CN109537133A - A kind of decomposable Environment Compatible Textiles and its processing technology - Google Patents
A kind of decomposable Environment Compatible Textiles and its processing technology Download PDFInfo
- Publication number
- CN109537133A CN109537133A CN201811644235.9A CN201811644235A CN109537133A CN 109537133 A CN109537133 A CN 109537133A CN 201811644235 A CN201811644235 A CN 201811644235A CN 109537133 A CN109537133 A CN 109537133A
- Authority
- CN
- China
- Prior art keywords
- fiber
- weft
- warp
- yarn
- soybean
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of decomposable Environment Compatible Textiles, including the warp and weft for mutually working out, the warp is formed by soybean fiber and cotton fiber are blended, the weft is worked out by soybean fiber, bamboo fibre and flax fiber blending, and the percentage of weight shared by the soybean fiber and cotton fiber in the warp is respectively 60%~80% and 40~20%, the percentage of place weight is respectively 40%~60%, 40~30% and 20~10% when soybean fiber, bamboo fibre and flax fiber blending in the weft.The decomposable Environment Compatible Textiles, with natural anti-mould and anti-moth antibacterial effect, in addition there is soybean fiber category degradability aftergrowth azelon, and the preparation process of soybean fiber is all natural pollution-free, not only the decomposability of textile had been improved, but also can guarantee the environmental protection in preparation.
Description
Technical field
The invention belongs to textile processing technical fields, and in particular to a kind of decomposable Environment Compatible Textiles and its processing work
Skill.
Background technique
Textile is textile fabric by a kind of product made of processing weaving, is divided into woven fabric and looped fabric two major classes,
China is one of the country for producing textile earliest in the world, and the main place of production is the ground such as Zhejiang Hangzhou Pu institute, Hebei Qinghe.Weaving
The correct stacking method of product is to be advantageously selected for divulging information, and convenient for fire prevention, full-cotton fabric is preferably placed in draughty place, such as
From door, the place nearest from window, one meter of door is conventional door width, and 6 to 7 volumes put a row, and the 2nd layer of longitudinal direction is laid flat, and quantity must be with
Bottom is identical, and the 3rd layer still laterally lays flat, and quantity is identical, and so on.
Textile uses more and more extensive in people's lives, but in environment increasingly serious today, not only to protect
The comfort that card textile uses, should also reduce pollution in production, convenient for decomposing after the completion of use, to respond ring at this stage
The general trend of events of guarantor.
Summary of the invention
The purpose of the present invention is to provide a kind of decomposable Environment Compatible Textiles and its processing technologys, to solve above-mentioned background
The problem of being proposed in technology.
To achieve the above object, it the invention provides the following technical scheme: a kind of decomposable Environment Compatible Textiles, including is used for
The warp and weft mutually worked out, the warp are formed by soybean fiber and cotton fiber are blended, and the weft is by soybean fiber, bamboo
Fiber and flax fiber blending are worked out, and the percentage of weight shared by the soybean fiber and cotton fiber in the warp is respectively
60%~80% and 40~20%, in the weft when soybean fiber, bamboo fibre and flax fiber blending where weight percentage
Respectively 40%~60%, 40~30% and 20~10%.
Preferably, the warp and weft use plain weave or twill weave.
A kind of processing technology of decomposable Environment Compatible Textiles, comprising the following steps:
S1, preparatory process: soybean fiber and cotton fiber being sent into doubling winder and carries out yarn and forms mixed and warp, will be big
Beans fiber, bamboo fibre and flaxen fiber, which are sent into doubling winder, to carry out yarn and forms mixed and weft；
S2, winding procedure: simultaneously warp and mixed and weft will be mixed obtained in step S1 and is sent into winder both interior progress winders, together
When control groove drum linear speed in 1000~1200m/min, rolling density is 0.35~0.4g/cm3；
S3, warping process: the yarn for obtaining winder in step S2 is subjected to section warping by warping machine, controls warping
The speed of beaming of machine is 330~370m/min, and rolling density is 0.4~0.6g/cm3；
S4, sizing operation: the yarn after the completion of warping is added and is matched based on chemical sizwe PVA and acrylic size
It is that pair is matched in the stock tank of material, and antistatic agent is added with partial denaturation starch, carries out starching, drying is transferred to after the completion of starching
Entering to dry dry-cure in room；
S5, weaving process；Yarn obtained in step S4 is weaved using rapier loom, wherein weaving speed is
170~210r/min；
S6, finishing process；The former fabric that step S5 has been weaved is tested, then the villus on burning-off cloth cover,
It is sent into forming machine and carries out shaping, complete after requiring, packed.
Preferably, in step S1, the preparation before soybean fiber feeding doubling winder is the following steps are included: (1) preparation spinning is former
Liquid；(2) stoste is extruded to form thread from spinneret orifice；(3) stoste thread is frozen into as-spun fibre；(4) as-spun fibre package or
Directly post-processed.
Preferably, it in step S2, to reduce electrostatic phenomenon and broken end, prevents from extending other than yarn, using metal drum.
Preferably, in step S4, temperature control of the slurry groove temperature control at 90 DEG C~100 DEG C, in baking room when starching
At 100 DEG C or less.
Technical effect and advantage of the invention: the decomposable Environment Compatible Textiles and its processing technology, by soybean fiber,
Textile is made in the combination branch of flaxen fiber, cotton fiber and bamboo fibre, is natural fiber by bamboo fibre, cotton fiber and flaxen fiber,
It can be extracted according in various plants, belong to green product with the feature of environmental protection, and imitate with natural anti-mould and anti-moth antibacterial
In addition fruit has soybean fiber category degradability aftergrowth azelon, and the preparation process of soybean fiber is all natural pollution-free,
Not only the decomposability of textile had been improved, but also can guarantee the environmental protection in preparation, sizing operation is in addition selected before weaving, moreover it is possible to
It is enough to improve whole antistatic effect, and weaving is made to be more easier to carry out.
Specific embodiment
Below in conjunction with the contents of the present invention, the technical solution in the present invention is clearly and completely described, it is clear that
Described content is only a part of content of the present invention, rather than whole contents.Based on the content in the present invention, this field
Those of ordinary skill's every other content obtained without making creative work belongs to what the present invention protected
Range.
Embodiment 1
It is described including the warp and weft for mutually working out the present invention provides a kind of decomposable Environment Compatible Textiles
Warp is formed by soybean fiber and cotton fiber are blended, and the weft is worked out by soybean fiber, bamboo fibre and flax fiber blending,
And the percentage of weight shared by the soybean fiber and cotton fiber in the warp is respectively 60%% and 40%, it is big in the weft
The percentage of weight is respectively 40%%, 40% and 20% where when beans fiber, bamboo fibre and flax fiber blending.
Specifically, the warp and weft use plain weave or twill weave.
A kind of processing technology of decomposable Environment Compatible Textiles, comprising the following steps:
S1, preparatory process: soybean fiber and cotton fiber being sent into doubling winder and carries out yarn and forms mixed and warp, will be big
Beans fiber, bamboo fibre and flaxen fiber, which are sent into doubling winder, to carry out yarn and forms mixed and weft；
S2, winding procedure: simultaneously warp and mixed and weft will be mixed obtained in step S1 and is sent into winder both interior progress winders, together
When control groove drum linear speed in 1000m/min, rolling density 0.35g/cm3；
S3, warping process: the yarn for obtaining winder in step S2 is subjected to section warping by warping machine, controls warping
The speed of beaming of machine is 330m/min, rolling density 0.4g/cm3；
S4, sizing operation: the yarn after the completion of warping is added and is matched based on chemical sizwe PVA and acrylic size
It is that pair is matched in the stock tank of material, and antistatic agent is added with partial denaturation starch, carries out starching, drying is transferred to after the completion of starching
Entering to dry dry-cure in room；
S5, weaving process；Yarn obtained in step S4 is weaved using rapier loom, wherein weaving speed is
170r/min；
S6, finishing process；The former fabric that step S5 has been weaved is tested, then the villus on burning-off cloth cover,
It is sent into forming machine and carries out shaping, complete after requiring, packed.
Specifically, the preparation before soybean fiber feeding doubling winder is the following steps are included: (1) preparation spinning is former in step S1
Liquid；(2) stoste is extruded to form thread from spinneret orifice；(3) stoste thread is frozen into as-spun fibre；(4) as-spun fibre package or
Directly post-processed.
Specifically, to reduce electrostatic phenomenon and broken end, preventing from extending other than yarn, using metal drum in step S2.
Specifically, in step S4, temperature of the slurry groove temperature control in 90 DEG C DEG C, baking room is controlled 100 when starching
DEG C or less.
Embodiment 2
A kind of decomposable Environment Compatible Textiles, including the warp and weft for mutually working out, the warp is by soybean fibre
Peacekeeping cotton fiber is blended to be formed, and the weft is worked out by soybean fiber, bamboo fibre and flax fiber blending, and in the warp
Soybean fiber and cotton fiber shared by the percentage of weight be respectively 70% and 30%, soybean fiber, bamboo fibre in the weft
Percentage with place weight when flax fiber blending is respectively 50%, 35% and 15%.
Specifically, the warp and weft use plain weave or twill weave.
A kind of processing technology of decomposable Environment Compatible Textiles, comprising the following steps:
S1, preparatory process: soybean fiber and cotton fiber being sent into doubling winder and carries out yarn and forms mixed and warp, will be big
Beans fiber, bamboo fibre and flaxen fiber, which are sent into doubling winder, to carry out yarn and forms mixed and weft；
S2, winding procedure: simultaneously warp and mixed and weft will be mixed obtained in step S1 and is sent into winder both interior progress winders, together
When control groove drum linear speed in 1100m/min, rolling density 0.38g/cm3；
S3, warping process: the yarn for obtaining winder in step S2 is subjected to section warping by warping machine, controls warping
The speed of beaming of machine is 350m/min, rolling density 0.5g/cm3；
S4, sizing operation: the yarn after the completion of warping is added and is matched based on chemical sizwe PVA and acrylic size
It is that pair is matched in the stock tank of material, and antistatic agent is added with partial denaturation starch, carries out starching, drying is transferred to after the completion of starching
Entering to dry dry-cure in room；
S5, weaving process；Yarn obtained in step S4 is weaved using rapier loom, wherein weaving speed is
190r/min；
S6, finishing process；The former fabric that step S5 has been weaved is tested, then the villus on burning-off cloth cover,
It is sent into forming machine and carries out shaping, complete after requiring, packed.
Specifically, the preparation before soybean fiber feeding doubling winder is the following steps are included: (1) preparation spinning is former in step S1
Liquid；(2) stoste is extruded to form thread from spinneret orifice；(3) stoste thread is frozen into as-spun fibre；(4) as-spun fibre package or
Directly post-processed.
Specifically, to reduce electrostatic phenomenon and broken end, preventing from extending other than yarn, using metal drum in step S2.
Specifically, in step S4, at 95 DEG C, the temperature in baking room is controlled at 100 DEG C for slurry groove temperature control when starching
Below.
Embodiment 3
A kind of decomposable Environment Compatible Textiles, including the warp and weft for mutually working out, the warp is by soybean fibre
Peacekeeping cotton fiber is blended to be formed, and the weft is worked out by soybean fiber, bamboo fibre and flax fiber blending, and in the warp
Soybean fiber and cotton fiber shared by the percentage of weight be respectively 80% and 20%, soybean fiber, bamboo fibre in the weft
Percentage with place weight when flax fiber blending is respectively 60%, 30% and 10%.
Specifically, the warp and weft use plain weave or twill weave.
A kind of processing technology of decomposable Environment Compatible Textiles, comprising the following steps:
S1, preparatory process: soybean fiber and cotton fiber being sent into doubling winder and carries out yarn and forms mixed and warp, will be big
Beans fiber, bamboo fibre and flaxen fiber, which are sent into doubling winder, to carry out yarn and forms mixed and weft；
S2, winding procedure: simultaneously warp and mixed and weft will be mixed obtained in step S1 and is sent into winder both interior progress winders, together
When control groove drum linear speed in 1200m/min, rolling density 0.4g/cm3；
S3, warping process: the yarn for obtaining winder in step S2 is subjected to section warping by warping machine, controls warping
The speed of beaming of machine is 370m/min, rolling density 0.6g/cm3；
S4, sizing operation: the yarn after the completion of warping is added and is matched based on chemical sizwe PVA and acrylic size
It is that pair is matched in the stock tank of material, and antistatic agent is added with partial denaturation starch, carries out starching, drying is transferred to after the completion of starching
Entering to dry dry-cure in room；
S5, weaving process；Yarn obtained in step S4 is weaved using rapier loom, wherein weaving speed is
210r/min；
S6, finishing process；The former fabric that step S5 has been weaved is tested, then the villus on burning-off cloth cover,
It is sent into forming machine and carries out shaping, complete after requiring, packed.
Specifically, the preparation before soybean fiber feeding doubling winder is the following steps are included: (1) preparation spinning is former in step S1
Liquid；(2) stoste is extruded to form thread from spinneret orifice；(3) stoste thread is frozen into as-spun fibre；(4) as-spun fibre package or
Directly post-processed.
Specifically, to reduce electrostatic phenomenon and broken end, preventing from extending other than yarn, using metal drum in step S2.
Specifically, in step S4, at 100 DEG C, the temperature in baking room is controlled at 100 DEG C for slurry groove temperature control when starching
Below.
Finally, it should be noted that the foregoing is only a preferred embodiment of the present invention, it is not intended to restrict the invention,
Although the present invention is described in detail referring to the foregoing embodiments, for those skilled in the art, still may be used
To modify the technical solutions described in the foregoing embodiments or equivalent replacement of some of the technical features,
All within the spirits and principles of the present invention, any modification, equivalent replacement, improvement and so on should be included in of the invention
Within protection scope.
Claims (6)
1. a kind of decomposable Environment Compatible Textiles, including the warp and weft for mutually working out, it is characterised in that: the warp
It is formed by soybean fiber and cotton fiber are blended, the weft is worked out by soybean fiber, bamboo fibre and flax fiber blending, and institute
The percentage for stating weight shared by soybean fiber and cotton fiber in warp is respectively 60%~80% and 40~20%, the weft
The percentage of weight is respectively 40%~60%, 40~30% and 20 where when middle soybean fiber, bamboo fibre and flax fiber blending
~10%.
2. a kind of decomposable Environment Compatible Textiles according to claim 1, it is characterised in that: the warp and weft use
Plain weave or twill weave.
3. a kind of processing technology of described in any item decomposable Environment Compatible Textiles, feature exist according to claim 1~2
In: the following steps are included:
S1, preparatory process: soybean fiber and cotton fiber are sent into doubling winder and carries out yarn and forms mixed and warp, by soybean fibre
Dimension, bamboo fibre and flaxen fiber, which are sent into doubling winder, to carry out yarn and forms mixed and weft；
S2, winding procedure: simultaneously warp and mixed and weft will be mixed obtained in step S1 and is sent into winder both interior progress winders, same to time control
For groove drum linear speed processed in 1000~1200m/min, rolling density is 0.35~0.4g/cm3；
S3, warping process: the yarn for obtaining winder in step S2 is subjected to section warping by warping machine, controls warping machine
Speed of beaming is 330~370m/min, and rolling density is 0.4~0.6g/cm3；
S4, sizing operation: the yarn after the completion of warping is added and is equipped with portion based on chemical sizwe PVA and acrylic size
Dividing converted starch is that pair is matched in the stock tank of material, and antistatic agent is added, and carries out starching, starching is transferred in baking room after the completion
Entering to dry dry-cure；
S5, weaving process；Yarn obtained in step S4 is weaved using rapier loom, wherein weaving speed be 170~
210r/min；
S6, finishing process；The former fabric that step S5 has been weaved is tested, and then the villus on burning-off cloth cover, is being sent into
It is carried out shaping in forming machine, completes after requiring, packed.
4. a kind of decomposable Environment Compatible Textiles according to claim 3 and its processing technology, it is characterised in that: step S1
In, the preparation before soybean fiber feeding doubling winder is the following steps are included: (1) prepares spinning solution；(2) by stoste from spinneret pore pressure
Thread is formed out；(3) stoste thread is frozen into as-spun fibre；(4) as-spun fibre is wrapped or is directly post-processed.
5. a kind of processing technology of decomposable Environment Compatible Textiles according to claim 3, it is characterised in that: step S2
In, to reduce electrostatic phenomenon and broken end, prevent from extending other than yarn, using metal drum.
6. a kind of processing technology of decomposable Environment Compatible Textiles according to claim 3, it is characterised in that: step S4
In, at 90 DEG C~100 DEG C, the temperature in baking room is controlled at 100 DEG C or less for slurry groove temperature control when starching.