CN109354389A - A kind of spherical glass processing technology - Google Patents
A kind of spherical glass processing technology Download PDFInfo
- Publication number
- CN109354389A CN109354389A CN201810975786.7A CN201810975786A CN109354389A CN 109354389 A CN109354389 A CN 109354389A CN 201810975786 A CN201810975786 A CN 201810975786A CN 109354389 A CN109354389 A CN 109354389A
- Authority
- CN
- China
- Prior art keywords
- glass
- heating
- air grid
- way
- roller
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of spherical glass processing technologys, it is loaded including glass, glass heating, glass bending forms and glass unloading, it is characterized in that, the glass heating is by being set to the upper and lower heater strip of heated table group upper and lower in heating furnace to glass while heating, heating temperature is higher than heating temperature below the glass above the glass, partition heating is carried out above the glass, heating temperature is gradually successively decreased by outer rim to centre above the glass；The glass bending molding is that the glass after heating is removed to heating furnace and is transported to molding roller-way, form the glass after sufficiently softening gradually under self gravitation effect with molding roller-way, cool down under the forced ventilation of upper and lower air grid tempering simultaneously, the present invention can efficiently produce spherical glass, and glass molding precision can be effectively controlled during production, improve the quality of production, increased economic benefit.
Description
Technical field
The present invention relates to glass working arts field, specifically a kind of spherical glass processing technology.
Background technique
Arc glass is very widely used in the present age and brings the visual appearance of beauty, such as decorative wall, building, balcony, family
Tool etc..It usually needs in a mold to form the heated softening of the plate glass made according to service condition, then annealed system
At forming.With the industrialized fast development of society, people are continuously increased the use demand amount of glass, to glass quality requirement
Be continuously improved, therefore, how in the case where guaranteeing quality improving production efficiency, at the competition direction of glass processing industry.
Currently, glass bending processing flow is loading-heating-brake forming-cooling-unloading, that is to say will first be put down
Glass sheet, which is placed on, to be loaded in section and is transmitted by loading roller into being heated and softened in bringing-up section, and the glass after softening enters bending
Modification is carried out according to curved roller-way group in profiled section, makes glass further to ideal arc after then moving back and forth；Most
Achieve the purpose that sizing by air grid blowing cold quenching, then exports discharging.
Production bend glass uses the equipment such as curved steel rod and flexible axle, but this glass fibre reinforced plastic equipment more now, is producing
When curved strengthened glass, a kind of single surface glass can only be produced, spherical glass can not be produced, or in the mistake of production
Spheric curvature is unable to accurately control in journey, so that warpage occurs in the bend glass of production, is caused in the actual use process,
Muti-piece spherical glass can not be spliced, thus cause economic loss, and during glass size is biggish.
Summary of the invention
The purpose of the present invention is to provide a kind of spherical glass processing technologys, to solve mentioned above in the background art ask
Topic.
To achieve the above object, the invention provides the following technical scheme:
A kind of spherical glass processing technology, including glass loads, glass heating, glass bending forms and glass unloading, feature
It is,
Glass heating is by being set to the upper and lower heater strip of heated table group upper and lower in heating furnace to glass simultaneously
It is heated, heating temperature is higher than heating temperature below the glass above the glass, carries out subregion above the glass and adds
Heat, the glass top heating temperature are gradually successively decreased by outer rim to centre；
The glass bending molding is that the glass after heating is removed heating furnace and is transported to molding roller-way, and adjustment is upper and lower
Air grid and the radian for forming roller-way, open upper and lower air grid and adjust separately the wind pressure of upper and lower air grid, make after sufficiently softening
Glass gradually forms under self gravitation effect with molding roller-way, while the tempering that cools down under the forced ventilation of upper and lower air grid.
As a further solution of the present invention: the glass after the abundant softening is moved back and forth on molding roller-way,
Reciprocal distance is greater than glass arc length 5-10cm.
As a further solution of the present invention: heating temperature is 705 DEG C -725 DEG C above the glass, below the glass
Heating temperature is 680 DEG C -690 DEG C.
As a further solution of the present invention: the heating time is 330s-680s.
As a further solution of the present invention: the upper and lower air grid blowing time started lags behind the molding roller-way
Crooked radian adjustment time, the lag time are 20s-25s.
As a further solution of the present invention: the upper air grid wind pressure is less than lower air grid wind pressure, and the upper air grid wind pressure is
200-1200pa, the lower air grid wind pressure are 900-3000pa.
As a further solution of the present invention: the blow-time of the upper and lower air grid is 200s-300s.
As a further solution of the present invention: the air outlet of the upper air grid to the glass top surface being located on forming roller road
Distance be 40-50mm, the distance of air outlet to the lower glass surface of lower air grid is 20mm.
As a further solution of the present invention: the upper and lower air grid and the crooked radian and the glass for forming roller-way
Finished product radian it is identical.
As a further solution of the present invention: the roller-way wheel diameter on the molding roller-way is grading structure.
Compared with prior art, the beneficial effects of the present invention are:
1, this method moves back and forth to glass by heating ceramic roller-way during heating to glass, and then makes
It is more uniform to obtain glass heating, reducing ceramic roller influences glass heating bring, and is making heating temperature above glass
Degree is higher than lower section heating temperature, furthermore partition heating is used in the top of glass, so that the heating temperature of glass upper surface is by outer
It helps and is gradually decreased to centre, so that the process of glass foreign aid and middle part in cooling during molding of the glass after heating
In receive different internal stress, and then the effect in internal stress have four it is circumferentially intermediate form stable bending, and then can be with
Process spherical glass；
2 present invention molding roller-way after the molding roller-way that the glass after abundant softening all arrives just starts bending deformation, Er Qie
After molding roller-way bending deformation starts, the blow-time of upper and lower air grid lags behind the bending time started of molding roller-way, Jin Erke
At the beginning of postponing glass tempering, so that glass can persistently keep soft state after coming out of the stove in a longer period of time, into
And the molding rate of glass improved, while being also possible that the cooling of glass rear and front end can start simultaneously at, before reducing glass
The temperature difference of rear end increases the precision of glass radian control in forming process, allows the glass particle degree after tempering more preferable；
3, the present invention is during carrying out glass cooling tempering, so that the wind pressure of upper air grid is less than the wind pressure of lower air grid, thus
During carrying out cooling tempering to glass, the temperature decrease rate of glass upper end is less than the rate of temperature fall of glass lower end surface,
It is described during glass cools down tempering, since the difference of local temperature causes the internal stress of glass upper and lower end face different, into
One step accelerates the rate that glass is bent upwards, and accelerates the curved rate of glass, can effectively avoid in unformed preceding glass
The problem of glass is down to tempering temperature, thus improve the quality of production.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this field is common
Technical staff's every other embodiment obtained without making creative work belongs to the model that the present invention protects
It encloses.
Embodiment 1；
A kind of spherical glass processing technology, comprising the following steps:
Step 1, glass load: the glass having a size of 1.5m*1.5m * 6mm being cleaned and is dried, after processing
Glass be placed on charging roller upper end, glass is transported in heating furnace by charging roller；
Step 2, glass heating: glass heating is the upper and lower heater strip by being set to heated table group upper and lower in heating furnace
Glass is heated simultaneously, heating temperature is higher than heating temperature below the glass above glass, carries out subregion above glass
Heating, wherein the temperature along moving direction of glass rear and front end is 725 DEG C, along glass motion direction, both side ends heating temperature is
725 DEG C, glass medium position heating temperature is 690 DEG C, and heating temperature is gradually successively decreased by outer rim to centre above glass, and glass adds
The hot time is 330s；
Step 3, glass bending molding: the glass bending molding is that the glass after heating is removed to heating furnace and is transported to
Roller-way is formed, when the glass after abundant softening is all moved to above molding roller-way, adjusts upper and lower air grid and molding roller-way
Radian, open upper and lower air grid, air grid wind pressure is 1200pa in adjustment, and windward pitch is from glass upper surface 250mm, adjustment
Lower air grid wind pressure is 3000pa and leeward pitch is from glass lower end surface 20mm, the upper and lower air grid lag after glass to molding roller-way
20s starts blowing cooling and carries out tempering to glass, and blow-time 200s, during cooling down tempering, glass is with forming roller
Road group moves back and forth, and reciprocal distance is greater than glass arc length 5-10cm；
Form roller-way use flexible axle roller-way, molding roller-way upper roller road size of wheel along molding roller-way axis direction by both ends to centre by
Step reduces；Molding roller-way upper roller road size of wheel is gradually reduced along glass run direction by rear and front end to centre；
Step 4, glass unloading: continuing to cool down to the glass after tempering, until room temperature, is then moved to unloading roller-way and carries out
Unloading.
Embodiment 2；
A kind of spherical glass processing technology, comprising the following steps:
Step 1, glass load: the glass having a size of 1.5m*1.5m*8mm thickness being cleaned and is dried, will be handled
Glass afterwards is placed on charging roller upper end, and glass is transported in heating furnace by charging roller；
Step 2, glass heating: glass heating is the upper and lower heater strip by being set to heated table group upper and lower in heating furnace
Glass is heated simultaneously, heating temperature is higher than heating temperature below the glass above glass, carries out subregion above glass
Heating, wherein the temperature along moving direction of glass rear and front end is 710 DEG C, along glass motion direction, both side ends heating temperature is
705 DEG C, glass medium position heating temperature is 690 DEG C, and heating temperature is gradually successively decreased by outer rim to centre above glass, and glass adds
The hot time is 460s；
Step 3, glass bending molding: the glass bending molding is that the glass after heating is removed to heating furnace and is transported to
Roller-way is formed, when the glass after abundant softening is all moved to above molding roller-way, adjusts upper and lower air grid and molding roller-way
Radian, open upper and lower air grid, air grid wind pressure is 500pa and windward pitch from glass upper surface 200mm in adjustment, under adjustment
Air grid wind pressure is 1600pa and leeward pitch is from glass lower end surface 20mm, and upper and lower air grid lags 25s after glass to molding roller-way
Start blowing cooling and tempering is carried out to glass, blow-time 300s, during cooling down tempering, glass is with molding roller-way group
It moves back and forth, reciprocal distance is greater than glass arc length 5-10cm；
Form roller-way use flexible axle roller-way, molding roller-way upper roller road size of wheel along molding roller-way axis direction by both ends to centre by
Step reduces；Molding roller-way upper roller road size of wheel is gradually reduced along glass run direction by rear and front end to centre；
Step 4, glass unloading: continuing to cool down to the glass after tempering, until room temperature, is then moved to unloading roller-way and carries out
Unloading.
Embodiment 3；
A kind of spherical glass processing technology, comprising the following steps:
Step 1, glass load: the glass having a size of 1.5*1.5*10mm thickness being cleaned and is dried, will be handled
Glass afterwards is placed on charging roller upper end, and glass is transported in heating furnace by charging roller；
Step 2, glass heating: glass heating is the upper and lower heater strip by being set to heated table group upper and lower in heating furnace
Glass is heated simultaneously, heating temperature is higher than heating temperature below the glass above glass, carries out subregion above glass
Heating, wherein the temperature along moving direction of glass rear and front end is 710 DEG C, along glass motion direction, both side ends heating temperature is
705 DEG C, glass medium position heating temperature is 680 DEG C, and heating temperature is gradually successively decreased by outer rim to centre above glass, and glass adds
The hot time is 680s；
Step 3, glass bending molding: the glass bending molding is that the glass after heating is removed to heating furnace and is transported to
Roller-way is formed, when the glass after abundant softening is all moved to above molding roller-way, adjusts upper and lower air grid and molding roller-way
Radian, open upper and lower air grid, air grid wind pressure is 200pa and windward pitch from glass upper surface 250mm in adjustment, under adjustment
Air grid wind pressure is 900pa and leeward pitch is from glass lower end surface 20mm, and upper and lower air grid lags 20s after glass to molding roller-way
Start blowing cooling and tempering is carried out to glass, blow-time 200s, during cooling down tempering, glass is with molding roller-way group
It moves back and forth, reciprocal distance is greater than glass arc length 5-10cm；
Form roller-way use flexible axle roller-way, molding roller-way upper roller road size of wheel along molding roller-way axis direction by both ends to centre by
Step reduces；Molding roller-way upper roller road size of wheel is gradually reduced along glass run direction by rear and front end to centre；
Step 4, glass unloading: continuing to cool down to the glass after tempering, until room temperature, is then moved to unloading roller-way and carries out
Unloading.
The granularity of the spherical surface tempered glass produced by the processing technology of the application can achieve tempering requirement, Er Qiecheng
The spheric curvature of type glass is accurate, and produces the spherical glass that sagitta is 300m, and the radius minimum of spherical glass is reachable
To 880m.
It is obvious to a person skilled in the art that invention is not limited to the details of the above exemplary embodiments, Er Qie
In the case where without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by appended power
Benefit requires rather than above description limits, it is intended that all by what is fallen within the meaning and scope of the equivalent elements of the claims
Variation is included within the present invention.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiments being understood that.
Claims (10)
1. a kind of spherical glass processing technology, including glass loads, glass heating, glass bending forms and glass unloading, it is special
Sign is,
Glass heating is by being set to the upper and lower heater strip of heated table group upper and lower in heating furnace to glass simultaneously
It is heated, heating temperature is higher than heating temperature below the glass above the glass, carries out subregion above the glass and adds
Heat, the glass top heating temperature are gradually successively decreased by outer rim to centre；
The glass bending molding is that the glass after heating is removed heating furnace and is transported to molding roller-way, and adjustment is upper and lower
Air grid and the radian for forming roller-way, open upper and lower air grid and adjust separately the wind pressure of upper and lower air grid, make after sufficiently softening
Glass gradually forms under self gravitation effect with molding roller-way, while the tempering that cools down under the forced ventilation of upper and lower air grid.
2. a kind of spherical glass processing technology according to claim 1, which is characterized in that the glass after the abundant softening
It is moved back and forth on molding roller-way, reciprocal distance is greater than glass arc length 5-10cm.
3. a kind of spherical glass processing technology according to claim 1, which is characterized in that heating temperature above the glass
It is 705 DEG C -725 DEG C, heating temperature is 680 DEG C -690 DEG C below the glass.
4. a kind of spherical glass processing technology according to claim 1, which is characterized in that the heating time is 330s-
680s。
5. a kind of spherical glass processing technology according to claim 1, which is characterized in that the upper and lower air grid blowing is opened
Time lag begin in the crooked radian adjustment time of the molding roller-way, the lag time is 20s-25s.
6. a kind of spherical glass processing technology according to claim 1, which is characterized in that under the upper air grid wind pressure is less than
Air grid wind pressure, the upper air grid wind pressure are 200-1200pa, and the lower air grid wind pressure is 900-3000pa.
7. a kind of spherical glass processing technology according to claim 1, which is characterized in that the blowing of the upper and lower air grid
Time is 200s-300s.
8. a kind of spherical glass processing technology according to claim 1, which is characterized in that the air outlet of the upper air grid arrives
The distance of glass top surface on molding roller-way is 40-50mm, the distance of air outlet to the lower glass surface of lower air grid is
20mm。
9. a kind of spherical glass processing technology according to claim 1, which is characterized in that the upper and lower air grid and at
The crooked radian of type roller-way is identical as the finished product radian of the glass.
10. a kind of spherical glass processing technology according to claim 1, which is characterized in that the roller on the molding roller-way
Road wheel diameter is grading structure.