CN109137242A - A polyester fiber plain fabric - Google Patents

A polyester fiber plain fabric Download PDF

Info

Publication number
CN109137242A
CN109137242A CN201811106359.1A CN201811106359A CN109137242A CN 109137242 A CN109137242 A CN 109137242A CN 201811106359 A CN201811106359 A CN 201811106359A CN 109137242 A CN109137242 A CN 109137242A
Authority
CN
China
Prior art keywords
plain weave
fabric
machine
transported
weave fabric
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201811106359.1A
Other languages
Chinese (zh)
Inventor
相里海霞
卢雪康
丁冬炉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201811106359.1A priority Critical patent/CN109137242A/en
Publication of CN109137242A publication Critical patent/CN109137242A/en
Withdrawn legal-status Critical Current

Abstract

本发明提供一种聚酯纤维平纹面料，包括底面层，所述底面层由90%聚酯纤维以及10%氨纶丝组成，与现有技术相比，本发明具有如下的有益效果：因本发明设置了聚酯纤维以及氨纶丝，使本发明具有易洗快干、吸湿排汗、抑菌防臭的功效的优点。The present invention provides a polyester fiber plain weave fabric, comprising a bottom surface layer, and the bottom surface layer is composed of 90% polyester fiber and 10% spandex filament. Compared with the prior art, the present invention has the following beneficial effects: Polyester fibers and spandex yarns are provided, so that the invention has the advantages of easy washing and quick drying, moisture absorption and perspiration, antibacterial and deodorization.

Description

A kind of polyester fiber plain fabric
Technical field
The present invention is a kind of polyester fiber plain fabric, belongs to garment material technical field.
Background technique
Polyester fiber is commonly called as " terylene ".It is that the polyester as made of organic dibasic acid and dihydric alcohol polycondensation is resulting through spinning Synthetic fibers, abbreviation PET fiber invent in nineteen forty-one, are the first big kinds of current synthetic fibers.Polyester fiber is maximum excellent Point is that wrinkle resistance and conformality are fine, intensity with higher and elastic recovery capability.Its strong durable, wash and wear does not glue Hair.
In the prior art, the polyester fiber elastic fabric made of weaving, absorbing sweat is not airtight, and feel is puckery hard, nonreactive Bacterium deodorant function, so being badly in need of wanting a kind of polyester fiber plain fabric to solve the above-mentioned problem.
Summary of the invention
In view of the deficienciess of the prior art, it is an object of the present invention to provide a kind of polyester fiber plain fabric, on solving State the problem of proposing in background technique.
To achieve the goals above, the present invention is to realize by the following technical solutions: a kind of polyester fiber plain weave face Material, including bottom surface layer, the bottom surface layer are made of 90% polyester fiber and 10% spandex thread；
The bottom surface layer is made of following steps:
Polyester fiber is spun into 75D/72F yarn first, then select 20D specification spandex thread, then by 75D/72F yarn with 20D spandex thread is delivered to simultaneously in close needle large circle machine, and polyester fiber and spandex interaction are hooked and knitted according to certain rule, is formed flat Line embryo cloth；
Plain weave embryo cloth is delivered in forming machine again, carries out pre-setting processing；
By pre-setting, treated that plain weave embryo cloth is delivered to boils in drift machine, carries out boiling drift processing；
Drift will be boiled again treated plain weave embryo cloth is delivered in overflow dyeing machine dyes；
Plain weave embryo cloth after dyeing is delivered in baking oven, drying and processing is carried out；
The plain weave embryo cloth after drying and processing is delivered in needle pincers formula boarding machine again and carries out shaping processing, finished product plain weave face is made Material；
Finally finished product plain fabric is tested, is put in storage after the assay was approved.
Further, described that plain weave embryo cloth is delivered in forming machine again, it carries out pre-setting and handles specific procedure of processing such as Under: plain weave embryo cloth is delivered in forming machine, and pre-setting temperature is adjusted to 180 DEG C~190 DEG C, by the speed of service adjust to 15~18m/min, forming machine carry out pre-setting processing to plain weave embryo cloth.
Further, described by pre-setting, treated that plain weave embryo cloth is delivered to boils in drift machine, carries out boiling drift processing specific Procedure of processing is as follows: by pre-setting, treated that plain weave embryo cloth is delivered to ZZG-60 type boils in drift machine, and running temperature is adjusted To 100~110 DEG C, and add 1.5% anti-creasing agent, 0.5% bleeding agent, 1.5% desizing agent, 1.5% sodium carbonate, 1.5% hydrogen peroxide and 5% antibacterial deodourizing auxiliary agent, by pearl embryo cloth kiering 1h, ZZG-60 type boil drift machine and carry out kiering processing to plain weave embryo cloth.
Further, it is described will boil drift again treated plain weave embryo cloth is delivered in overflow dyeing machine dye it is specific plus Steps are as follows for work: boiling drift, treated that plain weave embryo cloth is delivered in HS-550 type overflow dyeing machine, and dye liquor temperature is increased To 110~140 DEG C, and Dyeing formulations, 2% anti-creasing agent and 2% water softener are added, dye liquor temperature is reduced to 40 DEG C, stops drop Temperature is discharged waste liquid, and is rinsed well plain weave embryo cloth using clear water, and HS-550 type overflow dyeing machine dyes plain weave embryo cloth Processing.
Further, the plain weave embryo cloth by after dyeing is delivered in baking oven, carries out the specific procedure of processing of drying and processing As follows: by the pearl after dyeing embryo cloth is delivered in TH-3B type baking oven, and by the temperature of TH-3B type baking oven adjust to 55 DEG C~ 85 DEG C, and 2%~3% water-absorbing fast-drying auxiliary agent is added, handle 50~70min of time.
Further, the described plain weave embryo cloth after drying and processing is delivered in needle pincers formula boarding machine again carries out shaping place Reason, it is as follows to be made the specific procedure of processing of finished product plain fabric: the plain weave embryo cloth after drying and processing is delivered to needle pincers formula boarding machine In, setting temperature is adjusted to 160 DEG C~170 DEG C, the speed of service is adjusted to 12~15m/min, overfeeding is adjusted to 1%~ 3%, door width is adjusted to more than finished product 2cm~3cm, needle pincers formula boarding machine carry out shaping processing to plain weave embryo cloth.
Further, described that finally finished fabric is tested, it is as follows that it is put in storage specific procedure of processing after the assay was approved: will Finished fabric is placed on check-out console, in finished fabric fracture of wire, broken hole, whippletree, bad selvedge, skew of weft, dirty, plucking and shave Hair is tested, and such as without disadvantages described above, qualified finished fabric is packed in storage.
Beneficial effects of the present invention: a kind of polyester fiber plain fabric of the invention, because the present invention is provided with polyester fiber And spandex thread, so that the present invention is had effects that the advantages of quick-drying washable, moisture absorbing and sweat releasing, bacteriostatic deodorizing.
Specific embodiment
To be easy to understand the technical means, the creative features, the aims and the efficiencies achieved by the present invention, below with reference to Specific embodiment, the present invention is further explained.
The present invention provides a kind of technical solution: a kind of polyester fiber plain fabric, including bottom surface layer, bottom surface layer are gathered by 90% Ester fiber and 10% spandex thread composition.
Bottom surface layer is made of following steps:
Polyester fiber is spun into 75D/72F yarn first, then select 20D specification spandex thread, then by 75D/72F yarn with 20D spandex thread is delivered to simultaneously in close needle large circle machine, and polyester fiber and spandex interaction are hooked and knitted according to certain rule, is formed flat Line embryo cloth；
Plain weave embryo cloth is delivered in forming machine again, carries out pre-setting processing；
By pre-setting, treated that plain weave embryo cloth is delivered to boils in drift machine, carries out boiling drift processing；
Drift will be boiled again treated plain weave embryo cloth is delivered in overflow dyeing machine dyes；
Plain weave embryo cloth after dyeing is delivered in baking oven, drying and processing is carried out；
The plain weave embryo cloth after drying and processing is delivered in needle pincers formula boarding machine again and carries out shaping processing, finished product plain weave face is made Material；
Finally finished product plain fabric is tested, is put in storage after the assay was approved.
As an embodiment of the present invention: plain weave embryo cloth being delivered in forming machine again, it is specific to carry out pre-setting processing Procedure of processing is as follows: plain weave embryo cloth being delivered in forming machine, and pre-setting temperature is adjusted to 180 DEG C~190 DEG C, will be run Speed is adjusted to 15~18m/min, and forming machine carries out pre-setting processing to plain weave embryo cloth.
As an embodiment of the present invention: by pre-setting, treated that plain weave embryo cloth is delivered to boils in drift machine, is boiled It is as follows that drift handles specific procedure of processing: by pre-setting, treated that plain weave embryo cloth is delivered to ZZG-60 type boils in drift machine, and will fortune Trip temperature is adjusted to 100~110 DEG C, and adds 1.5% anti-creasing agent, 0.5% bleeding agent, 1.5% desizing agent, 1.5% sodium carbonate, 1.5% Hydrogen peroxide and 5% antibacterial deodourizing auxiliary agent, by pearl embryo cloth kiering 1h, ZZG-60 type boil drift machine and carry out at kiering to plain weave embryo cloth Reason.
As an embodiment of the present invention: drift will be boiled again treated that plain weave embryo cloth is delivered in overflow dyeing machine carries out It is as follows to dye specific procedure of processing: boiling drift, treated that plain weave embryo cloth is delivered in HS-550 type overflow dyeing machine, and will dye Liquid temperature is increased to 110~140 DEG C, and adds Dyeing formulations, 2% anti-creasing agent and 2% water softener, and dye liquor temperature is reduced to 40 DEG C, stop cooling, waste liquid is discharged, and rinse plain weave embryo cloth well using clear water, HS-550 type overflow dyeing machine is to plain weave embryo Cloth carries out dyeing processing.
As an embodiment of the present invention: the plain weave embryo cloth after dyeing being delivered in baking oven, drying and processing tool is carried out Body procedure of processing is as follows: by the pearl after dyeing embryo cloth is delivered in TH-3B type baking oven, and by the temperature tune of TH-3B type baking oven Whole to 55 DEG C~85 DEG C, and 2%~3% water-absorbing fast-drying auxiliary agent is added, handle 50~70min of time.
As an embodiment of the present invention: again by the plain weave embryo cloth after drying and processing be delivered in needle pincers formula boarding machine into It is as follows that the specific procedure of processing of finished product plain fabric is made in row setting treatment: the plain weave embryo cloth after drying and processing is delivered to needle pincers In formula boarding machine, setting temperature is adjusted to 160 DEG C~170 DEG C, the speed of service is adjusted to 12~15m/min, by overfeeding tune It is whole to 1%~3%, door width is adjusted to more than finished product 2cm~3cm, needle pincers formula boarding machine carry out shaping processing to plain weave embryo cloth.
As an embodiment of the present invention: finally finished fabric being tested, after the assay was approved the specific processing of storage Steps are as follows: finished fabric being placed on check-out console, to the fracture of wire, broken hole, whippletree, bad selvedge, skew of weft, dirty in finished fabric Dirty, plucking and shaving are tested, and such as without disadvantages described above, qualified finished fabric is packed in storage.
The above shows and describes the basic principles and main features of the present invention and the advantages of the present invention, for this field skill For art personnel, it is clear that invention is not limited to the details of the above exemplary embodiments, and without departing substantially from spirit of the invention or In the case where essential characteristic, the present invention can be realized in other specific forms.Therefore, in all respects, should all incite somebody to action Embodiment regards exemplary as, and is non-limiting, the scope of the present invention by appended claims rather than on state Bright restriction, it is intended that including all changes that fall within the meaning and scope of the equivalent elements of the claims in the present invention It is interior.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art The other embodiments being understood that.

Claims (7)

1.一种聚酯纤维平纹面料，包括底面层，其特征在于：所述底面层由90%聚酯纤维以及10%氨纶丝组成；1. a polyester fiber plain weave fabric, comprising bottom surface layer, it is characterized in that: described bottom surface layer is made up of 90% polyester fiber and 10% spandex yarn; 所述底面层由以下步骤制成：The bottom layer is made by the following steps: 首先将聚酯纤维纺成75D/72F纱线，然后选用20D规格的氨纶丝，然后将75D/72F纱线与20D氨纶丝同时输送至密针大圆机中，按照一定的规律将聚酯纤维和氨纶交互勾织，形成平纹胚布；First, the polyester fiber is spun into 75D/72F yarn, then 20D spandex yarn is selected, and then the 75D/72F yarn and 20D spandex yarn are transported to the dense needle large circular machine at the same time. Spandex interlaced to form plain fabric; 再将平纹胚布输送至定型机中，进行预定型处理；Then the plain weave fabric is transported to the setting machine for pre-forming treatment; 将预定型处理后的平纹胚布输送至煮漂机中，进行煮漂处理；Conveying the pre-formed plain fabric to the scouring and bleaching machine for scouring and bleaching treatment; 再将煮漂处理后的平纹胚布输送至溢流染色机中进行染色；Then, the plain weave fabric after the scouring and bleaching treatment is transported to the overflow dyeing machine for dyeing; 将染色后的平纹胚布输送至烘箱内，进行烘干处理；The dyed plain weave fabric is transported to the oven for drying treatment; 再将烘干处理后的平纹胚布输送至针铗式定形机中进行定型处理，制成成品平纹面料；Then, the plain weave fabric after drying treatment is transported to the pin-clip type setting machine for shaping treatment, and the finished plain weave fabric is made; 最后将成品平纹面料进行检验，检验合格后入库。Finally, the finished plain weave fabrics are inspected and put into storage after passing the inspection. 2.根据权利要求1所述的一种聚酯纤维平纹面料，其特征在于：所述再将平纹胚布输送至定型机中，进行预定型处理具体加工步骤如下：将平纹胚布输送至定型机中，并将预定型温度调整至180℃～190℃，将运行速度调整至15～18m/min，定型机对平纹胚布进行预定型处理。2. A polyester fiber plain weave fabric according to claim 1, characterized in that: the plain weave fabric is transported to the shaping machine again, and the specific processing steps for pre-forming treatment are as follows: the plain weave fabric is transported to the shaping machine In the machine, the pre-forming temperature is adjusted to 180 ℃ ~ 190 ℃, and the running speed is adjusted to 15 ~ 18 m/min, and the sizing machine performs pre-forming processing on the plain fabric. 3.根据权利要求1所述的一种聚酯纤维平纹面料，其特征在于：所述将预定型处理后的平纹胚布输送至煮漂机中，进行煮漂处理具体加工步骤如下：将预定型处理后的平纹胚布输送至ZZG-60型煮漂机内，并将运行温度调整至100～110℃，并添加1.5%防皱剂、0.5%渗透剂、1.5%退浆剂、1.5%碳酸钠、1.5%双氧水以及5%抗菌防臭助剂，将珠地胚布煮练1h，ZZG-60型煮漂机对平纹胚布进行煮练处理。3. A polyester fiber plain weave fabric according to claim 1, characterized in that: the pre-processed plain weave fabric is transported to a scouring and bleaching machine, and the specific processing steps for scouring and bleaching are as follows: The plain weave cloth after type treatment is transported to ZZG-60 type scouring and bleaching machine, and the operating temperature is adjusted to 100 ~ 110 ℃, and 1.5% anti-wrinkle agent, 0.5% penetrating agent, 1.5% desizing agent, 1.5% Sodium carbonate, 1.5% hydrogen peroxide and 5% antibacterial and deodorant additives are used to scour the piqué fabric for 1 hour, and the ZZG-60 scouring and bleaching machine scours the plain weave fabric. 4.根据权利要求1所述的一种聚酯纤维平纹面料，其特征在于：所述再将煮漂处理后的平纹胚布输送至溢流染色机中进行染色具体加工步骤如下：将煮漂处理后的平纹胚布输送至HS-550型溢流染色机中，并将染液温度升高至110～140℃，并添加染色配料、2%防皱剂以及2%软水剂，将染液温度降低至40℃，停止降温，排出废液，并使用清水将平纹胚布冲洗干净，HS-550型溢流染色机对平纹胚布进行染色处理。4. A kind of polyester fiber plain weave fabric according to claim 1, is characterized in that: the described plain weave fabric after the scouring and bleaching treatment is transported to the overflow dyeing machine for dyeing and the specific processing steps are as follows: The treated plain fabric is transported to the HS-550 overflow dyeing machine, and the temperature of the dye liquor is raised to 110-140°C, and dyeing ingredients, 2% anti-wrinkle agent and 2% water softener are added to the dye liquor. When the temperature is lowered to 40°C, the cooling is stopped, the waste liquid is discharged, and the plain fabric is rinsed with clean water, and the HS-550 overflow dyeing machine is used to dye the plain fabric. 5.根据权利要求1所述的一种聚酯纤维平纹面料，其特征在于：所述将染色后的平纹胚布输送至烘箱内，进行烘干处理具体加工步骤如下：将染色后的珠地胚布输送至TH-3B型烘箱内，并将TH-3B型烘箱的温度调整至55℃～85℃，并添加2%～3%的吸水速干助剂，处理时间50～70min。5. a kind of polyester fiber plain weave fabric according to claim 1 is characterized in that: the described plain weave fabric after dyeing is transported into the oven, and the concrete processing steps of drying treatment are as follows: The embryonic cloth is transported to the TH-3B type oven, and the temperature of the TH-3B type oven is adjusted to 55℃～85℃, and 2%～3% water-absorbing quick-drying auxiliary is added, and the processing time is 50～70min. 6.根据权利要求1所述的一种聚酯纤维平纹面料，其特征在于：所述再将烘干处理后的平纹胚布输送至针铗式定形机中进行定型处理，制成成品平纹面料具体加工步骤如下：将烘干处理后的平纹胚布输送至针铗式定形机中，将定型温度调整至160℃～170℃，将运行速度调整至12～15m/min，将超喂调整至1%～3%，将门幅调整至大于成品2cm～3cm，针铗式定形机对平纹胚布进行定型处理。6. A polyester fiber plain weave fabric according to claim 1, characterized in that: the plain weave fabric after the drying treatment is transported to a pin-clip type setting machine for shaping treatment, and a finished plain weave fabric is made The specific processing steps are as follows: the plain weave fabric after drying treatment is transported to the pin-clip type setting machine, the setting temperature is adjusted to 160℃～170℃, the running speed is adjusted to 12～15m/min, and the overfeed is adjusted to 1% to 3%, adjust the width of the door to 2cm to 3cm larger than the finished product, and shape the plain fabric with a pin-clip type setting machine. 7.根据权利要求1所述的一种聚酯纤维平纹面料，其特征在于：所述最后将成品面料进行检验，检验合格后入库具体加工步骤如下：将成品面料放置在检验台上，对成品面料上的断丝、破洞、横杠、坏边、纬斜、脏污、拉毛以及剃毛进行检验，如无以上缺陷，将合格成品面料打包入库。7. A kind of polyester fiber plain weave fabric according to claim 1, it is characterized in that: the finished fabric is finally inspected, and the specific processing steps of storage after passing the inspection are as follows: the finished fabric is placed on the inspection table, and the The finished fabrics are inspected for broken wires, holes, horizontal bars, bad edges, weft skew, dirt, hair pulling and shaving. If there are no above defects, the qualified finished fabrics will be packed into the warehouse.
CN201811106359.1A 2018-09-21 2018-09-21 A polyester fiber plain fabric Withdrawn CN109137242A (en)