CN110280457A - A kind of string and its preparation process of resist chemical - Google Patents
A kind of string and its preparation process of resist chemical Download PDFInfo
- Publication number
- CN110280457A CN110280457A CN201910510869.3A CN201910510869A CN110280457A CN 110280457 A CN110280457 A CN 110280457A CN 201910510869 A CN201910510869 A CN 201910510869A CN 110280457 A CN110280457 A CN 110280457A
- Authority
- CN
- China
- Prior art keywords
- steel wire
- string
- resist chemical
- quenching
- wire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to string manufacturing technology fields, especially a kind of string of resist chemical, including string ontology and the resist chemical layer that string body surface is arranged in, the string ontology is by core of carbon structure steel wire and uses copper wire, welding wire or alloy wire to wind crust.And its preparation process comprising steps of S1, by carbon structure steel wire heating, quenching；S2, auxiliary agent is added in the quenching steel wire Jing Guo surface preparation；S3, quenching steel wire taking-up progress redraing, simultaneously cold quenching is spare；The preparation of S4, resist chemical layer solution.S5, cleaning coating.S6, winding air-dry；S7, secondary coating.The present invention applies the coating operation of secondary chemical attack layer by carrying out primary coating operation in carbon structure steel wire and crust again, so that the resist chemical layer of the string of resist chemical is divided into multilayer, increases the ability of its resist chemical.
Description
Technical field
The present invention relates to string manufacturing technology field more particularly to the strings and its preparation process of a kind of resist chemical.
Background technique
Chinese musical instruments manufacturing has basically formed more complete industrial production system, can process the world substantially
Upper all big kind musical instruments, covering extensive fields, kind is numerous, the about a type of piano, violin, western wind instrument etc. more than different classes of 1200
Number, specification more than 30,000, the big kind musical instrument such as piano.Its product has formed Virtual production pattern, and piano iron plate, is hit soundboard
The main piano component profession processing factory such as string machine, shell initially forms scale, and existing string is anti-chemical rotten most without resisting greatly
The sweat of the ability of erosion, especially human hand if things go on like this causes the corrosion attack of string, and seriously affected string uses the longevity
Life and tone color, thus it is proposed that the string and its preparation process of a kind of resist chemical.
Summary of the invention
The purpose of the present invention is to solve existing string exists in the prior art greatly most without anti-resist chemical
Ability, the especially sweat of human hand if things go on like this causes the corrosion attack of string, seriously affected the service life of string
And the shortcomings that tone color, and the string and its preparation process of a kind of resist chemical proposed.
To achieve the goals above, present invention employs following technical solutions:
Including string ontology and the anti-of string body surface is arranged in the string and its preparation process for designing a kind of resist chemical
Chemical attack layer, the resist chemical layer include that mass ratio is 1: 0.5: 2: 1.5: 10 titanium nitride TiN, titanium carbide TiC, carbon nitrogen
Change titanium TiCN, aluminium nitride AlN and nano coating CrAlN/ZrO2, the resist chemical layer to pass through by physical vapour deposition (PVD)
(PVD) or chemical vapor deposition (CVD) method between 250-400 DEG C temperature preparation, and be coated in the string ontology
Outside, the string ontology by core of carbon structure steel wire and use copper wire, welding wire or alloy wire for wind crust.
Preferably, the core section of the carbon structure steel wire of the string ontology is regular hexagon.
Preferably, the carbon content of the carbon structure steel wire is 0.6-0.8%.
Preferably, the preparation process of the string of a kind of resist chemical, comprising the following specific steps
S1, by carbon structure steel wire by by the steel wire of a drawing, surface preparation obtains Soxhlet again after heating, quenching
The quenching steel wire of body；
S2, quenching steel wire Jing Guo surface preparation is sent into smelting furnace and is heated, heating temperature is 700-850 DEG C, during which to quenching
Fiery steel wire surface sprinkles auxiliary agent, and the auxiliary agent includes 25 parts of nylon fiber and 25 parts of titanium dioxide in parts by weight；
S3, quenching steel wire is taken out into progress redraing, it is spare places into progress cold quenching in 2-9 DEG C of deionized water.
S4, by physical vapour deposition (PVD) (PVD) or chemical vapor deposition (CVD) method by mass ratio it is 1: 0.5: 2:
1.5: 10 titanium nitride TiN, titanium carbide TiC, titanium carbonitride TiCN, aluminium nitride AlN and nano coating CrAlN/ZrO2 are in 250-400
Temperature between DEG C is prepared into resist chemical layer solution.
S5, material is put into for the carbon structure steel wire after the winding crust and cold quenching of copper wire, welding wire or alloy wire
Cleaning in supersonic wave cleaning machine, takes out hot blast drying, and resist chemical layer solution obtained in S4 is coated uniformly on winding
The outside of crust and carbon structure steel wire.
S6, the winding crust for being coated with resist chemical layer are wrapped in the structural carbon steel coated with resist chemical layer
Silk outside, and it is placed again into cleaning in supersonic wave cleaning machine, take out hot blast drying.
S7, the carbon structure steel wire that outside obtained in S6 is wound with winding crust is subjected to secondary resist chemical layer
Operation is coated, finished product is obtained.
The string and its preparation process of a kind of resist chemical proposed by the present invention, beneficial effect are: by carbon
The outer application resist chemical layer of structure steel wire simultaneously winds the crust for being also coated with resist chemical layer, while applying again
The coating operation of secondary chemical attack layer makes the resist chemical layer of the string of resist chemical be divided into multilayer, increases it
The ability of resist chemical.
Specific embodiment
The following is a clear and complete description of the technical scheme in the embodiments of the invention, it is clear that described embodiment
Only a part of the embodiment of the present invention, instead of all the embodiments.
Including string ontology and the anti-of string body surface is arranged in a kind of string and its preparation process of resist chemical
Chemical attack layer, the resist chemical layer include that mass ratio is 1: 0.5: 2: 1.5: 10 titanium nitride TiN, titanium carbide TiC, carbon nitrogen
Change titanium TiCN, aluminium nitride AlN and nano coating CrAlN/ZrO2, the resist chemical layer to pass through by physical vapour deposition (PVD)
(PVD) or chemical vapor deposition (CVD) method between 250-400 DEG C temperature preparation, and be coated in the string ontology
Outside, the string ontology by core of carbon structure steel wire and use copper wire, welding wire or alloy wire for wind crust,
The carbon content of the carbon structure steel wire is 0.6-0.8%, and the core section of the carbon structure steel wire of the string ontology is positive
Hexagon.
A kind of preparation process of the string of resist chemical, comprising the following specific steps
S1, by carbon structure steel wire by by the steel wire of a drawing, surface preparation obtains Soxhlet again after heating, quenching
The quenching steel wire of body；
S2, quenching steel wire Jing Guo surface preparation is sent into smelting furnace and is heated, heating temperature is 700-850 DEG C, during which to quenching
Fiery steel wire surface sprinkles auxiliary agent, and the auxiliary agent includes 25 parts of nylon fiber and 25 parts of titanium dioxide in parts by weight；
S3, quenching steel wire is taken out into progress redraing, it is spare places into progress cold quenching in 2-9 DEG C of deionized water.
S4, by physical vapour deposition (PVD) (PVD) or chemical vapor deposition (CVD) method by mass ratio it is 1: 0.5: 2:
1.5: 10 titanium nitride TiN, titanium carbide TiC, titanium carbonitride TiCN, aluminium nitride AlN and nano coating CrAlN/ZrO2 are in 250-400
Temperature between DEG C is prepared into resist chemical layer solution.
S5, material is put into for the carbon structure steel wire after the winding crust and cold quenching of copper wire, welding wire or alloy wire
Cleaning in supersonic wave cleaning machine, takes out hot blast drying, and resist chemical layer solution obtained in S4 is coated uniformly on winding
The outside of crust and carbon structure steel wire.
S6, the winding crust for being coated with resist chemical layer are wrapped in the structural carbon steel coated with resist chemical layer
Silk outside, and it is placed again into cleaning in supersonic wave cleaning machine, take out hot blast drying.
S7, the carbon structure steel wire that outside obtained in S6 is wound with winding crust is subjected to secondary resist chemical layer
Operation is coated, finished product is obtained.
The present invention in use, by carbon structure steel wire outer application resist chemical layer and wind same
Crust coated with resist chemical layer, while applying the coating operation of secondary chemical attack layer again, make resist chemical
The resist chemical layer of string be divided into multilayer, increase the ability of its resist chemical.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (4)
1. a kind of string of resist chemical, including string ontology and the resist chemical layer that string body surface is arranged in,
It is characterized in that, the resist chemical layer includes that mass ratio nitrogenizes for 1: 0.5: 2: 1.5: 10 titanium nitride TiN, titanium carbide TiC, carbon
Titanium TiCN, aluminium nitride AlN and nano coating CrAlN/ZrO2, the resist chemical layer pass through by physical vapour deposition (PVD) (PVD)
Or temperature preparation of chemical vapor deposition (CVD) method between 250-400 DEG C, and it is coated in the outer of the string ontology
Side, the string ontology is by core of carbon structure steel wire and uses copper wire, welding wire or alloy wire to wind crust.
2. a kind of string of resist chemical according to claim 1, which is characterized in that the carbon knot of the string ontology
The core section of structure steel wire is regular hexagon.
3. a kind of string of resist chemical according to claim 1 or 2, which is characterized in that the carbon structure steel wire
Carbon content be 0.6-0.8%.
4. a kind of preparation process of the string of resist chemical according to claim 1, comprising the following specific steps
S1, by carbon structure steel wire by by the steel wire of a drawing, surface preparation obtains Soxhlet again after heating, quenching
The quenching steel wire of body；
S2, quenching steel wire Jing Guo surface preparation is sent into smelting furnace and is heated, heating temperature is 700-850 DEG C, during which to quenching
Fiery steel wire surface sprinkles auxiliary agent, and the auxiliary agent includes 25 parts of nylon fiber and 25 parts of titanium dioxide in parts by weight；
S3, quenching steel wire is taken out into progress redraing, it is spare places into progress cold quenching in 2-9 DEG C of deionized water；
It S4, by physical vapour deposition (PVD) (PVD) or chemical vapor deposition (CVD) method by mass ratio is 1: 0.5: 2: 1.5: 10
Titanium nitride TiN, titanium carbide TiC, titanium carbonitride TiCN, aluminium nitride AlN and nano coating CrAlN/ZrO2 are between 250-400 DEG C
Temperature be prepared into resist chemical layer solution；
S5, material is put into ultrasound for the carbon structure steel wire after the winding crust and cold quenching of copper wire, welding wire or alloy wire
Cleaning in wave cleaning machine, takes out hot blast drying, and resist chemical layer solution obtained in S4 is coated uniformly on winding crust
With the outside of carbon structure steel wire；
S6, the winding crust for being coated with resist chemical layer are wrapped in outside the carbon structure steel wire coated with resist chemical layer
Side, and it is placed again into cleaning in supersonic wave cleaning machine, take out hot blast drying；
S7, the carbon structure steel wire that outside obtained in S6 is wound with winding crust is carried out to secondary resist chemical layer coating
Operation obtains finished product.