CN108797224A - A kind of preparation method of disposable paper cup - Google Patents
A kind of preparation method of disposable paper cup Download PDFInfo
- Publication number
- CN108797224A CN108797224A CN201810756263.3A CN201810756263A CN108797224A CN 108797224 A CN108797224 A CN 108797224A CN 201810756263 A CN201810756263 A CN 201810756263A CN 108797224 A CN108797224 A CN 108797224A
- Authority
- CN
- China
- Prior art keywords
- preparation
- disposable paper
- dixie cup
- paper cup
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation methods of disposable paper cup, include the following steps：S1, it after mixing bagasse, polylactic acid, tackifying resin, isobornyl acrylate, ethylmaltol and water, stirs, then impurity is removed with double-layer filtering net, obtain filtrate；S2, filtrate is placed after extrusion drainage, exhaust supernatant liquor, obtain fining-off raw material；Fining-off raw material is added on mold, hot pressing, obtains dixie cup blank mould；S3, with laminating machine single side polyethylene film is drenched to dixie cup blank mould front, sided corona treatment is carried out to dixie cup blank mould reverse side, then pattern needed for press printing is used, then film at the beginning of dixie cup is cut into fan type slice, thin piece, it is folded into round dixie cup body, it is affectedly bashful in the corresponding thumb of cup body and food in hand and refers to corresponding position setting cellucotton layer, obtain disposable paper cup.Dixie cup produced by the present invention has excellent water resistance.
Description
Technical field
The present invention relates to dixie cups, and in particular to a kind of preparation method of disposable paper cup.
Background technology
Dixie cup is that the body paper made of chemical wood pulp (white board) is machined, bonds a kind of paper appearance being made
Device, appearance are in cup shape.For the dixie cup waxing that frozen food uses, ice cream, jam and butter etc. can be contained.It is used for hot drink
Dixie cup apply plastics, resistance to 90 DEG C of temperatures above, or even water can be bloomed.The characteristics of dixie cup is safety and sanitation, light and handy convenience.Public field
Institute, restaurant, dining room all can be used, and be disposable products.But the water resistance of existing dixie cup is not high, cannot meet the need in market
It asks.
Invention content
Technical problems based on background technology, the present invention propose a kind of preparation method of disposable paper cup.This hair
Bright dixie cup obtained has excellent water resistance.
A kind of preparation method of disposable paper cup proposed by the present invention, includes the following steps：Include the following steps：
S1, it after mixing bagasse, polylactic acid, tackifying resin, isobornyl acrylate, ethylmaltol and water, stirs,
Impurity is removed with double-layer filtering net again, obtains filtrate；
S2, filtrate is placed after extrusion drainage, exhaust supernatant liquor, obtain fining-off raw material；Fining-off raw material is added to
On mold, hot pressing obtains dixie cup blank mould；
S3, single side polyethylene film is drenched to dixie cup blank mould front with laminating machine, sided corona treatment is carried out to dixie cup blank mould reverse side, so
Pattern needed for press printing is used afterwards, and film at the beginning of dixie cup is then cut into fan type slice, thin piece, round dixie cup body is folded into, is affectedly bashful in hand
Cellucotton layer is arranged in the corresponding thumb of cup body and food middle finger corresponding position, obtains disposable paper cup.
Preferably, in S1, the speed of stirring is 2000-3000r/min, time 20-30min.
Preferably, in S2, the time of placement is 6-7h.
Preferably, in S2, the temperature of hot pressing is 150-180 DEG C, time 3-5min.
Preferably, in S3, polyethylene is modified poly ethylene, and preparation method is：It is added into the polyethylene of 1 parts by weight
The linseed oil of 1.2-3.5 parts by weight, is warming up to 150-250 DEG C, is stirred to react 1.5-2.5h, and the big of 0.4-0.9 parts by weight is added
Legumin, ultrasonication 25-50min under 350-500W, obtains modified poly ethylene.
Preferably, in S3, polyethylene is modified poly ethylene, and preparation method is：It is added 2 into the polyethylene of 1 parts by weight
The linseed oil of parts by weight is warming up to 200 DEG C, is stirred to react 2h, is added the soybean protein of 0.5 parts by weight, under 400W at ultrasonic wave
35min is managed, modified poly ethylene is obtained.
Preferably, in S3, the area of cellucotton layer is 5-8cm2。
The present invention raw material include：Bagasse, polylactic acid, tackifying resin, isobornyl acrylate, ethylmaltol etc.,
Each materials compatibility is preferable, assigns good water-fast and environmental-protecting performance of the invention, in a preferred approach, modified poly ethylene is selected to make
For the film of the present invention, and using linseed oil and soybean protein polyethylene is carried out it is composite modified, at high temperature, polyethylene with it is sub-
Sesame oil carries out graft reaction, due to containing hydroxyl in linseed oil, can form the network structure with certain degree of cross linking, while sub-
Double bond in sesame oil when polyethylene forms a film and cures can self-crosslinked oxidation, effectively improve the degree of cross linking of modified poly ethylene film；Separately
Outside, it can assign modified poly ethylene stronger hydrophobicity, and flax oil containing several hydrophobic long-chains in the molecule of linseed oil
Ester group in son can reinforce intermolecular active force and cohesive energy, improve the mechanical property of modified poly ethylene, to assign this
Invent excellent hardness and water resistance；Soybean protein is added, under the action of ultrasonic wave, soybean protein strand is unfolded, point
The chemical bond ruptures such as ammonia key, disulfide bond, expose hydrophobic group between subchain, are enriched in polyethylene surface, can increase and change
Property polyethylene hydrophobicity, further promoted the present invention water resistance.Through experiment, relative to dixie cup on the market, the present invention
Water resistance improve 13-18%.
Specific implementation mode
In the following, technical scheme of the present invention is described in detail by specific embodiment.
Embodiment 1
A kind of preparation method of disposable paper cup, includes the following steps：Include the following steps：
S1, it after mixing bagasse, polylactic acid, tackifying resin, isobornyl acrylate, ethylmaltol and water, stirs,
Impurity is removed with double-layer filtering net again, obtains filtrate；
S2, filtrate is placed after extrusion drainage, exhaust supernatant liquor, obtain fining-off raw material；Fining-off raw material is added to
On mold, hot pressing obtains dixie cup blank mould；
S3, single side polyethylene film is drenched to dixie cup blank mould front with laminating machine, sided corona treatment is carried out to dixie cup blank mould reverse side, so
Pattern needed for press printing is used afterwards, and film at the beginning of dixie cup is then cut into fan type slice, thin piece, round dixie cup body is folded into, is affectedly bashful in hand
Cellucotton layer is arranged in the corresponding thumb of cup body and food middle finger corresponding position, obtains disposable paper cup.
Embodiment 2
A kind of preparation method of disposable paper cup, includes the following steps：Include the following steps：
S1, it after mixing bagasse, polylactic acid, tackifying resin, isobornyl acrylate, ethylmaltol and water, stirs,
Impurity is removed with double-layer filtering net again, obtains filtrate；
S2, filtrate is placed after extrusion drainage, exhaust supernatant liquor, obtain fining-off raw material；Fining-off raw material is added to
On mold, hot pressing obtains dixie cup blank mould；
S3, single side polyethylene film is drenched to dixie cup blank mould front with laminating machine, sided corona treatment is carried out to dixie cup blank mould reverse side, so
Pattern needed for press printing is used afterwards, and film at the beginning of dixie cup is then cut into fan type slice, thin piece, round dixie cup body is folded into, is affectedly bashful in hand
Cellucotton layer is arranged in the corresponding thumb of cup body and food middle finger corresponding position, obtains disposable paper cup；
Wherein, in S1, the speed of stirring is 2500r/min, time 25min.
Embodiment 3
A kind of preparation method of disposable paper cup, includes the following steps：Include the following steps：
S1, it after mixing bagasse, polylactic acid, tackifying resin, isobornyl acrylate, ethylmaltol and water, stirs,
Impurity is removed with double-layer filtering net again, obtains filtrate；
S2, filtrate is placed after extrusion drainage, exhaust supernatant liquor, obtain fining-off raw material；Fining-off raw material is added to
On mold, hot pressing obtains dixie cup blank mould；
S3, single side polyethylene film is drenched to dixie cup blank mould front with laminating machine, sided corona treatment is carried out to dixie cup blank mould reverse side, so
Pattern needed for press printing is used afterwards, and film at the beginning of dixie cup is then cut into fan type slice, thin piece, round dixie cup body is folded into, is affectedly bashful in hand
Cellucotton layer is arranged in the corresponding thumb of cup body and food middle finger corresponding position, obtains disposable paper cup；
Wherein, in S1, the speed of stirring is 2500r/min, time 27min；
In S2, the time of placement is 6.5h；
In S2, the temperature of hot pressing is 165 DEG C, time 4min；
In S3, polyethylene is modified poly ethylene, and preparation method is：2 parts by weight are added into the polyethylene of 1 parts by weight
Linseed oil is warming up to 200 DEG C, is stirred to react 2h, is added the soybean protein of 0.5 parts by weight, ultrasonication 35min under 400W,
Obtain modified poly ethylene；
In S3, the area of cellucotton layer is 7cm2。
Embodiment 4
A kind of preparation method of disposable paper cup, includes the following steps：Include the following steps：
S1, it after mixing bagasse, polylactic acid, tackifying resin, isobornyl acrylate, ethylmaltol and water, stirs,
Impurity is removed with double-layer filtering net again, obtains filtrate；
S2, filtrate is placed after extrusion drainage, exhaust supernatant liquor, obtain fining-off raw material；Fining-off raw material is added to
On mold, hot pressing obtains dixie cup blank mould；
S3, single side polyethylene film is drenched to dixie cup blank mould front with laminating machine, sided corona treatment is carried out to dixie cup blank mould reverse side, so
Pattern needed for press printing is used afterwards, and film at the beginning of dixie cup is then cut into fan type slice, thin piece, round dixie cup body is folded into, is affectedly bashful in hand
Cellucotton layer is arranged in the corresponding thumb of cup body and food middle finger corresponding position, obtains disposable paper cup；
Wherein, in S1, the speed of stirring is 2000r/min, time 30min；
In S2, the time of placement is 6h；
In S2, the temperature of hot pressing is 180 DEG C, time 3min；
In S3, polyethylene is modified poly ethylene, and preparation method is：3.5 parts by weight are added into the polyethylene of 1 parts by weight
Linseed oil, be warming up to 150 DEG C, be stirred to react 2.5h, be added the soybean protein of 0.4 parts by weight, ultrasonication under 500W
25min obtains modified poly ethylene；
In S3, the area of cellucotton layer is 8cm2。
Embodiment 5
A kind of preparation method of disposable paper cup, includes the following steps：Include the following steps：
S1, it after mixing bagasse, polylactic acid, tackifying resin, isobornyl acrylate, ethylmaltol and water, stirs,
Impurity is removed with double-layer filtering net again, obtains filtrate；
S2, filtrate is placed after extrusion drainage, exhaust supernatant liquor, obtain fining-off raw material；Fining-off raw material is added to
On mold, hot pressing obtains dixie cup blank mould；
S3, single side polyethylene film is drenched to dixie cup blank mould front with laminating machine, sided corona treatment is carried out to dixie cup blank mould reverse side, so
Pattern needed for press printing is used afterwards, and film at the beginning of dixie cup is then cut into fan type slice, thin piece, round dixie cup body is folded into, is affectedly bashful in hand
Cellucotton layer is arranged in the corresponding thumb of cup body and food middle finger corresponding position, obtains disposable paper cup；
Wherein, in S1, the speed of stirring is 3000r/min, time 20min；
In S2, the time of placement is 7h；
In S2, the temperature of hot pressing is 150 DEG C, time 5min；
In S3, polyethylene is modified poly ethylene, and preparation method is：1.2 parts by weight are added into the polyethylene of 1 parts by weight
Linseed oil, be warming up to 250 DEG C, be stirred to react 1.5h, be added the soybean protein of 0.9 parts by weight, ultrasonication under 350W
50min obtains modified poly ethylene；
In S3, the area of cellucotton layer is 5cm2。
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Any one skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (7)
1. a kind of preparation method of disposable paper cup, which is characterized in that include the following steps：
S1, it after mixing bagasse, polylactic acid, tackifying resin, isobornyl acrylate, ethylmaltol and water, stirs, then use
Double-layer filtering net removes impurity, obtains filtrate；
S2, filtrate is placed after extrusion drainage, exhaust supernatant liquor, obtain fining-off raw material；Fining-off raw material is added into mold
On, hot pressing obtains dixie cup blank mould；
S3, single side polyethylene film is drenched to dixie cup blank mould front with laminating machine, sided corona treatment is carried out to dixie cup blank mould reverse side, is then used
Film at the beginning of dixie cup is then cut into fan type slice, thin piece by pattern needed for press printing, is folded into round dixie cup body, and cup body is affectedly bashful in hand
Cellucotton layer is arranged in corresponding thumb and food middle finger corresponding position, obtains disposable paper cup.
2. the preparation method of disposable paper cup according to claim 1, which is characterized in that in S1, the speed of stirring is 2000-
3000r/min, time 20-30min.
3. the preparation method of disposable paper cup according to claim 1 or claim 2, which is characterized in that in S2, the time of placement is 6-
7h。
4. the preparation method of disposable paper cup according to claim 1 or claim 2, which is characterized in that in S2, the temperature of hot pressing is
150-180 DEG C, time 3-5min.
5. the preparation method of disposable paper cup according to claim 1 or claim 2, which is characterized in that in S3, polyethylene is modified poly-
Ethylene, preparation method are：The linseed oil of 1.2-3.5 parts by weight is added into the polyethylene of 1 parts by weight, is warming up to 150-250
DEG C, it is stirred to react 1.5-2.5h, is added the soybean protein of 0.4-0.9 parts by weight, ultrasonication 25-50min under 350-500W,
Obtain modified poly ethylene.
6. the preparation method of disposable paper cup according to claim 5, which is characterized in that in S3, polyethylene is modified poly- second
Alkene, preparation method are：The linseed oil of 2 parts by weight is added into the polyethylene of 1 parts by weight, is warming up to 200 DEG C, is stirred to react
The soybean protein of 0.5 parts by weight is added in 2h, and ultrasonication 35min under 400W obtains modified poly ethylene.
7. the preparation method of disposable paper cup according to claim 1 or claim 2, which is characterized in that in S3, the area of cellucotton layer
For 5-8cm2。