CN110343468A - It is a kind of for steel plate and the aqueous quick-drying weldable shop iron oxide red primer of fashioned iron - Google Patents
It is a kind of for steel plate and the aqueous quick-drying weldable shop iron oxide red primer of fashioned iron Download PDFInfo
- Publication number
- CN110343468A CN110343468A CN201910683540.7A CN201910683540A CN110343468A CN 110343468 A CN110343468 A CN 110343468A CN 201910683540 A CN201910683540 A CN 201910683540A CN 110343468 A CN110343468 A CN 110343468A
- Authority
- CN
- China
- Prior art keywords
- iron oxide
- oxide red
- drying
- aqueous
- quick
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention provides a kind of for steel plate and the aqueous quick-drying weldable shop iron oxide red primer of fashioned iron, the following ingredient based on mass number: aqueous alkide resin 5-10wt%, deionized water 23-30wt%, dispersing agent 0.1-1wt%, dissipating infusion 0.1-0.3wt%, iron oxide red 10-20wt%, barium sulfate 15-30wt%, water-base resin 15-30wt%, anti-flash rusting agent 0.3-1wt%, levelling agent 0.1-0.8wt%, thickener 0.2-0.8wt%；Preparation method is as follows, including disperses, grinding, paint detection, filters and packages；It is described it is pre-dispersed include by aqueous alkide resin 5-10wt%, deionized water 23-30wt%, dispersing agent 0.1-1wt%, dissipate infusion 0.1-0.3wt%, iron oxide red 10-20wt%, barium sulfate 15-30wt% mix and uniform stirring；After being handled by dispersion mixing, temperature is reduced to 40 DEG C, then carries out sand milling process again, after toning by fineness control within 25um；Obtained slurry is filtered with 100 mesh stainless steel filtering nets to get aqueous quick-drying weldable shop iron oxide red primer component is arrived.The aqueous quick-drying weldable shop iron oxide red primer that in the present invention, the fast drying of bottoming, protective value are good, adhesive force is strong, good mechanical property, filling capacity is strong, matching performance is good.
Description
Technical field
The invention belongs to iron oxide red primer technical field more particularly to a kind of aqueous quick-drying solderabilities for steel plate and fashioned iron
Precoat iron oxide red primer.
Background technique
Currently, in engineering machinery and anticorrosive paint product, due to by construction environment, workpiece surface processing, product
The preservative treatment that the influence of the reasons such as use environment, engineering machinery and heavy antisepsis field use mainly still uses antirust paint to material
Material carries out the processing of surface anticorrosion with painting, although antirust paint in the prior art can protect metal surface from the chemistry of atmosphere etc.
Or electrochemical corrosion, but there are still the following shortcomings, first, drying time is long, after being sprayed on metal surface, surface drying wants 3 hours, real
Dry to want 24 hours or more, second, antiseptic property is not comprehensive, most of antirust paint plays not strong acid, highly basic, seawater, salt fog etc.
To antisepsis, when being especially used in hull bottom, poor water resistance does not have etch-proof effect in the seawater, in order to increase anti-corrosion
Effect, existing relatively large engineering machinery and heavy antisepsis field can first coat one layer of high anti-corrosion primer, existing high anti-corrosion mostly
Priming paint is mostly based on common epoxy primer, though adhesive force of the epoxy systems in all coating systems is preferable, oil,
Under contaminated environment, adhesive force can have a greatly reduced quality, to eventually lead to pull-away, be locally corroded, seriously affect large size
It is mechanical using safe.Therefore, inventing a kind of aqueous quick-drying weldable shop iron oxide red primer for steel plate and fashioned iron seems non-
It is often necessary.
Summary of the invention
In order to solve the above technical problem, the present invention provides a kind of for steel plate and the aqueous quick-drying weldable shop of fashioned iron
Iron oxide red primer, to solve the problems, such as that existing iron oxide red primer quick-drying is poor.
It is a kind of for steel plate and the aqueous quick-drying weldable shop iron oxide red primer of fashioned iron, the following ingredient based on mass number:
Aqueous alkide resin 5-10wt%, deionized water 23-30wt%, dispersing agent 0.1-1wt%, infusion 0.1-0.3wt%, iron oxide red 10- are dissipated
20wt%, barium sulfate 15-30wt%, water-base resin 15-30wt%, anti-flash rusting agent 0.3-1wt%, levelling agent 0.1-0.8wt%, thickening
Agent 0.2-0.8wt%；Preparation method is as follows, including disperses, grinding, paint detection, filters and packages；It is described it is pre-dispersed include by water
Property alkyd resin 5-10wt%, deionized water 23-30wt%, dispersing agent 0.1-1wt%, dissipate infusion 0.1-0.3wt%, iron oxide red 10-
20wt%, barium sulfate 15-30wt% mix and uniform stirring；After handling by dispersion mixing, temperature is reduced to 40 DEG C,
Then sand milling process is carried out again, after toning by fineness control within 25um；System is filtered with 100 mesh stainless steel filtering nets
Slurry is obtained to get aqueous quick-drying weldable shop iron oxide red primer component is arrived.
Preferably, when use that the removing surface of metalwork is clean, remove the greasy dirt and floating rust on surface, and painting property quick-drying
Weldable shop iron oxide red primer.
Compared with prior art, the invention has the benefit that in the present invention, the fast drying of bottoming, protective value be good,
The aqueous quick-drying weldable shop iron oxide red primer that adhesive force is strong, good mechanical property, filling capacity is strong, matching performance is good.
Specific embodiment
It is described further below in conjunction with the present invention:
It is a kind of for steel plate and the aqueous quick-drying weldable shop iron oxide red primer of fashioned iron, the following ingredient based on mass number: aqueous
Alkyd resin 5-10wt%, deionized water 23-30wt%, dispersing agent 0.1-1wt%, infusion 0.1-0.3wt%, iron oxide red 10- are dissipated
20wt%, barium sulfate 15-30wt%, water-base resin 15-30wt%, anti-flash rusting agent 0.3-1wt%, levelling agent 0.1-0.8wt%, thickening
Agent 0.2-0.8wt%；Preparation method is as follows, including disperses, grinding, paint detection, filters and packages；It is described it is pre-dispersed include by water
Property alkyd resin 5-10wt%, deionized water 23-30wt%, dispersing agent 0.1-1wt%, dissipate infusion 0.1-0.3wt%, iron oxide red 10-
20wt%, barium sulfate 15-30wt% mix and uniform stirring；After handling by dispersion mixing, temperature is reduced to 40 DEG C,
Then sand milling process is carried out again, after toning by fineness control within 25um；System is filtered with 100 mesh stainless steel filtering nets
Slurry is obtained to get aqueous quick-drying weldable shop iron oxide red primer component is arrived.
Preferably, when use that the removing surface of metalwork is clean, remove the greasy dirt and floating rust on surface, and painting property quick-drying
Weldable shop iron oxide red primer.
Embodiment 1:
The present invention provide it is a kind of for steel plate and the aqueous quick-drying weldable shop iron oxide red primer of fashioned iron, based on quality wt% number
Following ingredient: aqueous alkide resin 8wt%, deionized water 25wt%, dispersing agent 0.6wt%, dissipate infusion 0.2wt%, iron oxide red 15wt%,
Barium sulfate 25wt%, water-base resin 25wt%, anti-flash rusting agent 0.5wt%, levelling agent 0.2wt%, thickener 0.5wt%；Preparation method is such as
Under, including disperse, grinding, paint detection, filter and package；It is described it is pre-dispersed include by aqueous alkide resin 5-10wt%, go from
Sub- water 23-30wt%, dispersing agent 0.1-1wt%, infusion 0.1-0.3wt%, iron oxide red 10-20wt%, barium sulfate 15-30wt% progress are dissipated
Mix simultaneously uniform stirring；After being handled by dispersion mixing, temperature is reduced to 40 DEG C, then carries out sand milling process again,
After toning by fineness control within 25um；With 100 mesh stainless steel filtering nets be filtered obtained slurry to get to aqueous quick-drying can
Weldering property precoating iron oxide red primer component.
Through testing:
Fineness :≤25 μm
Viscosity: 70-75KU
Drying time: standard thickness single coating, 25 DEG C,
Surface drying≤0.5h does solid work≤8h,
Hardness: >=0.4
Adhesive force :≤2(cross-hatching, grade)
Grinability: good
Nitrocellulose lacquer resistance: it has not stung, not bleeding
Resistance to salt water: 48 hours not blistering, does not fall off, wrinkle resistant, good with the matching performance of other assorted finishing coats.
Using technical solutions according to the invention or those skilled in the art under the inspiration of technical solution of the present invention,
Similar technical solution is designed, and reaches above-mentioned technical effect, is to fall into protection scope of the present invention.
Claims (2)
1. a kind of for steel plate and the aqueous quick-drying weldable shop iron oxide red primer of fashioned iron, which is characterized in that based on mass number
Following ingredient: aqueous alkide resin 5-10wt%, deionized water 23-30wt%, dispersing agent 0.1-1wt%, infusion 0.1- is dissipated
0.3wt%, iron oxide red 10-20wt%, barium sulfate 15-30wt%, water-base resin 15-30wt%, anti-flash rusting agent 0.3-1wt%, levelling agent
0.1-0.8wt%, thickener 0.2-0.8wt%；Preparation method is as follows, including disperses, grinding, paint detection, filters and packages；Institute
Stating pre-dispersed includes by aqueous alkide resin 5-10wt%, deionized water 23-30wt%, dispersing agent 0.1-1wt%, scattered infusion 0.1-
0.3wt%, iron oxide red 10-20wt%, barium sulfate 15-30wt% mix and uniform stirring；After being handled by dispersion mixing,
Temperature is reduced to 40 DEG C, then carries out sand milling process again, after toning by fineness control within 25um；It is stainless with 100 mesh
Steel strainer is filtered obtained slurry to get aqueous quick-drying weldable shop iron oxide red primer component is arrived.
2. it is according to claim 1 a kind of for steel plate and the aqueous quick-drying weldable shop iron oxide red primer of fashioned iron, it is special
Sign is, when use is clean by the removing surface of metalwork, removes the greasy dirt and floating rust on surface, and painting property quick-drying solderability is pre-
Apply iron oxide red primer.