[go: up one dir, main page]

CN110183796A - 一种低成本废料回收pvc木塑板材 - Google Patents

一种低成本废料回收pvc木塑板材 Download PDF

Info

Publication number
CN110183796A
CN110183796A CN201910571228.9A CN201910571228A CN110183796A CN 110183796 A CN110183796 A CN 110183796A CN 201910571228 A CN201910571228 A CN 201910571228A CN 110183796 A CN110183796 A CN 110183796A
Authority
CN
China
Prior art keywords
powder
added
wood
waste
plastic plate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201910571228.9A
Other languages
English (en)
Other versions
CN110183796B (zh
Inventor
任军
杨宇
郁朋飞
王翠
唐龙祥
蔡二东
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Mengcheng County Xinruite Building Materials Co Ltd
Original Assignee
Mengcheng County Xinruite Building Materials Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mengcheng County Xinruite Building Materials Co Ltd filed Critical Mengcheng County Xinruite Building Materials Co Ltd
Priority to CN201910571228.9A priority Critical patent/CN110183796B/zh
Publication of CN110183796A publication Critical patent/CN110183796A/zh
Application granted granted Critical
Publication of CN110183796B publication Critical patent/CN110183796B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种低成本废料回收PVC木塑板材，它是由下述重量份的原料组成的：废旧PVC料130‑200、酯改性木粉30‑40、硬脂酸钙4‑6、壬二酸二辛酯5‑7、聚四氟乙烯粉3‑4、ac发泡剂10‑15，本发明的木塑材料采用聚四氟乙烯粉对木塑板材进行增韧改性，而有机化后的木粉则可以在有机基体间良好的分散，进而提高了成品板材的综合性能。

Description

一种低成本废料回收PVC木塑板材
技术领域
本发明属于PVC材料领域，具体涉及一种低成本废料回收PVC木塑板材。
背景技术
木塑复合材料是利用木粉、竹粉、果壳粉或农作物秸秆粉和塑料树脂或废旧塑料为主要原料,经高温混合、成型加工而制得的一种新型环保复合材料。木塑复合材料比原木材料有更好的耐老化性能、耐吸水性和耐翘曲性能，同时可以防虫蛀、抗腐蚀，无须防腐理进而减少环境污染,且成本比纯木材或塑料低40-60％，可以被加工成各种空心型材,因此木塑复合材料被广泛应用于许多领域，是最具潜力的一种新型材料。
目前一般选用聚氯乙烯、聚烯烃、聚苯乙烯等树脂作为木塑复合材料的基体，其中以PVC为基体的木塑复合材料是国内外学者进行发泡研究的重点，但由于PVC树脂加工时需要添加多种助剂，发泡有一定困难，加入植物纤维成分后，树脂熔体粘度、制品刚度等都有增加，也进一步增加了PVC植物纤维复合材料的发泡难度。同时PVC木塑复合板材中的PVC树脂分子链结构中有大量的极性C-Cl键，分子之间存在较大的作用力，因此相对于其他通用树脂,PVC属于硬脆材料，冲击强度较低，且具有缺口敏感性，受外力冲击时易脆裂，难以用作结构材料。这些缺点极大地限制了PVC在高性能领域的发展，为扩大其应用范围，需要对硬质PVC进行增韧改性。
发明内容
本发明的目的在于针对现有技术的缺陷和不足，提供一种低成本废料回收PVC木塑板材。
为实现上述目的，本发明采用以下技术方案：
一种低成本废料回收PVC木塑板材，它是由下述重量份的原料组成的：
废旧PVC料130-200、酯改性木粉30-40、硬脂酸钙4-6、壬二酸二辛酯5-7、聚四氟乙烯粉3-4、ac发泡剂10-15。
所述酯改性木粉是由下述重量份的原料组成的：
秸秆粉10-20、废旧木粉40-50、γ-(2,3-环氧丙氧)丙基三甲氧基硅烷10-13、催化剂0.01-0.02、丙烯酸6-9、松香3-4、8-羟基喹啉1-2、四丁基溴化铵0.04-0.05。
所述的催化剂为浓度为96-98％的盐酸水溶液。
所述酯改性木粉的制备方法，包括以下步骤：
(1)取γ-(2,3-环氧丙氧)丙基三甲氧基硅烷，加入到其重量20-30倍、35-40％的甲醇水溶液中，搅拌均匀，得硅烷溶液；
(2)取秸秆粉、废旧木粉混合，加入到浓度为0.7-1mol/l的氢氧化钠溶液中，浸泡2-3小时，出料，常温干燥，得预处理粉料；
(3)取上述预处理粉料，加入到硅烷溶液中，超声1-2小时，加入催化剂，在60-70℃下保温搅拌5-7小时，出料冷却，得改性分散液；
(4)取松香，加入到其重量15-20倍的无水乙醇中，送入到55-60℃的恒温水浴中，搅拌溶解，加入8-羟基喹啉，搅拌均匀，出料，与上述改性分散液混合，搅拌均匀，加入丙烯酸，送入到反应釜中，加入四丁基溴化铵，调节反应釜温度为115-120℃，保温搅拌2-3小时，出料冷却，旋蒸，除去溶剂，即得所述酯改性木粉。
所述板材的制备方法，包括以下步骤：
将废旧PVC料经过分选后干燥，磨粉，与硬脂酸钙混合，在100-120℃下预热20-30分钟，加入聚四氟乙烯粉、发泡剂、酯改性木粉搅拌均匀，送入到挤出机中，熔融挤出，冷却，即得。
本发明的优点：
本发明首先以秸秆粉、废旧木粉为原料，采用γ-(2,3-环氧丙氧)丙基三甲氧基硅烷处理，然后以盐酸为催化剂，制备poss改性的分散液，然后将松香分散到醇溶液中作为溶剂，将poss改性的分散液于丙烯酸共混反应，得到酯化改性的木粉，通过该反应，有效的改善了木粉在废旧PVC料间的分散性能，提高了成品材料的力学稳定性强度，本发明的木塑材料采用聚四氟乙烯粉对木塑板材进行增韧改性，而有机化后的木粉则可以在有机基体间良好的分散，进而提高了成品板材的综合性能，本发明的采用以废旧PVC料为基料，经过分选后重复利用，有效的降低了生产成本，且成品质量较好，综合性能优越。
具体实施方式
实施例1
一种低成本废料回收PVC木塑板材，它是由下述重量份的原料组成的：
废旧PVC料130、酯改性木粉30、硬脂酸钙4、壬二酸二辛酯5、聚四氟乙烯粉3、ac发泡剂10。
所述酯改性木粉是由下述重量份的原料组成的：
秸秆粉10、废旧木粉40、γ-(2,3-环氧丙氧)丙基三甲氧基硅烷10、催化剂0.01、丙烯酸6、松香3、8-羟基喹啉1、四丁基溴化铵0.04。
所述的催化剂为浓度为96％的盐酸水溶液。
所述酯改性木粉的制备方法，包括以下步骤：
(1)取γ-(2,3-环氧丙氧)丙基三甲氧基硅烷，加入到其重量20倍、35％的甲醇水溶液中，搅拌均匀，得硅烷溶液；
(2)取秸秆粉、废旧木粉混合，加入到浓度为0.7mol/l的氢氧化钠溶液中，浸泡2小时，出料，常温干燥，得预处理粉料；
(3)取上述预处理粉料，加入到硅烷溶液中，超声1小时，加入催化剂，在60℃下保温搅拌5小时，出料冷却，得改性分散液；
(4)取松香，加入到其重量15倍的无水乙醇中，送入到55℃的恒温水浴中，搅拌溶解，加入8-羟基喹啉，搅拌均匀，出料，与上述改性分散液混合，搅拌均匀，加入丙烯酸，送入到反应釜中，加入四丁基溴化铵，调节反应釜温度为115℃，保温搅拌2小时，出料冷却，旋蒸，除去溶剂，即得所述酯改性木粉。
所述板材的制备方法，包括以下步骤：
将废旧PVC料经过分选后干燥，磨粉，与硬脂酸钙混合，在100℃下预热20分钟，加入聚四氟乙烯粉、发泡剂、酯改性木粉搅拌均匀，送入到挤出机中，熔融挤出，冷却，即得。
实施例2
一种低成本废料回收PVC木塑板材，它是由下述重量份的原料组成的：
废旧PVC料200、酯改性木粉40、硬脂酸钙6、壬二酸二辛酯7、聚四氟乙烯粉4、ac发泡剂15。
所述酯改性木粉是由下述重量份的原料组成的：
秸秆粉20、废旧木粉50、γ-(2,3-环氧丙氧)丙基三甲氧基硅烷3、催化剂0.02、丙烯酸9、松香4、8-羟基喹啉2、四丁基溴化铵0.05。
所述的催化剂为浓度为98％的盐酸水溶液。
所述酯改性木粉的制备方法，包括以下步骤：
(1)取γ-(2,3-环氧丙氧)丙基三甲氧基硅烷，加入到其重量30倍、40％的甲醇水溶液中，搅拌均匀，得硅烷溶液；
(2)取秸秆粉、废旧木粉混合，加入到浓度为1mol/l的氢氧化钠溶液中，浸泡3小时，出料，常温干燥，得预处理粉料；
(3)取上述预处理粉料，加入到硅烷溶液中，超声2小时，加入催化剂，在70℃下保温搅拌7小时，出料冷却，得改性分散液；
(4)取松香，加入到其重量20倍的无水乙醇中，送入到60℃的恒温水浴中，搅拌溶解，加入8-羟基喹啉，搅拌均匀，出料，与上述改性分散液混合，搅拌均匀，加入丙烯酸，送入到反应釜中，加入四丁基溴化铵，调节反应釜温度为120℃，保温搅拌3小时，出料冷却，旋蒸，除去溶剂，即得所述酯改性木粉。
所述板材的制备方法，包括以下步骤：
将废旧PVC料经过分选后干燥，磨粉，与硬脂酸钙混合，在120℃下预热30分钟，加入聚四氟乙烯粉、发泡剂、酯改性木粉搅拌均匀，送入到挤出机中，熔融挤出，冷却，即得。
性能测试：
本发明实施例1的低成本废料回收PVC木塑板材：
拉伸强度：56.6MPa；
冲击强度：12.35KJ/m2；
断裂伸长率：6.1％；
弯曲强度：23.3MPa。
本发明实施例2的低成本废料回收PVC木塑板材：
拉伸强度：59.7MPa；
冲击强度：14.11KJ/m2；
断裂伸长率：6.4％；
弯曲强度：24.0MPa。

Claims (5)

1.一种低成本废料回收PVC木塑板材，其特征在于，它是由下述重量份的原料组成的：
废旧PVC料130-200、酯改性木粉30-40、硬脂酸钙4-6、壬二酸二辛酯5-7、聚四氟乙烯粉3-4、ac发泡剂10-15。
2.根据权利要求1所述的一种低成本废料回收PVC木塑板材，其特征在于，所述酯改性木粉是由下述重量份的原料组成的：
秸秆粉10-20、废旧木粉40-50、γ-(2,3-环氧丙氧)丙基三甲氧基硅烷10-13、催化剂0.01-0.02、丙烯酸6-9、松香3-4、8-羟基喹啉1-2、四丁基溴化铵0.04-0.05。
3.根据权利要求2所述的一种低成本废料回收PVC木塑板材，其特征在于，所述的催化剂为浓度为96-98％的盐酸水溶液。
4.根据权利要求2所述的一种低成本废料回收PVC木塑板材，其特征在于，所述酯改性木粉的制备方法，包括以下步骤：
(1)取γ-(2,3-环氧丙氧)丙基三甲氧基硅烷，加入到其重量20-30倍、35-40％的甲醇水溶液中，搅拌均匀，得硅烷溶液；
(2)取秸秆粉、废旧木粉混合，加入到浓度为0.7-1mol/l的氢氧化钠溶液中，浸泡2-3小时，出料，常温干燥，得预处理粉料；
(3)取上述预处理粉料，加入到硅烷溶液中，超声1-2小时，加入催化剂，在60-70℃下保温搅拌5-7小时，出料冷却，得改性分散液；
(4)取松香，加入到其重量15-20倍的无水乙醇中，送入到55-60℃的恒温水浴中，搅拌溶解，加入8-羟基喹啉，搅拌均匀，出料，与上述改性分散液混合，搅拌均匀，加入丙烯酸，送入到反应釜中，加入四丁基溴化铵，调节反应釜温度为115-120℃，保温搅拌2-3小时，出料冷却，旋蒸，除去溶剂，即得所述酯改性木粉。
5.根据权利要求1所述的一种低成本废料回收PVC木塑板材，其特征在于，所述板材的制备方法，包括以下步骤：
将废旧PVC料经过分选后干燥，磨粉，与硬脂酸钙混合，在100-120℃下预热20-30分钟，加入聚四氟乙烯粉、发泡剂、酯改性木粉搅拌均匀，送入到挤出机中，熔融挤出，冷却，即得。
CN201910571228.9A 2019-06-28 2019-06-28 一种低成本废料回收pvc木塑板材 Expired - Fee Related CN110183796B (zh)