CN109747193A - A kind of foam process of rubber pange sole formed - Google Patents
A kind of foam process of rubber pange sole formed Download PDFInfo
- Publication number
- CN109747193A CN109747193A CN201711141418.4A CN201711141418A CN109747193A CN 109747193 A CN109747193 A CN 109747193A CN 201711141418 A CN201711141418 A CN 201711141418A CN 109747193 A CN109747193 A CN 109747193A
- Authority
- CN
- China
- Prior art keywords
- rubber
- sole
- wear
- promotor
- foam process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The foam process of rubber pange sole formed of the invention belongs to the technical field of manufacturing process of rubber-moulding sole.The technique includes being packed into it in mold by certain weight ratio, in certain temperature and time, a kind of expansion type rubber-moulding sole is made in Jing Yici sulfidization molding after hole-forming material and wear-resistant material are kneaded synthetic films is made respectively.Had the characteristics that using sole made of the technique brisk, soft, comfortable and easy to wear.It is light-weight simultaneously, feed consumption is few, simple process, be the new process that a kind of rubber-moulding sole updates.With good Social benefit and economic benefit.
Description
Technical field
The foam process of rubber pange sole formed of the invention belongs to the technical field of manufacturing process of rubber-moulding sole.
Background technique
The manufacture craft of current all kinds of rubber soles takes general sulfidization molding technique, although having one than plastic sole
Fixed elasticity, but due to not by foam process.Therefore, the various leather shoes made of this kind of sole, cloth shoes etc., when wearing
It lacks flexibility, it is still not comfortable enough, there is the feeling of stiff plate foot.Meanwhile feed consumption is more at bottom processed, weight is larger.Especially as
Continuous improvement of people's living standards requires dress higher and higher, the highly desirable production to existing rubber-moulding sole
Technique improves, and a kind of light comfortable rubber pange sole formed by foaming is made.
It is an object of the invention to avoid shortcoming in the prior art, a kind of hair of rubber pange sole formed is provided
Bubble technique is made leather shoes comfortable and easy to wear, cloth shoes etc., meets people couple to produce all kinds of soles brisk, soft, elasticity is good
Wear the new requirement of form and quality.
The foam process of the invention for being characterized by the rubber pange sole formed be include hole-forming material and wear-resistant material difference
Synthesis raw stock, die-filling, vulcanization, the operational sequences such as molding are made in mixing, it is characterised in that:
1) the composition content of hole-forming material is (weight %):
Natural gum 10~20；Reclaimed rubber 45~60；
Resin 1.0~2.5；Zinc oxide 3.0~5.0；Captax 0.5~1.5；Promotor ZM0.3~1.0；Promotor
TT0.03~0.1；Gu horse grand 0.3~1.0；Carbon black 10~20；Clay 5~10；Antioxidant A 0.3~1.0；Stearic acid 0.5~
1.5；Sulphur 1.0~2.0；
2) the composition content of wear-resistant material is (weight %): natural gum 10~20；Reclaimed rubber 35~50；Captax 0.3~
1.0；Promotor ZM0.1~0.3；Promotor TT0.1~0.2；Antioxidant A 0.2~0.4；Zinc oxide 1.0~2.5；Stearic acid
1.5~3.0；Dark substitute 8~15；Machine oil 2~5；Clay 5~15；Precipitated calcium carbonate 3~10；Blowing agent H 0.5~1.2；Little Su
Make a call to 1.0~2.0；Sulphur 0.3~1.0.
The foam process of the rubber pange sole formed is: first by hole-forming material and wear-resistant material by above-mentioned respective formula composition
After ratio prepares, respectively be kneaded synthesis raw stock is made, then, according to hole-forming material: wear-resistant material=1: 3 weight ratio by this two
Kind of raw stock is packed into die for shoe-sole, 130 °~170 DEG C at a temperature of 3~7 minutes of vulcanization after, a sulfidization molding,
The rubber pange sole formed being made of wearing layer and foaming layer is made.
The foam process of rubber pange sole formed of the invention compared with the technique of rubber-moulding sole compare, have
Following advantage:
1, the process employs foaming technique, make manufactured rubber pange sole formed that there is brisk, soft, dress to relax
Suitable, the features such as elasticity is good, when walking, plays buffering health-care effect to each joint of foot especially ankle-joint, to effectively subtract
The feeling of fatigue of Qing Liao foot.
2, the technique keeps manufactured rubber pange sole formed light-weight, materials are few, save due to using foaming technique
Raw material, simple process is easy to spread, has good Social benefit and economic benefit.
It is further described below below in conjunction with foam process of the embodiment to rubber pange sole formed of the invention.It will
After hole-forming material and wear-resistant material are prepared in above-mentioned respective formula composition ratio, it is kneaded synthesis raw stock is made respectively, then, press
According to hole-forming material: wear-resistant material=1: this two kinds of raw stocks are placed in die for shoe-sole by 3 weight ratio, 150 DEG C at a temperature of heat
After five minutes, the rubber pange sole formed being made of wearing layer and foaming layer is made in a sulfidization molding for vulcanization.
Claims (1)
1. a kind of foam process of rubber pange sole formed, including hole-forming material and wear-resistant material are kneaded synthesis raw rubber is made respectively
Piece, die-filling, vulcanization, the operational sequences such as molding, it is characterised in that:
1) the composition content of hole-forming material is (weight %):
Natural gum 10~20；Reclaimed rubber 45~60；
Resin 1.0~2.5；Zinc oxide 3.0~5.0；Captax 0.5~1.5；Promotor ZM0.3~1.0；Promotor TT0.03
~0.1；Gu horse grand 0.3~1.0；Carbon black 10~20；Clay 5~10；Antioxidant A 0.3~1.0；Stearic acid 0.5~1.5；Sulphur
Sulphur 1.0~2.0；
2) the composition content of wear-resistant material is (weight %): natural gum 10~20；Reclaimed rubber 35~50；Captax 0.3~1.0；Promote
Into agent ZM0.1~0.3；Promotor TT0.1~0.2；Antioxidant A 0.2~0.4；Zinc oxide 1.0~2.5；Stearic acid 1.5~
3.0；Dark substitute 8~15；Machine oil 2~5；Clay 5~15；Precipitated calcium carbonate 3~10；Blowing agent H 0.5~1.2；Sodium bicarbonate 1.0
~2.0；Sulphur 0.3~1.0.