故此，本发明所述的复合金属胶体无机抗菌剂，具有比较稳定的抗菌金属析出性能和抗银变色能力。
进一步的，在所述步骤S5中，加入所述一氧化碳的压力为0.1-0.15MPa，所述还原反应的时间为0.8-1小时；在所述步骤S6中，所述过筛的筛网的孔径为400目。
在500℃焙烧，加入的一氧化碳的压力低于0.1MPa会降低氧化银和氧化铜的还原有效率，高于0.15MPa浪费资源。焙烧温度为500-600℃，高于440℃并维持0.8-1小时，可以提高氧化银和氧化铜还原为银铜胶体的还原率。还原气体也可采用氢气，采用一氧化碳比氢气更为方便且成本便宜，具有更好的经济效益。
羟基磷酸锆微粉的粒径越小，其表面积比越大，载有的银铜胶体的活性越高，常规的羟基磷酸锆微粉的粒径为325目，采用400目的过滤筛过滤可以去除粘结的粒径过大的复合金属胶体无机抗菌剂，避免使用时出现分布不均大颗粒的不良外观。
进一步的，本发明还提出了一种无机人造石，原料包括抗菌粘结液，所述抗菌粘结液的原料成分包括以上的所述的复合金属胶体无机抗菌剂，所述抗菌粘结液用于无机人造石的固态原料的粘结，所述抗菌粘结液均匀的分布于所述无机人造石中。
所述抗菌粘结液用于无机人造石的固态原料的粘结，均匀的分布于所述无机人造石中。包括在所述抗菌粘结液中的复合金属胶体无机抗菌剂均匀的分布于所述无机人造石中，且被粘结于所述无机人造石中，可使所述无机人造石的抗菌效果更为稳定和均匀。
所述无机人造石的固态原料包括石英石、大理石、岗石、长石、超石英石和着色剂。
进一步的，所述复合金属胶体无机抗菌剂占无机人造石的总体质量的百分比为1-3％；所述抗菌粘结液的原料成分还包括水，所述抗菌粘结液为加入于无机人造石之前的预配制混合液。
有益效果：含有1-3％的所述复合金属胶体无机抗菌剂的无机人造石，经检测其抗菌性能和抗菌耐久性，均能满足JC/T897－2014《抗菌陶瓷制品抗菌性能》标准的要求。所述无机人造石含有的所述复合金属胶体无机抗菌剂的含量低于1％，抗菌的性能指标不达标；所述无机人造石含有的所述复合金属胶体无机抗菌剂的含量高于3％，其抗菌性能的质量过剩，浪费资源。
由于现有技术的无机人造石的主要原料多为水泥系物料，碱性较高，先将原料含有水的所述抗菌粘结液配置好，再加入无机人造石的预制料，可以避免无机人造石中的水泥系物料的碱性破坏所述抗菌粘结液含有的银离子，避免银离子变为氢氧化银，导致铜原子转化铜离子的转化率降低，而影响所述复合金属胶体无机抗菌剂制得的无机人造石的抗菌性能。
实施例和对比例
根据以下所述制得各实施例和对比例的无机人造石，所述羟基磷酸锆钠微粉可采用市售的羟基磷酸锆钠微粉，粒度D50≦10μm，比表面积≧50m2/g，纯净度≧95％，所述硝酸银、纳米二氧化钛、硝酸铜和氧化锌为市售的化学纯的粉剂。
具体如下：
1、一种复合金属胶体无机抗菌剂，包括羟基磷酸锆微粉、银原子、铜原子、纳米二氧化钛和氧化锌，所述银原子、铜原子和纳米二氧化钛均为吸附于羟基磷酸锆微粉的胶体；所述紫外杀菌体为纳米二氧化钛,其表面微孔吸附有所述银原子和铜原子；
吸附于所述羟基磷酸锆微粉和纳米二氧化钛的铜原子、氧化锌和银原子的摩尔含量依次降低。
所述铜原子、纳米二氧化钛、氧化锌和银原子的摩尔含量比为4:2:2:1。
2、所述的复合金属胶体无机抗菌剂的制备方法，包括以下具体的步骤：
S1)配制含有硝酸银、纳米二氧化钛、硝酸铜和氧化锌的水溶液，制得银铜锌硝酸溶液；
S2)在银铜锌硝酸溶液中加入羟基磷酸锆钠微粉，用稀硝酸和稀氢氧化钠溶液调整pH值，水浴恒温并快速搅拌均匀，制得羟基磷酸锆微粉吸附溶液；
S3)将所述羟基磷酸锆微粉吸附溶液放入烘箱烘干，制得羟基磷酸锆微粉吸附干粉；
S4)将所述羟基磷酸锆微粉吸附干粉送入还原烧结炉加热，焙烧；
S5)往恒温的还原烧结炉加入一氧化碳，进行还原反应，制得羟基磷酸锆微粉吸附焙烧粉；
S6)将所述羟基磷酸锆微粉吸附焙烧粉过筛，即制得所述的复合金属胶体无机抗菌剂。
在所述步骤S1中，所述银铜锌硝酸溶液含有的硝酸铜、纳米二氧化钛、氧化锌、硝酸银和水的混合摩尔比为＝2.5:1:1:0.5:20；在所述步骤S2中，所述银铜锌硝酸溶液与羟基磷酸锆微粉的摩尔比为1:4，水浴温度为50℃，pH值为3-4；在所述步骤3中，所述烘干的温度100-120℃；在所述步骤S4中，所述焙烧的温度500-600℃，焙烧时间为3-4小时。在所述步骤S5中，加入所述一氧化碳的压力为0.1-0.15MPa，所述还原反应的时间为0.8-1小时；在所述步骤S6中，所述过筛的筛网的孔径为400目。
3、制备无机人造石，所述无机人造石的原料包括抗菌粘结液，所述抗菌粘结液含有以上所述复合金属胶体无机抗菌剂，所述抗菌粘结液的原料成分还包括水，所述抗菌粘结液为预制混合液，所述复合金属胶体无机抗菌剂占无机人造石的总体质量的百分比为1-3％。
4、各实施例的具体的原料成分的含量和比例、以及参数见表1，各对比例的具体的原料成分的含量和比例、以及参数见表2。
5、参照JC/T897－2014《抗菌陶瓷制品抗菌性能》标准，对没有添加抗菌剂的基材、各实施例和对比例制得的无机人造石取样，并进行有关的大肠杆菌、金黄色葡萄球菌和白色念珠菌的抗菌性能抗菌率和抗菌耐久性抗菌率的测试，实施例和基材的测试结果见表1，对比例的测试结果见表1。
表1各实施例以及基材的有关数据和测试结果
表2各对比例的有关数据和测试结果
下面根据以上的各个实施例和对比例的情况和检测结果分析说明：
1、根据JC/T897－2014《抗菌陶瓷制品抗菌性能》标准的要求，抗菌性能抗细菌率(％)≥90％为合格，抗菌耐久性能抗细菌率(％)≥85％为合格，基材的大肠杆菌、金黄色葡萄球菌和白色念珠菌的抗菌性能抗细菌率和抗菌耐久性能抗细菌率的检测结果均为不合格。
2、分析实施例1-6的检测结果：
(1)实施例1-3的大肠杆菌、金黄色葡萄球菌和白色念珠菌的抗菌性能抗细菌率(％)和抗菌耐久性能抗细菌率(％)均为合格，且抗细菌率的数值是依次递增的，说明随着活性铜离子的增加，抗菌效果得到加强。
(2)实施例1和2与实施例3的不同在于：硝酸铜加入的摩尔比较少，低于2.5摩尔比分别为2.0和2.3摩尔比，实施例1和2的肠杆菌、金黄色葡萄球菌和白色念珠菌的抗菌性能抗细菌率(％)和抗菌耐久性能抗细菌率(％)的检测结果均为合格，符合合格的标准；与实施例1和2的检测结果对比显示实施例3的抗菌杀菌效果最佳，所述银铜锌硝酸溶液含有的硝酸铜、氧化锌、硝酸银和水的摩尔混合比为＝2.5:1:0.5:20；故此，所述银铜锌硝酸溶液与羟基磷酸锆微粉的配比为1:4，含有的所述复合金属胶体无机抗菌剂占无机人造石的总体质量的百分比为1％，所述银铜锌硝酸溶液含有的硝酸铜、氧化锌、硝酸银和水的摩尔混合比为＝2:1:0.5:20，可以保障所述复合金属胶体无机抗菌剂制得的无机人造石均有良好的抗菌效果，适合高标准要求的场所使用；所述羟基磷酸锆微粉吸附的铜原子、纳米二氧化钛、氧化锌和银原子的摩尔含量比为4:2:2:1具有较好的性价比，可满足抗菌杀菌常规标准要求。
(3)实施例4与实施例3的不同在于：实施例4中没有加入氧化锌，实施例4的大肠杆菌和金黄色葡萄球菌的抗菌性能抗细菌率和抗菌耐久性能抗细菌率的检测结果均非常优秀，高于95％；但是实施例4的白色念珠菌的抗菌性能抗细菌率和抗菌耐久性能抗细菌率的检测结果均不合格；说明氧化锌对白色念珠菌具有较为突出的抗菌效果，铜离子对白色念珠菌的抗菌效果一般；
(4)实施例5与实施例4的不同在于：实施例5中没有加入氧化锌，但增加了0.5摩尔比的含量的硝酸银，实施例5的白色念珠菌的抗菌性能抗细菌率和抗菌耐久性能抗细菌率的检测结果合格，说明增加的硝酸银的0.5摩尔的含量对白色念珠菌具有较为突出的抗菌效果；结合实施例1-5进行对比，说明加入的浓度比为1摩尔比的氧化锌可以代替银离子对白色念珠菌具有较为突出的抗菌效果；
(5)实施例6与实施例1的不同在于：光照条件不一样，实施例1的是日常的白天室内光，实施例8采用的是8小时紫外线照射，实施例8的抗菌性能抗细菌率检测结果均合格，说明食品加工场晚上只要采用8小时的紫外照射可以获得良好的杀菌抗菌效果；紫外照射的方式不适合耐久性测试，故未实施相关检测；
(6)综合分析实施例1-6的成分和检测结果得知：所述抗菌粘结液的原料成分还包括水，所述抗菌粘结液为预配制混合液；本发明所述的复合金属胶体无机抗菌剂是有效的，所述的抗菌粘结液和所制得的无机人造石具有良好的抗菌效果并且具有良好的耐久性。所述银铜锌硝酸溶液与羟基磷酸锆微粉的配比为1:4，含有的所述复合金属胶体无机抗菌剂占无机人造石的总体质量的百分比为1-3％，所述银铜锌硝酸溶液含有的硝酸铜、氧化锌、硝酸银和水的摩尔混合比为＝2.5:1:1:0.5:20；可以保障所述复合金属胶体无机抗菌剂制得的无机人造石均具有最优的抗菌效果；所述羟基磷酸锆微粉吸附的铜原子、氧化锌和银原子的摩尔含量比为4:2:2:1具有较好的性价比。
3、分析对比例1，与实施例1对比，对比例1的不同为：对比例1的所述还原反应的时间为0.5小时，不足0.8小时的下限降低了氧化银的还原率，故而降低了抗菌功能的铜离子的转化率，导致对比例1的大肠杆菌、金黄色葡萄球菌的抗菌性能抗细菌率和抗菌耐久性能抗细菌率(％)的检测结果均为不合格。
4、分析对比例2，与实施例1对比，对比例2的不同为：对比例2的所述硝酸铜的加入的摩尔比为1.5，少于所述羟基磷酸锆微粉吸附的铜原子、纳米二氧化钛、氧化锌和银原子的摩尔含量比设置为4:2:2:1，故而降低了抗菌功能的铜离子的含量，导致对比例2的大肠杆菌、金黄色葡萄球菌的抗菌性能抗细菌率和抗菌耐久性能抗细菌率(％)的检测结果均为不合格。
5、分析对比例3，与实施例1对比，对比例3的不同为：对比例3加入的所述硝酸银的摩尔比为1，高于所述羟基磷酸锆微粉吸附的铜原子、纳米二氧化钛、氧化锌和银原子的摩尔含量比设置为4:2:2:1，对比例3的大肠杆菌、金黄色葡萄球菌和白色念珠菌的抗菌性能抗细菌率和抗菌耐久性能抗细菌率(％)的检测结果均达到了最高极限，质量过剩浪费资源。
6、分析对比例4，与实施例1对比，对比例4的不同为：对比例4加入的所述硝酸银的摩尔比为0.3，低于所述羟基磷酸锆微粉吸附的铜原子、纳米二氧化钛、氧化锌和银原子的摩尔含量比设置为4:2:2:1，造成铜离子未被完全的转化，导致对比例4的大肠杆菌、金黄色葡萄球菌的抗菌性能抗细菌率和抗菌耐久性能抗细菌率(％)的检测结果均不合格；故此，所述羟基磷酸锆微粉吸附的铜原子、纳米二氧化钛、氧化锌和银原子的摩尔含量比设置为4:2:2:1，比较适宜。
7、分析对比例5，与实施例1对比，对比例5的不同为：对比例5的所述抗菌粘结液不是预制混合液，且没有加入所述氧化锌，在碱性环境下所述羟基磷酸锆微粉吸附的银原子被碱化，失去了氧化铜原子为铜离子的作用，造成制得的无机人造石的大肠杆菌、金黄色葡萄球菌和白色念珠菌的抗菌性能抗细菌率和抗菌耐久性能抗细菌率(％)的检测结果均不合格。
8、分析对比例6，与实施例1和对比例5对比，对比例6的不同为：对比例5的所述抗菌粘结液虽然不是预制混合液，但是加入所述氧化锌，制得的无机人造石的大肠杆菌、金黄色葡萄球菌和白色念珠菌的抗菌性能抗细菌率和抗菌耐久性能抗细菌率(％)的检测结果虽然均不合格，但是检测结果的大肠杆菌、金黄色葡萄球菌和白色念珠菌的抗菌性能抗细菌率和抗菌耐久性能抗细菌率(％)均比对比例5的有较好的改善，说明氧化锌在碱性环境下对银原子被碱化具体明显的延缓作用，对所述复合金属胶体无机抗菌剂具有良好的稳定性的作用。
9、分析对比例7和8，与实施例1对比，对比例7和8的不同为：添加的抗菌活性的活性炭抗菌剂的含量比例不同，对比例7的为0.7％低于1％，对比例8的为3.5％超过了3％；对比例7的抗菌性能抗细菌率和抗菌耐久性能抗细菌率(％)的检测结果均为不合格；对比例8的抗菌性能抗细菌率和抗菌耐久性能抗细菌率(％)的检测结果均为合格，但与实施例3的对比改善有限，且实施例3的抗菌性能抗细菌率和抗菌耐久性能抗细菌率(％)的检测结果均非常优良，故此，所述复合金属胶体无机抗菌剂占无机人造石的总体质量的百分比设为1-3％较为合适。
10、分析对比例9，与实施例1对比，对比例9的不同在于：采用光照方式不同，只经过了2小时的紫外线照射后进行了抗菌性能抗细菌率的检测，对比例9的检测结果显示为不合格，但是都达到了80％的杀菌率，仍然具有明显的效果，说明纳米二氧化钛的光敏杀菌性能具有很好的效果。
综上所述，使用本发明所述的复合金属胶体无机抗菌剂制得的无机人造石，对大肠杆菌、金黄色葡萄球菌和白色念珠菌的抗菌效果均非常优良。
含有1-3％的所述复合金属胶体无机抗菌剂的无机人造石，抗菌性能和抗菌耐久性均能满足JC/T897－2014《抗菌陶瓷制品抗菌性能》标准的要求。
纳米二氧化钛在紫外线的照射下具有良好的杀菌作用，且对有机污染物的氧化分解具有催化作用，纳米二氧化钛还具有较好的吸附性能。非常适合日常需要用紫外线杀菌的工作环境，可以提供杀菌去污的效果，可以协助被吸附的抗菌物质提高广谱杀菌的有效率。
本发明所述的复合金属胶体无机抗菌剂，含有双重的吸附载体和多种的杀菌抗菌物质，具有良好的广谱杀菌效果，且不易流失，适合对抗菌杀菌要求标准高的场所使用，尤其是医疗和食品加工行业。
本发明提出了所述的复合金属胶体无机抗菌剂的制备方法，制得的含有双重载体结构和多种抗菌物质的无机抗菌剂，便于存储方便使用。
本发明使用所述的复合金属胶体无机抗菌剂的无机人造石，制得的无机人造石的抗菌性能和抗菌耐久性能均非常优良。
以上结合具体实施例描述了本发明的技术原理。这些描述只是为了解释本发明的原理，而不能以任何方式解释为对本发明保护范围的限制。基于此处的解释，本领域的技术人员不需要付出创造性的劳动即可联想到本发明的其它具体实施方式，这些方式都将落入本发明的保护范围之内。
Claims (10)
1.一种复合金属胶体无机抗菌剂，其特征在于，包括羟基磷酸锆微粉、银原子、铜原子和纳米二氧化钛；其中，所述纳米二氧化钛的表面微孔吸附有所述银原子和铜原子胶体，所述羟基磷酸锆微粉的表面吸附有银原子、铜原子和纳米二氧化钛胶体；所述银原子作为活化剂，所述铜原子作为待激活抗菌剂，所述纳米二氧化钛作为紫外杀菌体。
2.根据权利要求1所述的复合金属胶体无机抗菌剂，其特征在于，还包括氧化锌，所述氧化锌为稳定剂，所述氧化锌为吸附于羟基磷酸锆微粉的胶体，所述氧化锌用于延缓碱性环境下的氧化银被碱化，避免氧化银先转化为氢氧化银析出，而导致铜原子未能转化为铜离子。
3.根据权利要求2所述的复合金属胶体无机抗菌剂，其特征在于，吸附于所述羟基磷酸锆微粉和纳米二氧化钛吸附的铜原子、氧化锌和银原子的摩尔含量均依次降低。
4.根据权利要求2所述的复合金属胶体无机抗菌剂，其特征在于，所述羟基磷酸锆微粉吸附的所述铜原子、纳米二氧化钛、氧化锌和银原子的摩尔含量比为4:2:2:1。
5.根据权利要求1-4任一所述的复合金属胶体无机抗菌剂的制备方法，其特征在于，包括以下具体的步骤：
S1)往水中添加硝酸银、纳米二氧化钛、硝酸铜和氧化锌并搅拌混合均匀，制得银铜锌硝酸溶液；
S2)在银铜锌硝酸溶液中加入羟基磷酸锆钠微粉，用稀硝酸和稀氢氧化钠溶液调整pH值，水浴恒温并快速搅拌均匀，制得羟基磷酸锆微粉吸附溶液；
S3)将所述羟基磷酸锆微粉吸附溶液放入烘箱烘干，制得羟基磷酸锆微粉吸附干粉；
S4)将所述羟基磷酸锆微粉吸附干粉送入还原烧结炉加热，焙烧；
S5)往恒温的还原烧结炉加入一氧化碳，进行还原反应，制得羟基磷酸锆微粉吸附焙烧粉；
S6)将所述羟基磷酸锆微粉吸附焙烧粉过筛，即制得所述的复合金属胶体无机抗菌剂。
6.根据权利要求5所述的复合金属胶体无机抗菌剂的制备方法，其特征在于，在所述步骤S1中，所述银铜锌硝酸溶液含有的硝酸铜、纳米二氧化钛、氧化锌、硝酸银和水的混合摩尔比为＝2.5:1:1:0.5:20；在所述步骤S2中，所述银铜锌硝酸溶液与羟基磷酸锆微粉的摩尔比为1:4，水浴温度为50℃，pH值为3-4。
7.根据权利要求5所述的复合金属胶体无机抗菌剂的制备方法，其特征在于，在所述步骤3中，所述烘干的温度100-120℃；在所述步骤S4中，所述焙烧的温度500-600℃，焙烧时间为3-4小时。
8.根据权利要求5所述的复合金属胶体无机抗菌剂的制备方法，其特征在于，在所述步骤S5中，加入所述一氧化碳的压力为0.1-0.15MPa，所述还原反应的时间为0.8-1小时；在所述步骤S6中，所述过筛的筛网的孔径为400目。
9.一种无机人造石，其特征在于，原料包括抗菌粘结液，所述抗菌粘结液的原料成分包括权利要求1-4中任一项的所述的复合金属胶体无机抗菌剂，所述抗菌粘结液用于无机人造石的固态原料的粘结，所述抗菌粘结液均匀的分布于所述无机人造石中。
10.根据权利要求9所述的无机人造石，其特征在于，所述复合金属胶体无机抗菌剂占无机人造石的总体质量的百分比为1-3％；所述抗菌粘结液的原料成分还包括水，所述抗菌粘结液为加入于无机人造石之前的预配制混合液。