CN110183893A - 一种灰钙基耐水腻子 - Google Patents
一种灰钙基耐水腻子 Download PDFInfo
- Publication number
- CN110183893A CN110183893A CN201910593488.6A CN201910593488A CN110183893A CN 110183893 A CN110183893 A CN 110183893A CN 201910593488 A CN201910593488 A CN 201910593488A CN 110183893 A CN110183893 A CN 110183893A
- Authority
- CN
- China
- Prior art keywords
- parts
- mildew
- proof putty
- putty
- neutrality
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种灰钙基耐水腻子，其特征在于，该腻子按重量份包括15‑20份的凝胶，80‑85份的填充材料、0.4‑0.5份的保水剂纤维素、0.03‑0.05份的橧稠剂、1‑3份的84消毒粉、10‑20份的玻璃粉、0.3‑0.5份的防霉剂、1‑2份的量子催化剂和3‑5份的云母粉。它是一种不易霉变，粘附力强不易脱落，干燥后坚硬、耐水性能好、耐洗刷，分散性好，涂刷效果好的灰钙基耐水腻子。
Description
技术领域
本发明涉及用建筑材料技术领域，具体涉及一种灰钙基耐水腻子。
背景技术
腻子粉是平整墙体表面的一种装饰材料，是以无机胶凝材料为基料，配以黏结材料及其他助剂精细加工而成，是涂料粉刷前必不可少的一种产品，涂施于底漆上或直接涂施于物体上，用以清除被涂物表面上高低不平的缺陷。
传统建筑装修用的大白腻子外加剂主要用聚乙烯醇等高分子胶水，羧甲基纤维素，羧甲基淀粉，预糊化淀粉生产而成；但聚乙烯醇类胶水含甲醛，对人体有害，不符合环保要求，而羧甲基淀粉与预糊化淀粉虽然不含有害物质，但粘结力与抗霉变性差，在腻子粉中添加量大易造成腻子粉霉变，导致腻子粉脱落不美观，造成巨大浪费。同时，传统的腻子粉耐洗刷性差导致后续施工出现粉化现象，不耐水、表明硬度低，因此亟需寻找一种更环保、耐洗刷性好、干燥后硬度高且耐水子粉来解决上述问题。
发明内容
本发明的目的在于，克服现有技术中存在的缺陷，提供一种不易霉变，粘附力强不易脱落，干燥后坚硬、耐水性能好、耐洗刷，分散性好，涂刷效果好的灰钙基耐水腻子。
为实现上述目的，本发明的技术方案是一种灰钙基耐水腻子，该腻子按重量份包括15-20份的凝胶，80-85份的填充材料、0.4-0.5份的保水剂纤维素、0.03-0.05份的橧稠剂、1-3份的84消毒粉、10-20份的玻璃粉、0.3-0.5份的防霉剂、1-2份的量子催化剂和3-5份的云母粉。
其中优选的技术方案是，所述凝胶剂为氢氧化钙。
优选的技术方案还有，所述保水剂纤维素为羟丙基甲基纤维素醚。
优选的技术方案还有，所述增稠剂为淀粉醚。
优选的技术方案还有，所述填充材料的主要成分为碳酸钙。
优选的技术方案还有，所述防霉剂为纳米氧化锌。
优选的技术方案还有，所述量子催化剂为纳米二氧化钛。
优选的技术方案还有，所述玻璃粉与云母粉的粒度为20-50微米。
优选的技术方案还有，所述云母粉为合成云母粉。
本发明的优点和有益效果在于：
1、本发明的灰钙基耐水腻子不易霉变，粘附力强不易脱落，干燥后坚硬、耐水性能好、耐洗刷，分散性好，涂刷效果好。84消毒粉具有杀灭霉菌作用，并均匀的分散到纳米二氧化硅、纳米氧化锌等组分中，使本发明的防霉腻子粉具有优越的抗菌防霉功能。同时，本发明的防霉腻子粉具有良好的粘结强度，抹涂后不龟裂，不掉粉，适用于南方潮湿地带，尤其是厨房，卫生间，地下室等易发霉场所，而且本发明的防霉腻子粉不含对人体有害的成分，符合绿色环保的要求。
该腻子通过上述材料组合并调节其配比，各种材料协同作用，加水搅拌批刮于墙体上，凝胶材料中富含的氢氧化钙(Ca(OH)2)能够吸收空气中的二氧化碳(CO2)生成碳酸钙(CaCO3)和水(H2O)，随着水份散失的干燥反应慢慢结束。利用碳酸钙(CaCO3)分子体积大于氢氧化钙(Ca(OH)2)的原理，使腻子层形成密实的基面，具备耐水功能，遇潮气不粉化，水泡48小时不起泡脱落，是一款理想的内墙用耐水腻子粉。
2、本发明的灰钙基耐水腻子中含有的纳米二氧化硅、纳米氧化锌等可改善腻子粉的稳定性、分散性、触变性、耐候性以及耐洗刷性，使腻子粉与墙体结合强度大幅提高，涂膜硬度增加，表面自洁能力也获得改善。二氧化硅与纳米氧化锌庞大的比表面积、表面多介孔结构和超强的吸附能力以及奇异的理化特性，使防霉剂中的聚季铵盐等功能组分均匀地进入到纳米二氧化硅表面的介孔中，开发出高效、持久防霉的且有一定抗菌作用的防霉腻子粉。量子光催化剂是一种在光的照射下，自身不起变化，却可以促进化学反应的物质，光催化剂是利用自然界存在的光能转换成为化学反应所需的能量，来产生催化作用，使周围的氧气及水分子激发成极具氧化力的自由负离子。几乎可分解所有对人体和环境有害的有机物质及部分无机物质，不仅能加速反应，亦能运用自然界的定侓，不造成资源浪费与附加污染形成。最具代表性的例子为植物的“光合作用”，吸收二氧化碳，利用光能转化为氧气及有机物。由于光催化剂只是提供了反应的场所，它本身并不参与化学反应，所以它的作用效果是持久的(在存在大量矿物质的情况下，也存在钝化的可能。比如对硬水处理是可能发生碳酸钙等水垢沉积时作用效果会很快下降)。
纳米二氧化钛光催化剂是一种在光的照射下，自身不起变化，却可以促进化学反应的物质，就象植物的光合作用中的叶绿素。TiO2光催化剂在太阳光或室内荧光灯的照射下能产生抗菌、除臭、油污分解、防霉防藻、空气净化的作用。
3、碳酸钙的加入，使腻子粉具有良好的抗压、抗折强度，更好的打磨性和耐洗刷性。其中甲基纤维素的加入使防霉腻子粉具有更好的防水防潮性以及阻透防渗透性。
4、本发明的灰钙基耐水腻子的制备方法简单易行，按照不同组分的性质分批加入混合，保证防霉腻子粉的防霉效果达到最佳。
具体实施方式
下面结合实施例，对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案，而不能以此来限制本发明的保护范围。
实施例1
本发明是一种灰钙基耐水腻子，该腻子按重量份包括15份的氢氧化钙凝胶，80份的碳酸钙填充材料、0.4份的羟丙基甲基纤维素醚保水剂、0.03份的淀粉醚橧稠剂、2份的84消毒粉、10份的玻璃粉、0.3份的纳米氧化锌防霉剂、1份的纳米二氧化钛量子催化剂和3份的云母粉。
所述玻璃粉与云母粉的粒度为20-50微米。
所述云母粉为合成云母粉。
实施例2
本发明是一种灰钙基耐水腻子，该腻子按重量份包括17.5份的氢氧化钙凝胶，83份的碳酸钙填充材料、0.45份的羟丙基甲基纤维素醚保水剂、0.04份的淀粉醚橧稠剂、1份的84消毒粉、15份的玻璃粉、0.4份的纳米氧化锌防霉剂、1.5份的纳米二氧化钛量子催化剂和4份的云母粉。
所述玻璃粉与云母粉的粒度为20-50微米。
所述云母粉为合成云母粉。
实施例3
本发明是一种灰钙基耐水腻子，该腻子按重量份包括20份的氢氧化钙凝胶，85份的碳酸钙填充材料、0.5份的羟丙基甲基纤维素醚保水剂、0.05份的淀粉醚橧稠剂、2份的84消毒粉、20份的玻璃粉、0.5份的纳米氧化锌防霉剂、2份的纳米二氧化钛量子催化剂和5份的云母粉。
所述玻璃粉与云母粉的粒度为20-50微米。
所述云母粉为合成云母粉。
云母粉是一种非金属矿物，含有多种成分，其中主要有SiO2，含量一般在49％左右，Al2O3含量在30％左右。云母粉具有良好的弹性、韧性。绝缘性、耐高温、耐酸碱、耐腐蚀、附着力强等特性，是一种优良的添加剂。它广泛地应用于电器、电焊条、橡胶、塑料、造纸、油漆、涂料、颜料、陶瓷、化妆品、新型建材等行业，用途极其广泛。
玻璃粉是一种易打磨抗划高透明粉料，粒径小、分散性好、透明度高、防沉效果较好；经过多次表面改进，具有良好的亲和能力，并且有较强的位阻能力，能方便地分散于涂料中，成膜后可增加涂料丰满度，制成的水晶透明底漆类，既保持清漆的透明度，又提供良好的打磨性。
纳米氧化锌与纳米二氧化钛均属于半导体催化剂的电子结构，在光或灯光照射下，当一个具有一定能量的光子或者具有超过这个半导体带隙能量Eg的光子射入半导体时，一个电子从价带VB激发到导带CB，而留下了一个空穴。激发态的导带电子和价带空穴能够重新结合消除输入的能量和热，电子在材料的表面态被捕捉，价态电子跃迁到导带，价带的空穴把周围环境中的羟基电子抢夺过来使羟基变成自由基，作为强氧化剂而完成对有机物的降解，将病菌和病毒杀死，将滋生或吸附在中性腻子中的病菌和病毒杀死，增加了中性批墙腻子的防霉性能。有效解决了传统内墙中性腻子粉发霉长斑的问题。产品在南方或是潮湿多雨季节有很好的适应性。
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。
Claims (9)
1.一种灰钙基耐水腻子，其特征在于，该腻子按重量份包括15-20份的凝胶，80-85份的填充材料、0.4-0.5份的保水剂纤维素、0.03-0.05份的橧稠剂、1-3份的84消毒粉、10-20份的玻璃粉、0.3-0.5份的防霉剂、1-2份的量子催化剂和3-5份的云母粉。
2.如权利要求1所述的中性防霉腻子，其特征在于，所述凝胶剂为氢氧化钙。
3.如权利要求1所述的中性防霉腻子，其特征在于，所述保水剂纤维素为羟丙基甲基纤维素醚。
4.如权利要求1所述的中性防霉腻子，其特征在于，所述增稠剂为淀粉醚。
5.如权利要求1所述的中性防霉腻子，其特征在于，所述填充材料的主要成分为碳酸钙。
6.如权利要求1所述的中性防霉腻子，其特征在于，所述防霉剂为纳米氧化锌。
7.如权利要求1所述的中性防霉腻子，其特征在于，所述量子催化剂为纳米二氧化钛。
8.如权利要求1所述的中性防霉腻子，其特征在于，所述玻璃粉与云母粉的粒度为20-50微米。
9.如权利要求8所述的中性防霉腻子，其特征在于，所述云母粉为合成云母粉。