CN110107053A - A kind of floor and preparation method thereof with crackle - Google Patents
A kind of floor and preparation method thereof with crackle Download PDFInfo
- Publication number
- CN110107053A CN110107053A CN201910431935.8A CN201910431935A CN110107053A CN 110107053 A CN110107053 A CN 110107053A CN 201910431935 A CN201910431935 A CN 201910431935A CN 110107053 A CN110107053 A CN 110107053A
- Authority
- CN
- China
- Prior art keywords
- paint
- layer
- crackle
- pattern
- transparent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of floor and preparation method thereof with crackle, including substrate layer have pattern layer on substrate layer, and pattern layer, which is equipped with, splits paint layer, and splitting has crackle or crack on paint layer.The floor with crackle can enrich floor pattern, enhancing visual impact.
Description
Technical field:
The present invention relates to floor fields, are especially a kind of floor and preparation method thereof with crackle.
Background technique:
It floor is made using plastic material, to replace natural timber, reduces the destruction to money original naturally, be plastics now
The trend of panel products exploitation.Requirement of the existing floor to decoration is higher and higher, and the pattern printed on floor is itself ink
Reflection, lack the reflection of other elements, how to enrich the vision of pattern on floor and enhance the impact force of vision, at needing
It solves the problems, such as.
Summary of the invention:
The tool that the technical problem to be solved by the invention is to provide one kind can enrich floor pattern, enhances visual impact
There is the floor of crackle.
The technical solution of the invention is as follows, provides a kind of floor with crackle, including substrate layer, has on substrate layer
Pattern layer, pattern layer, which is equipped with, splits paint layer, and splitting has crackle or crack on paint layer.
Preferably, splitting paint layer equipped with transparent protective layer.
Preferably, splitting paint layer is that plane lacquer painting layer or cracking with crackle have crack, in the paint of upper and lower relief fabric
Surface layer.
Preferably, it is completely corresponding or local corresponding with the lines of pattern layer to split paint layer.
Preferably, splitting paint layer and the lines of pattern layer is not corresponding.
Preferably, pattern layer is any one of printing pattern layer, the figuratum film of tool, pure color paint layer, pure color film layer.
Preferably, substrate layer be one of PVC substrate, pet substrate, PP substrate, magnesium substrate, pressure plare and plank or
It is several to be laminated.
Preferably, splitting in paint layer containing pearl powder or light piece with decorative effect.,
Further, at least one layer of paint layer is split, when splitting paint layer with multilayer, the see-through of different colours is selected to split
Paint layer, which stacks gradually, is presented two or more color effects.Different in width or length can be also set in splitting for different colours on paint layer
Crackle, highlight visual effect.
The present invention also provides a kind of preparation methods on floor with crackle, include the following steps, the first step, clear up substrate
Layer surface, roller coating plays the UV paint of adhewsive action, coating weight 10-15g/m on substrate layer2, use 150-200mj/cm2Solidification
Energy is solidified；Second step paints the UV paint that roller coating again plays a transition role, coating weight 8-10g/m in the UV of attachment2,
Use 50-70mj/cm2Solidification energy solidified, third step paints print pattern, ink consumption in the UV to play a transition role
4-8g/m2, use 100-150mj/cm2Solidification energy solidified；4th step, showering transparent crack priming paint, thickness on pattern
0.2-2.0mm is dry；5th step prints transparent crack finishing coat, transparent crack finishing coat and pattern to flower on transparent crack priming paint
Lines it is corresponding so that transparent crack priming paint cracks to flower；6th step is painted in transparent crack finishing coat surface spraying UV,
Curing molding.
Alternatively, PVC, mountain flour, stabilizer, lubricant are stirred by the first step in proportion, squeezed out by screw extruder,
Substrate layer is made；Second step mats formation substrate layer and the figuratum film of tool cut out in iron pan, is pressed with hot pressing press, temperature
120-150 DEG C, pressure 3-6MPA of degree, then it is cooling with cold pressing press, 20-40 DEG C of temperature, pressure 4-10MPA；Third step, in pattern
There is the UV of attached function to paint for upper roller coating, coating weight 10-15g/m2, use 150-200mj/cm2Solidification energy solidified；
4th step paints showering transparent crack priming paint in the UV of attachment, and thickness 0.2-2.0mm is dry；5th step, at transparent crack bottom
It paints and transparent crack finishing coat is printed to flower, transparent crack finishing coat is corresponding with the lines of pattern, so that transparent crack priming paint is to flower
Place cracks；6th step is in transparent crack finishing coat surface spraying UV paint, curing molding.
Or PVC, mountain flour, stabilization, lubricant are stirred in proportion, are squeezed out by screw extruder by the first step,
Substrate layer is made；Second step mats formation substrate layer and the figuratum film of tool cut out in iron pan, is pressed with hot pressing press, temperature
120-150 DEG C, pressure 3-6MPA of degree, then it is cooling with cold pressing press, 20-40 DEG C of temperature, pressure 4-10MPA；Third step, in pattern
There is the UV of attached function to paint for upper roller coating, coating weight 10-15g/m2, use 150-200mj/cm2Solidification energy solidified；
4th step paints showering transparent crack paint, thickness 0.2-2.0mm, 40-50 DEG C of natural cracking in the UV of attachment；5th step, in table
Face sprays UV paint, curing molding.
It is also possible to the first step, PET, mountain flour, stabilization, lubricant is stirred in proportion, is squeezed by screw extruder
Out, substrate layer is made；Second step has the pure color paint of attached function, dry solidification in substrate layer surface roller coating；Third step, pure
Showering pure color crackle paint on colored paint, thickness 0.2-2.0mm, 40-50 DEG C of natural cracking；4th step, in surface spraying UV paint, solidification
Molding.
Using after above scheme compared with prior art, the invention has the following advantages that by the way that crackle is arranged on floor,
The vision of pattern and enhance the impact force of vision on abundant floor.
Detailed description of the invention:
Fig. 1 is the cross-sectional view of the embodiment of the present invention 1.
Fig. 2 is the effect diagram of the embodiment of the present invention 1.
Fig. 3 is the cross-sectional view of the embodiment of the present invention 2.
Fig. 4 is the cross-sectional view of the embodiment of the present invention 3.
Fig. 5 is the effect diagram of the embodiment of the present invention 3.
The effect diagram of the position Fig. 6 the embodiment of the present invention 4.
Specific embodiment:
With regard to specific embodiment, the invention will be further described with reference to the accompanying drawing:
Embodiment 1
As illustrated in fig. 1 and 2, a kind of floor with crackle, including substrate layer 1 have pattern layer 2, pattern on substrate layer 1
Layer 2, which is equipped with, splits paint layer 3, splits paint layer 3 equipped with transparent protective layer 4.
Wherein, splitting paint layer 3 is the plane lacquer painting layer with crackle, splits that paint layer 3 and the lines of pattern layer 2 be completely corresponding or office
Portion is corresponding, and pattern layer 2 is printing pattern layer and the pattern for forming printing, and substrate layer 1 is PVC substrate, pet substrate, PP substrate, magnesium
Any one of substrate, pressure plare and plank, transparent protective layer 4 can be UV paint or PUR coating.And for vision effect
Fruit splits the pearl powder or light piece that can be also had additional in paint layer with decorative effect.It is one layer that paint layer is split in the present embodiment, when splitting
When paint layer has multilayer, the paint layer that splits that different colours can be selected stacks gradually the two or more color effects of presentation, can also be not
Setting different in width or the crackle of length on paint layer are split with color, highlights visual effect.
Its specific preparation method is as follows, includes the following steps, the first step, clears up substrate layer surface, the roller coating on substrate layer
Play the UV paint of adhewsive action, coating weight 10-15g/m2, use 150-200mj/cm2Solidification energy solidified；Second step,
The UV of attachment paints the UV paint that roller coating again plays a transition role, coating weight 8-10g/m2, use 50-70mj/cm2Solidification energy
Solidified, third step, paints print pattern, ink consumption 4-8g/m in the UV to play a transition role2, use 100-150mj/cm2's
Solidification energy is solidified；4th step, the showering transparent crack priming paint on pattern, thickness 0.2-2.0mm are dry；5th step,
Transparent crack finishing coat is printed to flower on transparent crack priming paint, transparent crack finishing coat is corresponding with the lines of pattern, so that transparent crack
Priming paint cracks to flower；6th step is in transparent crack finishing coat surface spraying UV paint, curing molding.Among these, transparent to split
Line priming paint and transparent crack finishing coat are nitro crack paint or UV crackle paint, pass through shape after crackle priming paint and crackle finishing coat haptoreaction
At crackle, that is to say, that after showering transparent crack priming paint in pattern layer, according to the lines of the pattern of pattern layer in transparent crack
Transparent crack finishing coat is printed on priming paint, is realized to flower effect, saturating after then transparent crack priming paint and transparent crack finishing coat react
Crackle is formed on bright crackle priming paint, the depth of crackle is 0.1-1.5mm.Certainly, the coating of transparent crack priming paint is other than showering,
Coating method is also possible to roller coating or spraying.
In addition, substrate layer can be single or multi-layer structure, so that different soft and hard degree be presented according to soft or hard needs.
As the embodiment 2 for improving formation
As shown in figure 3, a kind of floor with crackle, including substrate layer 1, have pattern layer 2, pattern layer 2 on substrate layer 1
It is equipped with and splits paint layer 3, split paint layer 3 equipped with transparent protective layer 4.Wherein, splitting paint layer is the plane lacquer painting layer with crackle, splits paint
Layer is completely corresponding or local corresponding with the lines of pattern layer, and pattern layer is to have figuratum film, and substrate layer is PVC substrate, transparent
Protective layer is UV paint.And for visual effect, split in paint layer containing pearl powder or light piece with decorative effect.Further
, split paint layer with two layers or more, split for two layers paint layer select different colours split paint layer stack gradually present it is two or more
Color effects.Also visual effect can be highlighted in the crackle for splitting setting different in width on paint layer of different colours.
Preparation method is as follows, and the first step is stirred PVC, mountain flour, stabilizer, lubricant in 100:25:3:2 ratio mixed
It closes, is squeezed out by screw extruder, PVC base layer is made；Second step mats formation substrate layer and the figuratum film of tool cut out
It in iron pan, is pressed with hot pressing press, 120-150 DEG C of temperature, pressure 3-6MPA, then cooling with cold pressing press, 20-40 DEG C of temperature,
Pressure 4-10MPA；Third step, there is the UV of attached function to paint for roller coating on pattern, coating weight 10-15g/m2, use 150-
200mj/cm2Solidification energy solidified；4th step paints showering transparent crack priming paint, thickness 0.2- in the UV of attachment
2.0mm is dry；5th step prints transparent crack finishing coat, the line of transparent crack finishing coat and pattern to flower on transparent crack priming paint
Road is corresponding, so that transparent crack priming paint cracks to flower, for more preferable effect, and the transparent crack bottom that is coated in pattern layer
Paint and the transparent crack finishing coat printed to flower can realize transparent crack finishing coat on transparent crack priming paint by the control of temperature
The lines of formation cracks to form crackle or crack, width and deep-controlled in 0.1-1.5mm；6th step is in transparent crack finishing coat
Surface sprays UV paint, curing molding.
As an improvement, paint layer can be split with two layers different colours by splitting paint layer, and selects and see-through split paint layer without limiting
Paint layer is split to be transparent.
As another embodiment 3
As illustrated in figures 4-5, a kind of floor with crackle, including substrate layer 1, with having figuratum film on substrate layer 1
2, roller coating has had the UV of adhewsive action to paint on film 2, and the UV of adhewsive action paints that showering is transparent to split paint layer 3, and transparent split sets on paint layer 3
There is the UV to shield to paint 4.The transparent paint layer that splits is transparent crack paint layer of the cracking at crack.The depth in crack is 0.1-
1.5mm, width 0.1-1.5mm.And for visual effect, split in paint layer containing pearl powder or light with decorative effect
Piece.Further, split paint layer with two layers, split for two layers paint layer select different colours split paint layer stack gradually present it is two or more
Color effects.
Preparation method is as follows, the first step, and by PVC, mountain flour, stabilization, lubricant, 100:25:3:2 is stirred in proportion, leads to
Screw extruder extrusion is crossed, substrate layer is made；Second step mats formation substrate layer and the figuratum film of tool cut out in iron pan,
It is pressed with hot pressing press, 120-150 DEG C of temperature, pressure 3-6MPA, then cooling with cold pressing press, 20-40 DEG C of temperature, pressure 4-
10MPA；Third step, there is the UV of attached function to paint for roller coating on pattern, coating weight 10-15g/m2, use 150-200mj/cm2
Solidification energy solidified；4th step paints showering transparent crack paint in the UV of attachment, thickness 0.2-2.0mm, and 40-50 DEG C
Natural cracking；5th step, in surface spraying UV paint, curing molding.
Embodiment 4
As shown in fig. 6, a kind of floor with crackle, including PET base material layer, pure color of the roller coating as pattern on substrate layer
Paint, pure color paint showering pure color crackle paint, thickness 0.2-2.0mm, and natural cracking and are formed with crackle 11, and pure color, which is painted, to be coated with
The UV paint to shield.And for visual effect, split in paint layer containing pearl powder or light piece with decorative effect.Into
One step, pure color paint can be set to two layers, and two layers of pure color paint selects different colours so that two different face are presented in cracks
Color effect.
Specific preparation method is as follows, and PET, mountain flour, stabilization, lubricant are stirred in proportion, pass through screw rod by the first step
Extruder squeezes out, and substrate layer is made；Second step has the pure color paint of attached function, dry solidification in substrate layer surface roller coating；Third
Step, paints showering pure color crackle paint, thickness 0.2-2.0mm, 40-50 DEG C of natural cracking in pure color；4th step sprays UV on surface
Paint, curing molding.
By above-mentioned technological means, it may make the pattern on floor more abundant, enhance visual impact, and technique
Simply, facilitate operation.
Only the preferred embodiment of the present invention has been described above, but is not to be construed as limiting the scope of the invention.It is all
The equivalent structure or equivalent flow shift done using description of the invention, be included in scope of patent protection of the invention it
It is interior.
Claims (12)
1. a kind of floor with crackle, including substrate layer, has pattern layer on substrate layer, it is characterised in that: set in pattern layer
Have and split paint layer, splitting has crackle or crack on paint layer.
2. the floor according to claim 1 with crackle, it is characterised in that: split paint layer equipped with transparent protective layer.
3. the floor according to claim 1 with crackle, it is characterised in that: splitting paint layer is the plane lacquer painting with crackle
Layer or cracking have crack, the lacquer painting layer in upper and lower relief fabric.
4. the floor according to claim 1 with crackle, it is characterised in that: split paint layer it is corresponding with the lines of pattern layer or
It does not correspond to.
5. the floor according to claim 1 with crackle, it is characterised in that: split in paint layer and contain with decorative effect
Pearl powder or light piece.
6. the floor according to claim 1 with crackle, it is characterised in that: pattern layer is printing pattern layer, has figure
Any one of the film of case, pure color paint layer, pure color film layer.
7. the floor according to claim 1 with crackle, it is characterised in that: substrate layer is PVC substrate, pet substrate, PP
One or more of substrate, magnesium substrate, pressure plare and plank are laminated.
8. the floor according to claim 1 with crackle, it is characterised in that: at least one layer of paint layer is split, when splitting paint layer
When with multilayer, the see-through paint layer that splits of different colours is selected to stack gradually the two or more color effects of presentation.
9. the preparation method on the floor according to claim 1-3 with crackle, it is characterised in that: including following
Step, the first step clear up substrate layer surface, and roller coating plays the UV paint of adhewsive action, coating weight 10-15g/m on substrate layer2,
Use 150-200mj/cm2Solidification energy solidified；Second step paints the UV that roller coating again plays a transition role in the UV of attachment
Paint, coating weight 8-10g/m2, use 50-70mj/cm2Solidification energy solidified, third step, play a transition role UV paint
Upper print pattern, ink consumption 4-8g/m2, use 100-150mj/cm2Solidification energy solidified；4th step, drenches on pattern
Transparent crack priming paint is applied, thickness 0.2-2.0mm is dry；5th step prints transparent crack face to flower on transparent crack priming paint
Paint, transparent crack finishing coat is corresponding with the lines of pattern, so that transparent crack priming paint cracks to flower；6th step is transparent
Crackle finishing coat surface sprays UV paint, curing molding.
10. the preparation method on the floor according to claim 1-3 with crackle, it is characterised in that: the first step
PVC, mountain flour, stabilizer, lubricant are stirred in proportion, squeezed out by screw extruder, substrate layer is made；Second step,
Substrate layer and the figuratum film of tool cut out are mated formation in iron pan, pressed with hot pressing press, 120-150 DEG C of temperature, pressure 3-
6MPA, then it is cooling with cold pressing press, 20-40 DEG C of temperature, pressure 4-10MPA；Third step, roller coating has attached function on pattern
UV paint, coating weight 10-15g/m2, use 150-200mj/cm2Solidification energy solidified；4th step is painted in the UV of attachment
Upper showering transparent crack priming paint, thickness 0.2-2.0mm are dry；5th step prints transparent crack to flower on transparent crack priming paint
Finishing coat, transparent crack finishing coat is corresponding with the lines of pattern, so that transparent crack priming paint cracks to flower；6th step is saturating
Bright crackle finishing coat surface sprays UV paint, curing molding.
11. the preparation method on the floor according to claim 1 with crackle, it is characterised in that: the first step, by PVC, stone
Powder, stabilization, lubricant are stirred in proportion, are squeezed out by screw extruder, and substrate layer is made；Second step, by substrate layer and
The figuratum film of the tool cut out is mated formation in iron pan, is pressed with hot pressing press, 120-150 DEG C of temperature, pressure 3-6MPA, then with cold
Press press cooling, 20-40 DEG C of temperature, pressure 4-10MPA；Third step, there is the UV of attached function to paint for roller coating on pattern, coating
Amount is 10-15g/m2, use 150-200mj/cm2Solidification energy solidified；It is transparent to paint showering in the UV of attachment for 4th step
Crackle paint, thickness 0.2-2.0mm, 40-50 DEG C of natural cracking；5th step, in surface spraying UV paint, curing molding.
12. the preparation method on the floor according to claim 1 with crackle, it is characterised in that: the first step, by PET, stone
Powder, stabilization, lubricant are stirred in proportion, are squeezed out by screw extruder, and substrate layer is made；Second step, in substrate layer table
Face roller coating has the pure color paint of attached function, dry solidification；Third step paints showering pure color crackle paint, thickness 0.2- in pure color
2.0mm, 40-50 DEG C of natural crackings；4th step, in surface spraying UV paint, curing molding.