CN108947372A - 一种水泥混凝土面层楼地面用水泥砂浆 - Google Patents
一种水泥混凝土面层楼地面用水泥砂浆 Download PDFInfo
- Publication number
- CN108947372A CN108947372A CN201810847927.7A CN201810847927A CN108947372A CN 108947372 A CN108947372 A CN 108947372A CN 201810847927 A CN201810847927 A CN 201810847927A CN 108947372 A CN108947372 A CN 108947372A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- agent
- cement mortar
- reducing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种水泥混凝土面层楼地面用水泥砂浆，包括由以下原料制备而成：橡胶粉水泥砂浆、压电陶瓷粉、硅藻土、聚对苯二甲酸乙二酯纤维、改性乳化沥青、活化改性沸石、水分散多元醇树脂、石膏、聚氨酯溶液、三聚磷酸钠、外掺剂、高效减水剂、硬化剂、硅酸镁铝触变润滑剂、硅灰、膨胀剂、减水剂、阻锈剂和水。本发明通过将水分散多元醇树脂、三聚磷酸钠、外掺剂引入橡胶粉水泥砂浆砂浆中可提高橡胶粉水泥砂浆砂浆的粘结力，并具有优良的抗渗性、抗裂性、抗冲击性、抗冻融性等性能；且通过采用的复合阻锈剂，水泥适应性良好、与减水剂、膨胀剂等外加剂之间具有较好的相容性。
Description
技术领域
本发明涉及一种水泥砂浆，具体是一种水泥混凝土面层楼地面用水泥砂浆。
背景技术
由橡胶粉水泥砂浆、沙子、高效减水剂2-5份、硬化剂3-6份、硅酸镁铝触变润滑剂1-4份和水的混合物叫橡胶粉水泥砂浆砂浆。用于建筑工程等场所，如建房等。普通的橡胶粉水泥砂浆砂浆主要成分就是橡胶粉水泥砂浆和砂子，橡胶粉水泥砂浆砂子结合在一起的粘合力也是蛮强的，但是随着干燥、过分潮湿环境的影响，会影响橡胶粉水泥砂浆砂浆的粘着力。
橡胶粉水泥砂浆作为一种水硬性胶凝材料在建筑工程领域得到广泛的应用，其主要特性为加入适量水后具有的可塑性，不仅能够在空气中硬化，也能够在水中硬化。橡胶粉水泥砂浆特别适用于制造混凝土，并被广泛的应用于路面铺设、房屋建筑等场合。现有的建筑材料如橡胶粉水泥砂浆砂浆具有施工简便、强度高等特点被广泛应用，但随着用户需求的提高，对于建筑材料性能的要求越来越高。
发明内容
本发明的目的在于提供一种水泥混凝土面层楼地面用水泥砂浆，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：
一种水泥混凝土面层楼地面用水泥砂浆，包括由以下重量份的原料制备而成：橡胶粉水泥砂浆85～100份、压电陶瓷粉20～35份、硅藻土20～30份、聚对苯二甲酸乙二酯纤维15～30份、改性乳化沥青10～20份、活化改性沸石10～15份、水分散多元醇树脂20～35份、石膏10～20份、聚氨酯溶液10～15份、三聚磷酸钠15～20份、外掺剂5～10份、高效减水剂2～5份、硬化剂3～6份、硅酸镁铝触变润滑剂1～4份、硅灰10～30份、膨胀剂20～40份、减水剂3～9份、阻锈剂0.5～2份和水6～12份。
作为本发明进一步的方案：所述水泥砂浆包括由以下重量份的原料制备而成：橡胶粉水泥砂浆94份、压电陶瓷粉25份、硅藻土26份、聚对苯二甲酸乙二酯纤维19份、改性乳化沥青15份、活化改性沸石13份、水分散多元醇树脂28份、石膏18份、聚氨酯溶液13份、三聚磷酸钠18份、外掺剂8份、高效减水剂3.5份、硬化剂4.5份、硅酸镁铝触变润滑剂2.5份、硅灰20份、膨胀剂30份、减水剂6份、阻锈剂1份、硅灰20份、膨胀剂30份、减水剂6份、阻锈剂1份、和水9份。
作为本发明进一步的方案：所述外掺剂为萘系缩合物。
作为本发明进一步的方案：所述硬化剂为硬脂酸、氢氧化钠和氧化钙的混合物。
作为本发明进一步的方案：所述的膨胀剂为硫铝酸钙类膨胀剂中的Sino-t60型膨胀剂。
作为本发明进一步的方案：所述的减水剂为萘磺酸盐减水剂中的ZWL-Ⅱ型减水剂。
作为本发明进一步的方案：所述的阻锈剂为三乙醇胺、乙醇胺和苯甲酸钠以质量比1:2:1复合而成的混合物。
作为本发明进一步的方案：所述的硅灰为活性硅灰。
与现有技术相比，本发明的有益效果是：
本发明通过将水分散多元醇树脂、三聚磷酸钠、外掺剂引入橡胶粉水泥砂浆砂浆中可提高橡胶粉水泥砂浆砂浆的粘结力，并具有优良的抗渗性、抗裂性、抗冲击性、抗冻融性等性能；且通过采用的复合阻锈剂，水泥适应性良好、与减水剂、膨胀剂等外加剂之间具有较好的相容性，掺入水泥砂浆后对材料强度无不利影响，并且可在一定程度改善水泥砂浆拌合物的流动性，且砂浆基体致密度较高、防腐阻锈能力较好，具有优良的粘结性能、体积稳定性与施工性。
具体实施方式
下面将对本发明的技术方案进行清楚、完整地描述，显然，所描述的实施例是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
一种水泥混凝土面层楼地面用水泥砂浆，包括由以下重量份的原料制备而成：橡胶粉水泥砂浆85份、压电陶瓷粉20份、硅藻土20份、聚对苯二甲酸乙二酯纤维15份、改性乳化沥青10份、活化改性沸石10份、水分散多元醇树脂20份、石膏10份、聚氨酯溶液10份、三聚磷酸钠15份、外掺剂5份、高效减水剂2份、硬化剂3份、硅酸镁铝触变润滑剂1份、硅灰10份、膨胀剂20份、减水剂3份、阻锈剂0.5份和水6份。
作为本发明进一步的方案：所述外掺剂为萘系缩合物。
作为本发明进一步的方案：所述硬化剂为硬脂酸、氢氧化钠和氧化钙的混合物。
作为本发明进一步的方案：所述的膨胀剂为硫铝酸钙类膨胀剂中的Sino-t60型膨胀剂。
作为本发明进一步的方案：所述的减水剂为萘磺酸盐减水剂中的ZWL-Ⅱ型减水剂。
作为本发明进一步的方案：所述的阻锈剂为三乙醇胺、乙醇胺和苯甲酸钠以质量比1:2:1复合而成的混合物。
作为本发明进一步的方案：所述的硅灰为活性硅灰。
实施例2
一种水泥混凝土面层楼地面用水泥砂浆，包括由以下重量份的原料制备而成：橡胶粉水泥砂浆94份、压电陶瓷粉25份、硅藻土26份、聚对苯二甲酸乙二酯纤维19份、改性乳化沥青15份、活化改性沸石13份、水分散多元醇树脂28份、石膏18份、聚氨酯溶液13份、三聚磷酸钠18份、外掺剂8份、高效减水剂3.5份、硬化剂4.5份、硅酸镁铝触变润滑剂2.5份、硅灰20份、膨胀剂30份、减水剂6份、阻锈剂1份、硅灰20份、膨胀剂30份、减水剂6份、阻锈剂1份、和水9份。
作为本发明进一步的方案：所述外掺剂为萘系缩合物。
作为本发明进一步的方案：所述硬化剂为硬脂酸、氢氧化钠和氧化钙的混合物。
作为本发明进一步的方案：所述的膨胀剂为硫铝酸钙类膨胀剂中的Sino-t60型膨胀剂。
作为本发明进一步的方案：所述的减水剂为萘磺酸盐减水剂中的ZWL-Ⅱ型减水剂。
作为本发明进一步的方案：所述的阻锈剂为三乙醇胺、乙醇胺和苯甲酸钠以质量比1:2:1复合而成的混合物。
作为本发明进一步的方案：所述的硅灰为活性硅灰。
实施例3
一种水泥混凝土面层楼地面用水泥砂浆，包括由以下重量份的原料制备而成：橡胶粉水泥砂浆100份、压电陶瓷粉35份、硅藻土30份、聚对苯二甲酸乙二酯纤维30份、改性乳化沥青20份、活化改性沸石15份、水分散多元醇树脂35份、石膏20份、聚氨酯溶液15份、三聚磷酸钠20份、外掺剂10份、高效减水剂5份、硬化剂6份、硅酸镁铝触变润滑剂4份、硅灰30份、膨胀剂40份、减水剂9份、阻锈剂2份和水12份。
作为本发明进一步的方案：所述外掺剂为萘系缩合物。
作为本发明进一步的方案：所述硬化剂为硬脂酸、氢氧化钠和氧化钙的混合物。
作为本发明进一步的方案：所述的膨胀剂为硫铝酸钙类膨胀剂中的Sino-t60型膨胀剂。
作为本发明进一步的方案：所述的减水剂为萘磺酸盐减水剂中的ZWL-Ⅱ型减水剂。
作为本发明进一步的方案：所述的阻锈剂为三乙醇胺、乙醇胺和苯甲酸钠以质量比1:2:1复合而成的混合物。
作为本发明进一步的方案：所述的硅灰为活性硅灰。
本发明通过将水分散多元醇树脂、三聚磷酸钠、外掺剂引入橡胶粉水泥砂浆砂浆中可提高橡胶粉水泥砂浆砂浆的粘结力，并具有优良的抗渗性、抗裂性、抗冲击性、抗冻融性等性能；且通过采用的复合阻锈剂，水泥适应性良好、与减水剂、膨胀剂等外加剂之间具有较好的相容性，掺入水泥砂浆后对材料强度无不利影响，并且可在一定程度改善水泥砂浆拌合物的流动性，且砂浆基体致密度较高、防腐阻锈能力较好，具有优良的粘结性能、体积稳定性与施工性。
以上所记载，仅为利用本创作技术内容的实施例，任何熟悉本项技艺者运用本创作所做的修饰、变化，皆属本创作主张的专利范围，而不限于实施例所揭示者。
若未特别说明，实施例中所采用的技术手段为本领域人员所熟知的常规手段，所采用的试剂和产品也均为可商业获得的。所用试剂的来源、商品名以及必要时列出其组成成分者，均在首次出现时标明。
Claims (8)
1.一种水泥混凝土面层楼地面用水泥砂浆，其特征是，包括由以下重量份的原料制备而成：橡胶粉水泥砂浆85～100份、压电陶瓷粉20～35份、硅藻土20～30份、聚对苯二甲酸乙二酯纤维15～30份、改性乳化沥青10～20份、活化改性沸石10～15份、水分散多元醇树脂20～35份、石膏10～20份、聚氨酯溶液10～15份、三聚磷酸钠15～20份、外掺剂5～10份、高效减水剂2～5份、硬化剂3～6份、硅酸镁铝触变润滑剂1～4份、硅灰10～30份、膨胀剂20～40份、减水剂3～9份、阻锈剂0.5～2份和水6～12份。
2.根据权利要求1所述的水泥混凝土面层楼地面用水泥砂浆，其特征是，所述水泥砂浆包括由以下重量份的原料制备而成：橡胶粉水泥砂浆94份、压电陶瓷粉25份、硅藻土26份、聚对苯二甲酸乙二酯纤维19份、改性乳化沥青15份、活化改性沸石13份、水分散多元醇树脂28份、石膏18份、聚氨酯溶液13份、三聚磷酸钠18份、外掺剂8份、高效减水剂3.5份、硬化剂4.5份、硅酸镁铝触变润滑剂2.5份、硅灰20份、膨胀剂30份、减水剂6份、阻锈剂1份、硅灰20份、膨胀剂30份、减水剂6份、阻锈剂1份、和水9份。
3.根据权利要求1所述的水泥混凝土面层楼地面用水泥砂浆，其特征是，所述外掺剂为萘系缩合物。
4.根据权利要求1所述的水泥混凝土面层楼地面用水泥砂浆，其特征是，所述硬化剂为硬脂酸、氢氧化钠和氧化钙的混合物。
5.根据权利要求1所述的水泥混凝土面层楼地面用水泥砂浆，其特征是，所述的膨胀剂为硫铝酸钙类膨胀剂中的Sino-t60型膨胀剂。
6.根据权利要求1所述的水泥混凝土面层楼地面用水泥砂浆，其特征是，所述的减水剂为萘磺酸盐减水剂中的ZWL-Ⅱ型减水剂。
7.根据权利要求1所述的水泥混凝土面层楼地面用水泥砂浆，其特征是，所述的阻锈剂为三乙醇胺、乙醇胺和苯甲酸钠以质量比1:2:1复合而成的混合物。
8.根据权利要求1所述的水泥混凝土面层楼地面用水泥砂浆，其特征是，所述的硅灰为活性硅灰。