CN107974177A - A kind of surface of metal product antirusting treating method - Google Patents
A kind of surface of metal product antirusting treating method Download PDFInfo
- Publication number
- CN107974177A CN107974177A CN201711291751.3A CN201711291751A CN107974177A CN 107974177 A CN107974177 A CN 107974177A CN 201711291751 A CN201711291751 A CN 201711291751A CN 107974177 A CN107974177 A CN 107974177A
- Authority
- CN
- China
- Prior art keywords
- metal product
- treating method
- antirusting treating
- paint
- antirusting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of surface of metal product antirusting treating method, it is related to metal product processing technology field, by one layer of antirust paint of surface of metal product brushing；The paint film that the antirust paint that the present invention brushes surface of metal product is formed, with hardness height, damage resistant, strong adhesive force, salt spray resistance, salt water resistance, acid and alkali-resistance, water-fast, oil resistant, ultraviolet light are reusable in old coating surface, paint film will not be caused to damage, superpower paint film flexibility etc..The general paint film service life was up to 58 years.
Description
Technical field
The invention belongs to metal product processing technology field, and in particular to a kind of surface of metal product antirusting treating method.
Background technology
Antirust paint is a kind of coating for the chemistry or electrochemical corrosion for protecting metal surfaces from air, seawater etc..It is main
It is divided into physical and two major class of chemically antirust paint.The former by the Shi Dang Pei He of pigment and paint vehicle, formed the paint film of densification with
Prevent the intrusion of corrosive substance, such as iron oxide red, aluminium powder, graphite antirust paint；Hou person acts on by the chemistry suppression rust of rust resisting pigment, such as
Red lead, zinc chromate anti-rust paint etc..With the antirust of the metals such as what bridge, Chuan Bo, Guanxi roads.Antirust paint is subject to because of it with rust-proof effect
People's pro-gaze, but the noxious material at present contained by antirust paint on the market is numerous, very not environmentally.
The content of the invention
The purpose of the present invention is for it is existing the problem of, there is provided a kind of surface of metal product antirusting treating method.
The present invention is achieved by the following technical solutions：
A kind of surface of metal product antirusting treating method, by one layer of antirust paint of surface of metal product brushing, the antirust paint
It is made by weight of following component：Water alcohol acid lotion 80, double cyclopentenyl ethyoxyl（Methyl）Acrylate 12-15,
Sodium Polyacrylate 3-5, organobentonite 5-8, calcium stearate 1-3, ethanol 12-15, dibutyl phthalate 3-6, aphthenic acids
Manganese 2-8, lead naphthenate 1-3, inositol hexaphosphate 2-4, vegetable oil 3-6, maleic anhydride 0.5-0.8.
Further, solids content is 55% in the water alcohol acid lotion.
Further, the organobentonite is by 800 DEG C of calcining 15min processing.
Further, the bentonite granularity is 1200 mesh.
Further, the vegetable oil is linseed oil.
Further, the dibutyl phthalate and vegetable oil weight part ratio are 1:1.
Further, the thickness of one layer of antirust paint of surface of metal product brushing is 60 μm.
The present invention has the following advantages compared with prior art：The antirust paint shape that the present invention brushes surface of metal product
Into paint film, have hardness height, damage resistant, strong adhesive force, salt spray resistance, salt water resistance, acid and alkali-resistance, water-fast, oil resistant, ultraviolet light,
It is reusable in old coating surface, paint film will not be caused to damage, superpower paint film flexibility etc..The general paint film service life is up to 5-
8 years.
Embodiment
Embodiment 1
A kind of surface of metal product antirusting treating method, by one layer of antirust paint of surface of metal product brushing, the antirust paint
It is made by weight of following component：Water alcohol acid lotion 80, double cyclopentenyl ethyoxyl（Methyl）Acrylate 12, poly- third
Olefin(e) acid sodium 3, organobentonite 5, calcium stearate 1, ethanol 12, dibutyl phthalate 3, manganese naphthenate 2, lead naphthenate 1, flesh
Six phosphate 2 of alcohol, vegetable oil 3, maleic anhydride 0.5.
Further, solids content is 55% in the water alcohol acid lotion.
Further, the organobentonite is by 800 DEG C of calcining 15min processing.
Further, the bentonite granularity is 1200 mesh.
Further, the vegetable oil is linseed oil.
Further, the dibutyl phthalate and vegetable oil weight part ratio are 1:1.
Further, the thickness of one layer of antirust paint of surface of metal product brushing is 60 μm.
Embodiment 2
A kind of surface of metal product antirusting treating method, by one layer of antirust paint of surface of metal product brushing, the antirust paint
It is made by weight of following component：Water alcohol acid lotion 80, double cyclopentenyl ethyoxyl（Methyl）Acrylate 15, poly- third
Olefin(e) acid sodium 5, organobentonite 8, calcium stearate 3, ethanol 15, dibutyl phthalate 6, manganese naphthenate 8, lead naphthenate 3, flesh
Six phosphate 4 of alcohol, vegetable oil 6, maleic anhydride 0.8.
Further, solids content is 55% in the water alcohol acid lotion.
Further, the organobentonite is by 800 DEG C of calcining 15min processing.
Further, the bentonite granularity is 1200 mesh.
Further, the vegetable oil is linseed oil.
Further, the dibutyl phthalate and vegetable oil weight part ratio are 1:1.
Further, the thickness of one layer of antirust paint of surface of metal product brushing is 60 μm.
Embodiment 3
A kind of surface of metal product antirusting treating method, by one layer of antirust paint of surface of metal product brushing, the antirust paint
It is made by weight of following component：Water alcohol acid lotion 80, double cyclopentenyl ethyoxyl（Methyl）Acrylate 13, poly- third
Olefin(e) acid sodium 4, organobentonite 6, calcium stearate 2, ethanol 13, dibutyl phthalate 5, manganese naphthenate 5, lead naphthenate 2, flesh
Six phosphate 3 of alcohol, vegetable oil 5, maleic anhydride 0.7.
Further, solids content is 55% in the water alcohol acid lotion.
Further, the organobentonite is by 800 DEG C of calcining 15min processing.
Further, the bentonite granularity is 1200 mesh.
Further, the vegetable oil is linseed oil.
Further, the dibutyl phthalate and vegetable oil weight part ratio are 1:1.
Further, the thickness of one layer of antirust paint of surface of metal product brushing is 60 μm.
Metallic anti-rust paint performance indicator of the present invention：
1st, paint film color and appearance：Flat smooth, color meet standard jig and aberration scope
2nd, viscosity (23 ± 1 °C of coating -4 viscosity meters, S)：80-120；
3rd, fineness≤50；
4th, drying time (25 °C)：Surface drying 25-30min, does solid work 48h；
5th, pliability mm≤2；
6th, hardness >=2H；
7th, high temperature resistant（130°C）≥450h；
8th, impact resistance 50；
9th, salt spray resistance (120h grades) >=2；
10th, water resistance (29 ± 1 °C of 240h)：It is not blistering, do not fall off；
11st, oil resistant (90# gasoline, 56h)：It is not blistering, do not fall off；
12nd, alkali resistance（GB/T9755-2001）：By 48 it is small when；
13rd, artificial weathering ageing resistance（GB/T9755-2001）：By 1000 it is small when.
Claims (7)
1. a kind of surface of metal product antirusting treating method, it is characterised in that by one layer of antirust of surface of metal product brushing
Paint, the antirust paint are made of following component by weight：Water alcohol acid lotion 80, double cyclopentenyl ethyoxyl（Methyl）Third
Olefin(e) acid ester 12-15, Sodium Polyacrylate 3-5, organobentonite 5-8, calcium stearate 1-3, ethanol 12-15, two fourth of phthalic acid
Ester 3-6, manganese naphthenate 2-8, lead naphthenate 1-3, inositol hexaphosphate 2-4, vegetable oil 3-6, maleic anhydride 0.5-0.8.
A kind of 2. surface of metal product antirusting treating method as claimed in claim 1, it is characterised in that the aqueous alcoholic yogurt
Solids content is 55% in liquid.
A kind of 3. surface of metal product antirusting treating method as claimed in claim 1, it is characterised in that the organobentonite
By 800 DEG C of calcining 15min processing.
A kind of 4. surface of metal product antirusting treating method as claimed in claim 3, it is characterised in that the organobentonite
Granularity be 1200 mesh.
5. a kind of surface of metal product antirusting treating method as claimed in claim 1, it is characterised in that the vegetable oil is Asia
Sesame oil.
A kind of 6. surface of metal product antirusting treating method as claimed in claim 1, it is characterised in that the phthalic acid
Dibutyl ester is 1 with vegetable oil weight part ratio:1.
A kind of 7. surface of metal product antirusting treating method as claimed in claim 1, it is characterised in that the metal product table
The thickness that one layer of antirust paint is brushed in face is 60 μm.