CN110122955A - A kind of self-adhering-type hot melt lining cloth - Google Patents
A kind of self-adhering-type hot melt lining cloth Download PDFInfo
- Publication number
- CN110122955A CN110122955A CN201910433152.3A CN201910433152A CN110122955A CN 110122955 A CN110122955 A CN 110122955A CN 201910433152 A CN201910433152 A CN 201910433152A CN 110122955 A CN110122955 A CN 110122955A
- Authority
- CN
- China
- Prior art keywords
- hot melt
- self
- adhering
- lining cloth
- melt adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention provides a kind of self-adhering-type hot melt lining cloths.The self-adhering-type hot melt lining cloth includes base fabric and multiple hot melt adhesive tablets, multiple self-adhesion micelles；Wherein, the hot melt adhesive tablet distributing binder that is scattered is fixed in base fabric, and each hot melt adhesive tablet is far from the self-adhesion micelle that is adhesively fixed on the surface of base fabric；The partial size of self-adhesion micelle is 0.1mm-1.2mm, and the partial size of hot melt adhesive tablet is 0.1mm-1.2mm, and in terms of the gross area of base fabric, the bond area of hot melt adhesive tablet and base fabric is 20%-80%.The self-adhering-type hot melt lining cloth, which can directly heat to glue, to scald on fabric, needs not move through pre- boiling hot process, saves largely manually, can be improved production efficiency.
Description
Technical field
The present invention relates to a kind of lining cloth more particularly to a kind of heat molten type lining cloth of self-adhesion, belong to textile technology field.
Background technique
Currently, in the production process of ready-made clothes, for the needs for realizing moulding and appearance, often in the superior and the subordinate of ready-made clothes
The lining cloth of hot melt built at the wormiam bones such as neck, placket, button and cuff (Suture portions).
The lining cloth generally includes two processes, i.e., operator use by hand iron or positioning device to hot melt lining cloth and at
Clothing cut-parts carry out pre- boiling hot (claiming pre- scald afterwards), make the hot melt glue layer substance on hot melt lining cloth temporary melting, temporary adhesion is fixed
In the correct position of outer fabric panel, forming temporarily viscous complex (prevents lining cloth and outer fabric panel to be mutually displaced before entering bonder
And influence quality and appearance)；Then behaviour is a worker to be placed in be sent on the cloth feeding curtain of bonder by temporary viscous complex and glue
Hot pressing is carried out in conjunction machine, so that hot melt lining cloth and ready-made clothes outer fabric panel are permanently bonded together and (machine were claimed to bond afterwards).
Since ready-made clothes is fallen, shirt portion position component is more, and in order to realize the bonding of lining cloth and fabric, clothing factory usually needs to expend
Largely manually carry out operation processing.
Summary of the invention
In order to solve the above-mentioned technical problem, the purpose of the present invention is to provide one kind can directly heat viscous scald on fabric
Lining cloth, which needs not move through pre- boiling hot process, saves a large amount of artificial, can be improved production efficiency.
In order to achieve the above technical purposes, present invention firstly provides a kind of self-adhering-type hot melt lining cloth, self-adhering-type hot melts
Lining cloth includes base fabric and multiple hot melt adhesive tablets, multiple self-adhesion micelles；Wherein, the hot melt adhesive tablet distributing binder that is scattered is fixed on base fabric
On, each hot melt adhesive tablet is far from the self-adhesion micelle that is adhesively fixed on the surface of base fabric；The partial size of self-adhesion micelle is 0.1mm-
The partial size of 1.2mm, hot melt adhesive tablet are 0.1mm-1.2mm, and in terms of the gross area of base fabric, the bond area of hot melt adhesive tablet and base fabric is
20%-80%.
Self-adhering-type hot melt lining cloth of the invention passes through the self-adhesion micelle of specified particle diameter and the hot melt adhesive tablet of specified particle diameter, so that
The self-adhering-type hot melt lining cloth does not need pre- ironing process, can temporarily stick on fabric at room temperature, be torn off when needing and stick at fabric again
Correct position.Self-adhesion micelle can before hot melt temporarily with fabric bond, hot melt adhesive tablet can in the molten state with fabric
Bonding.That is, hot melt glues before scalding, self-adhesion micelle plays a major role, and hot melt adhesive tablet is not had an effect, directly by self-adhering-type fusible interlining
Cloth pressing is fixed on fabric, to prevent lining cloth and fabric to be displaced before entering bonder；When carrying out heating viscous scald, hot melt
Micelle works, and self-adhesion micelle is not had an effect, and is permanently bonded to self-adhering-type hot melt lining cloth on fabric by bonder.
The partial size of micelle in the present invention refers to that it is parallel to the diameter of the maximum cross-section of base fabric.
In a specific embodiment of the invention, hot melt adhesive tablet and self-adhesion micelle are correspondingly arranged, each hot melt adhesive tablet
One self-adhesion micelle of corresponding distribution on surface.
Self-adhering-type hot melt lining cloth of the invention, multiple self-adhesion particle size of the gel can be essentially identical or different；Multiple hot melt adhesive tablets
Size can be essentially identical or different.
In a specific embodiment of the invention, hot melt adhesive tablet is evenly spaced apart to be distributed in base fabric, adjacent hot melt adhesive
0.1mm-1.2mm is divided between grain.
Specifically, the interval of adjacent hot melt adhesive tablet can be 0.12mm, 0.15mm, 0.3mm, 0.6mm, 0.9mm etc..
In a specific embodiment of the invention, the partial size of self-adhesion micelle can for 0.12mm, 0.15mm, 0.3mm,
0.6mm, 0.9mm etc..
In a specific embodiment of the invention, the partial size of hot melt adhesive tablet can for 0.12mm, 0.15mm, 0.3mm,
0.6mm, 0.9mm etc..
In a specific embodiment of the invention, the volume of self-adhesion micelle account for self-adhesion micelle and hot melt adhesive tablet volume it
The 5%-70% of sum.For example, the volume of self-adhesion micelle account for the sum of volume of self-adhesion micelle and hot melt adhesive tablet 10%, 15%,
20%, 50%, 60%, 65% etc..
In a specific embodiment of the invention, the volume of self-adhesion micelle and the volume ratio of hot melt adhesive tablet are 5-70:30-
95。
Self-adhering-type hot melt lining cloth of the invention can be more advantageous to realization certainly under the premise of the adhesive strength for guaranteeing to need
Viscose glue grain and hot melt adhesive tablet freely remove.
In a specific embodiment of the invention, in terms of the gross area of base fabric, the bonding of hot melt adhesive tablet and self-adhesion micelle
The gross area is 15%-80%.
In a specific embodiment of the invention, self-adhesion micelle can be coated in a manner of powder point, slurry point.Into one
Step ground, in terms of the gross area of base fabric, the coating weight of self-adhesion micelle is 0.5g/sq.m-30g/sq.m (sq.m: square metre).For example,
The coating weight of self-adhesion micelle can for 0.8g/sq.m, 8g/sq.m, 10g/sq.m, 15g/sq.m, 0.8g/sq.m, 20g/sq.m,
25g/sq.m etc..
In a specific embodiment of the invention, hot melt adhesive tablet can be coated in a manner of powder point, slurry point.Into one
Step ground, in terms of the gross area of base fabric, the coating weight of hot melt adhesive tablet is 3g/sq.m-40g/sq.m.For example, the coating of self-adhesion micelle
Amount can be 8g/sq.m, 10g/sq.m, 15g/sq.m, 0.8g/sq.m, 20g/sq.m, 25g/sq.m, 30g/sq.m etc..
In a specific embodiment of the invention, the raw material of the hot melt adhesive tablet used can be thermoplastic resin；Into one
Step ground, the raw material of the hot melt adhesive tablet used is one or more of polyethylene, polyvinyl chloride, polyester, polyurethane, polyamide
Combination.
In a specific embodiment of the invention, the hot melt adhesive tablet that uses can be the hot melt adhesive tablet that can remove.Into one
Step ground, the raw material that can remove hot melt adhesive tablet can be polyvinyl alcohol.
Self-adhering-type hot melt lining cloth of the invention, using when can remove hot melt adhesive tablet, hot melt adhesive tablet washing can be removed.It can be with
After ready-made clothes production is complete, factory arranges to remove when ready-made clothes washing process, can also be in the water-washing process after consumer wears
It removes, and then obtains special ready-made clothes effect.
In a specific embodiment of the invention, the raw material of the self-adhesion micelle used for synthetic resin, synthetic rubber or
Natural resin.
Further, the self-adhesion micelle used is acrylate rubber or acrylate resin.
In a specific embodiment of the invention, base fabric can use tatting base fabric, Weft knitting base fabric, warp knit inlaid thread
Base fabric or non-woven base cloth.
In a specific embodiment of the invention, which further includes release film or release paper.Wherein,
Release paper or release film primarily serve the effect of protection self-adhering-type hot melt lining cloth, soil resistant.
Further, release film or release paper be located at self-adhesive particle shape at layer surface.
The grammes per square metre of self-adhering-type hot melt lining cloth of the invention is 10g/sq.m-300g/sq.m.
After treatment, the adhesive strength under 5cm width is 3N-30N to self-adhering-type hot melt lining cloth of the invention.
In a specific embodiment of the invention, processing can be handled using pressing.Wherein, the temperature of pressing is 60
DEG C -200 DEG C, the pressure of pressing is 0.01kgf/cm2-10kgf/cm2, the time of pressing is 1s-40s.
In a specific embodiment of the invention, processing can use ultrasonication.Wherein, the frequency of ultrasonic treatment
For 20KHz-120KHz, the time of ultrasonic treatment is 0.01s-10s.
In a specific embodiment of the invention, processing can be handled using hot wind.Wherein, the temperature of hot wind processing is
60 DEG C -300 DEG C, the time of hot wind processing is 0.01s-120s, and the pressure of hot wind processing is 0.01kgf/cm2-10kgf/cm2。
In the preparation, self-adhesion micelle can be coated self-adhering-type hot melt lining cloth of the invention in a manner of powder point, slurry point；
Hot melt adhesive tablet can be coated in a manner of powder point, slurry point.
Self-adhesion micelle in self-adhering-type hot melt lining cloth of the invention does not need specially treated, and finger pressing can temporarily and face
Material bonding, hot melt adhesive tablet can be bonded with fabric in the molten state.Self-adhering-type hot melt lining cloth of the invention need to only be pressed on
The correct position of fabric directly crosses machine bonding, saves pre- boiling hot process, saves largely manually, can greatly mention
High efficiency.
Self-adhering-type hot melt lining cloth of the invention can be sticked at temporarily on fabric at room temperature, be torn off when needing and sticked at fabric again
Correct position, tearing stickup for 2-10 times does not influence its adherence.
Detailed description of the invention
Fig. 1 is a structural schematic diagram of the self-adhering-type hot melt lining cloth of the embodiment of the present invention；
Fig. 2 is another structural schematic diagram of the self-adhering-type hot melt lining cloth of the embodiment of the present invention.
Main Reference symbol description:
1 Weft knitting base fabric, 21 hot melt adhesive tablet, 31 self-adhesion micelle, 4 release film
Specific embodiment
In order to which technical characteristic of the invention, purpose and beneficial effect are more clearly understood, now to skill of the invention
Art scheme carries out described further below, but should not be understood as that limiting the scope of the invention.
Embodiment 1
A kind of self-adhering-type hot melt Weft knitting lining cloth is present embodiments provided, includes needle with structure as shown in Figure 1
Weft-knitted base fabric 1 is knitted, hot melt adhesive tablet 21 (polyethylene, partial size 0.5mm), Mei Gere are intervally distributed in Weft knitting base fabric 1
Melten gel grain 21 is correspondingly arranged a self-adhesion micelle 31 (acrylate, partial size 0.5mm) wherein, the layout pitch of hot melt adhesive tablet 21
For 0.5mm.The coating weight of hot melt adhesive tablet is 25g/sq.m.The volume of self-adhesion micelle accounts for self-adhesion micelle and hot melt adhesive tablet total volume
10%.The self-adhesive glue layer that self-adhesion micelle 31 is formed, hot melt adhesive tablet 21 form hot melt adhesive layer, and self-adhering-type hot melt tatting lining cloth may be used also
Comprising one layer of release film 4, as shown in Figure 2.When processing with outer fabric panel, release film 4 is torn, so that self-adhesive glue layer be allowed to connect with fabric
Touching bonding.
Embodiment 2
The present embodiment has carried out performance test to the self-adhering-type hot melt Weft knitting lining cloth of embodiment 1, as a result such as 1 institute of table
Show.
Wherein, fabric OC80A80A-19B684DK, 150 × 76,80/2 × 80/2 choice refreshments Oxford are spun, white；Lining cloth is such as
Shown in table 1, density, yarn count are respectively 50 × 50,20 × 20；Be denoted as self-adhering-type hot melt adhesive Weft knitting lining cloth EX0842-ZL and
EX1253-ZL；
When processing, bonding processing is carried out using flat hot press, processing conditions is 165 DEG C, 12S, 3.5kgf/sq.cm,
10cm × 5cm (long × wide) sample is taken to carry out peel strength test.
For comparison, choose simple EX0842 and EX1253 as lining cloth, using identical fabric and binding appts and
Identical bond condition prepares sample, and is tested, data such as table 1.
Table 1
In table 1 statistics indicate that, under equal conditions, the peel strength of lining cloth EX0842-ZL, EX1253-ZL of embodiment 1
It is held essentially constant.But production efficiency can get a promotion, as shown in table 2.
The comparison of 2 production efficiency of table
In table 2 statistics indicate that, on the basis of keeping line balancing, using self-adhering-type hot melt lining cloth of the invention, one
Production efficiency can obtain 50% or more promotion.
Above embodiments explanation, self-adhering-type hot melt lining cloth of the invention, the self-adhesion when being bonded with outer fabric panel, on lining cloth
Micelle need to only press can be by lining cloth and outer fabric panel temporary adhesion, and the position of such as bonding is not correct enough, can also easily mutually
Removing, put in correct position afterwards pressing again can temporary adhesion formed complex, then by this complex be sent into bonder into
Row pressing, to form permanent adhesive body；And common hot melt lining cloth is needed before permanent adhesive using iron or positioning device
Pre- scald is carried out to lining cloth and ready-made clothes cut-parts.Therefore, self-adhering-type hot melt lining cloth of the invention saves pre- boiling hot process, saves a large amount of
Manually, production efficiency is greatly improved.
Claims (10)
1. a kind of self-adhering-type hot melt lining cloth, which is characterized in that the self-adhering-type hot melt lining cloth includes base fabric and multiple hot melt adhesive tablets, more
A self-adhesion micelle；Wherein, the hot melt adhesive tablet distributing binder that is scattered is fixed in base fabric, and each hot melt adhesive tablet is far from the surface of base fabric
Be adhesively fixed a self-adhesion micelle；The partial size of the self-adhesion micelle is 0.1mm-1.2mm, and the partial size of the hot melt adhesive tablet is
0.1mm-1.2mm, in terms of the gross area of the base fabric, the bond area of hot melt adhesive tablet and base fabric is 20%-80%.
2. self-adhering-type hot melt lining cloth according to claim 1, which is characterized in that the hot melt adhesive tablet is evenly spaced apart to be distributed
In base fabric, 0.1mm-1.2mm is divided between adjacent hot melt adhesive tablet.
3. self-adhering-type hot melt lining cloth according to claim 1, which is characterized in that the volume and hot melt adhesive of the self-adhesion micelle
The volume ratio of grain is 5-70:30-95.
4. self-adhering-type hot melt lining cloth according to claim 1, which is characterized in that in terms of the gross area of the base fabric, hot melt
The bonding gross area of micelle and self-adhesion micelle is 15%-80%.
5. self-adhering-type hot melt lining cloth according to claim 1, which is characterized in that the self-adhering-type hot melt lining cloth further includes release
Film or release paper, the release film or release paper are located at the surface of the self-adhesive glue layer.
6. self-adhering-type hot melt lining cloth according to claim 1, which is characterized in that the hot melt adhesive tablet is that can remove hot melt adhesive
Grain；
Preferably, the raw material for removing hot melt adhesive tablet is polyvinyl alcohol.
7. self-adhering-type hot melt lining cloth according to claim 1, which is characterized in that the raw material of the hot melt adhesive tablet is poly- second
The combination of one or more of alkene, polyvinyl chloride, polyester, polyurethane, polyamide.
8. self-adhering-type hot melt lining cloth according to claim 1, which is characterized in that the raw material of the self-adhesion micelle is synthesis tree
Rouge, synthetic rubber or natural resin；
Preferably, the raw material of the self-adhesion micelle is acrylate rubber or acrylate resin.
9. self-adhering-type hot melt lining cloth according to claim 1, which is characterized in that the base fabric is tatting base fabric, knitting latitude
Compile base fabric, warp knit inlaid thread base fabric or non-woven base cloth.
10. -9 described in any item self-adhering-type hot melt lining cloths according to claim 1, which is characterized in that the self-adhering-type hot melt lining cloth
Grammes per square metre be 5g/sq.m-300g/sq.m.