CN108751848A - 一种高强度耐水瓷砖粘合剂及其制备方法 - Google Patents
一种高强度耐水瓷砖粘合剂及其制备方法 Download PDFInfo
- Publication number
- CN108751848A CN108751848A CN201810657902.0A CN201810657902A CN108751848A CN 108751848 A CN108751848 A CN 108751848A CN 201810657902 A CN201810657902 A CN 201810657902A CN 108751848 A CN108751848 A CN 108751848A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- resistance
- tile adhesives
- strength water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种高强度耐水瓷砖粘合剂及其制备方法，其由以下重量份的原料制成：普通硅酸盐水泥50‑60份、盐石膏20‑30份、板岩28‑34份、贝得石22‑28份、辉绿岩15‑20份、镁强粉10‑15份、准球形玻璃粉5‑10份、硅酸镁锂8‑16份、醋酸乙烯‑叔碳酸乙烯酯‑丙烯酸丁酯三元共聚乳胶粉4‑8份、海菜粉3‑6份、印度树胶2‑5份、4‑氯‑N‑(硬脂酰胺甲基)吡啶1‑2份、松香酸钙皂0.5‑1.5份、硬脂酸锆0.5‑1.5份。本发明制得的粘合剂不仅具有较高的粘接强度，还具有优良的耐水性、耐热性、耐酸碱腐蚀性、耐老化性、耐冻融性和耐候性，安全环保，施工方便，是一种非常理想的瓷砖粘结材料。
Description
发明领域
本发明涉及一种絮凝沉积制剂及其制备方法，具体涉及一种高强度耐水瓷砖粘合剂及其制备方法。
背景技术
瓷砖粘合剂，又称瓷砖胶、瓷砖粘结剂或瓷砖粘胶泥，主要用于粘贴瓷砖、面砖、地砖等装饰材料，广泛适用于内外墙面、地面、浴室、厨房等建筑的饰面装饰场所。目前瓷砖粘结剂多采用水泥砂浆，这种瓷砖粘结剂还存在着粘结强度低和耐水性差的缺点，影响瓷砖的耐久性，瓷砖容易剥落。
发明内容
本发明的目的在于提供一种高强度耐水瓷砖粘合剂及其制备方法。本发明制得的粘合剂不仅具有较高的粘接强度，还具有优良的耐水性、耐热性、耐酸碱腐蚀性、耐老化性、耐冻融性和耐候性。
为实现上述目的，本发明所采取的技术方案为：
本发明公开了一种高强度耐水瓷砖粘合剂，其由以下重量份的原料制成：
普通硅酸盐水泥50-60份、盐石膏20-30份、板岩28-34份、贝得石22-28份、辉绿岩15-20份、镁强粉10-15份、准球形玻璃粉5-10份、硅酸镁锂8-16份、醋酸乙烯-叔碳酸乙烯酯-丙烯酸丁酯三元共聚乳胶粉4-8份、海菜粉3-6份、印度树胶2-5份、4-氯-N-(硬脂酰胺甲基)吡啶1-2份、松香酸钙皂0.5-1.5份、硬脂酸锆0.5-1.5份。
优选地，一种高强度耐水瓷砖粘合剂，其由以下重量份的原料制成：普通硅酸盐水泥54-56份、盐石膏23-27份、板岩30-32份、贝得石24-26份、辉绿岩17-19份、镁强粉12-14份、准球形玻璃粉6-8份、硅酸镁锂10-14份、醋酸乙烯-叔碳酸乙烯酯-丙烯酸丁酯三元共聚乳胶粉5-7份、海菜粉4-5份、印度树胶3-4份、4-氯-N-(硬脂酰胺甲基)吡啶1.2-1.8份、松香酸钙皂0.8-1.2份、硬脂酸锆0.9-1.1份。
优选地，一种高强度耐水瓷砖粘合剂，其由以下重量份的原料制成：普通硅酸盐水泥55份、盐石膏25份、板岩31份、贝得石25份、辉绿岩18份、镁强粉13份、准球形玻璃粉7份、硅酸镁锂12份、醋酸乙烯-叔碳酸乙烯酯-丙烯酸丁酯三元共聚乳胶粉6份、海菜粉4.5份、印度树胶3.5份、4-氯-N-(硬脂酰胺甲基)吡啶1.5份、松香酸钙皂1份、硬脂酸锆1份。
本发明还公开了一种高强度耐水瓷砖粘合剂的制备方法，包括以下步骤：
(1)将盐石膏、板岩、贝得石、辉绿岩混合，粉碎，过筛，待用；
(2)将海菜粉、镁强粉、准球形玻璃粉一同加入到步骤(1)制得的粉碎料中，搅拌混合15-25min，得混合料A；
(3)将硅酸镁锂、印度树胶、乙烯-叔碳酸乙烯酯-丙烯酸丁酯三元共聚乳胶粉加入到普通硅酸盐水泥中，搅拌混合5-10min，得混合料B；
(4)将步骤(1)制得的混合料A以及4-氯-N-(硬脂酰胺甲基)吡啶、松香酸钙皂、硬脂酸锆一同加入到混合料B中，搅拌混合10-20min，出料分装即可。
优选地，步骤(1)中所述过筛目数为300-500目。
优选地，步骤(2)中所述搅拌转速为50-100r/min。
优选地，步骤(3)中所述搅拌转速为100-150r/min。
优选地，步骤(4)中所述搅拌转速为80-120r/min。
本发明的有益效果：
本发明添加的盐石膏、板岩、贝得石、辉绿岩与普通硅酸盐水泥配合使用，不仅可以显著改善粘合剂的粘结性能，还可以提高粘合剂的机械强度、防潮性和耐水性；添加的醋酸乙烯-叔碳酸乙烯酯-丙烯酸丁酯三元共聚乳胶粉与海菜粉、印度树胶配合使用，协同互补增效，可以显著提高粘合剂的粘结强度、抗水性、抗酸碱腐蚀性和耐候性，添加的镁强粉和准球形玻璃粉，可以显著改善粘合剂的力学性能、化学稳定性、热稳定性、耐水性和耐老化性，添加的4-氯-N-(硬脂酰胺甲基)吡啶、松香酸钙皂、硬脂酸锆三种原料相互配合作为防水剂，显著提高粘合剂的耐水性。本发明制得的粘合剂不仅具有较高的粘接强度，还具有优良的耐水性、耐热性、耐酸碱腐蚀性、耐老化性、耐冻融性和耐候性，安全环保，施工方便，是一种非常理想的瓷砖粘结材料。
具体实施方式
下面结合具体实施例对本发明所述技术方案作进一步的说明。
实施例1：
一种高强度耐水瓷砖粘合剂，其由以下重量份的原料制成：普通硅酸盐水泥50份、盐石膏20份、板岩28份、贝得石22份、辉绿岩15份、镁强粉10份、准球形玻璃粉5份、硅酸镁锂8份、醋酸乙烯-叔碳酸乙烯酯-丙烯酸丁酯三元共聚乳胶粉4份、海菜粉3份、印度树胶2份、4-氯-N-(硬脂酰胺甲基)吡啶1份、松香酸钙皂0.5份、硬脂酸锆0.5份。
一种高强度耐水瓷砖粘合剂的制备方法，包括以下步骤：
(1)将盐石膏、板岩、贝得石、辉绿岩混合，粉碎，过300目筛，待用；
(2)将海菜粉、镁强粉、准球形玻璃粉一同加入到步骤(1)制得的粉碎料中，在搅拌转速为50r/min的条件下搅拌混合25min，得混合料A；
(3)将硅酸镁锂、印度树胶、乙烯-叔碳酸乙烯酯-丙烯酸丁酯三元共聚乳胶粉加入到普通硅酸盐水泥中，在搅拌转速为100r/min的条件下搅拌混合10min，得混合料B；
(4)将步骤(1)制得的混合料A以及4-氯-N-(硬脂酰胺甲基)吡啶、松香酸钙皂、硬脂酸锆一同加入到混合料B中，在搅拌转速为80r/min的条件下搅拌混合20min，出料分装即可。
实施例2：
一种高强度耐水瓷砖粘合剂，其由以下重量份的原料制成：普通硅酸盐水泥55份、盐石膏25份、板岩31份、贝得石25份、辉绿岩18份、镁强粉13份、准球形玻璃粉7份、硅酸镁锂12份、醋酸乙烯-叔碳酸乙烯酯-丙烯酸丁酯三元共聚乳胶粉6份、海菜粉4.5份、印度树胶3.5份、4-氯-N-(硬脂酰胺甲基)吡啶1.5份、松香酸钙皂1份、硬脂酸锆1份。
本发明还公开了一种高强度耐水瓷砖粘合剂的制备方法，包括以下步骤：
(1)将盐石膏、板岩、贝得石、辉绿岩混合，粉碎，过400目筛，待用；
(2)将海菜粉、镁强粉、准球形玻璃粉一同加入到步骤(1)制得的粉碎料中，在搅拌转速为80r/min的条件下搅拌混合20min，得混合料A；
(3)将硅酸镁锂、印度树胶、乙烯-叔碳酸乙烯酯-丙烯酸丁酯三元共聚乳胶粉加入到普通硅酸盐水泥中，在搅拌转速为120r/min的条件下搅拌混合8min，得混合料B；
(4)将步骤(1)制得的混合料A以及4-氯-N-(硬脂酰胺甲基)吡啶、松香酸钙皂、硬脂酸锆一同加入到混合料B中，在搅拌转速为100r/min的条件下搅拌混合15min，出料分装即可。
实施例3：
一种高强度耐水瓷砖粘合剂，其由以下重量份的原料制成：普通硅酸盐水泥60份、盐石膏30份、板岩34份、贝得石28份、辉绿岩20份、镁强粉15份、准球形玻璃粉10份、硅酸镁锂16份、醋酸乙烯-叔碳酸乙烯酯-丙烯酸丁酯三元共聚乳胶粉8份、海菜粉6份、印度树胶5份、4-氯-N-(硬脂酰胺甲基)吡啶2份、松香酸钙皂1.5份、硬脂酸锆1.5份。
一种高强度耐水瓷砖粘合剂的制备方法，包括以下步骤：
(1)将盐石膏、板岩、贝得石、辉绿岩混合，粉碎，过500目筛，待用；
(2)将海菜粉、镁强粉、准球形玻璃粉一同加入到步骤(1)制得的粉碎料中，在搅拌转速为100r/min的条件下搅拌混合15min，得混合料A；
(3)将硅酸镁锂、印度树胶、乙烯-叔碳酸乙烯酯-丙烯酸丁酯三元共聚乳胶粉加入到普通硅酸盐水泥中，在搅拌转速为150r/min的条件下搅拌混合5min，得混合料B；
(4)将步骤(1)制得的混合料A以及4-氯-N-(硬脂酰胺甲基)吡啶、松香酸钙皂、硬脂酸锆一同加入到混合料B中，在搅拌转速为120r/min的条件下搅拌混合10min，出料分装即可。
对比例1
一种瓷砖粘合剂，其由以下重量份的原料制成：普通硅酸盐水泥50份、盐石膏85份、镁强粉15份、硅酸镁锂8份、海菜粉9份、松香酸钙皂2份。
一种高强度耐水瓷砖粘合剂的制备方法，包括以下步骤：
(1)将盐石膏粉碎，过300目筛，待用；
(2)将海菜粉和镁强粉加入到步骤(1)制得的粉碎料中，在搅拌转速为50r/min的条件下搅拌混合25min，得混合料A；
(3)将硅酸镁锂加入到普通硅酸盐水泥中，在搅拌转速为100r/min的条件下搅拌混合10min，得混合料B；
(4)将步骤(1)制得的混合料A以及松香酸钙皂一同加入到混合料B中，在搅拌转速为80r/min的条件下搅拌混合20min，出料分装即可。
瓷砖粘合剂的性能测试
采用国标48mm×48mm泰陶瓷砖作为测试用标准瓷砖，普通硅酸盐水泥采用P·042.5等级产品。
瓷砖的处理方式遵循国家标准的要求，先将试验陶瓷砖浸水24h，沸水煮2h，105℃烘干4h，标准试验条件下至少放置24h。实验数据为5块瓷砖测试后的平均值。
测试方法按照《陶瓷墙地砖胶粘剂》JCT 547-2005标准要求测试实验。
上述实施例1-3和对比例1制得的瓷砖粘合剂与现有的瓷砖粘合剂的主要性能检测如下表所示：
表1
| 检测项目 | 实施例1 | 实施例2 | 实施例3 | 对比例1 |
| 剪切强度(MPa) | 2.35 | 2.49 | 2.41 | 1.57 |
| 线收缩(％) | 0.4 | 0.2 | 0.3 | 0.9 |
| 常温状态粘结强度(MPa) | 2.76 | 2.87 | 2.81 | 1.96 |
| 浸水后的粘结强度(MPa) | 2.01 | 2.12 | 2.07 | 1.32 |
| 热老化后的粘结强度(MPa) | 2.14 | 2.26 | 2.19 | 1.38 |
| 冻融循环后的粘结强度(MPa) | 2.23 | 2.31 | 2.25 | 1.51 |
| 水透性 | 无 | 无 | 无 | 有 |
由上表可以看出，与对比例1的瓷砖粘合剂相比较，本发明实施例1-3制得的瓷砖粘合剂在相同添加量的基础上采用多种组分协同配合作用，具有较高的粘结强度和较好的耐水性，且粘合层不透水，可以大大提高瓷砖的耐久性，瓷砖不容易剥落，延长瓷砖的使用寿命。
以上所述仅为本发明的优选实施例而已，并不用于限制本发明，对于本领域的技术人员来说，本发明可以有各种更改和变化。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (8)
1.一种高强度耐水瓷砖粘合剂，其特征在于，其由以下重量份的原料制成：普通硅酸盐水泥50-60份、盐石膏20-30份、板岩28-34份、贝得石22-28份、辉绿岩15-20份、镁强粉10-15份、准球形玻璃粉5-10份、硅酸镁锂8-16份、醋酸乙烯-叔碳酸乙烯酯-丙烯酸丁酯三元共聚乳胶粉4-8份、海菜粉3-6份、印度树胶2-5份、4-氯-N-(硬脂酰胺甲基)吡啶1-2份、松香酸钙皂0.5-1.5份、硬脂酸锆0.5-1.5份。
2.根据权利要求1所述的高强度耐水瓷砖粘合剂，其特征在于，其由以下重量份的原料制成：普通硅酸盐水泥54-56份、盐石膏23-27份、板岩30-32份、贝得石24-26份、辉绿岩17-19份、镁强粉12-14份、准球形玻璃粉6-8份、硅酸镁锂10-14份、醋酸乙烯-叔碳酸乙烯酯-丙烯酸丁酯三元共聚乳胶粉5-7份、海菜粉4-5份、印度树胶3-4份、4-氯-N-(硬脂酰胺甲基)吡啶1.2-1.8份、松香酸钙皂0.8-1.2份、硬脂酸锆0.9-1.1份。
3.根据权利要求1所述的高强度耐水瓷砖粘合剂，其特征在于，其由以下重量份的原料制成：普通硅酸盐水泥55份、盐石膏25份、板岩31份、贝得石25份、辉绿岩18份、镁强粉13份、准球形玻璃粉7份、硅酸镁锂12份、醋酸乙烯-叔碳酸乙烯酯-丙烯酸丁酯三元共聚乳胶粉6份、海菜粉4.5份、印度树胶3.5份、4-氯-N-(硬脂酰胺甲基)吡啶1.5份、松香酸钙皂1份、硬脂酸锆1份。
4.一种如权利要求1-3任一项所述的高强度耐水瓷砖粘合剂的制备方法，其特征在于，包括以下步骤：
(1)将盐石膏、板岩、贝得石、辉绿岩混合，粉碎，过筛，待用；
(2)将海菜粉、镁强粉、准球形玻璃粉一同加入到步骤(1)制得的粉碎料中，搅拌混合15-25min，得混合料A；
(3)将硅酸镁锂、印度树胶、乙烯-叔碳酸乙烯酯-丙烯酸丁酯三元共聚乳胶粉加入到普通硅酸盐水泥中，搅拌混合5-10min，得混合料B；
(4)将步骤(1)制得的混合料A以及4-氯-N-(硬脂酰胺甲基)吡啶、松香酸钙皂、硬脂酸锆一同加入到混合料B中，搅拌混合10-20min，出料分装即可。
5.根据权利要求4所述的高强度耐水瓷砖粘合剂的制备方法，其特征在于，步骤(1)中所述过筛目数为300-500目。
6.根据权利要求4所述的高强度耐水瓷砖粘合剂的制备方法，其特征在于，步骤(2)中所述搅拌转速为50-100r/min。
7.根据权利要求4所述的高强度耐水瓷砖粘合剂的制备方法，其特征在于，步骤(3)中所述搅拌转速为100-150r/min。
8.根据权利要求4所述的高强度耐水瓷砖粘合剂的制备方法，其特征在于，步骤(4)中所述搅拌转速为80-120r/min。