CN111113284A - 一种高散热型刚玉树脂切割砂轮 - Google Patents
一种高散热型刚玉树脂切割砂轮 Download PDFInfo
- Publication number
- CN111113284A CN111113284A CN201911286633.2A CN201911286633A CN111113284A CN 111113284 A CN111113284 A CN 111113284A CN 201911286633 A CN201911286633 A CN 201911286633A CN 111113284 A CN111113284 A CN 111113284A
- Authority
- CN
- China
- Prior art keywords
- parts
- corundum
- heat dissipation
- high heat
- abrasive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种高散热型刚玉树脂切割砂轮，由以下原料构成：棕刚玉磨料、氧化硅、黑锰矿石、铬刚玉磨料、碳化硼、过氧化甲乙酮、石墨粉、石英粉、松香、酚醛树脂、玻璃纤维、硼砂、硅藻土，与现有技术相比，本发明具有如下的有益效果：制成的砂轮硬度高，使用寿命长，能够适应砂轮使用时的高温环境，质量可靠，防爆性能好。
Description
技术领域
本发明是一种高散热型刚玉树脂切割砂轮，属于砂轮技术领域。
背景技术
砂轮是磨削加工中最主要的一类磨具。砂轮是在磨料中加入结合剂，经压坯、干燥和焙烧而制成的多孔体。由于磨料、结合剂及制造工艺不同，砂轮的特性差别很大，因此对磨削的加工质量、生产率和经济性有着重要影响。砂轮的特性主要是由磨料、粒度、结合剂、硬度、组织、形状和尺寸等因素决定。
现有的砂轮在高速运转过程中，易对结构造成一定的不稳定性，长时间的使用，造成温度升高，影响内部结构稳定，降低安全性，减少使用寿命。
发明内容
针对现有技术存在的不足，本发明目的是提供一种高散热型刚玉树脂切割砂轮，以解决上述背景技术中提出的问题。
为了实现上述目的，本发明是通过如下的技术方案来实现：一种高散热型刚玉树脂切割砂轮，由以下原料构成：棕刚玉磨料、氧化硅、黑锰矿石、铬刚玉磨料、碳化硼、过氧化甲乙酮、石墨粉、石英粉、松香、酚醛树脂、玻璃纤维、硼砂、硅藻土。
进一步地，由以下重量份原料构成：棕刚玉磨料30-50重量份、氧化硅8-10重量份、黑锰矿石3-5重量份、铬刚玉磨料2-4重量份、碳化硼5-8重量份、过氧化甲乙酮10-12重量份、石墨粉3-6重量份、石英粉2-4重量份、松香3-6重量份、酚醛树脂40-60重量份、玻璃纤维2-5重量份、硼砂3-7重量份、硅藻土2-5重量份。
进一步地，所述硅藻土中含有蛋白石，并含有粘土、炭质、褐铁矿、赤铁矿、黄铁矿、碳酸盐矿物、石英、白云母、海绿石以及长石。
进一步地，将预处理后的硼镁矿粉与氢氧化钠溶液混合，加温加压分解得偏硼酸钠溶液，再经碳化处理，得到原料中的硼砂。
进一步地，通过电炉中焦炭和氧化硼反应得到原理中的碳化硼。
进一步地，由以下重量份原料构成：棕刚玉磨料50重量份、氧化硅8重量份、黑锰矿石5重量份、铬刚玉磨料2重量份、碳化硼8重量份、过氧化甲乙酮12重量份、石墨粉6重量份、石英粉2重量份、松香6重量份、酚醛树脂40重量份、玻璃纤维5重量份、硼砂3重量份、硅藻土5重量份。
进一步地，由以下重量份原料构成：棕刚玉磨料50重量份、氧化硅10重量份、黑锰矿石5重量份、铬刚玉磨料4重量份、碳化硼8重量份、过氧化甲乙酮12重量份、石墨粉3重量份、石英粉4重量份、松香6重量份、酚醛树脂60重量份、玻璃纤维5重量份、硼砂7重量份、硅藻土5重量份。
本发明的有益效果：本发明的一种高散热型刚玉树脂切割砂轮，制成的砂轮硬度高，使用寿命长，能够适应砂轮使用时的高温环境，质量可靠，防爆性能好。
具体实施方式
为使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施方式，进一步阐述本发明。
本发明提供一种技术方案：一种高散热型刚玉树脂切割砂轮，由以下原料构成：棕刚玉磨料、氧化硅、黑锰矿石、铬刚玉磨料、碳化硼、过氧化甲乙酮、石墨粉、石英粉、松香、酚醛树脂、玻璃纤维、硼砂、硅藻土。
作为本发明的一个实施例：由以下重量份原料构成：棕刚玉磨料30-50重量份、氧化硅8-10重量份、黑锰矿石3-5重量份、铬刚玉磨料2-4重量份、碳化硼5-8重量份、过氧化甲乙酮10-12重量份、石墨粉3-6重量份、石英粉2-4重量份、松香3-6重量份、酚醛树脂40-60重量份、玻璃纤维2-5重量份、硼砂3-7重量份、硅藻土2-5重量份。
硅藻土中含有蛋白石，并含有粘土、炭质、褐铁矿、赤铁矿、黄铁矿、碳酸盐矿物、石英、白云母、海绿石以及长石。
将预处理后的硼镁矿粉与氢氧化钠溶液混合，加温加压分解得偏硼酸钠溶液，再经碳化处理，得到原料中的硼砂。
通过电炉中焦炭和氧化硼反应得到原理中的碳化硼。
作为本发明的一个实施例：由以下重量份原料构成：棕刚玉磨料50重量份、氧化硅8重量份、黑锰矿石5重量份、铬刚玉磨料2重量份、碳化硼8重量份、过氧化甲乙酮12重量份、石墨粉6重量份、石英粉2重量份、松香6重量份、酚醛树脂40重量份、玻璃纤维5重量份、硼砂3重量份、硅藻土5重量份。
作为本发明的一个实施例：由以下重量份原料构成：棕刚玉磨料50重量份、氧化硅10重量份、黑锰矿石5重量份、铬刚玉磨料4重量份、碳化硼8重量份、过氧化甲乙酮12重量份、石墨粉3重量份、石英粉4重量份、松香6重量份、酚醛树脂60重量份、玻璃纤维5重量份、硼砂7重量份、硅藻土5重量份。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点,对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。
此外，应当理解，虽然本说明书按照实施方式加以描述，但并非每个实施方式仅包含一个独立的技术方案，说明书的这种叙述方式仅仅是为清楚起见，本领域技术人员应当将说明书作为一个整体，各实施例中的技术方案也可以经适当组合，形成本领域技术人员可以理解的其他实施方式。
Claims (7)
1.一种高散热型刚玉树脂切割砂轮，其特征在于：由以下原料构成：棕刚玉磨料、氧化硅、黑锰矿石、铬刚玉磨料、碳化硼、过氧化甲乙酮、石墨粉、石英粉、松香、酚醛树脂、玻璃纤维、硼砂、硅藻土。
2.根据权利要求1所述的一种高散热型刚玉树脂切割砂轮，其特征在于：由以下重量份原料构成：棕刚玉磨料30-50重量份、氧化硅8-10重量份、黑锰矿石3-5重量份、铬刚玉磨料2-4重量份、碳化硼5-8重量份、过氧化甲乙酮10-12重量份、石墨粉3-6重量份、石英粉2-4重量份、松香3-6重量份、酚醛树脂40-60重量份、玻璃纤维2-5重量份、硼砂3-7重量份、硅藻土2-5重量份。
3.根据权利要求1所述的一种高散热型刚玉树脂切割砂轮，其特征在于：所述硅藻土中含有蛋白石，并含有粘土、炭质、褐铁矿、赤铁矿、黄铁矿、碳酸盐矿物、石英、白云母、海绿石以及长石。
4.根据权利要求1所述的一种高散热型刚玉树脂切割砂轮，其特征在于：将预处理后的硼镁矿粉与氢氧化钠溶液混合，加温加压分解得偏硼酸钠溶液，再经碳化处理，得到原料中的硼砂。
5.根据权利要求1所述的一种高散热型刚玉树脂切割砂轮，其特征在于：通过电炉中焦炭和氧化硼反应得到原理中的碳化硼。
6.根据权利要求1所述的一种高散热型刚玉树脂切割砂轮，其特征在于：由以下重量份原料构成：棕刚玉磨料50重量份、氧化硅8重量份、黑锰矿石5重量份、铬刚玉磨料2重量份、碳化硼8重量份、过氧化甲乙酮12重量份、石墨粉6重量份、石英粉2重量份、松香6重量份、酚醛树脂40重量份、玻璃纤维5重量份、硼砂3重量份、硅藻土5重量份。
7.根据权利要求1所述的一种高散热型刚玉树脂切割砂轮，其特征在于：由以下重量份原料构成：棕刚玉磨料50重量份、氧化硅10重量份、黑锰矿石5重量份、铬刚玉磨料4重量份、碳化硼8重量份、过氧化甲乙酮12重量份、石墨粉3重量份、石英粉4重量份、松香6重量份、酚醛树脂60重量份、玻璃纤维5重量份、硼砂7重量份、硅藻土5重量份。