CN1110703A - Rust-removing, rust-proof priming paint - Google Patents
Rust-removing, rust-proof priming paint Download PDFInfo
- Publication number
- CN1110703A CN1110703A CN 94107354 CN94107354A CN1110703A CN 1110703 A CN1110703 A CN 1110703A CN 94107354 CN94107354 CN 94107354 CN 94107354 A CN94107354 A CN 94107354A CN 1110703 A CN1110703 A CN 1110703A
- Authority
- CN
- China
- Prior art keywords
- rust
- parts
- zinc
- sodium
- chromic acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The rust-preventing and -removing priming paint features advanced productive technology, scientific and reasonable formula and good physical and emchanical performance, anti-rust power and durability.
Description
Rust-removing, rust of the present invention belongs to the novel material in chemical industry paint field.
That traditional paint generally has is poisonous, flavor is arranged, shortcoming such as inflammable, and environmental pollution is serious in the use, can have a strong impact on workman's physical and mental health, and complex process, and labor strength is big, uses dangerously, easily blasts and fire failure.
Rust-removing, rust of the present invention has overcome the shortcoming that traditional paint exists, and has solved the first three items of being known as in the world in the paint four problems (promptly water-soluble, nontoxic, do not burn, can recycle).
Rust-removing, rust of the present invention adopts advanced production technique, and scientific and reasonable prescription makes product have good physical and mechanical properties, rust-preventing characteristic and weather resistance.Rust-removing, rust of the present invention is grouped into by following one-tenth:
The composition parts by weight
Benzene emulsion 250～280
Sodium hexametaphosphate 99 33～47
Iron oxide red 95～115
Zinc-chrome yellow 37～48
Zinc phosphate 12～25
Talcum powder 48～70
Chromic acid II benzene guanidine 3～7
(trade name: chromic acid D)
Organic pottery clay 7～15
Ammoniacal liquor 3～7
Sodium polyacrylate 8～15
(trade name: dispersion agent-E)
Acrylate copolymer emulsion 14～25
(trade name: thickening material-JA)
Sodium Nitrite 1
The N-(2-benzimidazolyl-)-Urethylane 1～4
(trade name: derosal)
Tributyl phosphate 17～28
Propylene glycol 6～14
Pyranton 3～8
Water 150～180
Rust-removing, rust optimal components of the present invention is as follows:
The composition parts by weight
Benzene emulsion 260～270
Sodium hexametaphosphate 99 35～40
Iron oxide red 100～108
Zinc-chrome yellow 39～45
Zinc phosphate 16～20
Talcum powder 51～62
Chromic acid II benzene guanidine 4～6
(trade name: chromic acid D)
Organic pottery clay 8～12
Ammoniacal liquor 4～6
Sodium polyacrylate 11～15
(trade name: dispersion agent-E)
Acrylate copolymer emulsion 17～22
(trade name: thickening material-JA)
Sodium Nitrite 1
The N-(2-benzimidazolyl-)-Urethylane 1～3
(trade name: derosal)
Tributyl phosphate 19～25
Propylene glycol 8～12
Pyranton 5～8
Water 165～175
Under its technical process of rust-removing, rust of the present invention:
1, earlier water is added in the material-compound tank, add Sodium hexametaphosphate 99, sodium polyacrylate, acrylate copolymer emulsion, Sodium Nitrite, N-(2-benzimidazolyl-then successively)-Urethylane, tributyl phosphate (10), chromic acid II benzene guanidine, organic pottery clay, iron oxide red, zinc-chrome yellow, zinc phosphate, talcum powder, stir after 30 minutes, enter sand mill and grind, when fineness reaches regulation (below the 60 μ m), squeeze in the paint mixing tank by sieve bar pump.
2, ammoniacal liquor is added in the benzene emulsion, inject material-compound tank, add tributyl phosphate (12), propylene glycol, Pyranton again, after being uniformly dispersed, squeeze in the paint mixing tank by sieve bar pump.
3, in paint mixing tank, two kinds of slurries are stirred, i.e. final product.
Rust-removing, rust of the present invention is medium with water, so nontoxic, tasteless, pollution-free, do not burn.And easy-to-operate, easy cleanings such as brushing instrument.Test of many times shows, rust-removing, rust strong adhesion of the present invention, and drawing the circle method is secondary; Shock strength is 50 kilograms centimetres; Salt water resistance performance excellence, immerse in 3% the salt solution 7 days non-foaming, do not come off, non-corrosive, high temperature resistant, under 150 ℃ of high temperature 8 hours non-foaming, do not come off.The present invention is at improper ventilation or have the place construction of naked light more to demonstrate its unique advantages.Its invention reduces labor strength, preserves the ecological environment reducing China's steel corrosion, and aspects such as safety in production will produce huge economic benefit and social benefit.
Specify the present invention below by embodiment.
Embodiment 1
Earlier water is added in the material-compound tank for 175 parts, add 9 parts of 35 parts of dispersion agents of Sodium hexametaphosphate 99 then successively, 15 parts of thickening materials, 1 part of Sodium Nitrite, 1 part of derosal, 6 parts of tributyl phosphates, chromic acid D4 part, 8 parts of organic pottery clays, 97 parts of iron oxide reds, 40 parts of zinc-chrome yellows, 14 parts of zinc phosphates, 50 parts of talcum powder, stir after 30 minutes, enter sand mill and grind,, squeeze in the paint mixing tank by sieve bar pump when fineness reaches 60 μ m when following.
In 255 parts of 4 parts of addings of ammoniacal liquor benzene emulsions, inject material-compound tank, add 13 parts of tributyl phosphates again, 7 parts of propylene glycol, 4 parts of Pyrantons after being uniformly dispersed, are squeezed in the paint mixing tank by sieve bar pump.
In paint mixing tank, two kinds of slurries are stirred, promptly get final product, its composition is as follows:
The composition parts by weight
Benzene emulsion 255
Sodium hexametaphosphate 99 35
Iron oxide red 97
Zinc-chrome yellow 40
Zinc phosphate 14
Talcum powder 50
Chromic acid D 4
Organic pottery clay 8
Ammoniacal liquor 4
Dispersion agent-E 9
Thickening material-JA 15
Sodium Nitrite 1
Derosal 1
Tributyl phosphate 19
Propylene glycol 7
Pyranton 4
Water 175
Its performance is: sticking power (draw circle method) is secondary, 50 kilograms centimetres of shock strengths, and resistance to salt water 170 hours is non-foaming, do not come off, non-corrosive, viscosity are 46 seconds, and solids content is 50%.
Embodiment 2
Earlier water is added in the material-compound tank for 155 parts, add 45 parts of Sodium hexametaphosphate 99s then successively, 14 parts of dispersion agents, 23 parts of thickening materials, 1 part of Sodium Nitrite, 3 parts of derosal, 9 parts of tributyl phosphates, chromic acid D6 part, 14 parts of organic pottery clays, 113 parts of iron oxide reds, 46 parts of zinc-chrome yellows, 24 parts of zinc phosphates, 68 parts of talcum powder stirred after 30 minutes, entered sand mill and ground, when fineness reaches 60 μ m when following, squeeze in the paint mixing tank by sieve bar pump.
In 275 parts of 6 parts of addings of ammoniacal liquor benzene emulsions, inject material-compound tank, add 18 parts of tributyl phosphates again, 13 parts of propylene glycol, 7 parts of Pyrantons after being uniformly dispersed, are squeezed in the paint mixing tank by sieve bar pump.
In paint mixing tank, two kinds of slurries are stirred, promptly obtain final product.The following composition parts by weight of its composition
Benzene emulsion 275
Sodium hexametaphosphate 99 45
Iron oxide red 113
Zinc-chrome yellow 46
Zinc phosphate 24
Talcum powder 68
Chromic acid D 6
Organic pottery clay 14
Ammoniacal liquor 6
Dispersion agent-E 14
Thickening material-JA 23
Sodium Nitrite 1
Derosal 3
Tributyl phosphate 27
Propylene glycol 13
Pyranton 7
Water 155
Its performance is: sticking power (draw circle method) is secondary, and shock strength is 50 kilograms centimetres, resistance to salt water 192 hours, non-foaming, do not come off, non-corrosive, viscosity is 53 seconds, solids content is 58%.
Embodiment 3
Earlier water is added in the material-compound tank for 165 parts, add 37 parts of Sodium hexametaphosphate 99s then successively, 13 parts of dispersion agents, 19 parts of thickening materials, 1 part of Sodium Nitrite, 2 parts of derosal, 7 parts of tributyl phosphates, chromic acid D5 part, 10 parts of organic pottery clays, 103 parts of iron oxide reds, 42 parts of zinc-chrome yellows, 18 parts of zinc phosphates, 55 parts of talcum powder stirred after 30 minutes, entered sand mill and ground, when fineness reaches requirement 60 μ m when following, squeeze in the paint mixing tank by sieve bar pump.
In 265 parts of 5 parts of addings of ammoniacal liquor benzene emulsions, inject material-compound tank, add 13 parts of tributyl phosphates again, 10 parts of propylene glycol, 6 parts of Pyrantons after being uniformly dispersed, are squeezed in the paint mixing tank by sieve bar pump.
In paint mixing tank, two kinds of slurries are stirred, promptly get final product.
Its composition is as follows:
The composition parts by weight
Benzene emulsion 265
Sodium hexametaphosphate 99 37
Iron oxide red 103
Zinc-chrome yellow 42
Zinc phosphate 18
Talcum powder 55
Chromic acid D 5
Organic pottery clay 10
Ammoniacal liquor 5
Dispersion agent-E 13
Thickening material-JA 19
Sodium Nitrite 1
Derosal 2
Tributyl phosphate 20
Propylene glycol 10
Pyranton 6
Water 165
Its performance is: sticking power (draw circle method) is secondary, 50 kilograms centimetres of shock strengths, resistance to salt water 185 hours, non-foaming, do not come off, non-corrosive, viscosity is 48 seconds, solids content is 53%.
Claims (2)
1, a kind of rust-removing, rust is characterized in that being grouped into by following one-tenth:
The composition parts by weight
Benzene emulsion 250～280,
Sodium hexametaphosphate 99 33～47,
Iron oxide red 95～115,
Zinc-chrome yellow 37～48,
Zinc phosphate 12～25,
Talcum powder 48～70,
Chromic acid II benzene guanidine 3～7,
Organic pottery clay 7～15,
Ammoniacal liquor 3～7,
Sodium polyacrylate 8～15,
Acrylate copolymer emulsion 14～25,
Sodium Nitrite 1,
N-(2-benzimidazolyl-)-Urethylane 1～4,
Tributyl phosphate 17～28,
Propylene glycol 6～14,
Pyranton 3～8,
Water 150～180.
2, the described rust-removing, rust of a kind of claim 1 is characterized in that optimal components is composed as follows:
The composition parts by weight
Benzene emulsion 260～270,
Sodium hexametaphosphate 99 35～40,
Iron oxide red 100～108,
Zinc-chrome yellow 39～45,
Zinc phosphate 16～20,
Talcum powder 51～62,
Chromic acid II benzene guanidine 4～6,
Organic pottery clay 8～12,
Ammoniacal liquor 4～6,
Sodium polyacrylate 11～15,
Acrylate copolymer emulsion 17～22,
Sodium Nitrite 1,
The N-(2-benzimidazolyl-)-Urethylane 1～3,
Tributyl phosphate 19～25,
Propylene glycol 8～12,
Pyranton 5～8,
Water 165～175.