CN108998958A - Improve the processing method of woollen sweater feel made of 70S wool top - Google Patents
Improve the processing method of woollen sweater feel made of 70S wool top Download PDFInfo
- Publication number
- CN108998958A CN108998958A CN201810499712.0A CN201810499712A CN108998958A CN 108998958 A CN108998958 A CN 108998958A CN 201810499712 A CN201810499712 A CN 201810499712A CN 108998958 A CN108998958 A CN 108998958A
- Authority
- CN
- China
- Prior art keywords
- woollen sweater
- wool
- alkali
- feel
- sweater
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of wool processing technology field, especially a kind of processing method of woollen sweater；The purpose of the present invention overcomes the shortcomings of technology, provides one kind under the premise of not damaging wool, making woollen sweater made of 70S wool top after treatment has the processing method of woollen sweater feel made of a kind of raising 70S wool top of cashmere sense of touch；The first step, alkali tune index: alkali to be added in bath raio 1:20~1:30, the amount of alkali is that every woollen sweater needs 10~13 grams, then woollen sweater is put into the mixing liquid prepared, and is rotated 10~20 minutes by roller at normal temperature etc.；The processing method of woollen sweater feel made of a kind of raising 70S wool top designed by the present invention, enable to woollen sweater after treatment, the feel of woollen sweater can be as the feel of cashmere, it is more soft, it is more comfortable, soft to guarantee that woollen sweater is worn, meet the needs of actual use person.
Description
Technical field
The present invention relates to a kind of wool processing technology field, especially a kind of processing method of woollen sweater.
Background technique
The 70S wool top made of 100% wool is hair scale chip architecture on the market at present, relatively rough, and is passed through
Clothes feel made of 70S wool is not soft enough, and bundle body can be compared by wearing, to keep dress not comfortable enough.But 70S maos
Woollen sweater made of item seems unique style, is loved by consumers, and the demand in market is bigger, if making this sheep
Sweater can good hand touch, and it is now public all like cashmere sense, this at one we be badly in need of the technology to be solved.
Summary of the invention
The purpose of the present invention overcomes the shortcomings of technology, provides one kind under the premise of not damaging wool, 70S wool top is made
Woollen sweater there is the processing method of woollen sweater feel made of a kind of raising 70S wool top of cashmere sense of touch after treatment.
In order to achieve the above object, the processing method of woollen sweater feel made of a kind of raising 70S wool top designed by the present invention,
Its step are as follows:
The first step, alkali tune index: alkali to be added in bath raio 1:20~1:30, the amount of alkali is that every woollen sweater needs 10~13
Gram, then woollen sweater is put into the mixing liquid prepared, and is rotated 10~20 minutes by roller at normal temperature, roller turns
Speed is 14 revs/min, to guarantee that the alkaline index of wool reaches 9~9.5, wool is made to become more smooth, submissive and clean；
Cleaning treatment: woollen sweater the acid that pH value is 6~6.5 to be added in bath raio 1:40~1:60, is then put by second step
It impregnates 15~30 minutes in water and at normal temperature, to remove the alkaline solution and impurity on woollen sweater；
Third step, soft treatment: flexible solution is made in the softening agent that 6~6.5g/ part is added in 35~40 DEG C of water, then will
Woollen sweater is put into flexible solution and impregnates 20~30 minutes at normal temperature；
4th step, dehydration: being carried out dehydrating woollen sweater using industry washer, and dewatering time is 2~4min；
5th step, drying and processing: woollen sweater being placed into baking oven and carries out drying and processing, and drying time is 1~5 minute, drying
Temperature is 75~80 DEG C.
According to the above, the processing method of woollen sweater feel made of a kind of raising 70S wool top designed by the present invention,
Enable to woollen sweater after treatment, the feel of woollen sweater can be more soft as the feel of cashmere, to guarantee
Woollen sweater wears more comfortable, soft, meets the needs of actual use person.
Specific embodiment
Embodiment 1:
The processing method of woollen sweater feel made of a kind of raising 70S wool top of the present embodiment description, its step are as follows:
The first step, alkali tune index: alkali to be added in bath raio 1:25, the amount of alkali is that every woollen sweater needs 12 grams, then by sheep
Sweater is put into the mixing liquid prepared, and is rotated 15 minutes by roller at normal temperature, and the revolving speed of roller is 14 revs/min,
To guarantee that the alkaline index of wool reaches 9~9.5, wool is made to become more smooth, submissive and clean；
Cleaning treatment: woollen sweater the acid that pH value is 6 to be added in bath raio 1:50, is then put into water and normal by second step
Temperature is lower to impregnate 20 minutes, to remove the alkaline solution and impurity on woollen sweater；
Third step, soft treatment: flexible solution is made in the softening agent that 6g/ part is added in 38 DEG C of water, then puts woollen sweater
It impregnates 25 minutes in flexible solution and at normal temperature；
Dehydration: 4th step is carried out dehydrating woollen sweater using industry washer, dewatering time 3min；
5th step, drying and processing: woollen sweater being placed into baking oven and carries out drying and processing, and drying time is 3 minutes, drying temperature
It is 78 DEG C.
Embodiment 2:
The processing method of woollen sweater feel made of a kind of raising 70S wool top of the present embodiment description, its step are as follows:
The first step, alkali tune index: alkali to be added in bath raio 1:20, the amount of alkali is that every woollen sweater needs 10 grams, then by sheep
Sweater is put into the mixing liquid prepared, and is rotated 10 minutes by roller at normal temperature, and the revolving speed of roller is 14 revs/min,
To guarantee that the alkaline index of wool reaches 9~9.5, wool is made to become more smooth, submissive and clean；
Second step, cleaning treatment: in bath raio 1:40 be added pH value be 6.5 acid, then by woollen sweater be put into water and
It is impregnated 15 minutes under room temperature, to remove the alkaline solution and impurity on woollen sweater；
Third step, soft treatment: flexible solution is made in the softening agent that 6g/ part is added in 35 DEG C of water, then puts woollen sweater
It impregnates 20 minutes in flexible solution and at normal temperature；
Dehydration: 4th step is carried out dehydrating woollen sweater using industry washer, dewatering time 2min；
5th step, drying and processing: woollen sweater being placed into baking oven and carries out drying and processing, and drying time is 2 minutes, drying temperature
It is 80 DEG C.
Embodiment 3:
The processing method of woollen sweater feel made of a kind of raising 70S wool top of the present embodiment description, its step are as follows:
The first step, alkali tune index: alkali to be added in bath raio 1:30, the amount of alkali is that every woollen sweater needs 13 grams, then by sheep
Sweater is put into the mixing liquid prepared, and is rotated 20 minutes by roller at normal temperature, and the revolving speed of roller is 14 revs/min,
To guarantee that the alkaline index of wool reaches 9~9.5, wool is made to become more smooth, submissive and clean；
Second step, cleaning treatment: in bath raio 1:60 be added pH value be 6.5 acid, then by woollen sweater be put into water and
It is impregnated 30 minutes under room temperature, to remove the alkaline solution and impurity on woollen sweater；
Third step, soft treatment: flexible solution is made in the softening agent that 6.5g/ part is added in 40 DEG C of water, then by woollen sweater
It is put into flexible solution and impregnates 30 minutes at normal temperature；
Dehydration: 4th step is carried out dehydrating woollen sweater using industry washer, dewatering time 4min；
5th step, drying and processing: woollen sweater being placed into baking oven and carries out drying and processing, and drying time is 5 minutes, drying temperature
It is 75 DEG C.
Claims (1)
1. a kind of processing method for improving woollen sweater feel made of 70S wool top, it is characterised in that:
The first step, alkali tune index: alkali to be added in bath raio 1:20~1:30, the amount of alkali is that every woollen sweater needs 10~13
Gram, then woollen sweater is put into the mixing liquid prepared, and is rotated 10~20 minutes by roller at normal temperature, roller turns
Speed is 14 revs/min, to guarantee that the alkaline index of wool reaches 9~9.5, wool is made to become more smooth, submissive and clean；
Cleaning treatment: woollen sweater the acid that pH value is 6~6.5 to be added in bath raio 1:40~1:60, is then put by second step
It impregnates 15~30 minutes in water and at normal temperature, to remove the alkaline solution and impurity on woollen sweater；
Third step, soft treatment: flexible solution is made in the softening agent that 6~6.5g/ part is added in 35~40 DEG C of water, then will
Woollen sweater is put into flexible solution and impregnates 20~30 minutes at normal temperature；
4th step, dehydration: being carried out dehydrating woollen sweater using industry washer, and dewatering time is 2~4min；
5th step, drying and processing: woollen sweater being placed into baking oven and carries out drying and processing, and drying time is 1~5 minute, drying
Temperature is 75~80 DEG C.