CN108951274A - A kind of combined mica paper and preparation method thereof - Google Patents
A kind of combined mica paper and preparation method thereof Download PDFInfo
- Publication number
- CN108951274A CN108951274A CN201810769139.0A CN201810769139A CN108951274A CN 108951274 A CN108951274 A CN 108951274A CN 201810769139 A CN201810769139 A CN 201810769139A CN 108951274 A CN108951274 A CN 108951274A
- Authority
- CN
- China
- Prior art keywords
- mica
- paper
- mesh
- mica paper
- flake
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of combined mica paper and preparation method thereof, mica flake are first used the mesh screen of 8 mesh remove ore, silt, material end, and by big, thick mica scrap and mica interlayer calculus are removed, and are processed into qualified mica flake, are then carried out washing and flotation；Use the high-pressure hydraulic crush method based on impact force, the high pressure water flow pressure that nozzle sprays is in l-2MPa, and the pressure and flow of nozzle water flow are adjusted by technique requirement, to improve point stripping efficiency of mica and avoid excessively crushing, radius-thickness ratio big high-quality lodicule and higher pulping rate are obtained.Combined mica paper scale produced by the present invention is larger, it is able to maintain the chemical composition and crystalline texture of natural mica, tensile strength is high, the anti-cut general character and permeability and good permeability, although the mica paper to solve prior art preparation has the characteristics that slightly high, but have the defects that the anti-cut general character, permeability and poor air permeability, thus the problem of influencing mica paper quality.
Description
Technical field
The present invention relates to pulp technology for making paper, specially a kind of combined mica paper and preparation method thereof.
Background technique
Mica is a kind of laminar silicic acid salt mineral generated naturally, with excellent physical property and electric property and
The characteristic of the above performance is still kept at high operating temperatures, it has complete chemical inertness and low flammability, it is most important that it
With anti-high voltage, corona-resistant and the characteristic of radiation protection.Therefore it is wide mainly as a kind of very important insulating materials
It is general for the industrial departments such as electronics, motor, telecommunication, electric appliance, aviation, traffic, instrument, metallurgy, building materials, light industry and national defence and
Sophisticated industry field.
Mica paper is a kind of nonmetallic mineral material of paper-like, it is to pass through powder first using fine platy garrulous mica as raw material
It is broken to crush mica for tiny scale, in the case where no any adhesive, by being classified slurrying, then in mica papermaking
On machine, by the sucking action of Van der Waals force manufacture paper with pulp molding and squeezing drying form coiled material mica paper.
Mica paper is made of pure natural mica flake completely, does not add any cellulose and other organic substances, institute
It is exactly its final products and production method with it and the unique similitude of plain paper.Mica paper maintains the excellent of natural mica
Benign energy, and thickness is uniform, dielectric strength fluctuation range is small, corona inception voltage is high and stablizes；The voltage of its dielectric loss is special
Property insulate more stable than mica splitting, and thermal conductivity is good, and temperature rise is low when use.And mica paper has had and mica splitting product phase
Corresponding whole kind, therefore replaced natural mica splitting in many fields.
The invention of Patent No. 106192548A proposes a kind of high-strength composite mica paper and preparation method thereof, the invention
Although the mica paper of preparation has the characteristics that slightly high, have the defects that the anti-cut general character, permeability and poor air permeability, thus shadow
The quality for ringing mica paper, for this purpose, it is proposed that a kind of combined mica paper and preparation method thereof.
Summary of the invention
The purpose of the present invention is to provide a kind of combined mica paper and preparation method thereof, to solve to mention in above-mentioned background technique
Out the problem of.
To achieve the above object, the invention provides the following technical scheme: a kind of preparation method of combined mica paper, including such as
Lower step:
(1) mesh screen of 8 mesh mica flake is first used to remove ore, silt, material end, thick mica scrap and mica layer by big
Between calculus remove, be processed into qualified mica flake, then carry out washing and flotation；
(2) use the high-pressure hydraulic crush method based on impact force, the high pressure water flow pressure that nozzle sprays in l-2MPa, and
The pressure and flow of nozzle water flow are adjusted by technique requirement, to improve point stripping efficiency of mica and avoid excessive powder
It is broken, obtain radius-thickness ratio big high-quality lodicule and higher pulping rate；
(3) mica flake is further removed in outside slurry by hydraulic classification equipment after hydraulic fracture is slurried and is mixed with portion
Divide big and thick scale, calculus, sand grains, the good slurry after classification is screened again, removes -150 purpose of 120 mesh by screen fractionation
Scale；
(4) it is manufactured paper with pulp by cylinder mould machine with slower speed, paper machine speed is determined with the thickness of mica paper model,
Mica paper is manufactured paper with pulp generally using double net single cylinders or more net single cylinder paper machines, on cylinder mould machine after the dehydration of mica slurry, by fresh cleaning
Miva splitting between existing Van der Waals force and electrostatic attraction, so that miva splitting is mutually overlapped to form page, it is true by drier
Empty dry forming obtains combined mica paper.
Preferably, the silt being attached on mica flake, dust, material end are removed by washing in the step (1), passed through
Flotation removes the sundries such as grass roots, leaf, the rope end mixed in mica flake.
Preferably, in the step (3) by sieve control 8 mesh, 16 mesh, 40 mesh, 60 mesh, 80 mesh, 100 mesh sizes cloud
The ratio of female scale distribution.
Preferably, the dryer temperature of cylinder mould machine is controlled at 90 DEG C hereinafter, temperature is avoided to cross high cloud in the step (4)
Female paper takes off cylinder, blistering, while the too low mica paper of temperature being avoided to glue cylinder.
Preferably, after miva splitting is mutually overlapped to form page in the step (4), a small amount of adhesive is added.
The present invention also provides combined mica paper made from a kind of above-mentioned preparation method.
Compared with prior art, the beneficial effects of the present invention are: the present invention shells broken slurrying, energy by using high pressure moisture
In the case where guaranteeing not destroying natural mica physical property, any surface finish, epigranular and the big mica squama of radius-thickness ratio are obtained
Piece；The grade for not meeting papermaking requirement is rejected by hydraulic classiciation, retains the grade for being suitble to mica papermaking；By being classified process,
The mica powder for meeting papermaking requirement is obtained, and high performance mica paper of manufacturing paper with pulp out, combined mica paper scale obtained is larger, can protect
The chemical composition and crystalline texture of natural mica are held, high temperature resistant, thickness is uniform, and tensile strength is high, the anti-cut general character and permeability
And good permeability, although thus the mica paper for solving prior art preparation have the characteristics that it is slightly high, there are the anti-cut general character,
The defect of permeability and poor air permeability, thus the problem of influencing mica paper quality.
Specific embodiment
The following is a clear and complete description of the technical scheme in the embodiments of the invention, it is clear that described embodiment
Only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, the common skill in this field
Art personnel every other embodiment obtained without making creative work belongs to the model that the present invention protects
It encloses.
The present invention provides a kind of technical solution:
A kind of preparation method of combined mica paper, includes the following steps:
(1) mesh screen of 8 mesh mica flake is first used to remove ore, silt, material end, thick mica scrap and mica layer by big
Between calculus remove, be processed into qualified mica flake, then carry out washing and flotation；
(2) use the high-pressure hydraulic crush method based on impact force, the high pressure water flow pressure that nozzle sprays in l-2MPa, and
The pressure and flow of nozzle water flow are adjusted by technique requirement, to improve point stripping efficiency of mica and avoid excessive powder
It is broken, obtain radius-thickness ratio big high-quality lodicule and higher pulping rate；
(3) mica flake is further removed in outside slurry by hydraulic classification equipment after hydraulic fracture is slurried and is mixed with portion
Divide big and thick scale, calculus, sand grains, the good slurry after classification is screened again, removes -150 purpose of 120 mesh by screen fractionation
Scale；
(4) it is manufactured paper with pulp by cylinder mould machine with slower speed, paper machine speed is determined with the thickness of mica paper model,
Mica paper is manufactured paper with pulp generally using double net single cylinders or more net single cylinder paper machines, on cylinder mould machine after the dehydration of mica slurry, by fresh cleaning
Miva splitting between existing Van der Waals force and electrostatic attraction, so that miva splitting is mutually overlapped to form page, it is true by drier
Empty dry forming obtains combined mica paper.
The present invention also provides combined mica paper made from a kind of above-mentioned preparation method.
Embodiment one:
Mica flake is first used first the mesh screen of 8 mesh remove ore, silt, material end, thick mica scrap and mica by big
Interlayer calculus removes, and is processed into qualified mica flake, then carries out washing and flotation；Use the high pressure water based on impact force
Power crush method, the high pressure water flow pressure that nozzle sprays in l-2MPa, and the pressure of nozzle water flow and flow by technique requirement into
Row is adjusted, so that point stripping for improving mica and avoids excessively crushing efficiency, obtain the big high-quality lodicule of radius-thickness ratio and it is higher go out
Slurry rate；Mica flake, which is further removed after hydraulic fracture is slurried, through hydraulic classification equipment in outside slurry, is mixed with part greatly
The scale of thickness, calculus, sand grains, the good slurry after classification are screened again, remove the scale of -150 mesh of 120 mesh by screen fractionation；
It is manufactured paper with pulp by cylinder mould machine with slower speed, paper machine speed is determined with the thickness of mica paper model, mica paper is manufactured paper with pulp
It is general to use double net single cylinders or more net single cylinder paper machines, on cylinder mould machine after the dehydration of mica slurry, by the miva splitting of fresh cleaning
Between existing Van der Waals force and electrostatic attraction, so that miva splitting is mutually overlapped to form page, by drier be dried in vacuo shape,
Obtain combined mica paper.
Embodiment two:
In example 1, following processes are added:
The silt being attached on mica flake, dust, material end are removed by washing in step (1), cloud is removed by flotation
The sundries such as the grass roots, leaf, the rope end that mix in female fragment.
Mica flake is first used first the mesh screen of 8 mesh remove ore, silt, material end, thick mica scrap and mica by big
Interlayer calculus removes, and is processed into qualified mica flake, then carries out washing and flotation；It is broken that mica is attached to by washing removing
The silt of on piece, dust, material end, remove the sundries such as the grass roots, leaf, the rope end that mix in mica flake by flotation；Use with
High-pressure hydraulic crush method based on impact force, the high pressure water flow pressure that nozzle sprays in l-2MPa, and the pressure of nozzle water flow and
Flow is adjusted by technique requirement, so that point stripping for improving mica and avoids excessively crushing efficiency, it is big to obtain radius-thickness ratio
High-quality lodicule and higher pulping rate；Mica flake further removes slurry by hydraulic classification equipment after hydraulic fracture is slurried
The big and thick scale in part, calculus, sand grains are mixed with during material is outer, the good slurry after classification is screened again, removed by screen fractionation
The scale of -150 mesh of 120 mesh；It is manufactured paper with pulp by cylinder mould machine with slower speed, paper is determined with the thickness of mica paper model
Locomotive speed, mica paper are manufactured paper with pulp and are generally leaned on new on cylinder mould machine after the dehydration of mica slurry using double net single cylinders or more net single cylinder paper machines
Existing Van der Waals force and electrostatic attraction between the miva splitting of fresh cleaning, make miva splitting mutually be overlapped to form page, through overdrying
Dry device vacuum drying forming, obtains combined mica paper.
Embodiment three:
In example 2, following processes are added:
The mica flake distribution of 8 mesh, 16 mesh, 40 mesh, 60 mesh, 80 mesh, 100 mesh sizes is controlled in step (3) by sieve
Ratio.
Mica flake is first used first the mesh screen of 8 mesh remove ore, silt, material end, thick mica scrap and mica by big
Interlayer calculus removes, and is processed into qualified mica flake, then carries out washing and flotation；It is broken that mica is attached to by washing removing
The silt of on piece, dust, material end, remove the sundries such as the grass roots, leaf, the rope end that mix in mica flake by flotation；Use with
High-pressure hydraulic crush method based on impact force, the high pressure water flow pressure that nozzle sprays in l-2MPa, and the pressure of nozzle water flow and
Flow is adjusted by technique requirement, so that point stripping for improving mica and avoids excessively crushing efficiency, it is big to obtain radius-thickness ratio
High-quality lodicule and higher pulping rate；Mica flake further removes slurry by hydraulic classification equipment after hydraulic fracture is slurried
The big and thick scale in part, calculus, sand grains are mixed with during material is outer, the good slurry after classification is screened again, removed by screen fractionation
The scale of -150 mesh of 120 mesh；The mica flake distribution of 8 mesh, 16 mesh, 40 mesh, 60 mesh, 80 mesh, 100 mesh sizes is controlled by sieve
Ratio；It is manufactured paper with pulp by cylinder mould machine with slower speed, paper machine speed is determined with the thickness of mica paper model, mica
Paper is manufactured paper with pulp generally using double net single cylinders or more net single cylinder paper machines, on cylinder mould machine after the dehydration of mica slurry, by the cloud of fresh cleaning
Mother delaminate between existing Van der Waals force and electrostatic attraction, so that miva splitting is mutually overlapped to form page, it is dry by drier vacuum
Dry forming obtains combined mica paper.
Example IV:
In the third embodiment, following processes are added:
The dryer temperature of cylinder mould machine is controlled at 90 DEG C hereinafter, the excessively high mica paper of temperature is avoided to take off cylinder, rise in step (4)
Bubble, while the too low mica paper of temperature being avoided to glue cylinder.
Mica flake is first used first the mesh screen of 8 mesh remove ore, silt, material end, thick mica scrap and mica by big
Interlayer calculus removes, and is processed into qualified mica flake, then carries out washing and flotation；It is broken that mica is attached to by washing removing
The silt of on piece, dust, material end, remove the sundries such as the grass roots, leaf, the rope end that mix in mica flake by flotation；Use with
High-pressure hydraulic crush method based on impact force, the high pressure water flow pressure that nozzle sprays in l-2MPa, and the pressure of nozzle water flow and
Flow is adjusted by technique requirement, so that point stripping for improving mica and avoids excessively crushing efficiency, it is big to obtain radius-thickness ratio
High-quality lodicule and higher pulping rate；Mica flake further removes slurry by hydraulic classification equipment after hydraulic fracture is slurried
The big and thick scale in part, calculus, sand grains are mixed with during material is outer, the good slurry after classification is screened again, removed by screen fractionation
The scale of -150 mesh of 120 mesh；The mica flake distribution of 8 mesh, 16 mesh, 40 mesh, 60 mesh, 80 mesh, 100 mesh sizes is controlled by sieve
Ratio；It is manufactured paper with pulp by cylinder mould machine with slower speed, paper machine speed is determined with the thickness of mica paper model, mica
Paper is manufactured paper with pulp generally using double net single cylinders or more net single cylinder paper machines, on cylinder mould machine after the dehydration of mica slurry, by the cloud of fresh cleaning
Mother delaminate between existing Van der Waals force and electrostatic attraction, so that miva splitting is mutually overlapped to form page, it is dry by drier vacuum
Dry forming obtains combined mica paper；The dryer temperature of cylinder mould machine is controlled at 90 DEG C hereinafter, avoiding the excessively high mica paper of temperature de-
Cylinder, blistering, while the too low mica paper of temperature being avoided to glue cylinder.
Embodiment five:
In example IV, following processes are added:
After miva splitting is mutually overlapped to form page in step (4), a small amount of adhesive is added.
Mica flake is first used first the mesh screen of 8 mesh remove ore, silt, material end, thick mica scrap and mica by big
Interlayer calculus removes, and is processed into qualified mica flake, then carries out washing and flotation；It is broken that mica is attached to by washing removing
The silt of on piece, dust, material end, remove the sundries such as the grass roots, leaf, the rope end that mix in mica flake by flotation；Use with
High-pressure hydraulic crush method based on impact force, the high pressure water flow pressure that nozzle sprays in l-2MPa, and the pressure of nozzle water flow and
Flow is adjusted by technique requirement, so that point stripping for improving mica and avoids excessively crushing efficiency, it is big to obtain radius-thickness ratio
High-quality lodicule and higher pulping rate；Mica flake further removes slurry by hydraulic classification equipment after hydraulic fracture is slurried
The big and thick scale in part, calculus, sand grains are mixed with during material is outer, the good slurry after classification is screened again, removed by screen fractionation
The scale of -150 mesh of 120 mesh；The mica flake distribution of 8 mesh, 16 mesh, 40 mesh, 60 mesh, 80 mesh, 100 mesh sizes is controlled by sieve
Ratio；It is manufactured paper with pulp by cylinder mould machine with slower speed, paper machine speed is determined with the thickness of mica paper model, mica
Paper is manufactured paper with pulp generally using double net single cylinders or more net single cylinder paper machines, on cylinder mould machine after the dehydration of mica slurry, by the cloud of fresh cleaning
Mother delaminate between existing Van der Waals force and electrostatic attraction, so that miva splitting is mutually overlapped to form page, a small amount of adhesive be added；Through
Drier vacuum drying forming is crossed, combined mica paper is obtained；The dryer temperature of cylinder mould machine is controlled at 90 DEG C hereinafter, avoiding temperature
It spends high mica paper and takes off cylinder, blistering, while the too low mica paper of temperature being avoided to glue cylinder.
The present invention shells broken slurrying by using high pressure moisture, can guarantee the case where not destroying natural mica physical property
Under, obtain any surface finish, epigranular and the big mica flake of radius-thickness ratio；Papermaking requirement is not met by hydraulic classiciation rejecting
Grade retains the grade for being suitble to mica papermaking；By being classified process, the mica powder for meeting papermaking requirement is obtained, and it is high to manufacture paper with pulp out
The mica paper of performance, combined mica paper scale obtained is larger, is able to maintain the chemical composition and crystalline texture of natural mica, resistance to height
Temperature, thickness is uniform, and tensile strength is high, the anti-cut general character and permeability and good permeability, to solve prior art preparation
Although mica paper has the characteristics that slightly high, have the defects that the anti-cut general character, permeability and poor air permeability, to influence mica
The problem of paper quality.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (6)
1. a kind of preparation method of combined mica paper, characterized by the following steps:
(1) mesh screen of 8 mesh mica flake is first used to remove ore, silt, material end, thick mica scrap and mica interlayer knot by big
Stone removes, and is processed into qualified mica flake, then carries out washing and flotation；
(2) the high-pressure hydraulic crush method based on impact force is used, the high pressure water flow pressure that nozzle sprays is in l-2MPa, and nozzle
The pressure and flow of water flow are adjusted by technique requirement, to improve point stripping efficiency of mica and avoid excessively crushing, are obtained
Obtain radius-thickness ratio big high-quality lodicule and higher pulping rate；
(3) mica flake is further removed in outside slurry by hydraulic classification equipment after hydraulic fracture is slurried and is mixed with part greatly
And scale, the calculus, sand grains of thickness, the good slurry after classification are screened again, remove the squama of -150 mesh of 120 mesh by screen fractionation
Piece；
(4) it is manufactured paper with pulp by cylinder mould machine with slower speed, paper machine speed is determined with the thickness of mica paper model, mica
Paper is manufactured paper with pulp generally using double net single cylinders or more net single cylinder paper machines, on cylinder mould machine after the dehydration of mica slurry, by the cloud of fresh cleaning
Mother delaminate between existing Van der Waals force and electrostatic attraction, so that miva splitting is mutually overlapped to form page, it is dry by drier vacuum
Dry forming obtains combined mica paper.
2. a kind of combined mica paper according to claim 1, it is characterised in that: removed in the step (1) by washing
Silt, the dust, material end being attached on mica flake, remove grass roots, leaf, the rope end etc. that mix in mica flake by flotation
Sundries.
3. a kind of preparation method of combined mica paper according to claim 1, it is characterised in that: lead in the step (3)
Be sieved 8 mesh of network control system, 16 mesh, 40 mesh, 60 mesh, 80 mesh, 100 mesh sizes mica flake distribution ratio.
4. a kind of preparation method of combined mica paper according to claim 1, it is characterised in that: circle in the step (4)
The dryer temperature of net paper machine is controlled at 90 DEG C hereinafter, avoiding the excessively high mica paper of temperature from taking off cylinder, blistering, while avoiding temperature too low
Mica paper glues cylinder.
5. a kind of preparation method of combined mica paper according to claim 1, it is characterised in that: step (4) medium cloud
Mother delaminates mutually be overlapped to form page after, a small amount of adhesive is added.
6. a kind of combined mica paper, it is characterised in that: combined mica paper preparation as described in claim 1-5 any one
Method is prepared.