[go: up one dir, main page]

CN108101578A - 一种用再生环保活性材料制作混凝土砌块的方法 - Google Patents

一种用再生环保活性材料制作混凝土砌块的方法 Download PDF

Info

Publication number
CN108101578A
CN108101578A CN201711404807.1A CN201711404807A CN108101578A CN 108101578 A CN108101578 A CN 108101578A CN 201711404807 A CN201711404807 A CN 201711404807A CN 108101578 A CN108101578 A CN 108101578A
Authority
CN
China
Prior art keywords
active material
environment protecting
composition proportion
protecting active
regenerated environment
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711404807.1A
Other languages
English (en)
Inventor
周云国
周思嘉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhou Yunguo
Original Assignee
Shenzhen Silijia Chemical Engineering Construction Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shenzhen Silijia Chemical Engineering Construction Material Co Ltd filed Critical Shenzhen Silijia Chemical Engineering Construction Material Co Ltd
Priority to CN201711404807.1A priority Critical patent/CN108101578A/zh
Publication of CN108101578A publication Critical patent/CN108101578A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种用再生环保活性材料制作混凝土砌块的方法，利用废弃的混凝土、砖瓦、石膏和灰浆，从建筑垃圾固体废弃物中提取的，经有效处理和深加工而制成含硅质和钙质材料得到生环保活性材料，用建筑废料制造成的再生环保活性材料配制而成的混凝土砌块，采用新的方法能够减少人力，减少劳动强度，提高墙体的制作效率，有效保护环境。

Description

一种用再生环保活性材料制作混凝土砌块的方法
技术领域
本发明涉及混凝土技术领域，尤其涉及一种用再生环保活性材料制作混凝土砌块的方法。
背景技术
众所周知，进入21世纪后，随着经济和相关技术的发展，我国城镇化进程不断加快，人民对居住建筑需求逐年加大，新建建筑的增长对实现城乡人口转移、促进生产要素流动和集聚等方面发挥了重要作用，但也带来了以下问题：一是城市旧城区改造和城镇新区建设产生大量的建筑垃圾，例如废弃混凝土块、废旧砖头等，每年约有35亿吨左右，占到城市垃圾总量的70％以上，垃圾围城现象越来越严重，给城市建筑垃圾清运、填埋土地占用、城市环境污染和城市管理带来严峻的考验；二是随着经济快速发展和人民生活水平的不断提高，人们对建筑工程的质量、安全和节能、环保等方面的要求也越来越高，建筑逐渐向绿色化、环保节能化、舒适化的方向发展，需要新的材料和技术；三是虽然城镇化建设带来众多的就业岗位，但近年来，建筑行业“用工难”问题已显得十分突出，特别是传统手工砌墙，劳动强度大，易产生职业病，技术工人十分紧缺，阻碍了施工的顺利进行。要解决好以上问题，科技创新是必然的、重要的途径。
发明内容
本发明的目的就在于为了解决上述问题而提供一种用再生环保活性材料制作混凝土砌块的方法。
本发明通过以下技术方案来实现上述目的：
本发明包括以下步骤：
S1：收集建筑垃圾、破碎、筛选得到再生环保活性材料；
S2：用一定量的再生环保活性材料、水泥、外加剂和水加入搅拌机制成水泥浆；
S3：用铝粉发泡；
S4：将混凝土料浆用浇注泵浇注入模，利用不同的模具生产不同的制品；
S5：静养2.5小时进行切割，根据客户的不同要求，切出客户需要的不同规格的混凝土砌块；
S6：静养11个小时出来成品，自然养护2-3天即可得到成品的混凝土砌块。
本发明优选地，根据步骤S1，所述筑垃圾包括废弃的混凝土、砖瓦、石膏和灰浆，从建筑垃圾固体废弃物中提取的，经有效处理和深加工而制成含硅质和钙质材料得到生环保活性材料。
本发明优选地，根据步骤S2，所述再生环保活性材料的成份比重为40—70％，所述水泥的成份比重为15—35％，所述外加剂的成份比重为0.5—4％，所述水的成份比重为5—30％
本发明优选地，所述再生环保活性材料的成份比重最佳为60％，水泥的成份比重为最佳23％，所述外加剂的成份比重最佳为2％，所述水的成份比重最佳为15％。
本发明优选地，根据步骤S3，所述铝粉的成份比重为15-30％。
本发明优选地，所述铝粉的成份比重最佳为26.3％。
本发明的有益效果在于：
本发明提供一种用再生环保活性材料制作混凝土砌块的方法，利用建筑垃圾中的有效胶凝成分进行处理和加工，用建筑废料制造成的再生环保活性材料配制而成的混凝土砌块，采用新的方法能够减少人力，减少劳动强度，提高墙体的制作效率，有效保护环境。
具体实施方式
下面对本发明作进一步说明：
本发明包括以下步骤：
S1：收集建筑垃圾、破碎、筛选得到再生环保活性材料；
S2：用一定量的再生环保活性材料、水泥、外加剂和水加入搅拌机制成水泥浆，所述再生环保活性材料的成份比重为40—70％，所述水泥的成份比重为15—35％，所述外加剂的成份比重为0.5—4％，所述水的成份比重为5—30％；
S3：用铝粉发泡，所述铝粉的成份比重为15-30％；
S4：将混凝土料浆用浇注泵浇注入模，利用不同的模具生产不同的制品；
S5：静养2.5小时进行切割，根据客户的不同要求，切出客户需要的不同规格的混凝土砌块；
S6：静养11个小时出来成品，自然养护2-3天即可得到成品的混凝土砌块。
本发明优选地，根据步骤S1，所述筑垃圾包括废弃的混凝土、砖瓦、石膏和灰浆，从建筑垃圾固体废弃物中提取的，经有效处理和深加工而制成含硅质和钙质材料得到生环保活性材料。
实施例一：所述再生环保活性材料的成份比重最佳为60％，水泥的成份比重为最佳23％，所述外加剂的成份比重最佳为2％，所述水的成份比重最佳为15％，所述铝粉的成份比重最佳为26.3％。
综上所述，本发明提供一种用再生环保活性材料制作混凝土砌块的方法，利用建筑垃圾中的有效胶凝成分进行处理和加工，用建筑废料制造成的再生环保活性材料配制而成的混凝土砌块，采用新的方法能够减少人力，减少劳动强度，提高墙体的制作效率，有效保护环境。
本领域技术人员不脱离本发明的实质和精神，可以有多种变形方案实现本发明，以上所述仅为本发明较佳可行的实施例而已，并非因此局限本发明的权利范围，凡运用本发明说明书内容所作的等效结构变化，均包含于本发明的权利范围之内。

Claims (6)

1.一种用再生环保活性材料制作混凝土砌块的方法，其特征在于，包括以下步骤：
S1：收集建筑垃圾、破碎、筛选得到再生环保活性材料；
S2：用一定量的再生环保活性材料、水泥、外加剂和水加入搅拌机制成水泥浆；
S3：用铝粉发泡；
S4：将混凝土料浆用浇注泵浇注入模，利用不同的模具生产不同的制品；
S5：静养2.5小时进行切割，根据客户的不同要求，切出客户需要的不同规格的混凝土砌块；
S6：静养 11 个小时出来成品，自然养护2-3天即可得到成品的混凝土砌块。
2.根据权利要求1所述的一种用再生环保活性材料制作混凝土砌块的方法，其特征在于，根据步骤S1，所述筑垃圾包括废弃的混凝土、砖瓦、石膏和灰浆，从建筑垃圾固体废弃物中提取的，经有效处理和深加工而制成含硅质和钙质材料得到生环保活性材料。
3.根据权利要求1所述的一种用再生环保活性材料制作混凝土砌块的方法，其特征在于，根据步骤S2，所述再生环保活性材料的成份比重为40—70%，所述水泥的成份比重为15—35%，所述外加剂的成份比重为0.5—4%，所述水的成份比重为5—30%。
4.根据权利要求3所述的一种用再生环保活性材料制作混凝土砌块的方法，其特征在于，所述再生环保活性材料的成份比重最佳为60%，水泥的成份比重为最佳23%，所述外加剂的成份比重最佳为2%，所述水的成份比重最佳为15%。
5.根据权利要求1所述的一种用再生环保活性材料制作混凝土砌块的方法，其特征在于，根据步骤S3，所述铝粉的成份比重为15-30%。
6.根据权利要求5所述的一种用再生环保活性材料制作混凝土砌块的方法，其特征在于，所述铝粉的成份比重最佳为26.3%。
CN201711404807.1A 2017-12-22 2017-12-22 一种用再生环保活性材料制作混凝土砌块的方法 Pending CN108101578A (zh)