CN108610641A - A kind of aluminum strip based on flakey aluminium pigment - Google Patents
A kind of aluminum strip based on flakey aluminium pigment Download PDFInfo
- Publication number
- CN108610641A CN108610641A CN201611232463.6A CN201611232463A CN108610641A CN 108610641 A CN108610641 A CN 108610641A CN 201611232463 A CN201611232463 A CN 201611232463A CN 108610641 A CN108610641 A CN 108610641A
- Authority
- CN
- China
- Prior art keywords
- parts
- aluminium pigment
- flakey
- aluminum strip
- polymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of aluminum strips based on flakey aluminium pigment, are made of following parts by weight：5 99 parts of flakey aluminium pigment, 1 95 parts of wax, 15 parts of aluminium oxide, 24 parts of organic polymer, 35 parts of inorganic matter, 37 parts of polymer.The strip flakey aluminium pigment of the present invention is a kind of i.e. environmental protection (Diamond Search discharge), and the safety product (without dust pollution, no dust explosion risk) without application risk after improvement.Plastics, ink can be simply and easily widely used in, the fields such as paint solve the problems, such as that VOC emission is very high very big to environmental hazard and aluminium powder is very easy to that dust explosion occurs.
Description
Technical field
The present invention relates to aluminium pigment technical field, specially a kind of aluminum strip based on flakey aluminium pigment.
Background technology
Squamaceous aluminium pigment is typically pulpous state, and the form supply of material of paste or powdery, these pigment are frequently referred to aluminum paste
Or aluminium powder.The aluminium pigment of these forms is widely used in paint, the fields such as ink and plastics, the aluminium face of forms but these are supplied
Material has very big harm to environment, to health.Contain a large amount of volatile solvents inside aluminium paste, VOC emission is very high to ring
Border harm is very big；These solvents are inflammable and explosive simultaneously, abnormally dangerous.Aluminium powder is very easy to that dust explosion, elder brother in 2016 occurs
Mountain aluminium powder dust explosion is exactly wherein typical case；In addition the dust of aluminium powder also seriously affects the health of operating personnel.
Invention content
The purpose of the present invention is to provide a kind of aluminum strip based on flakey aluminium pigment, strip flakey aluminium face of the invention
Material is a kind of i.e. environmental protection (Diamond Search discharge), and safety product (without dust pollution, no dust without application risk after improvement
Risk of explosion).Plastics can be simply and easily widely used in, ink, it is very high to environment that the fields such as paint solve VOC emission
The problem of harm is very big and aluminium powder is very easy to that dust explosion occurs.
To achieve the above object, the present invention provides the following technical solutions：A kind of aluminum strip based on flakey aluminium pigment, by with
Lower parts by weight are constituted：5-99 parts of flakey aluminium pigment, 1-95 parts of wax, 1-5 parts of aluminium oxide, 2-4 parts of organic polymer, inorganic matter 3-
5 parts, 3-7 parts of polymer.
Preferably, the organic polymer includes one kind of acrylate copolymer, alkyd polymer and polyester resin.
Preferably, the inorganic matter includes one kind of silica, titanium oxide and zirconium oxide.
Preferably, the polymer includes polyethylene wax (PE waxes), polypropylene wax (PP waxes), ethane-acetic acid ethyenyl copolymerization
Wax (EVA waxes), oxidized polyethylene wax, acrylic resin and alkyd resin are one such or a variety of.
Preferably, production method is as follows：
S1, pigment processing：Above-mentioned flakey aluminium pigment is coated into aluminium oxide, organic polymer and inorganic matter successively；
S2, mixed processing：The temperature of mixing machine is adjusted to 25-250 degrees Celsius, by wax, polymer and the squama wrapped
It is mixed in sheet aluminium pigment input mixing machine, and removes solvent, to obtain mixture；
S3, extruding and discharging：Screw machine is chosen, the temperature of screw machine is then adjusted to 100-250 degrees Celsius, discharge diameter
It adjusting to 0.01-8 millimeters, then discharging length adjustment the mixture in S2 is added in screw machine to 0.01-100 millimeters, from
And obtain aluminum strip.
Preferably, wrappage includes following combination in the flakey aluminium pigment：Alumina layer, alumina layer+titanium dioxide
Silicon layer, alumina layer+polymeric layer, alumina layer+silicon dioxide layer+polymeric layer, alumina layer+polymeric layer+titanium dioxide
Silicon layer.
Preferably, the screw machine is single-screw machine or dual-screw-stem machine.
Compared with prior art, beneficial effects of the present invention are as follows：
1, by adding aluminium oxide, organic polymer, inorganic matter and polymer, when using novel pigment aluminum strip of the invention
There is no dust and solvent contamination, keeps entire working environment more clean, more healthy to human body.The aluminum strip of the present invention is a kind of non-
Dangerous material, client as using traditional aluminium pigment using dangerous material special transport vehicle without being transported, without with dangerous material storehouse
Library stores, and production and transportation cost all greatly reduces in these.
2, the present invention allows harmful environment, traditional aluminium pigment for having risk of explosion and being detrimental to health to become a kind of
Environmental-friendly novel pigment aluminum strip without risk of explosion and without health hazard.
3, novel pigment aluminum strip of the invention is applied to ink, paints and exempts from the fields such as painted plastic to make to compare conventional aluminum
The better color effect of pigment, and it is more convenient to use quick.
Specific implementation mode
Below in conjunction with the embodiment of the present invention, technical scheme of the present invention is clearly and completely described, it is clear that
Described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.Based on the implementation in the present invention
Example, every other embodiment obtained by those of ordinary skill in the art without making creative efforts belong to
The scope of protection of the invention.
A kind of aluminum strip based on flakey aluminium pigment, is made of following parts by weight：5-99 parts of flakey aluminium pigment, wax 1-95
Part, 1-5 parts of aluminium oxide, 2-4 parts of organic polymer, 3-5 parts of inorganic matter, 3-7 parts of polymer.
In the present invention, organic polymer includes one kind of acrylate copolymer, alkyd polymer and polyester resin.
In the present invention, inorganic matter includes one kind of silica, titanium oxide and zirconium oxide.
In the present invention, polymer includes polyethylene wax (PE waxes), polypropylene wax (PP waxes), ethane-acetic acid ethyenyl copolymerization wax
(EVA waxes), oxidized polyethylene wax, acrylic resin and alkyd resin are one such or a variety of.
In the present invention, production method is as follows：
S1, pigment processing：Above-mentioned flakey aluminium pigment is coated into aluminium oxide, organic polymer and inorganic matter successively；
S2, mixed processing：The temperature of mixing machine is adjusted to 25-250 degrees Celsius, by wax, polymer and the squama wrapped
It is mixed in sheet aluminium pigment input mixing machine, and removes solvent, to obtain mixture；
S3, extruding and discharging：Screw machine is chosen, the temperature of screw machine is then adjusted to 100-250 degrees Celsius, discharge diameter
It adjusting to 0.01-8 millimeters, then discharging length adjustment the mixture in S2 is added in screw machine to 0.01-100 millimeters, from
And obtain aluminum strip.
In the present invention, wrappage includes following combination in flakey aluminium pigment：Alumina layer, alumina layer+silica
Layer, alumina layer+polymeric layer, alumina layer+silicon dioxide layer+polymeric layer, alumina layer+polymeric layer+silica
Layer.
In the present invention, screw machine is single-screw machine or dual-screw-stem machine.
Embodiment 1
A kind of aluminum strip based on flakey aluminium pigment, production method are as follows：
S1, pigment processing：Above-mentioned 8 parts of flakey aluminium pigments are coated into upper 2 parts of aluminium oxide, 2 parts of organic polymers and 3 successively
Part inorganic matter；
S2, mixed processing：The temperature of mixing machine is adjusted to 190 degrees Celsius, by 6 parts of waxes, 3 polymer and wrap 8
It is mixed in part flakey aluminium pigment input mixing machine, and removes solvent, to obtain mixture；
S3, extruding and discharging：Screw machine is chosen, the temperature of screw machine is then adjusted to 190 degrees Celsius, discharging diameter adjustment
To 3 millimeters, then discharging length adjustment the mixture in S2 is added in screw machine, to 30 millimeters to obtain aluminum strip.
Embodiment 2
A kind of aluminum strip based on flakey aluminium pigment, production method are as follows：
S1, pigment processing：By above-mentioned 10 parts of flakey aluminium pigments coat successively upper 3 parts of aluminium oxide, 3 parts of organic polymers and
4 parts of inorganic matters；
S2, mixed processing：The temperature of mixing machine adjusted to 210 degrees Celsius, by 7 parts of waxes, 4 parts of polymer and is wrapped
It is mixed in 10 parts of flakey aluminium pigment input mixing machines, and removes solvent, to obtain mixture；
S3, extruding and discharging：Screw machine is chosen, the temperature of screw machine is then adjusted to 210 degrees Celsius, discharging diameter adjustment
To 5 millimeters, then discharging length adjustment the mixture in S2 is added in screw machine, to 40 millimeters to obtain aluminum strip.
Embodiment 3
A kind of aluminum strip based on flakey aluminium pigment, production method are as follows：
S1, pigment processing：By above-mentioned 12 parts of flakey aluminium pigments coat successively upper 5 parts of aluminium oxide, 4 parts of organic polymers and
5 parts of inorganic matters；
S2, mixed processing：The temperature of mixing machine is adjusted to 220 degrees Celsius, by 10 parts of waxes, 7 parts of polymer and is wrapped
12 parts of flakey aluminium pigments input mixing machine in mixed, and solvent is removed, to obtain mixture；
S3, extruding and discharging：Screw machine is chosen, the temperature of screw machine is then adjusted to 220 degrees Celsius, discharging diameter adjustment
To 6 millimeters, then discharging length adjustment the mixture in S2 is added in screw machine, to 50 millimeters to obtain aluminum strip.
Embodiment 4
4 parts of 6 parts of the flakey aluminium paste and polyethylene chloroflo of aluminium oxide will be coated, mixing machine has been added to, at 180 degrees Celsius
Under conditions of mix 30 minutes, and under conditions of 200 degrees Celsius solvent volatilize remove.Then it is squeezed using single-screw machine
Go out aluminum strip granulation, the bore of single-screw machine is 4 millimeters.
Embodiment 5
5 parts of 5 parts of the flakey aluminium paste and polyethylene chloroflo of aluminium oxide will be coated, mixing machine has been added to, at 180 degrees Celsius
Under conditions of mix 30 minutes, and under conditions of 200 degrees Celsius solvent volatilize remove.Then it is squeezed using single-screw machine
Go out aluminum strip granulation, the bore of single-screw machine is 5 millimeters.
Embodiment 6
6 parts of 4 parts of the flakey aluminium paste and acrylic resin of aluminium oxide will be coated, mixing machine has been added to, at 200 degrees Celsius
Under conditions of mix 30 minutes, and under conditions of 200 degrees Celsius solvent volatilize remove.Then it is squeezed using single-screw machine
Go out aluminum strip granulation, the bore of single-screw machine is 4 millimeters.
Embodiment 7
3 parts of 7 parts of the flakey aluminium paste and ethane-acetic acid ethyenyl copolymerization wax (EVA waxes) of aluminium oxide will be coated, has been added to mixed
Conjunction machine mixes 30 minutes under conditions of 200 degrees Celsius, and solvent is volatilized under conditions of 200 degrees Celsius and is removed.Then make
It is carried out squeezing out aluminum strip granulation with single-screw machine, the bore of single-screw machine is 4 millimeters.
Concrete case
One client of somewhere wants to do the silver-like effect plastic products of Gao Bailiang always, attempts many traditional aluminium pastes and aluminium powder,
But because these aluminium pigment pieces are easy to be destroyed by machine, it is unable to reach the metal sense and white luminance of customer requirement.
After product of the present invention, it is found that the metal sense of silver color and white luminance are obviously improved, and the requirement of client can be reached.Finally
Client is obtained to approve and smoothly take order.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
Understanding without departing from the principles and spirit of the present invention can carry out these embodiments a variety of variations, modification, replace
And modification, the scope of the present invention is defined by the appended.
Claims (7)
1. a kind of aluminum strip based on flakey aluminium pigment, which is characterized in that be made of following parts by weight：Flakey aluminium pigment 5-99
Part, 1-95 parts of wax, 1-5 parts of aluminium oxide, 2-4 parts of organic polymer, 3-5 parts of inorganic matter, 3-7 parts of polymer.
2. a kind of aluminum strip based on flakey aluminium pigment according to claim 1, it is characterised in that：The organic polymer
Include one kind of acrylate copolymer, alkyd polymer and polyester resin.
3. a kind of aluminum strip based on flakey aluminium pigment according to claim 1, it is characterised in that：The inorganic matter includes
One kind of silica, titanium oxide and zirconium oxide.
4. a kind of aluminum strip based on flakey aluminium pigment according to claim 1, it is characterised in that：The polymer includes
Polyethylene wax (PE waxes), polypropylene wax (PP waxes), ethane-acetic acid ethyenyl copolymerization wax (EVA waxes), oxidized polyethylene wax, acrylic acid
Resin and alkyd resin are one such or a variety of.
5. a kind of aluminum strip based on flakey aluminium pigment according to claim 1, which is characterized in that its production method is such as
Under：
S1, pigment processing：Above-mentioned flakey aluminium pigment is coated into aluminium oxide, organic polymer and inorganic matter successively；
S2, mixed processing：The temperature of mixing machine is adjusted to 25-250 degrees Celsius, by wax, polymer and the flakey wrapped
It is mixed in aluminium pigment input mixing machine, and removes solvent, to obtain mixture；
S3, extruding and discharging：Screw machine is chosen, the temperature of screw machine is then adjusted to 100-250 degrees Celsius, discharging diameter adjustment
To 0.01-8 millimeters, then discharging length adjustment the mixture in S2 is added in screw machine to 0.01-100 millimeters, to
Go out aluminum strip.
6. a kind of aluminum strip based on flakey aluminium pigment according to claim 1,2,3 or 5, it is characterised in that：The squama
Wrappage includes following combination in sheet aluminium pigment：Alumina layer, alumina layer+silicon dioxide layer, alumina layer+polymer
Layer, alumina layer+silicon dioxide layer+polymeric layer, alumina layer+polymeric layer+silicon dioxide layer.
7. a kind of aluminum strip based on flakey aluminium pigment according to claim 5, it is characterised in that：The screw machine is single
Screw machine or dual-screw-stem machine.