CN107955895A - 一种含Co的平板太阳能铝合金镀层及其制备方法 - Google Patents
一种含Co的平板太阳能铝合金镀层及其制备方法 Download PDFInfo
- Publication number
- CN107955895A CN107955895A CN201711167699.0A CN201711167699A CN107955895A CN 107955895 A CN107955895 A CN 107955895A CN 201711167699 A CN201711167699 A CN 201711167699A CN 107955895 A CN107955895 A CN 107955895A
- Authority
- CN
- China
- Prior art keywords
- aluminum alloy
- alloy coating
- preparation
- epoxy resin
- refining
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种含Co的平板太阳能铝合金镀层及其制备方法，镀层材料由以下质量比例的原料制得：0.8～1.3%Co、0.2～0.3%Ti、10～20%Zn、1～2%Ag、1.5～2.5%Mg、0.65～0.75%La、0.1～0.6%Ce、0.3～0.5%Sc，余量为铝。本发明镀层材料制备方法简单，与基体结合好，不易脱落；制备的铝合金镀层美观，耐腐蚀性和耐磨性好，强度和延展性高，吸热传热能力强。
Description
技术领域
本发明涉及太阳能利用及铝合金镀层技术领域，具体是一种含Co的平板太阳能铝合金镀层及其制备方法。
背景技术
能源利用在人类社会发展中占有举足轻重的地位，但过度的开发资源和低效率的资源利用，使人类面临着严峻的考验。众所周知，太阳能是一种来源最丰富和可广泛获取的可再生能源，对解决能源危机和环境问题具有重大的作用，且太阳能以独具的储量无限性、存在的普遍性、开发利用的清洁性，使其成为了各国竞相研究的热点。
铝合金是工业中应用最广泛的一类有色金属结构材料，在航空、航天、汽车、机械制造、船舶中已大量应用。铝合金重量轻、机械强度高、导电导热性能好。目前，铝合金镀层材料围绕添加多种合金元素来改善镀层的综合性能，采用更多的Al 组分来代替Zn，重点是实现铝的包覆保护能力与锌的牺牲阴极保护能力的最佳结合，并保证以尽可能简单的加工工艺和技术装备，实现镀层的抗剥落、高强度、易加工、易焊接、耐高温度、耐酸碱盐类腐蚀等优良性能于一体。在镀层材料的生产和应用两个环节同时实现减污、降本、增效、提质，是一个急需解决的技术难题。
钴（Co）的物理、化学性质决定了它是生产耐热合金、硬质合金、防腐合金、磁性合金和各种钴盐的重要原料。钴基合金或含钴合金钢用作燃汽轮机的叶片、叶轮、导管、喷气发动机、火箭发动机、导弹的部件和化工设备中各种高负荷的耐热部件以及原子能工业的重要金属材料。
发明内容
针对现有技术的不足，本发明提供了一种含Co的平板太阳能铝合金镀层及其制备方法，本发明镀层材料制备方法简单，与基体结合好，不易脱落；制备的铝合金镀层美观，耐腐蚀性和耐磨性好，强度和延展性高，吸热传热能力强。
一种含Co的平板太阳能铝合金镀层及其制备方法，铝合金镀层材料由以下质量比例的原料制得：0.8～1.3%Co、0.2～0.3%Ti、10～20%Zn、1～2%Ag、1.5～2.5%Mg、0.65～0.75%La、0.1～0.6%Ce、0.3～0.5%Sc，余量为铝。
铝合金镀层的制备方法包括如下步骤：
（1）往熔炼炉中加入铝锭或熔融铝液，加热使之完全融化并在700～800℃下保温；
（2）再按配方比例加入Co、Ti、Zn、Ag、Mg、La、Ce和Sc，搅拌均匀；
（3）然后对合金熔体进行炉内精炼，往合金熔体中加入精炼剂，并搅拌均匀，熔体精炼在封闭环境中完成；
（4）精炼后除渣、除气以及用变质剂NiC3进行处理，得到铝合金镀液；
（5）对太阳能平板基材表面进行清洁处理，向太阳能平板基材表面先均匀喷涂一层薄薄的环氧树脂乳液，晾至七成干，再均匀喷涂铝合金镀液，即可。
所述步骤（3）中精炼剂包括以下重量份数原料：NaCl 25～35%、KCl 25～35%、Na2SiF6 6～10%、K3AlF6 7～12%、K2SO4 4～10%、CaF2 6～10%。
所述步骤（5）中环氧树脂乳液是将环氧树脂溶于二甲苯中所得乳液，环氧树脂层厚度为10～20nm；铝合金镀层的厚度为20～40μm。
本发明的有益效果是：
Co是生产耐热合金、硬质合金、防腐合金、磁性合金和各种钴盐的重要原料；镧（La）和铈（Ce）都是储量丰富的稀土元素，La化学性质活泼，可制作合金，亦可做催化剂；Ce可掺入特种金属里充当合金添加剂；钪（Sc）用于制特种玻璃及轻质耐高温合金等。本发明在熔炼铝合金的时候还加入了精炼剂，所使用的精炼剂进入熔体后能够充分扩散，不吸附团聚，不堵孔；具有高效造干渣能力，不粘滞铝熔体；还具有较高的除气、除渣效率，精炼剂的使用有效地提高了铝合金镀液的质量。本发明在炼制铝合金的过程中还加入了NiC3，NiC3可提高合金的高温强度和体积、尺寸稳定性，并且有利于除渣。本发明镀层材料制备方法简单，与基体结合好，不易脱落；制备的铝合金镀层美观，耐腐蚀性和耐磨性好，强度和延展性高，吸热传热能力强。
具体实施方式
为了更加详细的介绍本发明，下面结合实施例，对本发明做进一步说明。
实施例1
一种含Co的平板太阳能铝合金镀层及其制备方法，铝合金镀层材料由以下质量比例的原料制得：1%Co、0.25%Ti、15%Zn、1.5%Ag、2%Mg、0.7%La、0.3%Ce、0.4%Sc，余量为铝。
铝合金镀层的制备方法包括如下步骤：
（1）往熔炼炉中加入铝锭或熔融铝液，加热使之完全融化并在750℃下保温；
（2）再按配方比例加入Co、Ti、Zn、Ag、Mg、La、Ce和Sc，搅拌均匀；
（3）然后对合金熔体进行炉内精炼，往合金熔体中加入精炼剂，并搅拌均匀，熔体精炼在封闭环境中完成；
（4）精炼后除渣、除气以及用变质剂NiC3进行处理，得到铝合金镀液；
（5）对太阳能平板基材表面进行清洁处理，向太阳能平板基材表面先均匀喷涂一层薄薄的环氧树脂乳液，晾至七成干，再均匀喷涂铝合金镀液，即可。
所述步骤（3）中精炼剂包括以下重量份数原料：NaCl 30%、KCl 30%、Na2SiF6 8%、K3AlF6 10%、K2SO4 7%、CaF2 8%。
所述步骤（5）中环氧树脂乳液是将环氧树脂溶于二甲苯中所得乳液，环氧树脂层厚度为15nm；铝合金镀层的厚度为30μm。
实施例2
一种含Co的平板太阳能铝合金镀层及其制备方法，铝合金镀层材料由以下质量比例的原料制得：0.8%Co、0.2%Ti、10%Zn、1%Ag、1.5%Mg、0.65%La、0.1%Ce、0.3%Sc，余量为铝。
铝合金镀层的制备方法包括如下步骤：
（1）往熔炼炉中加入铝锭或熔融铝液，加热使之完全融化并在700℃下保温；
（2）再按配方比例加入Co、Ti、Zn、Ag、Mg、La、Ce和Sc，搅拌均匀；
（3）然后对合金熔体进行炉内精炼，往合金熔体中加入精炼剂，并搅拌均匀，熔体精炼在封闭环境中完成；
（4）精炼后除渣、除气以及用变质剂NiC3进行处理，得到铝合金镀液；
（5）对太阳能平板基材表面进行清洁处理，向太阳能平板基材表面先均匀喷涂一层薄薄的环氧树脂乳液，晾至七成干，再均匀喷涂铝合金镀液，即可。
所述步骤（3）中精炼剂包括以下重量份数原料：NaCl 25%、KCl 25%、Na2SiF6 6%、K3AlF6 7%、K2SO4 4%、CaF2 6%。
所述步骤（5）中环氧树脂乳液是将环氧树脂溶于二甲苯中所得乳液，环氧树脂层厚度为10nm；铝合金镀层的厚度为40μm。
实施例3
一种含Co的平板太阳能铝合金镀层及其制备方法，铝合金镀层材料由以下质量比例的原料制得：1.3%Co、0.3%Ti、20%Zn、2%Ag、2.5%Mg、0.75%La、0.6%Ce、0.5%Sc，余量为铝。
铝合金镀层的制备方法包括如下步骤：
（1）往熔炼炉中加入铝锭或熔融铝液，加热使之完全融化并在800℃下保温；
（2）再按配方比例加入Co、Ti、Zn、Ag、Mg、La、Ce和Sc，搅拌均匀；
（3）然后对合金熔体进行炉内精炼，往合金熔体中加入精炼剂，并搅拌均匀，熔体精炼在封闭环境中完成；
（4）精炼后除渣、除气以及用变质剂NiC3进行处理，得到铝合金镀液；
（5）对太阳能平板基材表面进行清洁处理，向太阳能平板基材表面先均匀喷涂一层薄薄的环氧树脂乳液，晾至七成干，再均匀喷涂铝合金镀液，即可。
所述步骤（3）中精炼剂包括以下重量份数原料：NaCl 35%、KCl 35%、Na2SiF6 10%、K3AlF6 12%、K2SO4 10%、CaF2 10%。
所述步骤（5）中环氧树脂乳液是将环氧树脂溶于二甲苯中所得乳液，环氧树脂层厚度为20nm；铝合金镀层的厚度为20μm。
为了便于参考，本申请人对实施例1、实施例2和实施例3所得铝合金镀层的部分性能进行了检测对比，结果见下表：
由表可知，本发明的铝合金镀层的耐磨性、耐高温性好，附着力强，耐酸碱腐蚀性能优异，光透射率高、反射率低，光吸收效果好。
Claims (4)
1.一种含Co的平板太阳能铝合金镀层，其特征在于，所述铝合金镀层材料由以下质量比例的原料制得：0.8～1.3%Co、0.2～0.3%Ti、10～20%Zn、1～2%Ag、1.5～2.5%Mg、0.65～0.75%La、0.1～0.6%Ce、0.3～0.5%Sc，余量为铝。
2.根据权利要求1所述含Co的平板太阳能铝合金镀层，其特征在于，所述铝合金镀层的制备方法包括如下步骤：
（1）往熔炼炉中加入铝锭或熔融铝液，加热使之完全融化并在700～800℃下保温；
（2）再按配方比例加入Co、Ti、Zn、Ag、Mg、La、Ce和Sc，搅拌均匀；
（3）然后对合金熔体进行炉内精炼，往合金熔体中加入精炼剂，并搅拌均匀，熔体精炼在封闭环境中完成；
（4）精炼后除渣、除气以及用变质剂NiC3进行处理，得到铝合金镀液；
（5）对太阳能平板基材表面进行清洁处理，向太阳能平板基材表面先均匀喷涂一层薄薄的环氧树脂乳液，晾至七成干，再均匀喷涂铝合金镀液，即可。
3.根据权利要求2所述铝合金镀层的制备方法，其特征在于，所述步骤（3）中精炼剂包括以下重量份数原料：NaCl 25～35%、KCl 25～35%、Na2SiF6 6～10%、K3AlF6 7～12%、K2SO4 4～10%、CaF2 6～10%。
4.根据权利要求2所述铝合金镀层的制备方法，其特征在于，所述步骤（5）中环氧树脂乳液是将环氧树脂溶于二甲苯中所得乳液，环氧树脂层厚度为10～20nm；铝合金镀层的厚度为20～40μm。