CN109653023A - It is a kind of for manufacturing the translucent suction pipe paper and preparation method of translucent suction pipe - Google Patents
It is a kind of for manufacturing the translucent suction pipe paper and preparation method of translucent suction pipe Download PDFInfo
- Publication number
- CN109653023A CN109653023A CN201811473393.2A CN201811473393A CN109653023A CN 109653023 A CN109653023 A CN 109653023A CN 201811473393 A CN201811473393 A CN 201811473393A CN 109653023 A CN109653023 A CN 109653023A
- Authority
- CN
- China
- Prior art keywords
- paper
- suction pipe
- dry
- translucent
- body paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
It is a kind of for manufacturing the translucent suction pipe paper and preparation method of translucent suction pipe, the suction pipe paper includes body paper and oil-repellent, the body paper is translucent body paper or transparent body paper, the compound resin that solid content percentage is 0.1%-25% is glued or be coated on the surface of body paper, and obtains translucent suction pipe paper after dry and UV solidification；It has good transparency, and the status of plastic material can only be used by changing translucent suction pipe.Suction pipe paper surface is coated with UV resin, forms good UV resin layer on body paper surface, encloses the gap on body paper surface, has good impermeabilisation to act on the liquid such as water, improves the resistant to liquids penetrating power of suction pipe paper；And the UV resin of surface coating, can greatly improve the stiffness and hardness of paper, improve the intensity of paper straw in a liquid, improve the anti-softening ability of suction pipe.
Description
Technical field
The present invention relates to a kind of for making the onionskin and preparation method of translucent suction pipe, belongs to packaging material
Field.
Background technique
Suction pipe is mostly plastic material on Vehicles Collected from Market, and the opaque suction pipe in part uses paper material.Suction pipe is mostly disposable
It using, consumer would generally abandon suction pipe after use, and use the suction pipe of plastic material non-degradable under the conditions of nature,
Cause long-term environmental pollution.And paper straw under field conditions (factors) can fast degradation, but paper straw currently on the market is
Opaque suction pipe, translucent or transparent suction pipe can only be using plastic materials difficult to degrade under field conditions (factors).
Summary of the invention
Present invention aims to overcome that the shortcomings of the prior art, providing a kind of can make suction pipe with translucent spy
Property under the conditions of, while there is good biological degradability, prevent the translucent for making of the suction pipe long-term pollution environment abandoned
The onionskin and preparation method of suction pipe.
It is a kind of for manufacturing the translucent suction of translucent suction pipe the purpose of the present invention is what is completed by following technical solution
Pipe paper, the suction pipe paper include body paper and oil-repellent, and the body paper is translucent body paper or transparent body paper, in the table of body paper
The compound resin that solid content percentage is 0.1%-25% is glued or be coated on face, and is obtained after dry and UV solidification semi-transparent
Bright suction pipe paper.
As preferred: the body paper is made of full bleaching softwood pulp, quantitative in 30g/m2-200g/m2Between, thoroughly
Lightness is between 50%-90%, and cobb value is in 30g/m2Below；The compound resin is water-borne UV-curing resin unsaturated polyester (UP)
(UP), one of water urethane acrylate (PUA), water epoxy acrylate (EA) or a variety of.
As preferred: the compound resin is applied to body paper surface using sizing or roll-type, blade coating mode, applies
Glue amount is or coating weight is 1-15g/m2；Curing process is carried out to compound resin using UV solidification equipment after drying.
A method of it being used to prepare translucent suction pipe paper as described above, the preparation method includes the following steps:
A body paper is manufactured paper with pulp: use needlebush pulpboard for raw material, pulpboard is beaten after discongesting completely, and beating degree is 90 ° of SR, to
0.5%(is added in the slurry accomplished fluently in terms of oven dry stock quality) AKD, be uniformly mixed, after the processes such as screening and purifying, mixing
Good paper pulp is uniformly distributed on forming net by head box and forms wet web, and passes through the processes such as squeezing, dry for paper web
It is dry；Wet web be completely dried after quantification of 50g/m2；
The surface b dipping and gluing: the body paper that step 1 is manufactured paper with pulp it is dry to moisture content 10%-20% when, carried out by dipping and gluing disk
Dipping and gluing；Glue application solution in dipping and gluing disk is the UV waterborne polyester acrylate of 2% concentration；Translucent body paper passes through dipping
Sizing disk is laggard to cross size press roller, removes the glue application solution of body paper excess surface；
C is dry and UV solidifies: the body paper after the dipping and gluing of surface, and the drying of page is carried out by drying cylinder, aqueous in page
The solidification of UV resin is carried out when rate is below 10% by UV uv equipment；When into UV curing apparatus, page temperature should be kept
At 75 DEG C or more；Out when UV curing apparatus, page moisture is 6% or so；
Page after d curing process is obtained into pulleying to translucent suction pipe paper；
Suction pipe paper after dry solidification quantifies 52g/m2, top sizing amount is 2g/m2；Transparency is 75%；Cobb value is less than
20g/m2。
A method of it being used to prepare translucent suction pipe paper as described above, the preparation method includes the following steps:
A body paper is manufactured paper with pulp: use needlebush pulpboard for raw material, pulpboard is beaten after discongesting completely, and beating degree is 90 ° of SR, to
0.5%AKD(is added in the slurry accomplished fluently in terms of oven dry stock quality) latex, it is uniformly mixed, after the processes such as screening and purifying, mixes
The paper pulp got togather is uniformly distributed on forming net by head box and forms wet web, and passes through the processes such as squeezing, dry for paper
Width is dry；Wet web be completely dried after quantification of 30g/m2；
B top sizing: the body paper that step 1 is manufactured paper with pulp it is dry to moisture content 10%-15% when, pass through film transfer formula sizing applicator and carry out
Top sizing；Glue application solution is the UV aqueous polyurethane acrylate of 6% concentration；By controlling the pressure of gauge stick, resin added is adjusted
For 1g/m2；
C is dry and UV solidifies: the body paper after the dipping and gluing of surface is dried by hot air drier, heated-air drying temperature
Degree 90 DEG C, be disposed with UV solidification equipment in hot air drier end, when sheet moisture ratio is 8% by UV uv equipment into
The solidification of row UV resin；Out when UV curing apparatus, page moisture is 6% or so；
Page after d curing process is obtained into pulleying to translucent suction pipe paper；
Suction pipe paper after dry solidification quantifies 31g/m2, top sizing amount is 1g/m2；Transparency is 80%；Cobb value is less than
20g/m2。
A method of it being used to prepare translucent suction pipe paper as described above, the preparation method includes the following steps:
A body paper is manufactured paper with pulp: use needlebush pulpboard for raw material, pulpboard is beaten after discongesting completely, and beating degree is 90 ° of SR, to
0.5%AKD(is added in the slurry accomplished fluently in terms of oven dry stock quality) latex, it is uniformly mixed, after the processes such as screening and purifying, mixes
The paper pulp got togather is uniformly distributed on forming net by head box and forms wet web, and passes through the processes such as squeezing, dry for paper
Width is dry；Wet web be completely dried after quantification of 40g/m2；
B coating: when body paper drying to the moisture content 10% that step 1 is manufactured paper with pulp, top sizing is carried out by crossing print roll coating；Sizing
Liquid is the UV aqueous polyurethane acrylate of 5% concentration；
C is dry and UV solidifies: the body paper after the dipping and gluing of surface is dried by hot air drier, heated-air drying temperature
Degree 90 DEG C, be disposed with UV solidification equipment in hot air drier end, when sheet moisture ratio is 8% by UV uv equipment into
The solidification of row UV resin；Out when UV curing apparatus, page moisture is 6% or so；
Page after d curing process is obtained into pulleying to translucent suction pipe paper；
Suction pipe paper after dry solidification quantifies 42g/m2, top sizing amount is 2g/m2；Transparency is 78%；Cobb value is less than
20g/m2。
The suction pipe paper of the present invention for being used to manufacture translucent suction pipe, has good transparency, changes translucent suction
Pipe can only use the status of plastic material.Suction pipe paper surface is coated with UV resin, forms good UV resin layer on body paper surface,
The gap for enclosing body paper surface has good impermeabilisation to act on the liquid such as water, improves the resistant to liquids penetrating power of suction pipe paper.
And the UV resin of surface coating, can greatly improve the stiffness and hardness of paper, improve the intensity of paper straw in a liquid, mention
The anti-softening ability of high suction pipe.
The present invention has good biological degradability with can make suction pipe under the conditions of with translucent characteristic,
The features such as preventing the suction pipe long-term pollution environment abandoned.
Specific embodiment
In order to which the object of the invention, technical solution and advantage is more clearly understood, the present invention is carried out below further detailed
It describes in detail bright.It should be appreciated that described herein, specific examples are only used to explain the present invention, is not intended to limit the present invention.
Of the present invention a kind of for manufacturing the translucent suction pipe paper of translucent suction pipe, the suction pipe paper includes body paper
And oil-repellent, the body paper are translucent body paper or transparent body paper, are glued or are coated with solid content percentage on the surface of body paper
Translucent suction pipe paper is obtained than the compound resin for 0.1%-25%, and after dry and UV solidification.
Body paper of the present invention is made of full bleaching softwood pulp, quantitative in 30g/m2-200g/m2Between, transparency
Between 50%-90%, cobb value is in 30g/m2Below；The compound resin be water-borne UV-curing resin unsaturated polyester (UP) (UP),
One of water urethane acrylate (PUA), water epoxy acrylate (EA) are a variety of.
Compound resin of the present invention is applied to body paper surface using sizing or roll-type, blade coating mode, is glued
Amount is or coating weight is 1-15g/m2；Curing process is carried out to compound resin using UV solidification equipment after drying.
Preparation method of the present invention is described in detail by following examples:
Embodiment 1: it is a kind of for manufacturing the preparation method of the translucent suction pipe paper of translucent suction pipe, include the following steps:
A body paper is manufactured paper with pulp: use needlebush pulpboard for raw material, pulpboard is beaten after discongesting completely, and beating degree is 90 ° of SR, to
0.5%(is added in the slurry accomplished fluently in terms of oven dry stock quality) AKD, be uniformly mixed, after the processes such as screening and purifying, mixing
Good paper pulp is uniformly distributed on forming net by head box and forms wet web, and passes through the processes such as squeezing, dry for paper web
It is dry；Wet web be completely dried after quantification of 50g/m2；
The surface b dipping and gluing: the body paper that step 1 is manufactured paper with pulp it is dry to moisture content 10%-20% when, carried out by dipping and gluing disk
Dipping and gluing.Glue application solution in dipping and gluing disk is the UV waterborne polyester acrylate of 2% concentration；Translucent body paper passes through dipping
Sizing disk is laggard to cross size press roller, removes the glue application solution of body paper excess surface；
C is dry and UV solidifies: the body paper after the dipping and gluing of surface, and the drying of page is carried out by drying cylinder, aqueous in page
The solidification of UV resin is carried out when rate is below 10% by UV uv equipment；When into UV curing apparatus, page temperature should be kept
At 75 DEG C or more；Out when UV curing apparatus, page moisture is 6% or so；
Page after d curing process is obtained into pulleying to translucent suction pipe paper；
Suction pipe paper after dry solidification quantifies 52g/m2, top sizing amount is 2g/m2.Transparency is 75%.Cobb value is less than
20g/m2。
Embodiment 2: it is a kind of for manufacturing the preparation method of the translucent suction pipe paper of translucent suction pipe, include the following steps:
A body paper is manufactured paper with pulp: use needlebush pulpboard for raw material, pulpboard is beaten after discongesting completely, and beating degree is 90 ° of SR, to
0.5%AKD(is added in the slurry accomplished fluently in terms of oven dry stock quality) latex, it is uniformly mixed, after the processes such as screening and purifying, mixes
The paper pulp got togather is uniformly distributed on forming net by head box and forms wet web, and passes through the processes such as squeezing, dry for paper
Width is dry；Wet web be completely dried after quantification of 30g/m2；
B top sizing: the body paper that step 1 is manufactured paper with pulp it is dry to moisture content 10%-15% when, pass through film transfer formula sizing applicator and carry out
Top sizing；Glue application solution is the UV aqueous polyurethane acrylate of 6% concentration；By controlling the pressure of gauge stick, resin added is adjusted
For 1g/m2；
C is dry and UV solidifies: the body paper after the dipping and gluing of surface is dried by hot air drier, heated-air drying temperature
Degree 90 DEG C, be disposed with UV solidification equipment in hot air drier end, when sheet moisture ratio is 8% by UV uv equipment into
The solidification of row UV resin；Out when UV curing apparatus, page moisture is 6% or so；
Page after d curing process is obtained into pulleying to translucent suction pipe paper；
Suction pipe paper after dry solidification quantifies 31g/m2, top sizing amount is 1g/m2.Transparency is 80%.Cobb value is less than
20g/m2
Embodiment 3: it is a kind of for manufacturing the preparation method of the translucent suction pipe paper of translucent suction pipe, include the following steps:
A body paper is manufactured paper with pulp: use needlebush pulpboard for raw material, pulpboard is beaten after discongesting completely, and beating degree is 90 ° of SR, to
0.5%AKD(is added in the slurry accomplished fluently in terms of oven dry stock quality) latex, it is uniformly mixed, after the processes such as screening and purifying, mixes
The paper pulp got togather is uniformly distributed on forming net by head box and forms wet web, and passes through the processes such as squeezing, dry for paper
Width is dry；Wet web be completely dried after quantification of 40g/m2；
B coating: when body paper drying to the moisture content 10% that step 1 is manufactured paper with pulp, top sizing is carried out by crossing print roll coating；Sizing
Liquid is the UV aqueous polyurethane acrylate of 5% concentration；
C is dry and UV solidifies: the body paper after the dipping and gluing of surface is dried by hot air drier, heated-air drying temperature
Degree 90 DEG C, be disposed with UV solidification equipment in hot air drier end, when sheet moisture ratio is 8% by UV uv equipment into
The solidification of row UV resin；Out when UV curing apparatus, page moisture is 6% or so；
Page after d curing process is obtained into pulleying to translucent suction pipe paper；
Suction pipe paper after dry solidification quantifies 42g/m2, top sizing amount is 2g/m2；Transparency is 78%；Cobb value is less than
20g/m2。
Claims (6)
1. a kind of for manufacturing the translucent suction pipe paper of translucent suction pipe, the suction pipe paper includes body paper and oil-repellent,
It is characterized in that the body paper is translucent body paper or transparent body paper, being glued or be coated with solid content percentage on the surface of body paper is
The compound resin of 0.1%-25%, and translucent suction pipe paper is obtained after dry and UV solidification.
2. according to claim 1 for manufacturing the translucent suction pipe paper of translucent suction pipe, it is characterised in that the original
Paper is made of full bleaching softwood pulp, quantitative in 30g/m2-200g/m2Between, between 50%-90%, cobb value exists transparency
30g/m2Below；The compound resin be water-borne UV-curing resin unsaturated polyester (UP) (UP), water urethane acrylate (PUA),
One of water epoxy acrylate (EA) is a variety of.
3. according to claim 1 or 2 for manufacturing the translucent suction pipe paper of translucent suction pipe, it is characterised in that described
Compound resin is applied to body paper surface using sizing or roll-type, blade coating mode, and resin added is or coating weight is 1-15g/
m2；Curing process is carried out to compound resin using UV solidification equipment after drying.
4. a kind of method for being used to prepare the translucent suction pipe paper as described in claims 1 or 2 or 3, it is characterised in that the system
Preparation Method includes the following steps:
A body paper is manufactured paper with pulp: use needlebush pulpboard for raw material, pulpboard is beaten after discongesting completely, and beating degree is 90 ° of SR, to
0.5%(is added in the slurry accomplished fluently in terms of oven dry stock quality) AKD, be uniformly mixed, after the processes such as screening and purifying, mixing
Good paper pulp is uniformly distributed on forming net by head box and forms wet web, and passes through the processes such as squeezing, dry for paper web
It is dry；Wet web be completely dried after quantification of 50g/m2；
The surface b dipping and gluing: the body paper that step 1 is manufactured paper with pulp it is dry to moisture content 10%-20% when, carried out by dipping and gluing disk
Dipping and gluing；Glue application solution in dipping and gluing disk is the UV waterborne polyester acrylate of 2% concentration；Translucent body paper passes through dipping
Sizing disk is laggard to cross size press roller, removes the glue application solution of body paper excess surface；
C is dry and UV solidifies: the body paper after the dipping and gluing of surface, and the drying of page is carried out by drying cylinder, aqueous in page
The solidification of UV resin is carried out when rate is below 10% by UV uv equipment；When into UV curing apparatus, page temperature should be kept
At 75 DEG C or more；Out when UV curing apparatus, page moisture is 6% or so；
Page after d curing process is obtained into pulleying to translucent suction pipe paper；
Suction pipe paper after dry solidification quantifies 52g/m2, top sizing amount is 2g/m2；Transparency is 75%；Cobb value is less than
20g/m2。
5. a kind of method for being used to prepare the translucent suction pipe paper as described in claims 1 or 2 or 3, it is characterised in that the system
Preparation Method includes the following steps:
A body paper is manufactured paper with pulp: use needlebush pulpboard for raw material, pulpboard is beaten after discongesting completely, and beating degree is 90 ° of SR, to
0.5%AKD(is added in the slurry accomplished fluently in terms of oven dry stock quality) latex, it is uniformly mixed, after the processes such as screening and purifying, mixes
The paper pulp got togather is uniformly distributed on forming net by head box and forms wet web, and passes through the processes such as squeezing, dry for paper
Width is dry；Wet web be completely dried after quantification of 30g/m2；
B top sizing: the body paper that step 1 is manufactured paper with pulp it is dry to moisture content 10%-15% when, pass through film transfer formula sizing applicator and carry out
Top sizing；Glue application solution is the UV aqueous polyurethane acrylate of 6% concentration；By controlling the pressure of gauge stick, resin added is adjusted
For 1g/m2；
C is dry and UV solidifies: the body paper after the dipping and gluing of surface is dried by hot air drier, heated-air drying temperature
Degree 90 DEG C, be disposed with UV solidification equipment in hot air drier end, when sheet moisture ratio is 8% by UV uv equipment into
The solidification of row UV resin；Out when UV curing apparatus, page moisture is 6% or so；
Page after d curing process is obtained into pulleying to translucent suction pipe paper；
Suction pipe paper after dry solidification quantifies 31g/m2, top sizing amount is 1g/m2；Transparency is 80%；Cobb value is less than
20g/m2。
6. a kind of method for being used to prepare the translucent suction pipe paper as described in claims 1 or 2 or 3, it is characterised in that the system
Preparation Method includes the following steps:
A body paper is manufactured paper with pulp: use needlebush pulpboard for raw material, pulpboard is beaten after discongesting completely, and beating degree is 90 ° of SR, to
0.5%AKD(is added in the slurry accomplished fluently in terms of oven dry stock quality) latex, it is uniformly mixed, after the processes such as screening and purifying, mixes
The paper pulp got togather is uniformly distributed on forming net by head box and forms wet web, and passes through the processes such as squeezing, dry for paper
Width is dry；Wet web be completely dried after quantification of 40g/m2；
B coating: when body paper drying to the moisture content 10% that step 1 is manufactured paper with pulp, top sizing is carried out by crossing print roll coating；Sizing
Liquid is the UV aqueous polyurethane acrylate of 5% concentration；
C is dry and UV solidifies: the body paper after the dipping and gluing of surface is dried by hot air drier, heated-air drying temperature
Degree 90 DEG C, be disposed with UV solidification equipment in hot air drier end, when sheet moisture ratio is 8% by UV uv equipment into
The solidification of row UV resin；Out when UV curing apparatus, page moisture is 6% or so；
Page after d curing process is obtained into pulleying to translucent suction pipe paper；
Suction pipe paper after dry solidification quantifies 42g/m2, top sizing amount is 2g/m2；Transparency is 78%；Cobb value is less than
20g/m2。