CN109454793A - A kind of processing technology and its PVC bottle cover of PVC bottle cover - Google Patents
A kind of processing technology and its PVC bottle cover of PVC bottle cover Download PDFInfo
- Publication number
- CN109454793A CN109454793A CN201811174783.XA CN201811174783A CN109454793A CN 109454793 A CN109454793 A CN 109454793A CN 201811174783 A CN201811174783 A CN 201811174783A CN 109454793 A CN109454793 A CN 109454793A
- Authority
- CN
- China
- Prior art keywords
- mold
- cap
- pvc
- bottle cover
- processing technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of processing technology of PVC bottle cover and its PVC bottle covers, it is related to soaking molding product processing technique field, PVC sheath includes the sleeve and cap of integrally connected, the diameter of cap is greater than the diameter of sleeve, sleeve is that arc-shaped transition formula is connect with cap, circumferential edge of the cap far from sleeve is arranged along rounded corner, and processing technology includes the preparation of raw material, mold pretreatment, leaching modeling, cooling, discharging, back-end crop, cleaning and inspection and is packed and stored step；The characteristics of PVC sheath has good sealing performance and structural strength when being applied on red wine bottle, has production cost low, high in machining efficiency in processing, is suitable for bulk industrialized production.
Description
Technical field
The present invention relates to leaching molding product processing technique fields, more specifically, it relates to a kind of processing technology of PVC bottle cover
And its PVC bottle cover.
Background technique
In the bottling technology underdeveloped age, without pyrocondensation cap and tin cap, chateau, can be in bottleneck after sealing bottle with oak plug
Coating of wax is stamped to be sealed；So seal with wax, as the term suggests poured after the fiery wax heating and melting that being exactly will be red be filled in bottle mouth position with
The effect for playing isolation air is reduced the speed of wine oxidation, is played more by effectively contact of the isolation air with wine liquid of sealing with wax
Strong old effect.
Past, these were also that old potentiality are stronger mostly with the grape wine sealed with wax in some traditional grape wine producing regions
Wine；Some grape wine of today, the purpose for marketing also can be using bottle of sealing with wax, compared to more common bottle, the bottle sealed with wax
Undoubtedly unique in appearance, many people also will be considered that such encapsulation has more aesthetic feeling；Usual chateau can Heat artificially fire wax
It encapsulates, but processing efficiency is low for this envelope bottle mode, and higher cost.
Summary of the invention
In view of the deficienciess of the prior art, purpose of the present invention one is to provide a kind of processing technology of PVC bottle cover,
Have the effect of that cost is relatively low, high in machining efficiency, sealing effect is good.
To achieve the above object, the present invention provides the following technical scheme that
A kind of processing technology of PVC bottle cover, comprising the following steps: the preparation of S1, raw material: raw material is added after mixing to true
It is dissolved in empty material-compound tank, and obtains plastic solution；S2, mold pretreatment: mold is cleaned, and is delivered to temperature and is
Grilled mold processing is carried out in drying box between 350 ~ 400 DEG C；S3, leaching modeling: the mold handled through grilled mold immerses in plastic cement solution, makes
Plastic cement solution is full and uniform to be attached on mold；S4, cooling: the mold after leaching modeling is immersed in clean ice water and carries out cooling place
Reason makes product cooling and shaping be attached to die surface；S5, discharging: product is successively blown off from mold using air gun；S6, it cuts
Tail: back-end crop processing is carried out to product after molding；S7, cleaning: mold being put into clear water reserviors and is cleaned, and repeats step S2
Carry out processing work；S8, it examines and is packed and stored.
So set, raw material is added after mixing first to dissolving in vacuum material-compound tank, vacuum ingredient is utilized
Tank reduces the air content in plastic cement solution during dissolving to raw material, reduces the bubble generation of product after the molding of plastic cement solution,
Improve the molding quality of later product；Period clears up mold, impurity on mold of going out, product quality when improving leaching modeling,
Mold is delivered in the drying box that temperature is 350 ~ 400 DEG C after cleaning and carries out grilled mold processing, preheats the surface of mold；With
Afterwards, in impregnation, it is heated after mold and plastic solution joint after, so that plastic cement solution temperature moment is reached certain temperature
The flow velocity of degree, plastic cement solution is accelerated, and so that plastic cement solution is attached to the Adhesion enhancement on mold, it is more flat that leaching is moulded into flat surface
It is whole；Mold after leaching modeling, which is immersed, carries out cooling treatment into clean ice water, makes product fast cooling shaping and is attached to mould
Have surface, improves the cohesiveness between molecule, and then improve the structural strength of shaped article；By air gun to by product after molding
From mold loading and unloading material, reduce the abrasion to product, back-end crop finally is carried out to product, improves the quality of product, while mold carries out
Step S2 is repeated after cleaning, reaches cyclic process operation；Product carries out completing leaching molding product into being packed and stored after the assay was approved again
Producing process process；The product made of the impregnation, with cost is relatively low, high in machining efficiency, structural strength is good
And the effect that sealing effect is good, and be suitable for bulk industrialized production the characteristics of.
Further setting: in step s 2, it is 50 ~ 60 seconds that mold, which be in drying box the grilled mold processing time,.
So set, mold is made to be heated to predetermined temperature, it is quickly attached on mold convenient for plastic cement solution, plastic cement solution is attached
In it is more smooth on mold and attachment it is more stable.
Further setting: in step s3, the leaching modeling time that mold immerses in plastic cement solution is 8 ~ 10 seconds.
It is attached on mold so set, its plastic cement solution is made uniformly to soak modeling, improves the stability of its plastic cement solution leaching modeling
And leaching polymer amount.
Further setting: in step s 4, the cooling time that mold immerses in ice water is 6 ~ 8 seconds.
So set, the plastic cement solution fast cooling shaping for being attached to its leaching modeling on mold, improves its formed product matter
Amount.
Further setting: the mold includes bottom plate, is set to shaping column of the bottom plate wherein on an end face and is set to
For connecting the drive rod of driving mechanism on bottom plate other end.
So set, driving mechanism makes bottom plate that shaping column be driven to transport towards plastic cement solution direction by driving drive rod movement
It is dynamic, have the function that leaching modeling operation.
Further setting: the shaping column includes the cylinder and bolumn cap being wholely set, and the cylinder is connect with bottom plate, institute
The diameter for stating cylinder is less than the diameter setting of bolumn cap, and the two sides circumferential edge of the bolumn cap is arranged along equal rounded corner.
So set, plastic cement solution is respectively by being attached on cylinder and bolumn cap, according to the structure of cylinder and bolumn cap,
And then soak the product for being moulded into type difference outer dimension.
Further setting: the shaping column is provided with multiple, and multiple shaping columns are in array-like arrangement, and shaping column court
One end of bottom plate is respectively connected with threaded post, and the threaded post is fixedly connected with base thread.
So set, having the function that bulk production by multiple setting shaping columns, its production efficiency is improved；By setting
It sets threaded post and is detachably fixed shaping column and be set on bottom plate, convenient for the effect cleaned, replaced to shaping column, improve mould
The service performance of tool.
Further setting: the two sides of the bottom plate are connected with extension board.
So set, being placed in mold in relevant supporting table by extension board after the completion of leaching modeling, that is, shaping column is outstanding
Sky, and bolumn cap is placed downward and carries out cooling and shaping processing, it improves and processing operation performance is cooled and shaped to product.
The object of the invention has the function of satisfactory texture intensity secondly being to provide a kind of PVC sheath.
A kind of PVC sheath, sleeve and cap including integrally connected, the diameter of the cap are greater than the diameter of sleeve,
The sleeve is that arc-shaped transition formula is connect with cap, and circumferential edge of the cap far from sleeve is arranged along rounded corner.
So set, being placed on related bottle part respectively by sleeve and cap, the sealing to article in bottle part is improved
Performance；Simultaneously by integral type, rounded corner and the setting of arc-shaped transition formula, not only there is good structural strength, while also mentioning
The aesthetics of high PVC sheath.
Further setting: it is applied on red wine bottleneck.
So set, not only act as waterproof by the way that PVC sheath to be set on red wine bottleneck and completely cut off the effect of air,
Effectively contact of the isolation air with wine liquid, has the function of good seal performance and structural strength, while according to raw material
The selection of middle colorant has the effect of certain imitative wax.
By using above-mentioned technical proposal, the present invention compares compared with the prior art, has the advantage that
1, by raw material being added after mixing to dissolving in vacuum material-compound tank, using vacuum material-compound tank molten to raw material
During change, reduce the air content in plastic cement solution, reduces the bubble generation of product after the molding of plastic cement solution, improve later product
Molding quality；
2, grilled mold processing is carried out by the way that the mold after cleaning to be delivered in the drying box that temperature is 350 ~ 400 DEG C, makes leaching modeling work
Plastic cement solution is attached to the Adhesion enhancement on mold in skill, and it is more smooth that leaching is moulded into flat surface；
3, the mold after leaching modeling, which is immersed, carries out cooling treatment into clean ice water, makes product fast cooling shaping and is attached to
Die surface improves the cohesiveness between molecule, and then improves the structural strength of shaped article；
4, by the way that PVC sheath is set on red wine bottleneck, not only act as waterproof and completely cuts off the effect of air, effectively isolation is empty
Contact of the gas with wine liquid, has the function of good seal performance and structural strength, while according to the selection to colorant in raw material,
Has the effect of certain imitative wax.
Detailed description of the invention
Fig. 1 is the flow chart of the processing technology of PVC bottle cover；
Fig. 2 is the structural schematic diagram of mold in the processing technology of PVC bottle cover；
Fig. 3 is the structural schematic diagram of PVC sheath.
In figure: 1, bottom plate；2, shaping column；21, cylinder；22, bolumn cap；23, threaded post；24, extension board；3, drive rod；41,
Sleeve；42, cap.
Specific embodiment
It is described further referring to processing technology and its PVC bottle cover of the attached drawing to PVC bottle cover.
Embodiment 1: a kind of processing technology of PVC bottle cover, as shown in Figure 1, comprising the following steps:
The preparation of S1, raw material: PVC plastic particle and lytic agent formic acid are added after mixing molten to carrying out in vacuum material-compound tank
Change, then places into silane coupling agent, toughener styrene, curing agent sorb amide and colorant according to appropriate proportioning and put into vacuum
It is stirred in material-compound tank, and obtains plastic solution；
S2, mold pretreatment: cleaning mold, and being delivered to temperature by conveyer belt is the drying between 350 ~ 400 DEG C
Grilled mold processing is carried out in case, and the grilled mold processing time is 50 seconds；
S3, leaching modeling: the mold handled through grilled mold immerses leaching modeling 8 seconds in plastic cement solution, makes plastic cement solution is full and uniform to be attached to mould
On tool；
S4, cooling: the mold after leaching modeling is immersed into cooling 6 seconds in clean ice water, product cooling and shaping is made to be attached to mold table
Face；
S5, discharging: product is successively blown off from mold using air gun；
S6, back-end crop: back-end crop processing is carried out to product after molding；
S7, cleaning: mold being put into clear water reserviors and is cleaned, and is repeated step S2 and is carried out processing work；
S8, it examines and is packed and stored.
As shown in Figure 2, wherein mold includes bottom plate 1, is set to shaping column 2 and setting of the bottom plate 1 wherein on an end face
In the drive rod 3 for being used to connect driving mechanism on 1 other end of bottom plate；Shaping column 2 is provided with multiple, and multiple shaping columns 2 are in
Array-like arrangement, such as circumference array, rectangular array.
Shaping column 2 includes the cylinder 21 and bolumn cap 22 being wholely set, and cylinder 21 is vertical with bottom plate 1 to be connect, cylinder 21
The diameter that diameter is less than bolumn cap 22 is arranged, and the two sides circumferential edge of bolumn cap 22 is arranged along equal rounded corner.When leaching modeling, bolumn cap 22 is complete
It immerses in plastic solution, 21 part of cylinder is immersed in plastic solution, and bottom plate 1 is in above plastic solution and does not connect with plastic solution
Touching.
For convenient for carrying out independent relevant operation to shaping column 2, such as cleaning, replacement is equal in one end of shaping column 2 towards bottom plate 1
It is connected with threaded post 23, threaded post 23 is screwed with bottom plate 1 and connect.To carry out cooling treatment convenient for the mold after moulding to leaching,
It is symmetrically fixedly connected with extension board 24 in the two sides of bottom plate 1, is placed in mold in supporting table by extension board 24, and by bolumn cap
22 placements downward carry out cooling and shaping processing, make the thickness being attached on cylinder 21 after its plastic solution is cooling along 22 direction of bolumn cap
Progressive additive.
Embodiment 2: a kind of processing technology of PVC bottle cover, difference from Example 1 are, comprising the following steps:
The preparation of S1, raw material: PVC plastic particle and lytic agent formic acid are added after mixing molten to carrying out in vacuum material-compound tank
Change, then places into silane coupling agent, toughener styrene, curing agent sorb amide and colorant according to appropriate proportioning and put into vacuum
It is stirred in material-compound tank, and obtains plastic solution；
S2, mold pretreatment: cleaning mold, and being delivered to temperature by conveyer belt is the drying between 350 ~ 400 DEG C
Grilled mold processing is carried out in case, and the grilled mold processing time is 55 seconds；
S3, leaching modeling: the mold handled through grilled mold immerses leaching modeling 9 seconds in plastic cement solution, makes plastic cement solution is full and uniform to be attached to mould
On tool；
S4, cooling: the mold after leaching modeling is immersed into cooling 7 seconds in clean ice water, product cooling and shaping is made to be attached to mold table
Face；
S5, discharging: product is successively blown off from mold using air gun；
S6, back-end crop: back-end crop processing is carried out to product after molding；
S7, cleaning: mold being put into clear water reserviors and is cleaned, and is repeated step S2 and is carried out processing work；
S8, it examines and is packed and stored.
Embodiment 3: a kind of processing technology of PVC bottle cover, difference from Example 1 are, comprising the following steps:
The preparation of S1, raw material: PVC plastic particle and lytic agent formic acid are added after mixing molten to carrying out in vacuum material-compound tank
Change, then places into silane coupling agent, toughener styrene, curing agent sorb amide and colorant according to appropriate proportioning and put into vacuum
It is stirred in material-compound tank, and obtains plastic solution；
S2, mold pretreatment: cleaning mold, and being delivered to temperature by conveyer belt is the drying between 350 ~ 400 DEG C
Grilled mold processing is carried out in case, and the grilled mold processing time is 60 seconds；
S3, leaching modeling: the mold handled through grilled mold immerses leaching modeling 10 seconds in plastic cement solution, makes plastic cement solution is full and uniform to be attached to mould
On tool；
S4, cooling: the mold after leaching modeling is immersed into cooling 8 seconds in clean ice water, product cooling and shaping is made to be attached to mold table
Face；
S5, discharging: product is successively blown off from mold using air gun；
S6, back-end crop: back-end crop processing is carried out to product after molding；
S7, cleaning: mold being put into clear water reserviors and is cleaned, and is repeated step S2 and is carried out processing work；
S8, it examines and is packed and stored.
Embodiment 4: PVC sheath made of a kind of processing technology the PVC bottle cover of embodiment 1, as shown in figure 3, including
There are the sleeve 41 and cap 42 of integrally connected；The diameter of cap 42 is greater than the diameter of sleeve 41, and sleeve 41 and cap 42 are arc
The connection of shape transition type, and circumferential edge of the cap 42 far from sleeve 41 is arranged along rounded corner.
Embodiment 5: PVC sheath made of a kind of processing technology the PVC bottle cover of embodiment 2, as shown in figure 3, including
There are the sleeve 41 and cap 42 of integrally connected；The diameter of cap 42 is greater than the diameter of sleeve 41, and sleeve 41 and cap 42 are arc
The connection of shape transition type, and circumferential edge of the cap 42 far from sleeve 41 is arranged along rounded corner.
Embodiment 6: PVC sheath made of a kind of processing technology the PVC bottle cover of embodiment 3, as shown in figure 3, including
There are the sleeve 41 and cap 42 of integrally connected；The diameter of cap 42 is greater than the diameter of sleeve 41, and sleeve 41 and cap 42 are arc
The connection of shape transition type, and circumferential edge of the cap 42 far from sleeve 41 is arranged along rounded corner.
Embodiment 7: a kind of bottle cover applied on red wine bottleneck, including any one PVC into embodiment 6 of embodiment 4
Sheath.
Detect example 1:
The bending property of 4 ~ embodiment of embodiment 7 is detected according to GB/T1449-2005；It is detected and is implemented according to GB/T1447-2005
The tensile property of 4 ~ embodiment of example 7；Meanwhile by the port sealing of the PVC sheath in 4 ~ embodiment of embodiment 7, its sealing is detected
Property, concrete outcome see the table below
| Bending strength (MPa) | Bending strength (MPa) | Whether gas leakage | |
| Embodiment 4 | 48 | 32 | It is no |
| Embodiment 5 | 53 | 35 | It is no |
| Embodiment 6 | 50 | 36 | It is no |
The above is only a preferred embodiment of the present invention, protection scope of the present invention is not limited merely to above-described embodiment,
All technical solutions belonged under thinking of the present invention all belong to the scope of protection of the present invention.It should be pointed out that for the art
For those of ordinary skill, several improvements and modifications without departing from the principles of the present invention, these improvements and modifications are also answered
It is considered as protection scope of the present invention.
Claims (10)
1. a kind of processing technology of PVC bottle cover, which comprises the following steps:
The preparation of S1, raw material: raw material is added to dissolving in vacuum material-compound tank after mixing, and obtains plastic solution；
S2, mold pretreatment: cleaning mold, and is delivered to temperature to be baked in the drying box between 350 ~ 400 DEG C
Mould processing；
S3, leaching modeling: the mold handled through grilled mold immerses in plastic cement solution, makes plastic cement solution is full and uniform to be attached on mold；
S4, cooling: the mold after leaching modeling being immersed in clean ice water and carries out cooling treatment, and product cooling and shaping is made to be attached to mould
Has surface；
S5, discharging: product is successively blown off from mold using air gun；
S6, back-end crop: back-end crop processing is carried out to product after molding；
S7, cleaning: mold being put into clear water reserviors and is cleaned, and is repeated step S2 and is carried out processing work；
S8, it examines and is packed and stored.
2. the processing technology of PVC bottle cover according to claim 1, which is characterized in that in step s 2, mold is in drying
The grilled mold processing time is 50 ~ 60 seconds in case.
3. the processing technology of PVC bottle cover according to claim 1, it is characterised in that: in step s3, mold immerses plastic cement
The leaching modeling time in solution is 8 ~ 10 seconds.
4. the processing technology of PVC bottle cover according to claim 1, it is characterised in that: in step s 4, mold immerses ice water
In cooling time be 6 ~ 8 seconds.
5. the processing technology of PVC bottle cover according to claim 1, it is characterised in that: the mold includes bottom plate (1), sets
It is placed in shaping column (2) of the bottom plate (1) wherein on an end face and is set on bottom plate (1) other end for connecting driving mechanism
Drive rod (3).
6. the processing technology of PVC bottle cover according to claim 5, it is characterised in that: the shaping column (2) includes integrally setting
The cylinder (21) and bolumn cap (22) set, the cylinder (21) connect with bottom plate (1), and the diameter of the cylinder (21) is less than bolumn cap
(22) diameter setting, the two sides circumferential edge of the bolumn cap (22) are arranged along equal rounded corner.
7. the processing technology of PVC bottle cover according to claim 5, it is characterised in that: the shaping column (2) is provided with more
A, multiple shaping columns (2) are arranged in array-like, and one end of shaping column (2) towards bottom plate (1) is respectively connected with threaded post
(23), the threaded post (23) is screwed with bottom plate (1) connect.
8. the processing technology of PVC bottle cover according to claim 5, it is characterised in that: the two sides of the bottom plate (1) are connected with
Extension board (24).
9. a kind of processing technology of PVC bottle cover as described in claim 1 ~ 8 any one produces PVC sheath obtained,
Be characterized in that: the diameter of sleeve (41) and cap (42) including integrally connected, the cap (42) is greater than sleeve (41)
Diameter, the sleeve (421) are that arc-shaped transition formula is connect with cap (42), circumferential edge of the cap (42) far from sleeve (41)
It is arranged along rounded corner.
10. PVC sheath according to claim 9, it is characterised in that: be applied on red wine bottleneck.