CN109401585A - A kind of military button coating - Google Patents
A kind of military button coating Download PDFInfo
- Publication number
- CN109401585A CN109401585A CN201811155016.4A CN201811155016A CN109401585A CN 109401585 A CN109401585 A CN 109401585A CN 201811155016 A CN201811155016 A CN 201811155016A CN 109401585 A CN109401585 A CN 109401585A
- Authority
- CN
- China
- Prior art keywords
- military
- parts
- coating
- button
- varnish
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention proposes a kind of military button coating, include at least varnish host agent, curing agent and diluent, varnish host agent: curing agent: diluent=2:1:(0.5-0.8).The present invention is easy to produce sagging with coating coating varnish for current button, and spraying application requires high, the problem that qualification rate is not high, process costs are high, and varnish prepared by the present invention, gloss is high, appearance is plentiful, improves the efficiency of button painting.
Description
Technical field
The present invention relates to a kind of military button coating.
Background technique
Military button is relatively high with coating requirement, and coating will not only have excellent salt fog resistance, but also require wear-resisting sweat proof
The performances such as stain, while the elegance in order to show Chinese armyman, coating need the high richness of high glaze.Main use domestic at present:
Double-component acrylic acid polyurethane coating does finishing coat, and button is sprayed in apsilate cambered surface with coating, resist sagging in construction especially
It is important, and require coating limpid bright.
Environmentally friendly, the energy-efficient two big projects for having become countries in the world today economic development.Since military button coating is clear
Qi Yaoqiu surface effect is excellent, performance is good, and is sprayed on band in construction and is uneven in apsilate cambered surface, especially requires anti-stream
Hang performance.The resist sagging auxiliary agent of coating mostly uses bentonite, polyamide wax etc. at present, these auxiliary agents are colored and opaque, has
Gloss is had an effect on, research and development have certain difficulty.Our company develops the technique requirement for being able to satisfy military button coating, on should have
Obtain very excellent effect.
Summary of the invention
Sagging is easy to produce with coating coating varnish for current button, and spraying application requires high, and qualification rate is high, technique
Problem at high cost, the present invention propose a kind of military button coating, and gloss is high, appearance is plentiful, improve button painting
Efficiency.
The technical scheme of the present invention is realized as follows:
A kind of military button coating includes at least varnish host agent, curing agent and diluent.
Preferably, according to following weight ratio paint, varnish host agent: curing agent: diluent=2:1:(0.5-0.8).
Preferably, the varnish host agent the preparation method comprises the following steps:
1.1 press investment Hydroxylated acrylic resin, Polygel GA808X30 in clean cast feeder, with blender high speed
Stirring 10 minutes, stirs evenly；
1.2. solvent is put into order under stirring: dimethylbenzene, butyl acetate and propylene glycol methyl ether acetate, and
Levelling agent, defoaming agent and drier stir at low speed 10 minutes；
1.3. with 300 mesh filter screen filtrations to obtain the final product.
Preferably, in parts by weight:
Preferably, the curing agent the preparation method comprises the following steps:
2.1 put into order in the clean equipment that feeds intake HDI biuret, dimethylbenzene, butyl acetate, with blender low speed
Stirring 10 minutes, stirs evenly；
2.2 are packed with 300 mesh filter screen filtrations.
Preferably, in parts by weight:
50 parts of HDI biuret
25 parts of dimethylbenzene
25 parts of butyl acetate.
Preferably, the diluent the preparation method comprises the following steps:
3.1 put into order in the clean equipment that feeds intake propylene glycol methyl ether acetate, dimethylbenzene, butyl acetate, with stirring
It mixes device to stir at low speed 10 minutes, stirs evenly
3.2 are packed with 300 mesh filter screen filtrations.
Preferably, in parts by weight:
5.0 parts of dimethylbenzene
5.0 parts of butyl acetate
4.0 parts of propylene glycol methyl ether acetate.
The present invention is the beneficial effects are as follows: varnish levelling prepared by the present invention is good, up to mirror effect, surface needleless
Hole, dark to steep, no sag phenomenon.
Specific embodiment
Technical solution of the present invention is clearly and completely described below in conjunction with the embodiment of the present invention, it is clear that retouched
The embodiment stated is only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, originally
Field those of ordinary skill every other embodiment obtained without making creative work, belongs to the present invention
The range of protection.
1. button varnish host agent
1.1 formula compositions:
1.2. technique
1) divided by investment Hydroxylated acrylic resin, GA808X30 with blender high-speed stirred 10 in clean cast feeder
Clock stirs evenly.
2) solvent is put into order under stirring: dimethylbenzene, butyl acetate and propylene glycol methyl ether acetate, Yi Jiliu
Flat agent, defoaming agent and drier stir at low speed 10 minutes.
3) it is packed with 300 mesh filter screen filtrations.
2. button novolac curing agents
2.1. formula composition:
2.2. technique
1) put into order in the clean equipment that feeds intake HDI biuret, dimethylbenzene, butyl acetate, with blender low speed
Stirring 10 minutes, stirs evenly.
2) it is packed with 300 mesh filter screen filtrations.
3 varnish thinners
3.1. formula composition:
3.2 technique
1) put into order in the clean equipment that feeds intake propylene glycol methyl ether acetate, dimethylbenzene, butyl acetate, with stirring
Device stirs at low speed 10 minutes, stirs evenly.
2) it is packed with 300 mesh filter screen filtrations.
4. the production of template
4.1 paint
Varnish host agent: curing agent: diluent=2:1:(0.5-0.8)
4.2 spray plates
After mixing the paint mixed up, the making sheet by the way of spraying, diesis spraying.
4.3 dry
It is 10 hours roasting with 50 DEG C of baking oven after the template sprayed stands 15 minutes, after then template places 48 hours naturally
Test.
5. performance detection
Appearance: levelling is good, and surface is pin-free, dark to steep, no sag phenomenon.
| Project | Function |
| Neutral salt spray test (draws Ⅹ) | > 72h |
| Acetone wiping | 500 times or more |
| Alcohol wipe | 500 times or more |
| Nitric acid tests (1:1) | 10 minutes |
| Artificial perspiration | > 100h |
| RCA is wear-resisting | 70 circles |
| Transparency | It is good |
Polygel GA808X30 is used in formula as auxiliary rheological agents, this is a kind of novel auxiliary rheological agents, tradition
Resist sagging auxiliary agent such as: bentonite, fumed silica etc. be all powder, ground, and with color, opaque,
The clarity for influencing glossiness and paint film is unsuitable for being applied in varnish.The rheological characteristic of GA808 is than above-mentioned traditional rheology
Auxiliary agent has better rheological property, and transparent, not delustring, does not influence the clarity of paint film.These advantages essentially consist in GA808
The unique texture feature of product design, molecular structure are as follows:
Many of high polymer branched structure, branched structure it is various in style, there is different physical properties, except this it
Outside, there are many more functional groups for branch terminals, stable at normal temperature, and when high temperature is with reactive group is encountered, chemistry can occur
Reaction, forms more reticular structures.
Claims (8)
1. a kind of military button coating, which is characterized in that include at least varnish host agent, curing agent and diluent.
2. a kind of military button coating as described in claim 1, it is characterised in that: according to following weight ratio paint, varnish
Host agent: curing agent: diluent=2:1:(0.5-0.8).
3. a kind of military button coating as described in claim 1, it is characterised in that: the varnish host agent the preparation method comprises the following steps:
1.1 press investment Hydroxylated acrylic resin, Polygel GA808X30 in clean cast feeder, with blender high-speed stirred
It 10 minutes, stirs evenly；
1.2. solvent is put into order under stirring: dimethylbenzene, butyl acetate and propylene glycol methyl ether acetate and levelling
Agent, defoaming agent and drier stir at low speed 10 minutes；
1.3. with 300 mesh filter screen filtrations to obtain the final product.
4. a kind of military button coating as claimed in claim 3, it is characterised in that: in parts by weight:
5. a kind of military button coating as described in claim 1, which is characterized in that the curing agent the preparation method comprises the following steps:
2.1 put into HDI biuret in order in the clean equipment that feeds intake, dimethylbenzene, butyl acetate, are stirred at low speed with blender
It 10 minutes, stirs evenly；
2.2 are packed with 300 mesh filter screen filtrations.
6. a kind of military button coating as claimed in claim 5, which is characterized in that in parts by weight:
50 parts of HDI biuret
25 parts of dimethylbenzene
25 parts of butyl acetate.
7. a kind of military button coating as described in claim 1, which is characterized in that the diluent the preparation method comprises the following steps:
3.1 put into propylene glycol methyl ether acetate in order in the clean equipment that feeds intake, dimethylbenzene, butyl acetate, use blender
It stirs at low speed 10 minutes, stirs evenly
3.2 are packed with 300 mesh filter screen filtrations.
8. a kind of military button coating as claimed in claim 7, which is characterized in that in parts by weight:
5.0 parts of dimethylbenzene
5.0 parts of butyl acetate
4.0 parts of propylene glycol methyl ether acetate.