CN109016715A - Waterproof material - Google Patents
Waterproof material Download PDFInfo
- Publication number
- CN109016715A CN109016715A CN201810891706.XA CN201810891706A CN109016715A CN 109016715 A CN109016715 A CN 109016715A CN 201810891706 A CN201810891706 A CN 201810891706A CN 109016715 A CN109016715 A CN 109016715A
- Authority
- CN
- China
- Prior art keywords
- parts
- polymer colloid
- hot melt
- melt adhesive
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of waterproof material, including fetal membrane, isolation film and polymer colloid, the polymer colloid is uniformly applied between the fetal membrane and isolation film, is kneaded by the component of following parts by weight: 20~48 parts of hot melt adhesive；1.7~5 parts of naphthenic oil；10~20 parts of white cement；30~60 parts of quartz sand；0.3~1 part of green pigment；1-5 parts of nano silica, 1-3 parts of nano aluminium oxide.The present invention has excellent weatherability, peel strength and waterproof performance, and the waterproof barrier of skin-type can be made for construction material；Using the non-bituminous based raw material of environmental protection, component is uncomplicated and preparation process is simple, and production cost is low, the characteristics of having both economical and environmentally friendly, the bright prospects with large-scale industrial application.
Description
Technical field
The present invention relates to the field of building materials, and in particular to a kind of waterproof material.
Background technique
Currently, the waterproof material in China is still to account for the 65% of whole waterproof materials, high score based on asphalt base waterproofing material
Sub- waterproof roll accounts for 15% or so, other waterproof materials 20% or so.Wherein polymer membranes is typical novel building
Waterproof material develops non-in recent years because its performance is brilliant, meets the purpose of building materials innovation and the rise of light weight steel structure
Often rapidly.
In the prior art, on the one hand its peel strength is low for traditional asphalt-based material waterproof material, and waterproof performance is insufficient, with
Using the time extension, waterproof performance weaken；On the other hand, the use of asphalt-based material brings problem of environmental pollution,
The health of construction personnel is influenced, therefore there is an urgent need to develop the non-bituminous base waterproof materials of new good waterproof performance.Therefore, it makes
A kind of high polymer waterproof material of standby environment friendly and economical, has excellent weatherability, removing and waterproof performance, and can have
The various places for having waterproof to need are used widely, and are just had a very important significance.
Summary of the invention
The invention proposes a kind of high-effective water-proof and economic and environment-friendly waterproof materials.
To achieve the goals above, the present invention is achieved through the following technical solutions:
A kind of waterproof material, including fetal membrane, isolation film and polymer colloid, the polymer colloid are uniformly applied to described
It between fetal membrane and isolation film, is kneaded by the component of following parts by weight: 20~48 parts of hot melt adhesive；1.7~5 parts of naphthenic oil；It is white
10~20 parts of cement；30~60 parts of quartz sand；0.3~1 part of green pigment；1-5 parts of nano silica, 1-3 parts of nano aluminium oxide.
Further, the polymer colloid is kneaded by the component of following parts by weight: 30~48 parts of hot melt adhesive；Cycloalkanes
2~5 parts of oil；15~20 parts of white cement；30~50 parts of quartz sand；0.5~1 part of green pigment；3-5 parts of nano silica, nanometer
1-2 parts of aluminium oxide.
Further, the polymer colloid is kneaded by the component of following parts by weight: 30~40 parts of hot melt adhesive；Cycloalkanes
2~3 parts of oil；15~18 parts of white cement；30~40 parts of quartz sand；0.8~1 part of green pigment；It 3.5-5 parts of nano silica, receives
1-2 parts of aluminium oxide of rice.
Further, the polymer colloid is kneaded by the component of following parts by weight: 35 parts of hot melt adhesive；Naphthenic oil 3
Part；18 parts of white cement；35 parts of quartz sand；0.8 part of green pigment；3.5 parts of nano silica, 1 part of nano aluminium oxide.
Further, the preparation method of the polymer colloid is following steps:
1) it weighs by weight in 20~48 parts of hot melt adhesive and 1.7~5 parts of investment stills for air blowing of naphthenic oil, it is heated to 110~
150 DEG C, melts and stir evenly；
2) 10~20 parts of white cement, 30~60 parts of quartz sand and green pigment 0.3 are added into the mixture of step 1) preparation
~1 part, heating temperature is stirred evenly at 100~180 DEG C, and polymer colloid is prepared.
Waterproof material of the present invention, the beneficial effect is that: there is excellent weatherability, peel strength and waterproof performance, it can
The waterproof barrier of skin-type is made for construction material；Using the non-bituminous based raw material of environmental protection, component is uncomplicated and preparation process is simple
Single, production cost is low, the characteristics of having both economical and environmentally friendly, the bright prospects with large-scale industrial application.
Specific embodiment
It is next combined with specific embodiments below that present invention be described in more detail.
Embodiment 1
A kind of waterproof material, including fetal membrane, isolation film and polymer colloid, polymer colloid is uniformly in fetal membrane and isolation film
It between polymer colloid, is kneaded by the component of following parts by weight: 48 parts of hot melt adhesive；5 parts of naphthenic oil；20 parts of white cement；Stone
60 parts of sand；1 part of green pigment；5 parts of nano silica, 3 parts of nano aluminium oxide.
The preparation method of polymer colloid is following steps:
1) it weighs by weight in hot melt adhesive and naphthenic oil investment stills for air blowing, is heated to 150 DEG C, melts and stir evenly；
2) white cement, quartz sand and green pigment, heating temperature are added into the mixture of step 1) preparation to stir at 180 DEG C
It mixes uniformly, polymer colloid is prepared.
Embodiment 2
A kind of waterproof material, including fetal membrane, isolation film and polymer colloid, polymer colloid is uniformly in fetal membrane and isolation film
It between polymer colloid, is kneaded by the component of following parts by weight: 20 parts of hot melt adhesive；1.7 parts of naphthenic oil；10 parts of white cement；
30 parts of quartz sand；0.3 part of green pigment；1 part of nano silica, 1 part of nano aluminium oxide.
The preparation method of polymer colloid is following steps:
1) it weighs by weight in hot melt adhesive and naphthenic oil investment stills for air blowing, is heated to 110 DEG C, melts and stir evenly；
2) white cement, quartz sand and green pigment, heating temperature are added into the mixture of step 1) preparation to stir at 150 DEG C
It mixes uniformly, polymer colloid is prepared.
Embodiment 3
A kind of waterproof material, including fetal membrane, isolation film and polymer colloid, polymer colloid is uniformly in fetal membrane and isolation film
It between polymer colloid, is kneaded by the component of following parts by weight: 30 parts of hot melt adhesive；2 parts of naphthenic oil；15 parts of white cement；Stone
50 parts of sand；0.5 part of green pigment；3 parts of nano silica, 2 parts of nano aluminium oxide.
The preparation method of polymer colloid is following steps:
1) it weighs by weight in hot melt adhesive and naphthenic oil investment stills for air blowing, is heated to 150 DEG C, melts and stir evenly；
2) white cement, quartz sand and green pigment, heating temperature are added into the mixture of step 1) preparation to stir at 170 DEG C
It mixes uniformly, polymer colloid is prepared.
Embodiment 4
A kind of waterproof material, including fetal membrane, isolation film and polymer colloid, polymer colloid is uniformly in fetal membrane and isolation film
It between polymer colloid, is kneaded by the component of following parts by weight: 40 parts of hot melt adhesive；3 parts of naphthenic oil；18 parts of white cement；Stone
40 parts of sand；0.8 part of green pigment；3.5 parts of nano silica, 1 part of nano aluminium oxide.
The preparation method of polymer colloid is following steps:
1) it weighs by weight in hot melt adhesive and naphthenic oil investment stills for air blowing, is heated to 150 DEG C, melts and stir evenly；
2) white cement, quartz sand and green pigment, heating temperature are added into the mixture of step 1) preparation to stir at 180 DEG C
It mixes uniformly, polymer colloid is prepared.
Embodiment 5
A kind of waterproof material, including fetal membrane, isolation film and polymer colloid, polymer colloid is uniformly in fetal membrane and isolation film
It between polymer colloid, is kneaded by the component of following parts by weight: 35 parts of hot melt adhesive；3 parts of naphthenic oil；18 parts of white cement；Stone
35 parts of sand；0.8 part of green pigment；3.5 parts of nano silica, 1 part of nano aluminium oxide.
The preparation method of polymer colloid is following steps:
1) it weighs by weight in hot melt adhesive and naphthenic oil investment stills for air blowing, is heated to 120 DEG C, melts and stir evenly；
2) white cement, quartz sand and green pigment, heating temperature are added into the mixture of step 1) preparation to stir at 180 DEG C
It mixes uniformly, polymer colloid is prepared
It is provided for the embodiments of the invention technical solution above to be described in detail, specific case used herein
The principle and embodiment of the embodiment of the present invention are expounded, the explanation of above embodiments is only applicable to help to understand this
The principle of inventive embodiments；At the same time, for those skilled in the art, according to an embodiment of the present invention, in specific embodiment party
There will be changes in formula and application range, in conclusion the contents of this specification are not to be construed as limiting the invention.
Claims (5)
1. a kind of waterproof material, it is characterised in that: including fetal membrane, isolation film and polymer colloid, the polymer colloid is uniform
It is applied between the fetal membrane and isolation film, is kneaded by the component of following parts by weight: 20~48 parts of hot melt adhesive；Naphthenic oil
1.7~5 parts；10~20 parts of white cement；30~60 parts of quartz sand；0.3~1 part of green pigment；1-5 parts of nano silica, nanometer
1-3 parts of aluminium oxide.
2. waterproof material according to claim 1, it is characterised in that: the polymer colloid is mixed by the component of following parts by weight
It refines: 30~48 parts of hot melt adhesive；2~5 parts of naphthenic oil；15~20 parts of white cement；30~50 parts of quartz sand；Green pigment 0.5~1
Part；3-5 parts of nano silica, 1-2 parts of nano aluminium oxide.
3. waterproof material according to claim 1, it is characterised in that: the polymer colloid is mixed by the component of following parts by weight
It refines: 30~40 parts of hot melt adhesive；2~3 parts of naphthenic oil；15~18 parts of white cement；30~40 parts of quartz sand；Green pigment 0.8~1
Part；3.5-5 parts of nano silica, 1-2 parts of nano aluminium oxide.
4. waterproof material according to claim 1, it is characterised in that: the polymer colloid is mixed by the component of following parts by weight
It refines: 35 parts of hot melt adhesive；3 parts of naphthenic oil；18 parts of white cement；35 parts of quartz sand；0.8 part of green pigment；Nano silica 3.5
Part, 1 part of nano aluminium oxide.
5. waterproof material according to claim 1, it is characterised in that: the preparation method of the polymer colloid is following step
It is rapid:
1) it weighs by weight in 20~48 parts of hot melt adhesive and 1.7~5 parts of investment stills for air blowing of naphthenic oil, is heated to 110~150
DEG C, melt and stirs evenly；
2) 10~20 parts of white cement, 30~60 parts of quartz sand and green pigment 0.3~1 are added into the mixture of step 1) preparation
Part, heating temperature is stirred evenly at 100~180 DEG C, and polymer colloid is prepared.