CN108384447A - 一种可移印彩色图案型的陶瓷涂料和制备方法 - Google Patents
一种可移印彩色图案型的陶瓷涂料和制备方法 Download PDFInfo
- Publication number
- CN108384447A CN108384447A CN201810133042.0A CN201810133042A CN108384447A CN 108384447 A CN108384447 A CN 108384447A CN 201810133042 A CN201810133042 A CN 201810133042A CN 108384447 A CN108384447 A CN 108384447A
- Authority
- CN
- China
- Prior art keywords
- solution
- pattern type
- ceramic coating
- bat printing
- type ceramic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种可移印彩色图案型的陶瓷涂料和制备方法，其特征在于包括A溶液和B溶液，其中，A溶液由以下重量百分含量的组份组成：硅胶溶液40～50％，粉体填料10～20％，颜料填料5～15％，二氧化硅粉末1～10％，助剂1～5％，其余为溶剂；B溶液由以下成份组成：硅氧烷20～40％，其余为溶剂。
Description
技术领域
本发明涉及化工领域，尤其涉及一种可移印彩色图案型的陶瓷涂料和制备方法。
背景技术
目前水性陶瓷涂料一般有三种，第一种为一般的水性陶瓷涂料，此种常规水性陶瓷涂料无法直接在涂料上面移印水位线，只能打刻印水位线或者不印水位线，第二种是PTFE氟碳涂料，氟改性聚合树脂、颜料、助剂、溶剂等加工而成，此种涂料不环保，涂料一受热，产生一种有毒的气体，变色快，且不安全，遇300℃高温会产生明火、冒浓烟，环境和人体伤害极大，还不节能，烧结温度要在380℃以上，且需要30分钟以上，并且自洁性差，不抗污，第三种是有机硅防锈漆或有机硅喷粉，这种涂料存在不环保，对环境污染大，易氧化，且不耐候，不耐酸，不耐盐，同时也不节能，平时维护费用昂贵，并且不耐温、不阻燃，在180℃以上温度时，会产生明火、浓烟，在50℃以上容易变色、易龟裂，剥落，且表面硬度低，易划伤。
发明内容
本发明公开了一种可移印彩色图案型的陶瓷涂料和制备方法，用以解决现有技术的不足。
为解决上述问题，本发明的技术解决方案是：
一种可移印彩色图案型的陶瓷涂料，其特征在于包括A溶液和B溶液，其中，
A溶液由以下重量百分含量的组份组成：
硅胶溶液40～50％，粉体填料10～20％，颜料填料5～15％，二氧化硅粉末 1～10％，助剂1～5％，其余为溶剂；
B溶液由以下成份组成：
硅氧烷20～40％，其余为溶剂。
所述的硅胶溶液为硅溶胶或铝溶胶。
所述的粉体填料为晶须硅、高岭土、云母粉、沉淀硫酸钡和氧化铝纤维中的一种或多种混合物。
所述的助剂为甲基硅油、羟基硅油、改性硅油中的一种或多种混合物。
所述的颜料填料为钛白粉、云母氧化铁红、钛黄、铁蓝、铁黑、钴黑、铜铬黑、氧化铁红和氧化铁黄中的一种或多种混合物。
所述的硅氧烷为甲基三甲氧基硅烷、甲基三乙氧基硅烷、环氧基硅烷、正硅酸乙酯、甲基二甲氧基硅烷和苯基三甲氧基硅烷中的一种或多种混合物。
所述的溶剂为去离子水、乙醇、异丙醇、丙二醇、乙二醇丁醚、PMA、NMP、丁醇和丙二醇甲醚中的一种或多种混合物。
其制备方法如下：
将B溶液加入A溶液中，用力摇动，再放到滚动机上滚动，滚动机转速设定在120～150转/分钟，滚动时间大于2小时，直至混合的A溶液和B溶液由分层不相融的状态，逐渐反应完全变为完全相融的状态为止，其中,
A溶液的制备方法如下：
(1)、先搅拌硅胶溶液，然后渐渐地往硅胶溶液中添加溶剂并进行搅拌，然后再依次加入粉体填料、颜料填料和二氧化硅粉末；
(2)、用高速分散机分散15分钟；
(3)、用高速研磨机研磨45分钟；
(4)、岩田NK-2杯检测其粘度，流出时间为8～10秒；
(5)、使用300目以上滤网对混合溶液进行过滤；
(6)、使用刮板细度计使混合溶液细度控制在20μm以下。
B溶液的制备方法如下：
(1)、将20～40％的硅氧烷和溶剂混合一起；
(2)、将混合后的溶液放入到滚动机后，并放到有空调的室内，室内温度设定在25℃，控制涂料反应温度为40～50℃。
本发明的有益效果是：
所用的组合材料全部由无机材料组合而成，没有气味、对水资源，空气无污染，对大气没污染，从安全性方面，耐温高400℃，燃烧时没明火，只有很轻微的烟雾，对人体没伤害，柔韧性、硬度高、耐磨性好，硬度能达到5H，风沙等外物不易使其破裂，能在4.5KG压力下能耐磨3000次以上，自洁性好，不粘性强，灰尘、污物粘在表面，不会产生扩散、渗透，只要有风轻轻一吹或有水轻轻一冲，全部还原如新，耐候性好、耐酸、耐盐，不受高温、极寒低温的影响，耐温400°，低温－60°，30年不用维护，不破裂，不变色，可在常温下固化，不需要进行烘烤，既可以进行常温固化，且施工简单，能够适用于淋涂、刷涂、滚涂、空气喷涂、无气喷涂、空气辅助无气喷涂和静电喷涂等施工方式，此水性涂料可直接在涂膜上移印水位线和各种颜色的图案。
附图说明
图1为本发明为时间和温度关系图；
具体实施方式
下面结合附图对本发明的具体实施方式作进一步详细说明。
本发明包括A溶液和B溶液，其中，
A溶液由以下重量百分含量的组份组成：
硅胶溶液40～50％，粉体填料10～20％，颜料填料5～15％，二氧化硅粉末 1～10％，助剂1～5％，其余为溶剂；
B溶液由以下成份组成：
硅氧烷20～40％，其余为溶剂。
所述的硅胶溶液为硅溶胶或铝溶胶。
所述的粉体填料为晶须硅、高岭土、云母粉、沉淀硫酸钡和氧化铝纤维中的一种或多种混合物。
所述的助剂为甲基硅油、羟基硅油、改性硅油中的一种或多种混合物。
所述的颜料填料为钛白粉、云母氧化铁红、钛黄、铁蓝、铁黑、钴黑、铜铬黑、氧化铁红和氧化铁黄中的一种或多种混合物。
所述的硅氧烷为甲基三甲氧基硅烷、甲基三乙氧基硅烷、环氧基硅烷、正硅酸乙酯、甲基二甲氧基硅烷和苯基三甲氧基硅烷中的一种或多种混合物。
所述的溶剂为去离子水、乙醇、异丙醇、丙二醇、乙二醇丁醚、PMA、NMP、丁醇和丙二醇甲醚中的一种或多种混合物。
其制备方法如下：
将B溶液加入A溶液中，用力摇动，再放到滚动机上滚动，滚动机转速设定在120～150转/分钟，滚动时间大于2小时，直至混合的A溶液和B溶液由分层不相融的状态，逐渐反应完全变为完全相融的状态为止，其中,
A溶液的制备方法如下：
(1)、先搅拌硅胶溶液，然后渐渐地往硅胶溶液中添加溶剂并进行搅拌，然后再依次加入粉体填料、颜料填料和二氧化硅粉末；
(2)、用高速分散机分散15分钟；
(3)、用高速研磨机研磨45分钟；
(4)、岩田NK-2杯检测其粘度，流出时间为8～10秒；
(5)、使用300目以上滤网对混合溶液进行过滤；
(6)、使用刮板细度计使混合溶液细度控制在20μm以下。
B溶液的制备方法如下：
(1)、将20～40％的硅氧烷和溶剂混合一起；
(2)、将混合后的溶液放入到滚动机后，并放到有空调的室内，室内温度设定在25℃，控制涂料反应温度为40～50℃。
在实际应用中，此涂料在使用时，基材前准备时，型材的表面不能有任何的粉尘和油污，材料表面60-120目金刚砂喷砂处理，工艺需经过喷底油、底油在80-100℃时进行表面干燥、移印水位线或图案、冷却、喷面油、烘烤固化工艺，在工艺方面，除油和喷砂时，要求工件表面应是洁净的，可以先进行除油处理，在使用60-120目的棕刚玉或白刚玉进行喷砂处理，涂料在配料时，把涂料根据使用工厂的设备，喷枪使用涂料的粘度用稀释剂涂料稀释为设备使用的粘度，并要搅拌使之均匀分散，涂料过滤时采用滤网用300目过滤，把一些粗的结晶体过滤。
流程如下：基材前处理->工件预热(40℃左右)->喷底油->底油表干(100℃左右)->移印->冷却至40℃左右->喷面油->烘干固化(320℃/10Min)，在制作中，需按以下要求进行：
①洗枪建议使用水或酒精；如果之前喷过油性涂料，喷枪必须用酒精充分清洗，但建议喷枪最好不要混用
②喷枪的喷嘴直径：推荐1.0毫米；空气压力：推荐2～4Kgf/cm2。
③因陶瓷涂料粘度较低，沉降快，使用前应充分摇匀，使用时要开启搅拌，喷涂时应将喷枪出气量调小一些，雾化大些，这样漆膜不会流挂且省料。
④注意空压机必须使用油水分离器等过滤装置；底材在喷涂前预热到 40-60℃左右效果较好,具体预热温度应参考室温和施工状态进行调整。
⑤涂装双层涂膜时，先喷底油涂料，喷完底油后100-110℃进行表干，然后进行底油移印，移印后直接喷涂面油涂料，喷底涂时，应以均匀遮盖基材为宜，不宜过薄或过厚，双层厚度一般控制在15-45μm之间。
⑥漆膜烘烤固化以后不能再次喷涂陶瓷涂料，原因是漆膜表面具有良好的疏水不粘性，涂料无法附着。
⑦本涂料为水性，对人体安全无害。喷枪和料桶用毕可用酒精或去离子水清洗，溅到皮肤上用清水即可洗净。若盛装容器水洗有困难，可用乙醇或丙醇清洗。
烘烤固化时的要求如下：
①固化条件：推荐320℃/10min。
②超过以上烘烤时间没有关系，因为涂料一旦成膜，可以长期耐高温，其时间与温度的关系请参考附图1。
上述具体实施方式为本发明的优选实施例，并不能对本发明进行限定，其他的任何未背离本发明的技术方案而所做的改变或其它等效的置换方式，都包含在本发明的保护范围之内。
Claims (8)
1.一种可移印彩色图案型的陶瓷涂料，其特征在于包括A溶液和B溶液，其中，
A溶液由以下重量百分含量的组份组成：
硅胶溶液40～50％，粉体填料10～20％，颜料填料5～15％，二氧化硅粉末1～10％，助剂1～5％，其余为溶剂；
B溶液由以下成份组成：
硅氧烷20～40％，其余为溶剂。
2.根据权利要求1所述的一种可移印彩色图案型的陶瓷涂料，其特征在于：所述的硅胶溶液为硅溶胶或铝溶胶。
3.根据权利要求1所述的一种可移印彩色图案型的陶瓷涂料，其特征在于：所述的粉体填料为晶须硅、高岭土、云母粉、沉淀硫酸钡和氧化铝纤维中的一种或多种混合物。
4.根据权利要求1所述的一种可移印彩色图案型的陶瓷涂料，其特征在于：所述的助剂为甲基硅油、羟基硅油、改性硅油中的一种或多种混合物。
5.根据权利要求1所述的一种可移印彩色图案型的陶瓷涂料，其特征在于：所述的颜料填料为钛白粉、云母氧化铁红、钛黄、铁蓝、铁黑、钴黑、铜铬黑、氧化铁红和氧化铁黄中的一种或多种混合物。
6.根据权利要求1所述的一种可移印彩色图案型的陶瓷涂料，其特征在于：所述的硅氧烷为甲基三甲氧基硅烷、甲基三乙氧基硅烷、环氧基硅烷、正硅酸乙酯、甲基二甲氧基硅烷和苯基三甲氧基硅烷中的一种或多种混合物。
7.根据权利要求1所述的一种可移印彩色图案型的陶瓷涂料，其特征在于：所述的溶剂为去离子水、乙醇、异丙醇、丙二醇、乙二醇丁醚、PMA、NMP、丁醇和丙二醇甲醚中的一种或多种混合物。
8.一种可移印彩色图案型的陶瓷涂料的制备方法，其特征在于制备方法如下：
将B溶液加入A溶液中，用力摇动，再放到滚动机上滚动，滚动机转速设定在120～150转/分钟，滚动时间大于2小时，直至混合的A溶液和B溶液由分层不相融的状态，逐渐反应完全变为完全相融的状态为止，其中,
A溶液的制备方法如下：
(1)、先搅拌硅胶溶液，然后渐渐地往硅胶溶液中添加溶剂并进行搅拌，然后再依次加入粉体填料、颜料填料和二氧化硅粉末；
(2)、用高速分散机分散15分钟；
(3)、用高速研磨机研磨45分钟；
(4)、岩田NK-2杯检测其粘度，流出时间为8～10秒；
(5)、使用300目以上滤网对混合溶液进行过滤；
(6)、使用刮板细度计使混合溶液细度控制在20μm以下。
B溶液的制备方法如下：
(1)、将20～40％的硅氧烷和溶剂混合一起；
(2)、将混合后的溶液放入到滚动机后，并放到有空调的室内，室内温度设定在25℃，控制涂料反应温度为40～50℃。