CN108994990A - 一种提高藤条防霉效果的处理方法 - Google Patents
一种提高藤条防霉效果的处理方法 Download PDFInfo
- Publication number
- CN108994990A CN108994990A CN201811157748.7A CN201811157748A CN108994990A CN 108994990 A CN108994990 A CN 108994990A CN 201811157748 A CN201811157748 A CN 201811157748A CN 108994990 A CN108994990 A CN 108994990A
- Authority
- CN
- China
- Prior art keywords
- rattan
- parts
- processing method
- mold effect
- mould
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种提高藤条防霉效果的处理方法，涉及藤条加工技术领域。包括以下步骤：预处理、蒸煮、软化处理、防霉化处理和微波干燥。该发明涉及的提高藤条抗裂性能的处理方法，采用预处理和蒸煮处理使藤条软化，然后采用专用软化剂和防霉处理液对藤条进一步软化和防霉处理，效果明显且安全性高，最后采用微波干燥处理，更有利于软化剂和防霉处理液的渗入和发生发生作用，增强藤条木质纤维韧性，使得木质纤维形成束状纤维束，制备的藤条韧度较好，并具有良好的防霉效果。
Description
技术领域
本发明涉及藤条加工技术领域，具体涉及一种提高藤条防霉效果的处理方法。
背景技术
藤条，为热带藤蔓植物部分，其生长长度可达180多米，藤条质地坚韧、手感平滑、弹性性能好；藤条经处理后，可用于加工藤类工艺品、藤条家具、藤盘、藤箱等，其结实、耐用、观赏性高，具有美化家居生活的作用，藤类制品受到人们广泛喜爱。
由于藤条为木质类制品，未经特殊处理的藤条，制成工艺品及家居用品后，在高温高湿环境中，防腐防潮性能差，容易出现霉变，导致藤类制品使用寿命缩短。现在的处理剂多采用化学药剂，往往毒性较强，残留较严重，在编织品使用过程中往往会造成毒性残留物外泄，影响使用者健康。
发明内容
本发明的发明目的是，针对上述问题，提供一种提高藤条防霉效果的处理方法，制备的藤条韧度较好，可以更好的制作藤编制品，且有良好的防虫蛀和防霉效果。
为达到上述目的，本发明所采用的技术方案是：
一种提高藤条防霉效果的处理方法，包括以下步骤：
S1.预处理：选择完好，无虫蛀藤条，将藤条去叶后，用清水洗除杂质，然后放入质量分数为0.5～0.7％的食盐溶液中浸泡3～5h，取出藤条并沥干水分。
S2.蒸煮：将预处理后的藤条放入蒸煮液中，加热至90～95℃蒸煮15～20min，取出藤条，用清水冲洗干净备用。
所述蒸煮液包括：柠檬酸5～15％，高锰酸钾1～3％，磷酸三钠1～5％，其余为水。
S3.软化处理：将蒸煮后的藤条放入软化剂中浸泡2～12h。
S4.防霉化处理：将软化后的藤条沥干水分，在35～45℃下干燥至藤条的水分含量为30％～35％，取出静置至室温；然后放入防霉处理液中浸泡30～60min。
所述防霉处理液按照重量份由以下原料制成：
龙胆草5～8份、玉龙鞭2～5份、雷公藤1～3份、鱼腥草5～10份、曼陀罗5～10份、桑叶5～10份、山苍子油1～3份、陈皮精油0.5～2份、丁香精油1～2份、柑桔精油1～3份、肉桂精油0.2～4份、生姜精油1～2份、棕榈酸0.5～1.5份、壳聚糖1～3份、甲壳素1～3份、阻燃剂0.2～1份；
S5.微波干燥：将防霉化处理后的藤条置入温度为100～120℃、功率为400～500W的条件下微波干燥20～60min；然后在温度为35～45℃下烘干至水分含量为7～10％。
优选的，步骤S3中，浸泡过程中采用超声波进行处理，用频率为25～35kHz的超声波处理2～5h。
优选的，步骤S3中，所述软化剂按照重量份由以下原料制成：芦荟胶10～20份、壳聚糖季铵盐3～5份、浓度为15～20％氨水溶液5～15份、月桂酸单甘油酯3～5份、椰油酰胺丙基甜菜碱1～3份、冰醋酸10～20份、柠檬酸钾3～5份、木质素磺酸钠3～5份、甘油5～10份、过磷酸钙1～3份、茶皂素1～3份和水200～300份。
优选的，步骤S4中，所述阻燃剂为三氧化二锑。
优选的，步骤S5中，微波干燥后，向藤条喷洒1～3％的醋酸溶液，然后烘干。
由于采用上述技术方案，本发明具有以下有益效果：
1.本发明的提高藤条防霉效果的处理方法，采用预处理和蒸煮处理使藤条软化，然后采用专用软化剂和防霉处理液对藤条进一步软化和防霉处理，效果明显且安全性高，最后采用微波干燥处理，更有利于软化剂和防霉处理液的渗入和发生发生作用，增强藤条木质纤维韧性，使得木质纤维形成束状纤维束，制备的藤条韧度较好，并具有良好的防霉效果。
在微波干燥过程中，其发出的微波使藤条本身成为发热体，不需要热传导的过程，加热迅速，受热均匀，且由内到外进行脱水，水份排出速度快，电能消耗小，干燥效率高、效果好，并且可使藤条纤维打开，有利于软化剂和防霉处理液的渗透，从而使得藤条软化更充分、防霉效果更明显。另外，微波干燥时间过长会影响藤条的力学性能，因此，应该严格控制时间，当微波干燥时间不足以烘干时，再在烘箱内烘干为止。
采用以以天然植物成分为主要原料的防霉处理液，降低了生产成本，并且制得的消毒液无毒无害、防霉效果好，浸泡过的柳藤编制成产品后可长达20-30年不出现霉变和虫蛀现象，在使用过程不会产生和释放有害物质，可供人们放心使用。消毒液能充分杀死藤条内的寄生虫和细菌，增强藤条的防腐能力和阻燃效果。
2.本发明的提高藤条防霉效果的处理方法，以多种润滑剂和多种表面活性剂的复配，克服单一试剂的缺陷，从而提高藤条软化剂的性能。壳聚糖季铵盐、氨水溶液、芦荟胶、木质素磺酸钠、柠檬酸钾、甘油等润滑剂进行复配，各润滑剂之间产生协调效应，可以在藤条纤维素表面形成更稳定的润滑膜，降低藤条纤维素之间摩擦力，从而使软化剂更容易进入藤条纤维素结晶区之中，使纤维素晶格扩大和变得疏松，导致纤维素分子间相互移动变得易于发生，从而使藤条具有良好的塑性，进而使藤条呈现良好的软化性能；月桂酸单甘油酯、椰油酰胺丙基甜菜碱和木质素磺酸钠表面活性剂进行复配，各表面活性剂之间产生协调效应，可以形成更优的润湿、渗透性及吸附性能和降低表面张力的能力，从而提高软化剂渗透深度，进而提高藤条软化效果，同时，还可以离子化形成带电荷的离子，破坏藤条内部原有的电荷平衡，使藤条纤维素改变排列方向，并能使木素塑化，从而使藤条具有优良的编织性能。
3.本发明的提高藤条防霉效果的处理方法，采用以以天然植物成分为主要原料的防霉处理液，以龙胆草、玉龙鞭、雷公藤、鱼腥草、曼陀罗和桑叶结合，并协同山苍子油、陈皮精油、丁香精油、柑桔精油、肉桂精油和生姜精油共同期作用，能够提高防霉效果。通常一种植物精油或者提取物可以同时对多种病原微生物起作用，但是对植物病原微生物的抑制作用又具有选择性，不同种类的植物精油和提取物对不同品种的病原微生物的抑制能力不同。而且不同的提取物和精油之间有相互协同，成分之间会发生反应，结合使用可以提高其功能，而且防霉处理剂中的精油还能赋予荔枝以怡人的香味。
其中，山苍子油具有新鲜柠檬果香味、山苍子油对黄曲霉、桔青霉、总状毛霉、米根霉等多种霉菌均有较强的抗菌作用。
具体实施方式
为了使本发明的目的、技术方案及优点更加清楚明白，以下结合实施例，对本发明进行进一步详细说明。应当理解，此处所描述的具体实施例仅仅用以解释本发明，并不用于限定本发明。
实施例1
一种提高藤条防霉效果的处理方法，包括以下步骤：
S1.预处理：选择完好，无虫蛀藤条，将藤条去叶后，用清水洗除杂质，然后放入质量分数为0.6％的食盐溶液中浸泡4h，取出藤条并沥干水分。
S2.蒸煮：将预处理后的藤条放入蒸煮液中，加热至92℃蒸煮18min，取出藤条，用清水冲洗干净备用。
所述蒸煮液包括：柠檬酸10％，高锰酸钾2％，磷酸三钠3％，其余为水。
S3.软化处理：将蒸煮后的藤条放入软化剂中浸泡10h。
所述软化剂按照重量份由以下原料制成：芦荟胶8份、壳聚糖季铵盐4份、浓度为15～20％氨水溶液10份、月桂酸单甘油酯4份、椰油酰胺丙基甜菜碱2份、冰醋酸15份、柠檬酸钾4份、木质素磺酸钠4份、甘油6份、过磷酸钙2份、茶皂素2份和水250份。
S4.防霉化处理：将软化后的藤条沥干水分，在40℃下干燥至藤条的水分含量为32％，取出静置至室温；然后放入防霉处理液中浸泡30～60min。
所述防霉处理液按照重量份由以下原料制成：
龙胆草6份、玉龙鞭3份、雷公藤2份、鱼腥草8份、曼陀罗8份、桑叶7份、山苍子油2份、陈皮精油1份、丁香精油1.5份、柑桔精油2份、肉桂精油2份、生姜精油1.5份、棕榈酸1份、壳聚糖2份、甲壳素2份、阻燃剂0.5份；所述阻燃剂为三氧化二锑。
S5.微波干燥：将防霉化处理后的藤条置入温度为150℃、功率为150W的条件下微波干燥40min；然后在温度为40℃的烘箱内烘干至水分含量为8％。微波干燥后，向藤条喷洒2％的醋酸溶液，然后烘干。
实施例2
一种提高藤条防霉效果的处理方法，包括以下步骤：
S1.预处理：选择完好，无虫蛀藤条，将藤条去叶后，用清水洗除杂质，然后放入质量分数为0.7％的食盐溶液中浸泡5h，取出藤条并沥干水分。
S2.蒸煮：将预处理后的藤条放入蒸煮液中，加热至95℃蒸煮15min，取出藤条，用清水冲洗干净备用。
所述蒸煮液包括：柠檬酸15％，高锰酸钾1％，磷酸三钠1％，其余为水。
S3.软化处理：将蒸煮后的藤条放入软化剂中浸泡3h。
浸泡过程中采用超声波进行处理，用频率为25kHz的超声波处理。
所述软化剂按照重量份由以下原料制成：芦荟胶10份、壳聚糖季铵盐5份、浓度为15～20％氨水溶液15份、月桂酸单甘油酯5份、椰油酰胺丙基甜菜碱1份、冰醋酸10份、柠檬酸钾3份、木质素磺酸钠5份、甘油10份、过磷酸钙1份、茶皂素1份和水300份。
S4.防霉化处理：将软化后的藤条沥干水分，在35℃下干燥至藤条的水分含量为35％，取出静置至室温；然后放入防霉处理液中浸泡30min。
所述防霉处理液按照重量份由以下原料制成：
龙胆草8份、玉龙鞭2份、雷公藤3份、鱼腥草10份、曼陀罗5份、桑叶10份、山苍子油3份、陈皮精油0.5份、丁香精油1份、柑桔精油1份、肉桂精油4份、生姜精油1份、棕榈酸1.5份、壳聚糖1份、甲壳素1份、阻燃剂1份；所述阻燃剂为三氧化二锑。
S5.微波干燥：将防霉化处理后的藤条置入温度为100℃、功率为400W的条件下微波干燥60min；然后在温度为45℃下烘干至水分含量为7％。微波干燥后，向藤条喷洒3％的醋酸溶液，然后烘干。
实施例3
一种提高藤条防霉效果的处理方法，包括以下步骤：
S1.预处理：选择完好，无虫蛀藤条，将藤条去叶后，用清水洗除杂质，然后放入质量分数为0.5％的食盐溶液中浸泡3h，取出藤条并沥干水分。
S2.蒸煮：将预处理后的藤条放入蒸煮液中，加热至90℃蒸煮20min，取出藤条，用清水冲洗干净备用。
所述蒸煮液包括：柠檬酸5％，高锰酸钾3％，磷酸三钠5％，其余为水。
S3.软化处理：将蒸煮后的藤条放入软化剂中浸泡2h。
浸泡过程中采用超声波进行处理，用频率为35kHz的超声波处理。
芦荟胶20份、壳聚糖季铵盐3份、浓度为15～20％氨水溶液5份、月桂酸单甘油酯3份、椰油酰胺丙基甜菜碱3份、冰醋酸20份、柠檬酸钾5份、木质素磺酸钠3份、甘油5份、过磷酸钙3份、茶皂素3份和水200份。
S4.防霉化处理：将软化后的藤条沥干水分，在45℃下干燥至藤条的水分含量为30％，取出静置至室温；然后放入防霉处理液中浸泡60min。
所述防霉处理液按照重量份由以下原料制成：
龙胆草5份、玉龙鞭5份、雷公藤1份、鱼腥草5份、曼陀罗10份、桑叶5份、山苍子油1份、陈皮精油2份、丁香精油2份、柑桔精油3份、肉桂精油0.2份、生姜精油2份、棕榈酸0.5份、壳聚糖3份、甲壳素3份、阻燃剂0.2份；所述阻燃剂为三氧化二锑。
S5.微波干燥：将防霉化处理后的藤条置入温度为120℃、功率为500W的条件下微波干燥20min；然后在温度为35℃下烘干至水分含量为10％。微波干燥后，向藤条喷洒1～3％的醋酸溶液，然后烘干。
对比例1
一种提高藤条防霉效果的处理方法，与实施例3相比，没有步骤S4防霉化处理，其他步骤相同。
对比例2
一种提高藤条防霉效果的处理方法，与实施例3相比，步骤S5，没有微波干燥步骤，直接在温度为40℃的烘箱内烘干至水分含量为8％，其他步骤相同。
对比例3
一种提高藤条防霉效果的处理方法，与实施例3相比，步骤S4，防霉处理液中不含有山苍子油，其他原料和步骤相同。
将实施例1-3和对比例1-3制备的藤条进行测试，结果如下表1。
防霉效果具体测试方法为：将金黄色葡萄球菌、大肠杆菌、枯草芽孢杆菌接种于琼脂培养基中，在34℃培养箱中培养2天，挑选典型的菌落于灭菌的生理盐水中，制成108CFU/ml的混合细菌悬液，准备7个小烧杯，向每个小烧杯中注入30ml去离子水和0.3ml混合细菌悬液，分别向7个烧杯中加入实施例1-3、对比例1-4制备的藤条，藤条完全浸于溶液中，将样品在28℃条件下保存28天，分析每个烧杯含菌量，结果如下：
表1实施例1-3和对比例1-3测试结果对比
| 实施例1 | 实施例2 | 实施例3 | 对比例1 | 对比例2 | 对比例3 | |
| 菌落浓度(CFU/ml) | 4 | 3 | 3 | 25 | 12 | 8 |
从实施例1-3和对比例1-3的数据结合表1的数据可以看出，本发明处理的藤条具有较好的防霉效果。
从实施例3和对比例1的数据结合表1的数据可以看出，本实施例采用的以天然植物成分为主要原料的防霉处理液，不仅效果好，而且降低了生产成本、无毒无害。
从实施例3和对比例2的数据结合表1的数据可以看出，微波干燥可使藤条纤维打开，有利于防霉处理液的渗透，从而使得藤条防霉效果更明显。
从实施例3和对比例3的数据结合表1的数据可以看出，山苍子油具有较强的抗菌作用，与其他成分协同作用，效果明显。
上述说明是针对本发明较佳可行实施例的详细说明，但实施例并非用以限定本发明的专利申请范围。凡本发明所提示的技术构思下所完成的同等变化或修饰变更，均应属于本发明所涵盖专利范围。
Claims (5)
1.一种提高藤条防霉效果的处理方法，其特征在于，包括以下步骤：
S1.预处理：选择完好，无虫蛀藤条，将藤条去叶后，用清水洗除杂质，然后放入质量分数为0.5～0.7％的食盐溶液中浸泡3～5h，取出藤条并沥干水分；
S2.蒸煮：将预处理后的藤条放入蒸煮液中，加热至90～95℃蒸煮15～20min，取出藤条，用清水冲洗干净备用；
所述蒸煮液包括：柠檬酸5～15％，高锰酸钾1～3％，磷酸三钠1～5％，其余为水；
S3.软化处理：将蒸煮后的藤条放入软化剂中浸泡2～12h；
S4.防霉化处理：将软化后的藤条沥干水分，在35～45℃下干燥至藤条的水分含量为30％～35％，取出静置至室温；然后放入防霉处理液中浸泡30～60min；
所述防霉处理液按照重量份由以下原料制成：
龙胆草5～8份、玉龙鞭2～5份、雷公藤1～3份、鱼腥草5～10份、曼陀罗5～10份、桑叶5～10份、山苍子油1～3份、陈皮精油0.5～2份、丁香精油1～2份、柑桔精油1～3份、肉桂精油0.2～4份、生姜精油1～2份、棕榈酸0.5～1.5份、壳聚糖1～3份、甲壳素1～3份、阻燃剂0.2～1份；
S5.微波干燥：将防霉化处理后的藤条置入温度为100～120℃、功率为400～500W的条件下微波干燥20～60min；然后在温度为35～45℃下烘干至水分含量为7～10％。
2.根据权利要求1所述的提高藤条防霉效果的处理方法，其特征在于，步骤S3中，浸泡过程中采用超声波进行处理，用频率为25～35kHz的超声波处理2～5h。
3.根据权利要求1所述的提高藤条防霉效果的处理方法，其特征在于，步骤S3中，所述软化剂按照重量份由以下原料制成：芦荟胶10～20份、壳聚糖季铵盐3～5份、浓度为15～20％氨水溶液5～15份、月桂酸单甘油酯3～5份、椰油酰胺丙基甜菜碱1～3份、冰醋酸10～20份、柠檬酸钾3～5份、木质素磺酸钠3～5份、甘油5～10份、过磷酸钙1～3份、茶皂素1～3份和水200～300份。
4.根据权利要求1所述的提高藤条防霉效果的处理方法，其特征在于，步骤S4中，所述阻燃剂为三氧化二锑。
5.根据权利要求1所述的提高藤条防霉效果的处理方法，其特征在于，步骤S5中，微波干燥后，向藤条喷洒1～3％的醋酸溶液，然后烘干。