CN110158090A - 一种环保的反应型抛光光亮剂组合物及其制备方法与应用 - Google Patents
一种环保的反应型抛光光亮剂组合物及其制备方法与应用 Download PDFInfo
- Publication number
- CN110158090A CN110158090A CN201910563364.3A CN201910563364A CN110158090A CN 110158090 A CN110158090 A CN 110158090A CN 201910563364 A CN201910563364 A CN 201910563364A CN 110158090 A CN110158090 A CN 110158090A
- Authority
- CN
- China
- Prior art keywords
- acid
- brightener
- environmental protection
- response type
- polishing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种环保的反应型抛光光亮剂组合物及其制备方法与应用，属于精细化工领域。所述环保的反应型抛光光亮剂组合物按质量百分比包括以下组分：抛光剂5％‑10％，醇胺3％‑6％，络合剂3％‑5％，表面活性剂1％‑4％，光亮剂0.5％‑2.0％，增稠剂0.1％‑0.5％，缓蚀剂0.5％‑2％，酸洗剂1％‑3％，水75％‑85％。发明制备的环保的反应型抛光光亮剂组合物是传统光亮剂的更新换代产品，对不锈钢材质的清洗、光亮效果明显，对基材无腐蚀，对环境友好。
Description
技术领域
本发明属于精细化工领域，特别涉及一种环保的反应型抛光光亮剂组合物及其制备方法与应用。
背景技术
不锈钢具有较高的耐腐蚀、耐磨损、易加工等优良性能。在汽车、摩托车、日用五金、建筑、道路护栏等行业得到越来越广泛的应用。近年来，不锈钢的应用在迅速增长，但其表面往往有一层灰色氧化膜或毛刺，从而影响产品的质量，因此对不锈钢表面进行抛光处理，是不锈钢制品中最为常用的处理工艺。
光亮剂作用在工件表面，使其产生微观塑性变形，从而降低表面粗糙度；光亮剂作用在工件表面，能够迅速去除工件表面的油污及杂质，达到增亮效果；光亮剂应有一定的防锈作用，能够较长时间保持工件良好的表面状态，从而提高轧光质量。
金属抛光处理通常分为机械抛光、电化学抛光和化学抛光。化学抛光以优点突出而被广泛应用。目前，使用于不锈钢五金工具的化学光亮剂基本可分为王水型溶液、硫酸型溶液、磷酸型溶液、醋酸型溶液和过氧化氢型溶液等5种类型，它们存在的主要问题是：多数光亮剂中含有硝酸，抛光时会产生大量的含氮氧化物等有害气体，从而污染环境和危害人体健康；而双氧水型抛光液，易分解，维护困难，成本高，实用范围窄等缺点。因此，低毒或无毒的环保型抛光液的出现，就是顺应市场需求的。
发明内容
为克服上述现有技术中存在的缺点与不足，本发明的首要目的在于提供一种环保的反应型抛光光亮剂组合物。本发明的光亮剂对不锈钢制品的清洗效果极佳，材料表面光亮，对材质无腐蚀，对环境友好。
本发明的另一目的在于提供上述环保的反应型抛光光亮剂组合物的制备方法。本发明所述的制备方法十分简单，可采用常规的物理混合，机械搅拌均匀的方法进行制备。
本发明的再一目的在于提供上述环保的反应型抛光光亮剂组合物的应用。所述光亮剂可用于对不锈钢件、钢铁件、铜件(黄铜、紫铜、红铜)等金属基材的表面抛光的光亮剂，都有较好的抛光效果。
为达到上述目的，本发明采用的技术方案是：
一种环保的反应型抛光光亮剂组合物，按质量百分比包括以下组分：抛光剂5％-10％，醇胺3％-6％，络合剂3％-5％，表面活性剂1％-4％，光亮剂0.5％-2.0％，增稠剂0.1％-0.5％，缓蚀剂0.5％-2％，酸洗剂1％-3％，水75％-85％。
其中，所述的抛光剂为十二烷基苯磺酸、异构烷基磺酸、C12-C20重烷基苯磺酸、C10-C14直链烷基磺酸中的至少一种。
其中，所述的醇胺为单乙醇胺、二乙醇胺、三乙醇胺、异丙醇胺、异丁醇胺、二乙醇三异丙醇胺、三异丙醇胺、N-甲基一乙醇胺、N-甲基二乙醇胺中的至少一种。
其中，所述的络合剂为柠檬酸、酒石酸、苹果酸、葡萄糖酸、羟基乙酸、羟基丙酸、巯基乙酸、乙二胺四乙酸、二亚乙基三胺五醋酸、乙基乙二胺三乙酸、二羟乙基甘氨酸、次氮基三乙酸中的至少一种，这些有机酸可以作为酸洗抛光剂使用，同时又是良好的金属螯合剂。
其中，所述的表面活性剂主要是非离子表面活性剂，如异构醇聚氧乙烯醚(E-1310、E-1009)、脂肪醇聚氧乙烯醚(AEO-9、平平加O-15)、脂肪酸聚氧乙烯酯(LAE-9)、烷基酚聚氧乙烯醚(TX-9、TX-10、曲拉通X100)、聚乙二醇(PEG)、脂肪胺聚氧乙烯醚(AC1210)、蓖麻油聚氧乙烯醚(EL-40)中的至少一种。
其中，所述的光亮剂为植物油酸、油酸、硬脂酸、棕榈酸、肉豆蔻酸、蓖麻油酸、椰子油酸、妥尔油酸、大豆油酸、松香酸中的至少一种。
其中，所述的增稠剂为过乙基纤维素、甲基纤维素、羧甲基纤维素钠、羟乙基纤维素、羟丙基甲基纤维素、黄原酸、阿拉伯胶、卡拉胶中的至少一种。
其中，所述的缓蚀剂为尿素、硫脲、甲基苯并三氮唑、苯并三氮唑、2-苯基咪唑啉、2-巯基苯并噻唑、三氮唑、5-苯基四氮唑、8-羟基喹啉、丁炔二醇、丙炔醇、乌洛托品、五水偏硅酸钠、钨酸钠、钼酸钠中的至少一种。
其中，所述的酸洗剂为硫酸氢钠、磷酸、辛基磷酸、甲基磺酸、氨基磺酸中的一种。
本发明还提供上述环保的反应型抛光光亮剂组合物的制备方法，包括以下步骤：
1)将抛光剂和40％-60％(质量百分比)的水混合搅拌均匀；
2)加入醇胺、表面活性剂、光亮剂搅拌均匀，加热到50℃-60℃并反应20-40分钟；
3)停止加热，最后加入增稠剂、络合剂、缓蚀剂、酸洗剂和剩余的水，混合搅拌至体系均匀，样品呈现微黄粘稠液体，获得环保的反应型抛光光亮剂。
本发明所述环保的反应型抛光光亮剂组合物作为对不锈钢件、钢铁件、铜件(黄铜、紫铜、红铜)金属基材进行表面抛光的光亮剂，都有较好的抛光效果。
本发明的环保的反应型抛光光亮剂组合物，不含大量强酸、腐蚀性酸、易挥发性酸，如：硫酸、硝酸、氢氟酸、盐酸等，pH在4-6左右，环保性相对较好。
本发明相对于现有技术具有如下的优点及效果：本发明的反应型抛光光亮剂组合物，选用烷基苯磺酸、有机酸以及甲基磺酸等作为主抛光剂，不产生酸雾且环保性强，对金属基材的腐蚀性大大减弱；其中含有的烷基苯磺酸和醇胺，可以在加热条件下反应生成部分烷基苯磺酸醇胺皂，既是一种高效的防锈润滑剂，又具有良好的清洗效果；将样品配成粘度较高的液体，可以方便涂膜在需要抛光的设备表面，增加停留时间和抛光效率。高浓度的液体，也更方便运输。
具体实施方式
下面结合具体实施例，进一步阐述本发明。应理解，这些实施例仅用于说明本发明而不用于限制本发明的范围。此外应理解，在阅读了本发明的内容之后，本领域技术人员可以对本发明作各种改动或修改，这些等价形式同样落于本发明所限定的范围。
实施例1
一种环保的反应型抛光光亮剂组合物按质量百分比：十二烷基苯磺酸8.0％，二乙醇胺3.0％，三乙醇胺1.0％，脂肪醇聚氧乙烯醚2.0％，柠檬酸4.0％，椰子油0.5％，乙基纤维素0.5％，2-巯基苯并噻唑0.5％，氨基磺酸2.0％，水78.5％。
上述环保的反应型抛光光亮剂组合物的制备步骤如下：
1)准备以下配比的原料(质量百分比)：十二烷基苯磺酸8.0％，二乙醇胺3.0％，三乙醇胺1.0％，脂肪醇聚氧乙烯醚2.0％，柠檬酸4.0％，椰子油0.5％，乙基纤维素0.5％，2-巯基苯并噻唑0.5％，氨基磺酸2.0％，水78.5％。
2)将十二烷基苯磺酸8.0％和水50％混合搅拌均匀；
3)加入二乙醇胺3.0％，三乙醇胺1.0％，椰子油0.5％搅拌均匀，加热到50-60℃并反应30分钟左右；
4)停止加热，最后加入柠檬酸4.0％，乙基纤维素0.5％，2-巯基苯并噻唑0.5％，氨基磺酸2.0％，水28.5％，混合搅拌至体系均匀，样品呈现微黄粘稠液体，获得环保的反应型抛光光亮剂。
实施例2
一种环保的反应型抛光光亮剂组合物按质量百分比：十二烷基苯磺酸7.0％，异丙醇胺3.0％，三乙醇胺1.0％，双酚A聚氧乙烯醚1.5％，羟基乙酸2.0％，葡萄糖酸1.5％，棕榈硬脂酸0.5％，羧甲基纤维素0.5％，苯并三氮唑0.5％，辛基磷酸1.0％，水80.5％。
上述环保的反应型抛光光亮剂组合物的制备步骤如下：
1)准备以下配比的原料(质量百分比)：十二烷基苯磺酸7.0％，异丙醇胺3.0％，三乙醇胺1.0％，双酚A聚氧乙烯醚1.5％，羟基乙酸2.0％，葡萄糖酸1.5％，棕榈硬脂酸0.5％，羧甲基纤维素0.5％，苯并三氮唑0.5％，辛基磷酸1.0％，水80.5％。
2)将十二烷基苯磺酸7.0％和水50％混合搅拌均匀；
3)加入异丙醇胺3.0％，三乙醇胺1.0％，双酚A聚氧乙烯醚1.5％，棕榈硬脂酸0.5％搅拌均匀，加热到50-60℃并反应30分钟左右；
4)停止加热，最后加入羟基乙酸2.0％，葡萄糖酸1.5％，羧甲基纤维素0.5％，苯并三氮唑0.5％，辛基磷酸1.0％，水30.5％，混合搅拌至体系均匀，样品呈现微黄粘稠液体，获得环保的反应型抛光光亮剂。
实施例3
一种环保的反应型抛光光亮剂组合物按质量百分比：重烷基苯磺酸6.0％，单乙醇胺3.0％，聚醚1.5％，乙二胺四乙酸3.0％，甲基纤维素0.5％，蓖麻油酸0.5％，硫脲0.5％，硫酸氢钠2.0％，水83.0％。
上述环保的反应型抛光光亮剂组合物的制备步骤如下：
1)准备以下配比的原料(质量百分比)：重烷基苯磺酸6.0％，单乙醇胺3.0％，聚醚1.5％，乙二胺四乙酸3.0％，甲基纤维素0.5％，蓖麻油酸0.5％，硫脲0.5％，硫酸氢钠2.0％，水83.0％。
2)将重烷基苯磺酸6.0％和水50％混合均匀；
3)加入单乙醇胺3.0％，聚醚1.5％，蓖麻油酸0.5％搅拌均匀，加热到50-60℃并反应30分钟左右；
4)停止加热，最后加入乙二胺四乙酸3.0％，甲基纤维素0.5％，硫脲0.5％，硫酸氢钠2.0％，水33.0％，混合搅拌至体系均匀，样品呈现微黄粘稠液体，获得环保的反应型抛光光亮剂。
实施例4
一种环保的反应型抛光光亮剂组合物按质量百分比：十二烷基苯磺酸8.0％，三乙醇胺3.5％，月桂胺聚氧乙烯醚2.0％，柠檬酸5.0％，羟甲基丙基纤维素0.5％，大豆油0.5％，尿素0.5％，磷酸1.5％，水80.5％。
上述环保的反应型抛光光亮剂组合物的制备步骤如下：
1)准备以下配比的原料(质量百分比)：十二烷基苯磺酸8.0％，三乙醇胺3.5％，月桂胺聚氧乙烯醚2.0％，柠檬酸5.0％，羟甲基丙基纤维素0.5％，大豆油0.5％，尿素0.5％，磷酸1.5％，水80.5％。
2)将十二烷基苯磺酸8.0％和50％水混合搅拌均匀；
3)加入三乙醇胺3.5％，月桂胺聚氧乙烯醚2.0％，大豆油0.5％，搅拌均匀，加热到50-60℃并反应30分钟左右；
4)停止加热，最后加入柠檬酸5.0％，羟甲基丙基纤维素0.5％，尿素0.5％，磷酸1.5％和水30.5％，混合搅拌至体系均匀，样品呈现微黄粘稠液体，获得环保的反应型抛光光亮剂。
<化学抛光试验>
称取100ml环保的反应型抛光光亮剂组合物加入到150ml烧杯中，放入已知质量的不锈钢器具，静置2h进行化学抛光。
实验结束后取出不锈钢器具，清洗表面，自然干燥，检测其表面光洁度结果为光亮。
经过观察，本抛光液抛光后的不锈钢件与未抛光比，明显光亮度高，无白斑与麻点，也未见基材有腐蚀现象。
<腐蚀度计算>
进一步烘干样品，在分析天平是称重，计算其腐蚀度：
腐蚀度＝[(抛光前样品质量-抛光后样品质量)/抛光前样品质量]×100％
计算出本实施例的腐蚀度结果，如下表1所示。
表1实施例与对照例腐蚀度的实验结果
---不锈钢表面
由结果可知，由本专利提供的环保的反应型抛光光亮剂，经其处理后的不锈钢件，可以达到0.02％以下的腐蚀率，而市面上常见的银保护剂，腐蚀度高达0.2％。
称取100ml环保的反应型抛光光亮剂组合物加入到150ml烧杯中，放入已知质量的黄铜器具，静置2h进行化学抛光。
实验结束后取出黄铜器具，清洗表面，自然干燥，检测其表面光洁度结果为光亮。进一步烘干样品，在分析天平是称重，计算其腐蚀度：
腐蚀度＝[(抛光前样品质量-抛光后样品质量)/抛光前样品质量]×100％
计算出本实施例的腐蚀度结果，如下表2所示。
表2实施例与对照例腐蚀度的实验结果
---铜表面
由结果可知，由本专利提供的高效不锈钢抛光剂，经其处理后的不锈钢件，可以达到0.01％以下的腐蚀率，而市面上常见的银保护剂，腐蚀度高达0.15％。
上述实施例为本发明较佳的实施方式，但本发明的实施方式并不受上述实施例的限制，其他的任何未背离本发明的精神实质与原理下所作的改变、修饰、替代、组合、简化，均应为等效的置换方式，都包含在本发明的保护范围之内。
Claims (10)
1.一种环保的反应型抛光光亮剂组合物，其特征在于：按质量百分比包括以下组分：抛光剂5％-10％，醇胺3％-6％，络合剂3％-5％，表面活性剂1％-4％，光亮剂0.5％-2.0％，增稠剂0.1％-0.5％，缓蚀剂0.5％-2％，酸洗剂1％-3％，水75％-85％。
2.根据权利要求1所述的环保的反应型抛光光亮剂组合物，其特征在于：所述的抛光剂为十二烷基苯磺酸、异构烷基磺酸、C12-C20重烷基苯磺酸、C10-C14直链烷基磺酸中的至少一种。
3.根据权利要求1所述的环保的反应型抛光光亮剂组合物，其特征在于：所述的醇胺为单乙醇胺、二乙醇胺、三乙醇胺、异丙醇胺、异丁醇胺、二乙醇三异丙醇胺、三异丙醇胺、N-甲基一乙醇胺、N-甲基二乙醇胺中的至少一种。
4.根据权利要求1所述的环保的反应型抛光光亮剂组合物，其特征在于：所述的络合剂为柠檬酸、酒石酸、苹果酸、葡萄糖酸、羟基乙酸、羟基丙酸、巯基乙酸、乙二胺四乙酸、二亚乙基三胺五醋酸、乙基乙二胺三乙酸、二羟乙基甘氨酸、次氮基三乙酸中的至少一种。
5.根据权利要求1所述的环保的反应型抛光光亮剂组合物，其特征在于：所述的表面活性剂为异构醇聚氧乙烯醚、脂肪醇聚氧乙烯醚、脂肪酸聚氧乙烯酯、烷基酚聚氧乙烯醚、聚乙二醇、脂肪胺聚氧乙烯醚、蓖麻油聚氧乙烯醚中的至少一种。
6.根据权利要求1所述的环保的反应型抛光光亮剂组合物，其特征在于：所述的光亮剂为植物油酸、油酸、硬脂酸、棕榈酸、肉豆蔻酸、蓖麻油酸、椰子油酸、妥尔油酸、大豆油酸、松香酸中的至少一种。
7.根据权利要求1所述的环保的反应型抛光光亮剂组合物，其特征在于：所述的增稠剂为过乙基纤维素、甲基纤维素、羧甲基纤维素钠、羟乙基纤维素、羟丙基甲基纤维素、黄原酸、阿拉伯胶、卡拉胶中的至少一种。
8.根据权利要求1所述的环保的反应型抛光光亮剂组合物，其特征在于：所述的缓蚀剂为尿素、硫脲、甲基苯并三氮唑、苯并三氮唑、2-苯基咪唑啉、2-巯基苯并噻唑、三氮唑、5-苯基四氮唑、8-羟基喹啉、丁炔二醇、丙炔醇、乌洛托品、五水偏硅酸钠、钨酸钠、钼酸钠中的至少一种；
所述的酸洗剂为硫酸氢钠、磷酸、辛基磷酸、甲基磺酸、氨基磺酸中的一种。
9.权利要求1-8任一项所述的环保的反应型抛光光亮剂组合物的制备方法，其特征在于：包括以下步骤：
1)将抛光剂和质量百分比40％-60％的水混合搅拌均匀；
2)加入醇胺、表面活性剂、光亮剂搅拌均匀，加热到50℃-60℃并反应20-40分钟；
3)停止加热，最后加入增稠剂、络合剂、缓蚀剂、酸洗剂和剩余的水，混合搅拌至体系均匀，样品呈现微黄粘稠液体，获得环保的反应型抛光光亮剂。
10.权利要求1-8任一项所述的环保的反应型抛光光亮剂组合物的应用，其特征在于：所述抛光光亮剂作为对不锈钢件、钢铁件、铜件金属基材进行表面抛光的光亮剂。