CN107793881A - A kind of coating protection materials and preparation method thereof - Google Patents
A kind of coating protection materials and preparation method thereof Download PDFInfo
- Publication number
- CN107793881A CN107793881A CN201711041698.1A CN201711041698A CN107793881A CN 107793881 A CN107793881 A CN 107793881A CN 201711041698 A CN201711041698 A CN 201711041698A CN 107793881 A CN107793881 A CN 107793881A
- Authority
- CN
- China
- Prior art keywords
- parts
- mixture
- protection materials
- proportioning
- coating protection
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
This application discloses a kind of coating protection materials and preparation method thereof, its floating coat protection materials, including following raw material：Palm wax, zinc stearate, microwax, tea-seed oil, triethanolamine, Tween 80, polysorbas20, gum arabic powder, diatomite, butyl hydroxybenzoate, methyl hydroxybenzoate, ethylparaben, organobentonite, Lauxite, Tissuemat E, EEA resins, haloflex, chlorinated polypropylene, water soluble amino resin, alkyd resin, propane diols, deionized water, OP 10, OP 4.The application coating protection materials do not paint sense, exactly like ancient technique of waxing, are with the passing of time conserved with wax, furniture is not lost the refined gas of natural gloss, and feel is gentle, produce a kind of sensation for exactly liking bag slurry.The application provide coating protection materials be resistant to 100 DEG C of boiling water pour it is boiling hot and non-discolouring do not highlight, do not stay any vestige；Later period maintenance is also extremely convenient and simple, repairs with effect as before.
Description
Technical field
The application belongs to field of material technology, and in particular to a kind of coating protection materials and preparation method thereof.
Background technology
Woodwork and other products in the market needs to brush the material of maintenance, and material therefor has various paint, gathered
Ester paint, aqueous wood wax oil lacquer.First, above material is more containing formaldehyde, benzene, dimethylbenzene or other harmful chemical compositions
Or heavy metal.Secondly, complex process is cumbersome, it is necessary to be equipped with various process equipments and years of work in process for above-mentioned material
The technical staff of experience.3rd, the coating result processed with above-mentioned material has thick paint sense, having one's hair waved that To Be Protected from Heat, it is difficult to repair
It is multiple, lose original nature, the gas permeability of material and natural refined gas.Therefore, if being adopted for top-grade furnitures such as solid wood furnitures
Can be because being difficult to make user be satisfied with losing the gas of original nature with above-mentioned material making coatings, and later stage reparation is cumbersome, more
It is difficult to reply original effect.Especially refined gas, nature, environmental protection, the painting without a paint sense are required now with quite a few people
Layer so that the improvement of coating material becomes more important.
Coating best at present is also that optimal coating is ancient technique of waxing, without the paint sense of a tiny bit, day
Bag slurry is formed long, is the more naturally refined gas of household gloss, feel is gentle, more long more beautiful.But this ancient technology
Property it is strong, technique is cumbersome, and time-consuming, it is difficult to grasps, it is necessary to which high labour cost, adds cost；In addition, it also there is waterproof
Property is poor, more fears the drawbacks of hot water.
The content of the invention
In view of drawbacks described above of the prior art or deficiency, it is expected to provide a kind of coating protection materials and preparation method thereof.
In a first aspect, the application provides a kind of coating protection materials, including following raw material：
10-20 parts palm wax, 20-40 parts zinc stearate, 10-20 parts microwax, 15-30 parts tea-seed oil, the second of 10-50 parts three
Hydramine, 15-30 parts Tween 80,10-20 parts polysorbas20,50-100 parts gum arabic powder, 20-60 parts diatomite, 15-30 parts
Butyl hydroxybenzoate (butyl p-hydroxybenzoate), 10-25 parts methyl hydroxybenzoate, 10-30 parts ethylparaben, 20-50 parts are organic
(ethylene-ethylacrylate is copolymerized for bentonite, 20-50 parts Lauxite, 20-60 parts Tissuemat E, 80-160 part EEA resins
Thing), 20-60 parts haloflex, 50-100 parts chlorinated polypropylene, 150-300 parts water soluble amino resin, 50-100 part alcohol
Acid resin, 50-80 parts propane diols, 200-400 parts deionized water, 60-120 parts OP-10 (octyl phenol -10), 50-100 parts
OP-4 (octyl phenol phenol -4).
Second aspect, the application provide a kind of woodwork, metallic article or stone coated with above-mentioned coating protection materials
Material product.
The third aspect, the application provide a kind of preparation method of above-mentioned coating protection materials, comprised the following steps：
(1) palm wax, microwax, tea-seed oil are heated up to 75-85 DEG C by proportioning mixing, obtain mixture I；
(2) zinc stearate, triethanolamine, Tween 80 are heated up to 27-33 DEG C by proportioning mixing, obtain mixtures II；
(3) butyl hydroxybenzoate, methyl hydroxybenzoate, ethylparaben, propane diols are heated up to 18-22 DEG C by proportioning mixing,
Obtain mixtures III；
(4) it is the 30-40% of arabia gum powder, deionized water total amount is brewed by matching, obtain mixture IV；
(5) Tissuemat E, Lauxite are mixed by the 30-40% of proportioning plus deionized water total amount and is heated up to 32-38
DEG C, stir evenly to obtain mixture V；
(6) it is diatomite, organobentonite is brewed by the 30-40% of proportioning plus deionized water total amount, obtain mixture VI；
(7) EEA resins, haloflex, chlorinated polypropylene are stirred evenly by proportioning, obtains mixture VII；
(8) water soluble amino resin, alkyd resin are heated up to 23-27 DEG C by proportioning, stir evenly to obtain mixture VIII；
(9) OP-10, OP-4 are stirred evenly by proportioning to obtain mixture IX；
(10) by mixture I, mixtures II, mixture VI inputs together, 55-65 DEG C is heated up to, stirs evenly and is mixed
Thing X；
(11) mixtures III, mixture IV, mixture V are put into mixture X, stirs evenly to obtain mixture X I；
(12) mixture VII, mixture VIII, mixture IX are put into mixture X I, temperature control 60 DEG C-
Between 65 DEG C, 1-1.5h is persistently stirred, gets product coating protection materials.
The application has the advantages and positive effects of：Because the application is using as above technical scheme, coating protection materials
Sense is not painted, exactly likes ancient technique of waxing, is with the passing of time conserved with wax, furniture is not lost the refined gas of natural gloss, feel is gentle, production
A kind of raw sensation for exactly liking bag slurry.In addition, the coating protection materials that the application provides do not need senior skilled worker and process equipment, behaviour
It is simple to make technique, is easily mastered, construction safety, health environment-friendly, workmen and user will not be damaged.Through testing,
The application provide coating protection materials be resistant to 100 DEG C of boiling water pour it is boiling hot and non-discolouring do not highlight, do not stay any vestige；Later period maintenance
Also it is extremely convenient and simple, repair with effect as before.
Except the technical problem of the application described above solution, form the technical characteristic of technical scheme and by these
Outside advantage caused by the technical characteristic of technical scheme, wrapped in other technologies problem that the application can solve, technical scheme
Advantage caused by the other technical characteristics contained and these technical characteristics, will hereinafter be described in further detail.
Embodiment
The application is described in further detail with reference to embodiment.It is understood that tool described herein
Body embodiment is used only for explaining related invention, rather than the restriction to the invention.It should be noted that in situation about not conflicting
Under, the feature in embodiment and embodiment in the application can be mutually combined.
Following raw materials are commercially available prod unless otherwise stated.
Embodiment 1
The present embodiment provides a kind of coating protection materials, including following raw material：
15g palm waxs, 30g zinc stearates, 15g microwaxes, 20g tea-seed oils, 30g triethanolamines, 25g Tween 80s, 15g are told
Temperature 20,80g gum arabic powders, 40g diatomite, 25g butyl hydroxybenzoates, 20g methyl hydroxybenzoates, 20g ethylparabens, 30g
Organobentonite, 35g Lauxites, 40g Tissuemat Es, 120gEEA resins, 40g haloflexes, 80g chlorinated polypropylenes,
220g water soluble amino resins, 80g alkyd resins, 60g propane diols, 300g deionized waters, 90gOP-10,80gOP-4.
The preparation method of above-mentioned coating protection materials, comprises the following steps：
(1) palm wax, microwax, tea-seed oil are heated up to 80 DEG C by proportioning mixing, obtain mixture I；
(2) zinc stearate, triethanolamine, Tween 80 are heated up to 30 DEG C by proportioning mixing, obtain mixtures II；
(3) butyl hydroxybenzoate, methyl hydroxybenzoate, ethylparaben, propane diols are heated up to 20 DEG C by proportioning mixing, obtained
Mixtures III；
(4) it is arabia gum powder, 100g deionized waters is brewed by matching, obtain mixture IV；
(5) Tissuemat E, Lauxite are heated up to 35 DEG C by proportioning plus 100g deionized waters, stir evenly to obtain mixture V；
(6) it is diatomite, organobentonite is brewed by proportioning plus remaining 100g deionized waters, obtain mixture VI；
(7) EEA resins, haloflex, chlorinated polypropylene are stirred evenly by proportioning, obtains mixture VII；
(8) water soluble amino resin, alkyd resin are heated up to 25 DEG C by proportioning, stir evenly to obtain mixture VIII；
(9) OP-10, OP-4 are stirred evenly by proportioning to obtain mixture IX；
(10) by mixture I, mixtures II, mixture VI inputs together, 60 DEG C are heated up to, stirs evenly to obtain mixture X；
(11) mixtures III, mixture IV, mixture V are put into mixture X, stirs evenly to obtain mixture X I；
(12) mixture VII, mixture VIII, mixture IX are put into mixture X I, temperature control 60 DEG C-
Between 65 DEG C, 1-1.5h is persistently stirred, gets product coating protection materials.
Above-mentioned coating protection materials are used for woodwork, such as wood furniture；It can also be used for other materials surface, such as metal system
Product.The present embodiment also provides woodwork, metallic article, stone product coated with above-mentioned coating protection materials.
Embodiment 2
The present embodiment provides a kind of coating protection materials, including following raw material：
10g palm waxs, 20g zinc stearates, 20g microwaxes, 15g tea-seed oils, 10g triethanolamines, 15 Tween 80s, 10g are told
Warm 20,50 gum arabic powders, 20 diatomite, 15g butyl hydroxybenzoates, 10g methyl hydroxybenzoates, 30g ethylparabens, 20g have
Machine bentonite, 20g Lauxites, 20g Tissuemat Es, 80g EEA resins, 20g haloflexes, 50g chlorinated polypropylenes,
150g water soluble amino resins, 50g alkyd resins, 50g propane diols, 200g deionized waters, 60g OP-10,50g OP-4.
The preparation method of above-mentioned coating protection materials, comprises the following steps：
(1) palm wax, microwax, tea-seed oil are heated up to 75 DEG C by proportioning mixing, obtain mixture I；
(2) zinc stearate, triethanolamine, Tween 80 are heated up to 27 DEG C by proportioning mixing, obtain mixtures II；
(3) butyl hydroxybenzoate, methyl hydroxybenzoate, ethylparaben, propane diols are heated up to 18-22 DEG C by proportioning mixing,
Obtain mixtures III；
(4) it is arabia gum powder, 80g deionized waters is brewed by matching, obtain mixture IV；
(5) Tissuemat E, Lauxite are heated up to 32 DEG C by proportioning plus 60g deionized waters, stir evenly to obtain mixture V；
(6) it is diatomite, organobentonite is brewed by proportioning plus 60g deionized waters, obtain mixture VI；
(7) EEA resins, haloflex, chlorinated polypropylene are stirred evenly by proportioning, obtains mixture VII；
(8) water soluble amino resin, alkyd resin are heated up to 23 DEG C by proportioning, stir evenly to obtain mixture VIII；
(9) OP-10, OP-4 are stirred evenly by proportioning to obtain mixture IX；
(10) by mixture I, mixtures II, mixture VI inputs together, 55 DEG C are heated up to, stirs evenly to obtain mixture X；
(11) mixtures III, mixture IV, mixture V are put into mixture X, stirs evenly to obtain mixture X I；
(12) mixture VII, mixture VIII, mixture IX are put into mixture X I, temperature control at 60 DEG C,
1.5h is persistently stirred, gets product coating protection materials.
Above-mentioned coating protection materials are used for woodwork, such as wood furniture；It can also be used for other materials surface, such as metal system
Product.The present embodiment also provides woodwork, metallic article, stone product coated with above-mentioned coating protection materials.
Embodiment 3
The present embodiment provides a kind of coating protection materials, including following raw material：
20g palm waxs, 40g zinc stearates, 10g microwaxes, 30g tea-seed oils, 50g triethanolamines, 30g Tween 80s, 20g are told
Temperature 20,100g gum arabic powders, 60g diatomite, 30g butyl hydroxybenzoates, 25g methyl hydroxybenzoates, 10g ethylparabens,
50g organobentonites, 50g Lauxites, 60g Tissuemat Es, 160g EEA resins, 60g haloflexes, 100g chlorinations gather
Propylene, 300g water soluble amino resins, 100g alkyd resins, 80g propane diols, 400g deionized waters, 120g OP-10,100g
OP-4。
The preparation method of above-mentioned coating protection materials, comprises the following steps：
(1) palm wax, microwax, tea-seed oil are heated up to 85 DEG C by proportioning mixing, obtain mixture I；
(2) zinc stearate, triethanolamine, Tween 80 are heated up to 33 DEG C by proportioning mixing, obtain mixtures II；
(3) butyl hydroxybenzoate, methyl hydroxybenzoate, ethylparaben, propane diols are heated up to 22 DEG C by proportioning mixing, obtained
Mixtures III；
(4) it is arabia gum powder, 120g deionized waters is brewed by matching, obtain mixture IV；
(5) Tissuemat E, Lauxite are heated up to 38 DEG C by proportioning plus 140g deionized waters, stir evenly to obtain mixture V；
(6) it is diatomite, organobentonite is brewed by proportioning plus remaining 140g deionized waters, obtain mixture VI；
(7) EEA resins, haloflex, chlorinated polypropylene are stirred evenly by proportioning, obtains mixture VII；
(8) water soluble amino resin, alkyd resin are heated up to 27 DEG C by proportioning, stir evenly to obtain mixture VIII；
(9) OP-10, OP-4 are stirred evenly by proportioning to obtain mixture IX；
(10) by mixture I, mixtures II, mixture VI inputs together, 65 DEG C are heated up to, stirs evenly to obtain mixture X；
(11) mixtures III, mixture IV, mixture V are put into mixture X, stirs evenly to obtain mixture X I；
(12) mixture VII, mixture VIII, mixture IX are put into mixture X I, temperature control at 65 DEG C,
1h is persistently stirred, gets product coating protection materials.
Above-mentioned coating protection materials are used for woodwork, such as wood furniture；It can also be used for other materials surface, such as metal system
Product.The present embodiment also provides woodwork, metallic article, stone product coated with above-mentioned coating protection materials.
Comparative example 1
Protection of waxing is carried out to wood furniture using tradition technique of waxing.
By above-described embodiment 1, the gained coating protection materials of embodiment 2 coated on wood furniture, the gained layer of embodiment 3 is protected
Protective material together carries out visual inspection with comparative example 1 after drying and boiling water pours boiling hot detection coated on wire netting；Wherein boiling water
Pour to scald and be detected as directly carrying out pouring boiling hot 30s to coating surface using 100 DEG C of boiling water, detected whether discoloration after drying, highlighted, be
It is no to have vestige.Testing result is as shown in table 1.
The testing result of table 1
As it can be seen from table 1 coating protection materials obtained by each embodiment of the application are coated in woodwork or other product tables
Face, products obtained therefrom appearance are felt without paint, can reach and be waxed the same or like effect of technique with tradition；Waxed technique phase with tradition
Than, the resistance to boiling water of the application pours boiling hot performance and significantly improved, 100 DEG C of boiling water pour scald after it is non-discolouring, do not highlight, do not have vestige residual.
Above description is only the preferred embodiment of the application and the explanation to institute's application technology principle.People in the art
Member should be appreciated that invention scope involved in the application, however it is not limited to the technology that the particular combination of above-mentioned technical characteristic forms
Scheme, while should also cover in the case where not departing from the inventive concept, carried out by above-mentioned technical characteristic or its equivalent feature
The other technical schemes for being combined and being formed.Such as features described above have with (but not limited to) disclosed herein it is similar
The technical scheme that the technical characteristic of function is replaced mutually and formed.
Claims (3)
1. a kind of coating protection materials, it is characterised in that including following raw material：
10-20 parts palm wax, 20-40 parts zinc stearate, 10-20 parts microwax, 15-30 parts tea-seed oil, the ethanol of 10-50 parts three
Amine, 15-30 parts Tween 80,10-20 parts polysorbas20,50-100 parts gum arabic powder, 20-60 parts diatomite, 15-30 parts Ni Bo
Golden butyl ester, 10-25 parts methyl hydroxybenzoate, 10-30 parts ethylparaben, 20-50 parts organobentonite, 20-50 part ureaformaldehyde ureaformaldehydes
Resin, 20-60 parts Tissuemat E, 80-160 part EEA resins, 20-60 parts haloflex, 50-100 parts chlorinated polypropylene,
150-300 parts water soluble amino resin, 50-100 parts alkyd resin, 50-80 parts propane diols, 200-400 parts deionized water, 60-
120 parts of OP-10,50-100 part OP-4.
2. a kind of woodwork, metallic article or stone product coated with coating protection materials as claimed in claim 1.
3. a kind of preparation method of coating protection materials as claimed in claim 1, it is characterised in that comprise the following steps：
(1) palm wax, microwax, tea-seed oil are heated up to 75-85 DEG C by proportioning mixing, obtain mixture I；
(2) zinc stearate, triethanolamine, Tween 80 are heated up to 27-33 DEG C by proportioning mixing, obtain mixtures II；
(3) butyl hydroxybenzoate, methyl hydroxybenzoate, ethylparaben, propane diols are heated up to 18-22 DEG C by proportioning mixing, obtained
Mixtures III；
(4) it is the 30-40% of arabia gum powder, deionized water total amount is brewed by matching, obtain mixture IV；
(5) Tissuemat E, Lauxite are mixed by the 30-40% of proportioning plus deionized water total amount, is heated up to 32-38 DEG C, stirs
It is even to obtain mixture V；
(6) it is diatomite, organobentonite is brewed by the 30-40% of proportioning plus deionized water total amount, obtain mixture VI；
(7) EEA resins, haloflex, chlorinated polypropylene are stirred evenly by proportioning, obtains mixture VII；
(8) water soluble amino resin, alkyd resin are heated up to 23-27 DEG C by proportioning, stir evenly to obtain mixture VIII；
(9) OP-10, OP-4 are stirred evenly by proportioning to obtain mixture IX；
(10) by mixture I, mixtures II, mixture VI inputs together, 55-65 DEG C is heated up to, stirs evenly to obtain mixture X；
(11) mixtures III, mixture IV, mixture V are put into mixture X, stirs evenly to obtain mixture X I；
(12) mixture VII, mixture VIII, mixture IX are put into mixture X I, temperature control 60 DEG C -65 DEG C it
Between, 1-1.5h is persistently stirred, gets product coating protection materials.