CN110158219A - A kind of bilayer adds core fabric and preparation method thereof - Google Patents
A kind of bilayer adds core fabric and preparation method thereof Download PDFInfo
- Publication number
- CN110158219A CN110158219A CN201910458394.8A CN201910458394A CN110158219A CN 110158219 A CN110158219 A CN 110158219A CN 201910458394 A CN201910458394 A CN 201910458394A CN 110158219 A CN110158219 A CN 110158219A
- Authority
- CN
- China
- Prior art keywords
- yarn
- layer
- fabric
- weft yarn
- nexine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of bilayers to add core fabric and preparation method thereof, and the fabric includes surface layer, inner layer and heart yarn；The surface layer is interwoven by top layer warp thread and top layer weft yarn A, and the inner layer is interwoven by nexine warp thread and nexine weft yarn B, and the surface layer and inner layer pass through " under connect " binding method binding；The heart yarn is arranged between surface layer and inner layer, fills out heart yarn C for broadwise.The present invention fills out core weave method using bilayer, by by the intertexture of plant dyeing yarn and hemp yarn, and obtains a kind of fabric of novel components, not only environmentally friendly but also have excellent antimildew and antibacterial function.Simultaneously in Fabric Design, the arrangement design of core structure designs and plant dyeing yarn dyed yarn is filled out by using bilayer, forms the fabric with stereoscopic effect abundant and visual effect, is very suitable to do bed necessaries and blanket uses.
Description
Technical field
The present invention relates to textile technology fields, specifically, being related to a kind of bilayer adds core fabric and preparation method thereof.
Background technique
With the development of society and the progress of human civilization, environmental protection increasingly obtains the attention of people.Plant dyeing makes
It is natural dyestuff, pigment is extracted mainly from natural plant, yarn is dyed, do not made in dyeing course
With the chemical reagent of pollution environment, the serious pollution problem of chemical dye is avoided.Currently, having many chemical treatments in the market
Antimicrobial product, but its actual antibacterial durability is not high, and chemical substance existing for product easily causes carcinogen, to human body
It is harmful.
It is most of to be knitted based on product currently, the product of common plant dyeing weaving yarns on the market, part tatting
Product is also only some conventional plain cloths, far from meeting pursuit of the people for rich choice of products degree, and meanwhile it is also not mould proof
The excellent plant dyeing fabric of antibacterial functions.
A kind of antibiotic property two-layer fabric is disclosed in existing patent CN104018266A comprising top fabric woven and inner layer
Fabric, two-layer fabric is lifted by the warp thread of nexine fabric woven to be weaved with the weft yarns of top fabric woven, the surface layer and inner layer
Fabric tissue is plain weave, is formed respectively by respective warp thread and weft yarns, and the warp thread of the top fabric woven is Quality Pure Cotton Yarn Production,
Weft yarn is Sheng-bast fiber and combed cotton blended yarn, and the warp thread of the nexine fabric woven is Quality Pure Cotton Yarn Production, and weft yarn is bamboo fibre and combed cotton
Mixed yarn, the arrangement of top layer warp thread, nexine warp thread and the top layer weft yarn, nexine weft yarn of the two-layer fabric tissue are compared for 1:1, are adopted
Also there is preferable gas permeability and wearability so that fabric not only has excellent anti-microbial property with two-layer fabric institutional framework.
But stereoscopic effect and raised line visual effect can not be presented in the fabric.
Summary of the invention
In view of the drawbacks of the prior art, the object of the present invention is to provide a kind of bilayers to add core fabric and preparation method thereof.This
Invention fills out core weave method using bilayer, and by by the intertexture of plant dyeing yarn and hemp yarn, and it is novel to obtain one kind
The fabric of component, not only environmental protection but also have excellent antimildew and antibacterial function.Simultaneously in Fabric Design, cored structure is filled out by using bilayer
The arrangement design of design and plant dyeing yarn dyed yarn forms the fabric with stereoscopic effect abundant and visual effect, very
It is suitble to do bed necessaries and blanket uses.
Have it is two layers overlapped made of two groups of warp thread independent and two groups of weft yarns independent (or claim
Fabric in table two layers), referred to as two-layer fabric, the tissue for forming two-layer fabric are known as double-layered structure.In two-layer fabric, upper layer
Warp thread and weft yarn be known as table warp, outer weft；The warp thread and weft yarn of lower layer are known as back warp, back weft.Table passes through the tissue to interweave with outer weft
Referred to as table organization；The tissue that back warp and back weft interweave is organized in being known as.It is by various binding methods, two layers of full width of separation is tight
The fabric being thickly stiched together is known as bonded two-layer fabric.Increase the thickness of fabric in the present invention, elasticity makes fabric
Surface elevation and rich in stereoscopic effect, the thicker heart yarn not interweaved with surface layer and inner layer is inserted among two-layer fabrics in table,
And add core fabric to form bilayer.
The purpose of the present invention is what is be achieved through the following technical solutions:
The present invention provides a kind of bilayers to add core fabric, which is characterized in that including surface layer, inner layer and heart yarn；The table
Layer is interwoven by top layer warp thread and top layer weft yarn A, and the inner layer is interwoven by nexine warp thread and nexine weft yarn B, described
Surface layer and inner layer pass through " under connect " binding method binding；The heart yarn is arranged between surface layer and inner layer, fills out heart yarn C for broadwise.
Preferably, the top layer warp thread and nexine warp thread are 21s hemp yarn；The top layer weft yarn A is blue 21s plant dye
Dyed yarn, nexine weft yarn B are 21s hemp yarn, and it is 7s/2 coarse cotton yarn that broadwise, which fills out heart yarn C,.
The hemp yarn material that the present invention uses belongs to one kind of natural fiber, it in addition to good moisture absorption, it is ventilative,
Outside pleasant, uvioresistant function, mould proof, antibiotic property is optimal in numerous antimicrobial natural fibers.
Preferably, the arrangement that the broadwise fills out heart yarn C, top layer weft yarn A, nexine weft yarn B is compared for 1:2:2.
Preferably, the top layer weft yarn A, nexine weft yarn B, broadwise fill out putting in order for heart yarn C are as follows:
1) 1 A, 1 B, 1 A, 1 B, 1 C；1 A, 1 B, 1 A, 1 B, 1 C；
2) 1 A, 1 B, 1 B, 1 A, 1 C；
3) 1 B, 1 A, 1 B, 1 A, 1 C；Circulation 7 times.
Preferably, the top layer warp thread, the density of nexine warp thread are 82 pieces/inch；The top layer weft yarn A, nexine weft yarn
B, it is 100 pieces/inch that broadwise, which fills out the density of heart yarn C,.
Preferably, the surface layer, inner layer and binding are plain weave.
The present invention also provides the preparation methods that a kind of bilayer adds core fabric, comprising the following steps:
A, top layer warp thread and nexine warp thread are arranged according to 1:1, weft yarn weaving sequence is any one of the following manners:
1) 1 A, 1 B, 1 A, 1 B, 1 C；1 A, 1 B, 1 A, 1 B, 1 C；
2) 1 A, 1 B, 1 B, 1 A, 1 C；
3) 1 B, 1 A, 1 B, 1 A, 1 C；Circulation 7 times.
B, when being woven into top layer weft yarn, nexine weft yarn lifts to interweave with surface layer, forms binding place, surface layer and inner layer are connect
Knot.
Compared with prior art, the present invention have it is following the utility model has the advantages that
1, by the way that plant dyeing yarn and hemp yarn interweave, so that a kind of fabric of novel components is obtained, resulting face
The characteristics of expecting existing plant dyeing environment-friendly natural has both the function of hemp antimildew and antibacterial again, develops a novel mildew resistant antibiotic property
The excellent plant dyeing environment-friendly plus material of energy.
2, the arrangement design of core structure designs and plant dyeing yarn dyed yarn is filled out by using bilayer, is formed with abundant
The fabric of stereoscopic effect and raised line visual effect is very suitable to make blanket and bed necessaries uses.
Detailed description of the invention
Upon reading the detailed description of non-limiting embodiments with reference to the following drawings, other feature of the invention,
Objects and advantages will become more apparent upon:
Fig. 1 is the upper machine organization chart that the embodiment of the present invention 1 designs；Wherein all positions for having symbol to fill are in fabric
It is all through interlacing point in weaving process, blank position is latitude interlacing point；■-expression surface layer is through interlacing point , ╳-expression inner layer
Through interlacing point, zero-indicates that when knitting inner layer, all top layer warp threads are all lifted, i.e., on organization chart display through interlacing point,
△-expression heart yarn is located among surface layer and inner layer, ◆-indicate binding place；
Fig. 2 is the double-layer fabric pictorial diagram that the embodiment of the present invention 1 is made into.
Specific embodiment
The present invention is described in detail combined with specific embodiments below.Following embodiment will be helpful to the technology of this field
Personnel further understand the present invention, but the invention is not limited in any way.It should be pointed out that the ordinary skill of this field
For personnel, without departing from the inventive concept of the premise, various modifications and improvements can be made.These belong to the present invention
Protection scope.
Embodiment 1
It present embodiments provides a kind of bilayer and adds core fabric, as shown in Figure 1, including surface layer, inner layer and heart yarn；The table
Layer is interwoven by top layer warp thread (table yarn i.e. shown in FIG. 1) and top layer weft yarn A (outer weft yarn i.e. shown in FIG. 1), in described
Layer is interwoven by nexine warp thread (inner yarn i.e. shown in FIG. 1) and nexine weft yarn B (back weft yarn i.e. shown in FIG. 1), the surface layer
With inner layer by " under connect " binding method binding, binding place is formed；The heart yarn is arranged between surface layer and inner layer, fills out for broadwise
Heart yarn C (i.e. shown in FIG. 1 to fill out heart yarn).The top layer warp thread and nexine warp thread are 21s hemp yarn；The top layer weft yarn A is 21s
Plant dyeing yarn, nexine weft yarn B are 21s hemp yarn, and it is 7s/2 coarse cotton yarn that broadwise, which fills out heart yarn C,.
Its it is specific the preparation method is as follows:
A, top layer warp thread and nexine warp thread are arranged according to 1:1, weft yarn weaving sequence are as follows:
1) 1 A, 1 B, 1 A, 1 B, 1 C；1 A, 1 B, 1 A, 1 B, 1 C；
2) 1 A, 1 B, 1 B, 1 A, 1 C；
3) 1 B, 1 A, 1 B, 1 A, 1 C；Circulation 7 times.
With 1)~3) it is a systemic circulation.
Thus top layer warp thread and top layer weft yarn are interleaved with each other to form surface layer fabric, and nexine warp thread is interleaved with each other with nexine weft yarn
Inner layer fabric is formed, fills out core weft yarn between surface layer fabric and inner layer fabric, is not interweaved with surface layer fabric and inner layer fabric；
B, when being woven into top layer weft yarn, nexine weft yarn lifts to interweave with surface layer, forms binding place, surface layer and inner layer are connect
Knot.Form a binding place as shown in fig. 1 in a Weaving Cycle.
Bilayer made from the present embodiment adds core fabric as shown in Fig. 2, it shows stereoscopic effect abundant and raised line vision
Effect, and the fabric has excellent antimildew and antibacterial performance.
Comparative example 1
The preparation method of this comparative example and embodiment 1 is essentially identical, the difference is that only: only by inner layer in this comparative example
The material of weft yarn B is changed to 21s linen.
The bilayer of this comparative example preparation adds core fabric and also shows stereoscopic effect and raised line visual effect, and has centainly
Antibiotic property, but the fabric fungicidal properties does not have embodiment excellent effect.
Comparative example 2
The preparation method of this comparative example and embodiment 1 is essentially identical, the difference is that only: only by inner layer in this comparative example
The material of weft yarn B is changed to 21s all cotton grey rope yarn.
The bilayer of this comparative example preparation adds core fabric and also shows stereoscopic effect and raised line visual effect, but the fabric does not have
There is antimildew and antibacterial performance.
Comparative example 3
The preparation method of this comparative example and embodiment 1 is essentially identical, the difference is that only: only by inner layer in this comparative example
The material of weft yarn B is changed to this white yarn of 21s viscose.
The bilayer of this comparative example preparation adds core fabric and also shows stereoscopic effect and raised line visual effect, but the fabric does not have
There is antimildew and antibacterial performance.
Comparative example 4
The preparation method of this comparative example and embodiment 1 is essentially identical, the difference is that only: in the step A of this comparative example,
Weft yarn weaving sequence are as follows: 1 A yarn, 1 B yarn, 1 A yarn, 1 B yarn, 1 C yarn circulation are woven into.
The bilayer of this comparative example preparation adds core fabric not shown stereoscopic effect and raised line visual effect out.
There are many concrete application approach of the present invention, the above is only a preferred embodiment of the present invention.More than it should be pointed out that
Embodiment is merely to illustrate the present invention, and the protection scope being not intended to restrict the invention.For the common skill of the art
For art personnel, without departing from the principle of the present invention, several improvement can also be made, these improvement also should be regarded as this hair
Bright protection scope.
Claims (7)
1. a kind of bilayer adds core fabric, which is characterized in that including surface layer, inner layer and heart yarn；The surface layer by top layer warp thread and
Top layer weft yarn A is interwoven, and the inner layer is interwoven by nexine warp thread and nexine weft yarn B, and the surface layer and inner layer pass through
" under connect " binding method binding；The heart yarn is arranged between surface layer and inner layer, fills out heart yarn C for broadwise.
2. bilayer according to claim 1 adds core fabric, which is characterized in that the top layer warp thread and nexine warp thread are 21s
Hemp yarn；The top layer weft yarn A is 21s plant dyeing yarn, and nexine weft yarn B is 21s hemp yarn, and it is that 7s/2 is thick that broadwise, which fills out heart yarn C,
Cotton yarn.
3. bilayer according to claim 1 adds core fabric, which is characterized in that the broadwise fills out heart yarn C, top layer weft yarn A, inner
The arrangement of layer weft yarn B is compared for 1:2:2.
4. bilayer according to claim 1 adds core fabric, which is characterized in that the top layer weft yarn A, nexine weft yarn B, broadwise
Fill out putting in order for heart yarn C are as follows:
1) 1 A, 1 B, 1 A, 1 B, 1 C；1 A, 1 B, 1 A, 1 B, 1 C；
2) 1 A, 1 B, 1 B, 1 A, 1 C；
3) 1 B, 1 A, 1 B, 1 A, 1 C；Circulation 7 times.
5. bilayer according to claim 1 adds core fabric, which is characterized in that the top layer warp thread, the density of nexine warp thread
It is 82 pieces/inch；The density that the top layer weft yarn A, nexine weft yarn B, broadwise fill out heart yarn C is 100 pieces/inch.
6. bilayer according to claim 1 adds core fabric, which is characterized in that the surface layer, inner layer and binding are plain weave.
7. the preparation method that a kind of bilayer according to claim 1 adds core fabric, which comprises the following steps:
A, top layer warp thread and nexine warp thread are arranged according to 1:1, weft yarn weaving sequence are as follows:
1) 1 A, 1 B, 1 A, 1 B, 1 C；1 A, 1 B, 1 A, 1 B, 1 C；
2) 1 A, 1 B, 1 B, 1 A, 1 C；
3) 1 B, 1 A, 1 B, 1 A, 1 C are recycled 7 times with this；
B, when being woven into top layer weft yarn, nexine weft yarn lifts to interweave with surface layer, binding place is formed, by surface layer and inner layer binding.