CN108070757A - A kind of Al-Mg alloy powder - Google Patents
A kind of Al-Mg alloy powder Download PDFInfo
- Publication number
- CN108070757A CN108070757A CN201611019472.7A CN201611019472A CN108070757A CN 108070757 A CN108070757 A CN 108070757A CN 201611019472 A CN201611019472 A CN 201611019472A CN 108070757 A CN108070757 A CN 108070757A
- Authority
- CN
- China
- Prior art keywords
- alloy powder
- calculated
- mass percent
- following component
- surplus
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of Al-Mg alloy powders, are mainly made of the following component being calculated in mass percent：Mg4.6 6.8%, Al77 79%, Ca2.1 2.5%, Mn0.2 0.4%, Si0.2 0.4%, Ni0.08 0.15%, Cu0.5 1.2%, Ti0.1 0.2%, Re0.05 0.1%, Cr0.2 0.4%, Mo0.05 0.08%, Sn0.02 0.04%, Ce0.01 0.015%.The Al-Mg alloy powder of the present invention has many advantages, such as that density is low, intensity is high, good toughness, heat-resistance coefficient are high.
Description
Technical field
The present invention relates to field of preparing metal powder more particularly to a kind of Al-Mg alloy powders.
Background technology
Almag aluminium sheet essential element is aluminium, then mixes a small amount of magnesium or other metal materials to strengthen it firmly
Degree.Using Mg as the aluminium alloy of main adding elements, since its corrosion stability is good, rust-preventing aluminum alloy is also known as.Cause inherently metal,
Heat conductivility and intensity are especially prominent.Requirement of the bicycle in weight is higher and higher in the prior art, and light portable has become
One of essential condition of bicycle, how in the case of proof strength, reducing the weight of vehicle has become an important topic,
And its compressive property is also required to further study.
The content of the invention
In order to solve the above-mentioned technical problem, provide the hard amount of a germplasm light almag, the present invention provides following technical side
Case：
A kind of Al-Mg alloy powder is made of the following component being calculated in mass percent：Mg4.6-6.8%, Al77-79%,
Ca2.1-2.5%, Mn0.2-0.4%, Si0.2-0.4%, Ni0.08-0.15%, Cu0.5-1.2%, Ti0.1-0.2%,
Re0.05-0.1%, Cr0.2-0.4%, Mo0.05-0.08%, Sn0.02-0.04%, Ce0.01-0.015%, surplus are iron.
Further, it is made of the following component being calculated in mass percent：Mg5.8%, Al78%, Ca2.3%,
Mn0.3%, Si0.3%, Ni0.1%, Cu0.8%, Ti0.15%, Re0.075%, Cr0.3%, Mo0.07%, Sn0.03%,
Ce0.012%, surplus are iron.
Further, it is made of the following component being calculated in mass percent：Mg4.6%, Al77%, Ca2.1%,
Mn0.2%, Si0.4%, Ni0.15%, Cu1.2%, Ti0.2%, Re0.1%, Cr0.4%, Mo0.08%, Sn0.04%,
Ce0.015%, surplus are iron.
Further, it is made of the following component being calculated in mass percent：Mg6.8%, Al79%, Ca2.5%,
Mn0.4%, Si0.4%, Ni0.15%, Cu1.2%, Ti0.2%, Re0.1%, Cr0.4%, Mo0.08%, Sn0.04%,
Ce0.015%, surplus are iron.
The beneficial effects of the present invention are：Density is low, hardness is big, excellent thermal conductivity, compressive property are strong, and with acidproof
The characteristics of caustic corrosion, is particularly suitable to be used as cycle hub.
Specific embodiment
Embodiment 1,
A kind of Al-Mg alloy powder is made of the following component being calculated in mass percent：Mg5.8%, Al78%, Ca2.3%,
Mn0.3%, Si0.3%, Ni0.1%, Cu0.8%, Ti0.15%, Re0.075%, Cr0.3%, Mo0.07%, Sn0.03%,
Ce0.012%, surplus are iron.
Embodiment 2,
A kind of Al-Mg alloy powder is made of the following component being calculated in mass percent：Mg4.6%, Al77%, Ca2.1%,
Mn0.2%, Si0.4%, Ni0.15%, Cu1.2%, Ti0.2%, Re0.1%, Cr0.4%, Mo0.08%, Sn0.04%,
Ce0.015%, surplus are iron.
Embodiment 3,
A kind of Al-Mg alloy powder is made of the following component being calculated in mass percent：Mg6.8%, Al79%, Ca2.5%,
Mn0.4%, Si0.4%, Ni0.15%, Cu1.2%, Ti0.2%, Re0.1%, Cr0.4%, Mo0.08%, Sn0.04%,
Ce0.015%, surplus are iron.
Using above-mentioned foundation desirable embodiment of the present invention as enlightenment, by above-mentioned description, relevant staff is complete
Can various changes and amendments be carried out without departing from the scope of the technological thought of the present invention'.This invention it is technical
Scope is not limited to the content on specification, it is necessary to determine its technical scope according to right.
Claims (4)
1. a kind of Al-Mg alloy powder, which is characterized in that be made of the following component being calculated in mass percent：Mg4.6-6.8%,
Al77-79%, Ca2.1-2.5%, Mn0.2-0.4%, Si0.2-0.4%, Ni0.08-0.15%, Cu0.5-1.2%,
Ti0.1-0.2%, Re0.05-0.1%, Cr0.2-0.4%, Mo0.05-0.08%, Sn0.02-0.04%, Ce0.01-
0.015%, surplus is iron.
2. a kind of Al-Mg alloy powder as described in claim 1, it is characterised in that：By the following component group being calculated in mass percent
Into：Mg5.8%, Al78%, Ca2.3%, Mn0.3%, Si0.3%, Ni0.1%, Cu0.8%, Ti0.15%, Re0.075%,
Cr0.3%, Mo0.07%, Sn0.03%, Ce0.012%, surplus are iron.
3. a kind of Al-Mg alloy powder as described in claim 1, it is characterised in that：By the following component group being calculated in mass percent
Into：Mg4.6%, Al77%, Ca2.1%, Mn0.2%, Si0.4%, Ni0.15%, Cu1.2%, Ti0.2%, Re0.1%,
Cr0.4%, Mo0.08%, Sn0.04%, Ce0.015%, surplus are iron.
4. a kind of Al-Mg alloy powder as described in claim 1, it is characterised in that：By the following component group being calculated in mass percent
Into：Mg6.8%, Al79%, Ca2.5%, Mn0.4%, Si0.4%, Ni0.15%, Cu1.2%, Ti0.2%, Re0.1%,
Cr0.4%, Mo0.08%, Sn0.04%, Ce0.015%, surplus are iron.